Isolation and Characterization of Nanocrystalline Cellulose from Totally Chlorine Free Oil Palm Empty Fruit Bunch Pulp

Nanocrystalline cellulose (NCC) was isolated from a totally chlorine free (TCF) bleached oil palm empty fruit bunch (OPEFB) pulp via acid hydrolysis using a 58 % sulfuric acid concentration and ultrasonic treatment. The effects of acid concentration and hydrolysis time were investigated. Characterization of OPEFB–NCC was carried out using TEM, FTIR, ¹³C-NMR, XRD, zeta potential and TGA. The optimal hydrolysis time was 80 min as indicated by the leveling off of the OPEFB–NCC dimensions (length 150 nm and diameter 6.5 nm) with no significant loss of crystallinity at this point. The presence of a shoulder peak at 1231 cm^?1 (assigned to a sulfate group) in the FTIR spectrum of NCC is indicative of a successful esterification. This is further corroborated by the ¹³C-NMR analysis whereby the distinct C4 amorphous and crystalline peaks present in OPEFB–TCF pulp had almost disappeared and the cluster of signals for C2, C3, C5, and a well separated signal of C6 had merged into one single peak in the OPEFB–NCC sample. These observations allude to most of the amorphous region having been removed and to the strong possibility of sulfonation having not only occurred on the C6, but also on C2 and C3. OPEFB–NCC isolated over shorter hydrolysis time was more thermally stable; however, the char fraction decreases with hydrolysis time despite having a higher zeta potential. The results of this investigation demonstrate that NCC can be produced from pulp made by chlorine free environmentally benign processes with ensuing savings in energy and chemicals.     

Hybrid Composites Made from Oil Palm Empty Fruit Bunches/Jute Fibres: Water Absorption,Thickness Swelling and Density Behaviours

In this research, hybrid composite materials were prepared from combination of oil palm Empty fruit bunches (EFB) fibre and jute fibre as reinforcement, epoxy as polymer matrix. This study intended to investigate the effect of jute fiber hybridization and different layering pattern on the physical properties of oil palm EFB-Epoxy composites. Water absorption and thickness swelling test reveal that hybrid composite shows a moderate water absorption which is 11.20% for hybrid EFB/Jute/EFB composite and 6.08% for hybrid Jute/EFB/Jute composite. The thickness swelling and water absorption of the hybrid composites slightly increased as the layering pattern of hybrid composites changed. Hybrid composites are more water resistance and dimensional stable compare to the pure EFB composites. This is attributed to the more hydrophilic nature of EFB composites. Hybridization of oil palm EFB composites with jute fibres can improve the dimensional stability and density of pure EFB and Jute fibre reinforced composites has higher density of 1.2 g/cm³ compared to all other composites.     

Preparation and Fundamental Characterization of Cellulose Nanocrystal from Oil Palm Fronds Biomass

The objective of this work was to isolate cellulose nanocrystal (CNC) from oil palm fronds (Elaeis guineensis) and its subsequent characterization. Isolation involves sodium hydroxide/anthraquinone pulping with mechanical refining followed by total chlorine free bleaching (includes oxygen delignification, hydrogen peroxide oxidation and peracetic acid treatment) before acid hydrolysis. Bleaching significantly decreased kappa number and increased α-cellulose percentage of fibers as confirmed by Technical Association of the Pulp and Paper Industry standards. Transmission electron microscopy (TEM), X-ray diffraction, Fourier transform infrared spectroscopy and thermogravimetric analysis revealed that acid hydrolysis along with bleaching improved crystallinity index and thermal stability of the extracted nanocrystals. It was observed that CNC maintained its cellulose 1 polymorph despite hydrolysis treatment. Mean diameter as observed by TEM and average fiber aspect ratio of obtained CNC was 7.44 ± 0.17 nm and 16.53 ± 3.52, respectively making it suitable as a reinforcing material for nanocomposite.     

