碳纳米管负载TiO2对1,2,4-三氯苯的光降解研究

碳纳米管负载TiO2复合光催化剂与纳米TiO2光催化剂对1,2,4-三氯苯的光催化降解效果,及降解动力学的研究结果表明,复合光催化剂比纳米TiO2有更好的光催化降解效果,经254 nm紫外光辐照60 min后,使用复合光催化剂的1,2,4-三氯苯降解了70%,而使用纳米TiO2为催化剂的1,2,4-三氯苯仅降解了51%...     

MWNTs/TiO2对典型氯苯类化合物的光催化降解研究

研究复合光催化剂MWNTs/TiO2对典型氯苯类有机化合物光催化降解动力学及主要光降解路径.结果表明,同一初始浓度和相同光催化降解实验条件下,60min时典型氯苯类有机化合物的光降解率均达到90%以上.其中六氯苯和五氯苯的光催化降解速率常数分别为0.0664h-1和0.0670h-1,其大小明显高于其它氯苯类化合物.1,二氯苯的光催化降解反应速率常数仅为0.0430h4--1,在典型氯苯类化合物中最小.三氯苯的3种同分异构体——1,3-三氯苯、24-三氯苯和1,5-三氯苯的光催化降解速率常数分别为0.0547h2,1,,3,-1、0445h0.-1和0.0439h-1.六氯苯的主要光催化降解路径为:HCB→PeCB→1,2,3,5-TeCB→1,2,4-TCB→1,4-DCB.     

纳米复合GeO2/TiO2的制备及光催化性能研究

采用改进的Sol-gel方法,制备了一种新型的单分散椭球形微孔结构的纳米GeO2/TiO2复合光催化剂,并用TG-DTA、XRD、XPS、UV-vis、FT-IR、TEM、BET等手段进行了表征.以难生化降解的染料罗丹明B为目标降解物,采用HPLC测定不同光照时间下催化剂对染料降解的情况,考察了催化剂的光催化活性结果表明,改进的Sol-gel法制得的复合光催化剂具有明显的孔结构,而且比表面积大、粒径小、粒径分布窄、分散性好;与适量GeO2复合后能够有效提高TiO2纳米粒子的光催化活性;复合光催化剂的最佳制备条件为GeO2摩尔含量为0.1%,煅烧温度为400℃,所制得的GeO2/TiO2光催化活性比纯TiO2有显著提高.     

WC/TiO2纳米复合界面光催化剂制备及其光催化降解酚类污染物研究

设计并制备了新型WC/TiO2纳米复合界面光催化剂应用于酚类污染物的光催化降解反应中.采用X射线衍射(XRD)和扫描电子显微镜(SEM)技术分析了WC/TiO2纳米复合界面光催化剂的晶型和表面形貌.结果显示锐钛矿型TiO2纳米颗粒均匀地分散在WC纳米球表面并很好地构筑了WC/TiO2界面.研究了不同WC负载比例的WC/TiO2光催化剂在模拟太阳光照射下降解苯酚的光催化性能.结果表明:WC/TiO2复合界面的形成可以有效地提高TiO2光催化降解性能;其中,3%WC/TiO2(质量分数)光催化降解苯酚的活性最高.利用紫外-可见光谱(UV-Vis)和高效液相色谱-质谱联用技术(HPLC-MS)分析了WC/TiO2纳米复合界面光催化剂降解苯酚的中间产物,提出了苯酚在WC/TiO2界面上可能的降解机理.     

Fe3+、Ce3+掺杂TiO2光催化降解气相二苯并呋喃

以气相二苯并呋喃为研究对象,考察了在TiO2、Ce3+/TiO2和Fe3+/TiO2 3种不同光催化剂作用下,反应物初始浓度、湿度、气体循环速率和光强等因素对间歇式光催化反应速率的影响,并建立了估算和测定二苯并呋喃光催化反应常数和Langmuir吸附常数的数学模型和方法.结果表明,Fe3+和Ce3+掺杂修饰TiO2光催化剂后,提高了对二苯并呋喃的光催化降解活性,其中Fe3+/TiO2光催化活性最高;随着二苯并呋喃初始浓度的增大,其光催化降解速率也随之增大;适量的水蒸气存在可以促进二苯并呋喃的降解,但当水蒸气过量后,反而阻碍二苯并呋喃光催化降解;随着气体循环速率加快和光强的增大,二苯并呋喃光催化降解初始速率也随之增大;TiO2、Ce3+/TiO2和Fe3+/TiO2光催化降解二苯并呋喃反应速率常数k分别为34.54×10-5、36.23×10-5和37.95×10-4mg.(min.m2)-1.     

