30CrMnSiNi2A超强钢激光熔覆修复试验研究

目的研究激光熔覆技术,解决30CrMnSiNi2A钢制部件表面腐蚀、划伤、裂纹等缺陷的修复问题。方法利用光纤激光器在30CrMnSiNi2A钢表面进行同基体相近成分的合金粉末熔覆试验,优化激光熔覆工艺参数,开展熔覆层的微观组织、硬度、力学性能等方面试验研究,并对拉伸试样的断口进行分析。结果熔覆层与基体呈现牢固的冶金结合,基体热影响区域小,熔覆区的抗拉强度大于基体强度的80%,熔覆区材质的脆性较基材有所增加。结论激光熔覆可用于修复30CrMnSiNi2A钢制零件表面的腐蚀、划伤、裂纹等局部缺陷。     

模拟高低空交变环境下30CrMnSiNi2A钢力学性能研究

目的研究30CrMnSiNi2A钢制腔体的力学性能影响及演化规律。方法借助高低温低气压试验和中性盐雾试验交替进行,模拟高低空交替变化的腐蚀环境。通过比较静力拉伸试验和疲劳试验的结果,进一步揭示预腐蚀对静力拉伸性能和疲劳性能的影响。结果经过预腐蚀处理,30CrMnSiNi2A钢制腔体的力学抗拉强度下降了0.73%,规定塑延伸强度上升了0.04%,断后伸长率下降了0.95%。疲劳寿命数据与对数疲劳寿命数据均符合正态分布,未发生明显变化。结论高低空交变环境下,腔体内部会发生一定程度的腐蚀,但由于腐蚀程度较小,对30CrMnSiNi2A钢力学性能影响不大。     

提高深盲孔壳类零件温冲压模具寿命的措施

采用合理的模具结构、选择合适的模具材料、采用适宜的热处理工艺和表面强化工艺以及提高模具的加工质量等都可以显著提高温冲压模具的使用寿命。分析了超高强度钢制深盲孔壳体温冲压成形时,模具的工作条件及其失效形式,提出了能有效提高该壳体温冲压模具寿命的具体措施。     

JH125端面齿轮挤压工艺与模具简介

介绍125端面齿轮挤压工艺、模具设计,通过冷挤压、开式温挤压、闭式温挤压工艺试验和小批量生产,选择了适合批量生产、综合效益较好的JH125端面齿轮闭式温挤压工艺。     

腐蚀对30CrMnSiNi2A钢结构疲劳寿命的影响

采用周期浸润加速腐蚀试验与疲劳试验相结合的方法,研究了腐蚀及腐蚀与疲劳交替作用对某型飞机30CrMnSiNi2A机翼主梁疲劳寿命的影响.结果表明,腐蚀环境的影响会引起30CrMnSiNi2A高强度结构钢的疲劳寿命明显降低.与未腐蚀状态相比,预腐蚀5、10、15天后,某型飞机机翼主梁模拟件的平均疲劳寿命分别下降了17.3%、20.5%、33.2%;而在腐蚀与疲劳交替作用下,其平均疲劳寿命下降了22.8%.在给定的腐蚀环境和疲劳载荷谱作用下,平均疲劳寿命N50随预腐蚀时间t的变化可以用N50=1044.541-219.978t描述.     

空调机用黄铜三通阀的温挤压成形数值模拟

提出一种新的精密温挤压成形工艺代替传统热锻法来制造空调用三通阀。建立了该三通阀温挤压有限元分析模型,采用非线性有限元分析软件DEFORM-3D^TM对三通阀温挤压成形的过程进行了数值模拟,揭示了其塑性成形的机理,以及工艺参数对充填情况的影响规律,进一步获得了合理的温挤压工艺参数。     

基于正交试验的拉深旋压制杯工艺参数研究

对杯形毛坯的旋压成形工艺进行了研究,以期获得最佳的工艺参数。首先采用正交试验的方法,对旋压杯形毛坯的关键工艺参数进行分析;然后采用综合平衡分析法对工艺参数组合进行了优化,最后通过实际的旋压试验对所获得的优化工艺参数组合进行了验证。结果表明,采用综合平衡分析进行的工艺参数优化,可以制造出能够满足后续内齿轮旋压要求的杯形毛坯。     

240活塞铝裙等温挤压工艺条件的选用及特点

介绍了变形温度、应变速率、润滑剂的使用对LDll等温挤压的影响,在240活塞铝裙等温挤压生产中对上述工艺参数进行了选用及控制;同时就该件等温挤压工艺的特点与热模锻工艺进行了初步比较.     

长尾锥齿轮坯的温挤压

一、前言所谓“温挤压”就是把金属加热到相变点以下的某一合适温度时进行的挤压。它兼有冷、热挤压的优点。温挤压为成形工艺开创了新的途径。例如我们的试件为18Cr2Ni4WA钢,其常温强度如表1所示,为常用冷挤钢的1.6—2倍,大大超出了模具的承载能力,故以采用温挤压最为适宜。     

铝包钢丝拉拔工艺设计与试验

选用连续挤压包覆法生产的铝包钢丝毛坯，采用强制润滑拉拔技术进行拉拔试验研究。通过试验、比较筛选了适合铝包铜丝拉拔的耐温耐压润滑剂。在对铝包钢丝拉拔工艺进行合理设计的基础上，拉制出了产品。对产品的机械性能和电性能进行了测试，并对断口进行了扫描电镜的观察。结果表明，双金属的结合性能良好,各项性能指标均达到相关标准。这一试验研究对铝包钢丝的生产有指导意义。     