Properties of Poly(Vinyl Alcohol)/Chitosan Nanocomposite Films Reinforced with Oil Palm Empty Fruit Bunch Amorphous Lignocellulose Nanofibers

The objective of this study was to investigate the properties of poly(vinyl alcohol)/chitosan nanocomposite films reinforced with different concentration of amorphous LCNFs. The properties analyzed were morphological, physical, chemical, thermal, biological, and mechanical characteristics. Oil palm empty fruit bunch LCNFs obtained from multi-mechanical stages were more dominated by amorphous region than crystalline part. Varied film thickness, swelling degree, and transparency of PVA/chitosan nanocomposite films reinforced with amorphous part were produced. Aggregated LCNFs, which reinforced PVA/chitosan polymer blends, resulted in irregular, rough, and uneven external surfaces as well as protrusions. Based on XRD analysis, there were two or three imperative peaks that indicated the presence of crystalline states. The increase in LCNFs concentration above 0.5% to PVA/chitosan polymer blends led to the decrease in crystallinity index of the films. A noticeable alteration of FTIR spectra, which included wavenumber and intensity, was obviously observed along with the inclusion of amorphous LCNFs. That indicated that a good miscibility between amorphous LCNFs and PVA/chitosan polymer blend generated chemical interaction of those polymers during physical blending. Reinforcement of PVA/chitosan polymer blends with amorphous LCNFs influenced the changes of T_g (glass transition temperature), T_m (melting point temperature), and T_max (maximum degradation temperature). Three thermal phases of PVA/chitosan/LCNFs nanocomposite films were also observed, including absorbed moisture evaporation, PVA and chitosan polymer backbone structural degradation and LCNFs pyrolysis, and by-products degradation of these polymers. The addition of LCNFs 0.5% had the highest tensile strength and the addition of LCNFs above 0.5% decreased the strength. The incorporation of OPEFB LCNFs did not show anti-microbial and anti-fungal properties of the films. The addition of amorphous LCNFs 0.5% into PVA/chitosan polymer blends resulted in regular and smooth external surfaces, enhanced tensile strength, increased crystallinity index, and enhanced thermal stability of the films.     

Extraction of Cellulose Nanocrystals from Phormium tenax Fibres

Cellulose nanocrystals with an acicular structure ranged from 100 to 200 nm in length and 15 nm in width were extracted from Phormium tenax leaf fibres by acid hydrolysis. A two-step procedure for the extraction of nano-sized cellulose was studied and the obtained nanocrystals were characterized using morphological investigations (optical, scanning electron and atomic force microscopy), as well as physico-chemical characterization by Wide Angle X-ray Scattering, infrared spectroscopy and thermogravimetric analysis. A study of birefringence properties was also performed. The first chemical treatment leads to the production of holocellulose by the gradual removal of lignin, while the subsequent sulphuric acid hydrolysis process allows obtaining cellulose nanocrystals in an aqueous suspension. The results reported support the repeatability and the effectiveness of the procedure performed. Moreover, the high cellulose content of P. tenax fibre and their declining market interest, suggest the interest of this investigation and the possibility to use natural fibres for the production of a reinforcement phase to involve in the nanocomposite approach for industrial applications.     

Poly(lactic acid)/Cellulose Composites Obtained from Modified Cotton Fibers by Successive Acid Hydrolysis

This work is focused on the hydrolysis of cotton fibers from waste textiles to obtain micro and nanofibers to be used as reinforcements in polymer composites. To promote their compatibility with polymeric matrix, hydrolyzed cotton fibers were surface modified with various silane compounds. Thus, these fibers were mixed with commercial poly(lactic acid) (PLA) at 5% w/w loading by melt compounding. Acid treatments caused a decrease of the crystallinity index whereas the thermal stability was significantly improved, especially for cellulose fibers hydrolyzed in two steps. Morphological analysis revealed a reduction of the fibers diameter and a decrease of their length as a consequence of the hydrolysis. NMR analysis confirmed the silanization of the fibers by reaction with the silane agent. Tensile tests revealed that silanization treatments were able to increase the composite Young’s modulus and the stress at break with respect to the neat matrix, indicating that silanization improved the polymer/fiber compatibility interfacial adhesion. The overall results demonstrated that applying suitable surface modification strategies, waste cotton textiles can be effectively recycled as fillers in polymer based composites.     