RGO/TiO2光催化降解2,4-二氯苯氧乙酸研究

通过Hummers法及紫外光/热还原工艺制得还原氧化石墨烯(RGO),采用溶胶-凝胶-煅烧法,以RGO和钛酸酊脂为前驱体制备出RGO/TiO2光催化复合材料,并利用XRD、FT-IR等对其进行了表征.对RGO/TiO2光催化降解性能的研究发现,复合光催化剂RGO/TiO2对2,4-二氯苯氧乙酸(2,4-D)的光催化降解活性显著优于纯TiO2,并且发现负载量和pH值对光催化降解性能有较大的影响:RGO/TiO2投加量为1.2g·L~(-1)、RGO负载量2%、pH为3、初始浓度为50 mg·L~(-1)反应12 h,2,4-D去除率达到98.75%;2,4-D降解率随着RGO/TiO2投加量的增大先增大后减小;RGO/TiO2对2,4-D的降解为脱氯还原和催化氧化过程,产生氯酚、苯酚等中间产物.     

石墨烯/二氧化钛降解亚甲基蓝的研究

以钛酸丁酯和氧化石墨烯为前驱物,通过水热法制备石墨烯/二氧化钛(GR/TiO2)复合光催化剂。采用XRD、TEM和FT-IR等技术手段对GR/TiO2粉体的结构和形貌进行了表征。利用对亚甲基蓝光催化降解,考察了GR/TiO2的光催化降解能力,并研究了H2O2用量和p H等因素对光催化降解速率的影响。结果表明:复合催化剂中,TiO2为锐钛型晶体,粒径为25 nm左右,分散在薄纱状的石墨烯上;复合催化剂通过紫外光下光催化性能有所提高,对可见光产生响应,具有良好的稳定性;加入适量H2O2能提高反应速率,碱性条件下,对亚甲基蓝的降解效率更高。     

活性炭纤维负载纳米La-S/TiO_2光催化降解苯酚的研究

采用浸涂-焙烧法合成了活性炭纤维负载纳米La-S/TiO2复合光催化剂,并用扫描电子显微镜(SEM)对其表面形貌和结构变化进行了表征分析。在λ>400 nm的可见光光照下,考察了其对苯酚溶液的光催化降解能力。结果表明:负载型La-S/TiO2复合光催化剂比纳米La-S/TiO2光催化剂对苯酚具有更强的降解能力,苯酚的降解是在自由基的作用下进行的,经历了先形成不稳定的活性中间体,然后直接开环降解成脂肪酸等低分子量的化合物,接着被深度氧化的过程。     

TiO2-石墨烯（Gn）复合材料光催化降解O3研究

通过改性Hummer法及溶胶凝胶法,制备出TiO2-石墨烯光催化复合材料.经吸附-光催化活性实验选出光催化活性最高的含C量为1.5%(质量分数)的TiO2-石墨烯复合材料,并在自行设计的模拟大型客机环境的气相光催化反应器中,进行O3光催化降解实验研究.结果表明,TiO2-石墨烯复合光催化材料在较短时间内对O3有较高的降解效率,且其光催化活性显著优于纯TiO2材料.初始O3浓度为(0.150～0.200)×10-6时,复合光催化剂受紫外光激发60 min的光催化降解率为66.12%,初始O3浓度为(0.950～1.000)×10-6时,其光催化降解率约为77%,较低浓度时((0.100～0.150)×10-6),O3去除率也能达到45.45%.此外,通过探讨光催化材料的重复使用性能,表明复合光催化剂重复使用4次以内,其对O3的光催化降解率保持基本稳定.     

TiO2光催化降解水中内分泌干扰物17β-雌二醇

以低压汞灯为光源,采用间歇式光氧化反应器,研究了17β-雌二醇(E2)在纳米TiO2(Degussa P-25)悬浆体系中的光催化降解.考察了溶液pH、E2初始浓度、TiO2光催化剂投加量、UV光强、H2O2、O2对E2光催化降解的影响.结果表明,TiO2光催化工艺可以有效地去除水中的E2,E2的光降解过程符合一级反应动力学模型;TiO2投加量为200 mg/L时,在14 W低压汞灯照射下,初始浓度为400 μg/L的E2在自来水中的光降解一级反应速率常数为0.018 min-1,E2的光催化降解速率常数与其初始浓度、TiO2光催化剂的用量、溶液的pH值、UV光强等因素有关;外加H2O2、O2可以影响催化剂的光降解效率.     