奥氏体不锈钢铸造管坯的热挤压试验研究

介绍了一种新的奥氏体不锈钢无缝管材制备工艺 ,即对空心铸坯直接热挤压制备荒管。通过对铸坯热挤压荒管的组织与性能的实验研究 ,表明新工艺可获得组织和性能均与传统工艺水平相当的不锈钢荒管 ,但工艺流程缩短 ,生产成本降低。     

方头柱塞冷挤镦工艺及模具设计

分析了硬铝合金方头柱塞件的冷挤镦工艺 ,设计了方头柱塞冷挤镦件图 ,计算及选用了毛坯形状及尺寸 ,验算了许可变形程度 ,选择了冷成形用的设备 ,拟制了冷挤镦工艺前的毛坯处理并设计了方头柱塞冷挤镦模具结构。     

复杂多台阶空心零件复合挤压变形的控制

在为用挤压工艺生产快门壳而进行的工艺试验中,为了控制这种复杂多台阶空心零件复合挤压正、反挤方向的变形量,采用了改变润滑条件和凹模圆角的工艺措施,得到了预期的效果.从而为确定类似空心零件挤压生产工艺参数提供了一种简便而行之有效的方法.     

圆柱直齿轮温挤压精密成形工艺研究

采用温挤压精密成形技术,成功地研制出直齿圆柱齿轮零件,理论和实验证明,新工艺具有优质高效节材节能的特点,非常适合圆柱直齿轮,特别是大模数齿轮的精密成形。     

The effect of growth rate and ageing on colour variation of European pond turtles

Many chelonians have colourful dots, patches and stripes throughout their body that are made up, at least in part, of carotenoids. Therefore, turtles are very suitable models to study the evolution and functionality of carotenoid-based colouration. Recent studies suggested a close link between colouration and immune system in these taxa. However, more research is needed to understand the role of these colourful stripes and patches in turtle visual signalling. The purpose of this study was to explore the relationship between growth rate and colouration in European pond turtles. In particular, we wanted to answer the question of whether there is a trade-off between growth and colour expression. We also aimed to explore the effect of body size and age on colour variation. Turtles from a reintroduction-breeding program were recaptured, weighed and measured over an 8-year period to estimate their growth rates and age. We also measured with a spectrometer the reflectance of colour patches in two different body parts: shell and forelimb. We found that turtles with a faster growth rate had brighter limb stripes independently of their age. On the other hand, shell colouration was related to body size with larger turtles having brighter shell stripes and higher values of carotenoid chroma. Our results suggest that fast-growers may afford to express intense colourful limb stripes likely due to their higher intake of carotenoids that would modulate both growth and colour expression. However, shell colouration was related to body size probably due to ontogenetic differences in the diet, as juveniles are strictly carnivorous while adults are omnivorous. Alternatively, shell colouration might be involved in crypsis as the shell is visually exposed to predators.     

核桃壳生物炭对土壤中镉的钝化修复

通过室内模拟试验,研究了核桃壳生物炭（BC400、BC500、BC600）对人工Cd污染土壤（20 mg/kg）pH、Cd赋存形态分布的影响,并探究可能的修复机理。结果显示:经56 d修复后,与空白对照组相比,10%添加量的核桃壳生物炭BC400、BC500、BC600分别使土壤pH升高了1.07、1.31、1.38,弱酸可提取态Cd含量减少了17.02%、20.20%、24.53%,可还原态Cd含量减少了8.9%、19.1%、38.2%,可氧化态Cd含量增加了44.83%、78.45%、100%,残渣态Cd含量增加了66.03%、71.43%、89.21%。同时,土壤pH与土壤中弱酸可提取态Cd含量呈显著负相关（P<0.01）。综上,核桃壳生物炭能够对Cd污染土壤起到钝化修复作用。     

采用Washburn动态法研究水处理滤料的亲油亲水性

用Washbum动态法研究了核桃壳、磁铁矿和陶粒砂滤料的亲油亲水性，并对其表面结构进行了表征．结果表明，用Washburn动态法研究水处理滤料润湿性的实验重复性较好，实验方法可行．实验测得核桃壳、磁铁矿和陶粒砂的亲油亲水比（LHR）依次为76．41、1．057和0.8769，说明核桃壳滤料的亲油性很好，而磁铁矿和陶粒砂滤料表现了更好的亲水性．与SEM、EDS、FTIR分析结果一致，核桃壳、磁铁矿和陶粒砂滤料表面亲油亲水性的差别主要归因于其表面物理化学结构的不同．     

聚能罩挤压成形工艺研究

介绍聚能罩挤压成形的工艺过程、变形特点,分析了挤压件尺寸精度的变化规律以及变形程度与机械性能的关系.     

考虑脉动压力相关性的自由体随机振动分析

目的获得自由体在脉动压力载荷作用下的结构响应。方法采用有限元方法,建立锥壳自由体结构的随机振动分析有限元模型,根据自由体的脉动压力载荷和随机振动分析理论,计算自由体在脉动压力下的加速度响应均方根值。结果载荷为一定程度相关时的计算结果在完全相关和不相关之间,最小相差约15%,最大相差约50%。结论在进行自由体结构脉动压力下的响应分析时,载荷间的相关性是不能忽略的,分区加载可改善计算精度。     

可压缩材料挤压过程有限元模拟

利用QFORM通用有限元软件对可压缩材料挤压过程进行了数值模拟 ,研究了初始相对密度对等效应变和挤压力、挤压比对致密速度和挤压力的影响 ,同时 ,通过对平面应变和轴对称各种挤压工况进行模拟分析 ,给出了两种状态单位挤压力间的关系