Enhanced photocatalytic activity of fish scale loaded TiO2 composites under solar light irradiation

Fish scale (FS) loaded TiO₂ composites were investigated as photocatalysts in degradation of Methyl Orange under solar light irradiation. Composites were prepared through sol-gel method by varying mass ratio of TiO₂/FS at 90:10, 70:30 and 50:50, respectively. The catalysts prepared in this study were characterized by using XRD, SEM, FT-IR and nitrogen sorption. The effects of solar irradiation, mass ratio of TiO₂/FS composites, irradiation time and catalyst loadings were studied. Synergistic effect was found in TiO₂/FS of 90:10 composite which performed higher photocatalytic degradation than synthesized TiO₂ under solar light irradiation. However, further increasing fish scale content in the composites reduced the photocatalytic activity drastically. Under solar light irradiation, all the catalysts in this study exhibited photocatalytic activity, except TiO₂/FS of 50:50 composite that only acted as a weak biosorbent without performing any photocatalytic property. Photocatalytic degradation increased with increasing catalyst loading and irradiation time but decreased with increased of initial dye concentration.     

Visible light responsive N-F-codoped TiO2 photocatalysts for the degradation of 4-chlorophenol

Visible light responsive N-F-codoped TiO₂ photocatalysts exhibit a higher catalytic activity than N-doped TiO₂ for the degradation of 4-chlorophenol due to the synergistic effect of nonmetal elements.     

铜卟啉修饰In2TiO5纳米带的制备及其光催化性能

以5,10,15,20-四苯基铜卟啉（CuTPP）和5-（4-氨基苯基）-10,15,20-三苯基铜卟啉（CuAPTPP）为敏化剂,采用溶剂热法成功制备了铜卟啉敏化In₂TiO₅复合光催化剂.利用紫外、FT-IR、XRD、SEM、UV-vis DRS和N₂吸附脱附曲线对所得铜卟啉及复合光催化剂进行表征和分析.结果表明,铜卟啉负载于In₂TiO₅纳米带表面,复合光催化剂的禁带宽度及比表面积出现一定程度的减小,但未改变In₂TiO₅的晶型及形貌.其中,CuTPP敏化In₂TiO₅复合光催化剂的光催化活性最强,在模拟太阳光的照射下,120 min时罗丹明B（RhB）的降解率高达98.9%,而In₂TiO₅纳米带对RhB的降解率仅为33.5%,且循环使用5次后其光催化降解率仍保持在95%以上.     

TiO2诱导下左旋氧氟沙星的可见光降解及其机制

左旋氧氟沙星是一种新型污染物.单一的左旋氧氟沙星(LFV)和Ti O2无可见光响应,但二者共存下左旋氧氟沙星能发生显著的可见光降解.为此研究Ti O2用量、溶液p H以及左旋氧氟沙星浓度对Ti O2/Vis(可见光)降解左旋氧氟沙星的影响及机制.结果表明,左旋氧氟沙星能吸附在Ti O2表面,吸附服从准二级吸附动力学和Langmuir吸附等温线.吸附左旋氧氟沙星的Ti O2漫反射UV-Vis光谱进一步表明二者形成表面复合物.左旋氧氟沙星的Ti O2/Vis降解动力学符合LangmuirHinshelwood方程.合适的Ti O2浓度和中性p H有利于光解过程的进行.自由抑制实验、N2保护下左旋氧氟沙星的Ti O2/Vis降解实验揭示·O-2是该过程中的主要活性物种.同时,无氧左旋氧氟沙星-Ti O2悬浮液光照不同时间的UV-Vis光谱证明体系中存在电子向Ti O2导带的注入.依据实验结果提出吸附在Ti O2表面的左旋氧氟沙星与Ti O2形成表面复合物,在可见光照下发生电子迁移,从而引发左旋氧氟沙星降解.本研究表明利用污染与Ti O2形成表面复合物诱导其可见光降解可用来去除水中某些有机污染物.     

TiO2复合催化剂弱光催化降解模拟海水中苯酚及其催化活性的影响

为了获得适用于海水中有机污染物光降解催化剂,分别选用纳米SiO_2粒子和氧化石墨烯GO为载体,利用吸附相反应技术并结合热处理过程制备了基于TiO_2的复合催化剂,研究了弱光(光强小于1mW·cm~(-3))激发下复合催化剂光催化降解模拟海水中苯酚.结果表明,吸附相反应技术结合焙烧得到的La~(3+)掺杂TiO_2-SiO_2,表面亲水性较强和对苯酚吸附能力较弱,难以克服盐离子的干扰并有效降解模拟海水中高浓度苯酚.而吸附相反应技术结合醇溶剂热还原处理后,La~(3+)掺杂TiO_2-SiO_2催化剂表面亲水性显著减弱,但该催化剂在模拟海水中不能形成稳定的悬浮体系.吸附相反应技术得到的TiO_2-GO和La~(3+)掺杂TiO_2-GO中,TiO_2粒子粒径小于10nm且均匀负载于GO的表面.醇溶剂热还原处理可使TiO_2形成晶型结构,从而提高其催化活性,同时还能将GO表面的含氧基团还原,降低催化剂表面亲水性.从而提升催化剂对苯酚的吸附能力和对盐离子的抗干扰能力.另外,还原GO与小粒径TiO_2粒子紧密结合,使光生电子能很快转移至还原GO表面,增大光生电荷分离率,进一步提升催化剂的光降解性能.     

不同光源下TiO2/ACF同时脱硫脱硝实验研究

实验室制备了负载型二氧化钛光催化剂TiO₂/ACF,利用自行设计的光催化反应器,在紫外和可见2种光源下进行了同时脱硫脱硝试验,确定了最佳的试验条件,比较了2种不同光源下的脱除效率.结果表明,烟气中氧含量、反应温度、烟气含湿量、光照强度等是影响光催化的主要因素,在紫外光源的照射下,负载型TiO₂/ACF光催化剂脱除SO₂和NO的效率分别达到99.7%和64.3%,在可见光源的照射下,负载型TiO₂/ACF光催化剂脱除SO₂和NO的效率分别达到97.5%和49.6%, 5次平行试验结果表明,平行数据的标准偏差S较小.通过反应后吸收液的离子色谱分析,推测了2种不同光源下同时脱硫脱硝的反应机制.     

可见光响应漂浮式微球光催化剂及其光降解模拟海水中苯酚

为了将光催化技术应用于有机物污染海水的治理,本文首先利用水热还原得到了具有可见光响应的还原商用P25光催化剂,而后将还原后的P25作为活性组分负载在透明的有机玻璃空心微球表面,制成漂浮式微球光催化剂.还原后的P25的表征结果表明,水热条件下金属还原作用会将P25中少量Ti~(4+)还原成Ti~(3+),同时催化剂表面还形成了无序化-内部结晶的核壳结构.这两种结构变化都会显著拓展还原P25催化剂的可见光响应.含苯酚模拟污染海水的光降解实验发现,降解低浓度苯酚时,漂浮型微球光催化剂显示了优异的降解效率,降解5 h的去除率达到了95%以上.由于还原P25光催化剂的稳定性并且漂浮式微球光催化剂能简易回收,在多次重复实验中微球光催化剂都可以保持较高的催化活性.     

C3N4/BiOBr复合可见光催化剂的性能及其作用机制

利用水热合成法制备了C_3N_4/BiOBr复合可见光催化剂,通过XRD、FT-IR、SEM、DRS、PL等手段对催化剂的物相组成和光化学性能进行了系统表征,利用对罗丹明B(RhB)的降解实验评价了催化剂在可见光照下的光催化降解活性和稳定性并通过ESR分析和自由基捕获实验探究了RhB的光催化降解机制.结果表明,水热合成法可成功制备结晶性能良好的C_3N_4/BiOBr复合可见光催化剂;C_3N_4的复合降低了BiOBr光催化剂的电子-空穴的复合,提高了光催化降解活性,其中15%C_3N_4/BiOBr的活性最佳,可见光照18 min后RhB的脱色率达100%,较纯BiOBr提高了1.5倍,且重复使用5次后仍具有较高的光催化降解活性;复合催化剂光催化降解RhB过程中参与降解的主要活性物种为空穴(h~+)和超氧自由基(·O_2~-),其中h~+影响更为显著.     

TiO2表面沉积Ag粒子及其可见光下降解含盐废水中的苯酚

为了制备可见光激发下能高效降解含盐废水中有机物的光催化剂,首次以商用TiO_2光催化剂(P25)为载体,利用吸附相反应技术一步获得了Ag沉积的可见光响应复合光催化剂.同时,通过XPS、TEM、HRTEM及紫外可见漫反射光谱图,结合多种高含盐水体系中苯酚的光催化降解过程,研究了不同Ag沉积对催化剂可见光活性的影响.结果发现,吸附平衡后P25表面富含水的吸附层可作为反应和粒子的生成场所,生成量子尺寸的Ag粒子.另外,在吸附层中生成的Ag粒子均匀分布于P25表面并与之紧密结合,并在TiO_2晶格结构中引入晶格交错结构.Ag与TiO_2的表面等离子体共振效应和晶格交错结构共同提升了催化剂的可见光响应和电荷的分离效率,增强了催化剂对苯酚的可见光催化性能.在含盐废水体系中,盐离子数量越多,催化剂在可见光下降解苯酚过程受到的干扰越大.