Nanocomposites of Waterborne Polyurethane Reinforced with Cellulose Nanocrystals from Sisal Fibres

Cellulose nanocrystals (CNC) were isolated from sisal fibres and were incorporated in the form of an aqueous suspension to a waterborne polyurethane (WBPU) synthesized from components derived from natural sources using an aliphatic diisocyanate. Transparent nanocomposite films with different CNC contents were prepared using a casting method. The morphology, thermal behaviour and mechanical properties of the nanocomposite films were characterized. Homogeneous distribution of CNC in the WBPU, even at high CNC contents was observed, resulting in an increase of 100% in modulus for systems with 5 and 10 wt% of CNC, with high elongations around 650%.     

Diethylenetriaminepentaacetic Acid (DPTA)-modified Magnetic Cellulose Nanocrystals can Efficiently Remove Pb(II) from Aqueous Solution

Journal of Polymers and the Environment - Surface modification of cellulose nanocrystals (CNC) is essential for improving their reactivity and adsorption capacity. Oxidation, as a conventional...     

Extraction and Characterization of Microcrystalline Cellulose from Date Palm Fibers using Successive Chemical Treatments

Journal of Polymers and the Environment - The aim of present study is to extract microcrystalline cellulose (MCC) from fruit bunch branches fibers of Algerian date palm trees (phoenix dactylifera...     

萃取法回收钛白水解废酸中的硫酸

提出了以三异辛胺作萃取剂、H2O作反萃取剂从钛白水解废酸中萃取回收硫酸的新工艺。考察了萃取剂浓度、相调节剂浓度、相比及温度对萃取和反萃取的影响，并进行了模拟试验。在以40％三异辛胺、25％仲辛醇和35％航空煤油(均为质量分数)为萃取有机相，相比为2，以H2O为反萃剂，相比为1．5的条件下，质量浓度为146．02g/L的废酸经8级萃取和6级反萃取，硫酸回收率达到91．81％，产品酸质量浓度达119．73g/L。     

用棉籽油皂脚制备棉籽油甲酯

以002CR型阳离子交换树脂为催化剂,在固定床反应器中用高酸值棉籽油皂脚制备棉籽油甲酯,考察了各种因素对酯化反应的影响。实验结果表明,在甲醇与脂肪酸摩尔比为2、反应温度为60℃、停留时间为80min的条件下,酯化率为94．67％。工业化生产中可选用经脱水处理后的工业甲醇为原料,以降低生产成本。所得棉籽油甲酯的收率为90％,主要性能指标基本达到美国生物柴油标准要求。     

餐饮泔水油及废动植物油下脚料深加工利用大有可为--介绍<国家级科技成果重点推广计划>高效益环保项目“利用餐饮泔水油及废动植物油生产油酸、甘油、硬脂酸”新工艺

综述了我国的餐饮泔水油及废油脂资源浪费、破坏环境现状,对比介绍了新工艺显著的经济及环保效益.     

Optimal Design of Ozone Bleaching Parameters to Approach Cellulose Nanofibers Extraction from Sugarcane Bagasse Fibers

Cellulose nanofibers (CNFs) were isolated from sugarcane bagasse (SCB) through the combination of bio-refinery, sulfur-free, and totally chlorine free (TCF) chemo-mechanical pretreatments, with a focus on the optimal design of ozone bleaching parameters based on a response surface methodology (RSM). For this purpose, the most effective parameters in ozone bleaching (temperature, time, and pulp consistency) were set between 40 and 85 °C, 60 and 360 min, and 1–5 wt%, respectively. High-performance liquid chromatography (HPLC), Fourier transform infrared spectroscopy (FTIR), Kappa number, and scanning electron microscopy (SEM) were used to chemically and morphologically characterize the SCB fibers. The size distribution and morphology of CNFs were also evaluated by dynamic light scattering (DLS) and transmission electron microscopy (TEM). HPLC analysis revealed that percentage of cellulose increased from 41.5 to 91.39% after chemical pretreatments. FTIR and Kappa number analyses also confirmed the successful isolation of cellulose fibers from the SCB fibers after chemical pretreatments. Furthermore, DLS results showed that the hydrodynamic diameter of the isolated cellulose fibers reduced to 268 nm by dint of ultrasonication. Additionally, TEM images confirmed the isolation of CNFs: the average diameter of cellulose fibers decreased to about 28 nm after mechanical steps and the yield of fibrillation was found to be around 99%. According to the obtained results, the applied chemo-mechanical treatment appears to be promising for green and facile isolation of CNFs.     

Screening and Identification of Newly Isolated Basic Red 9-Degrading Bacteria from Textile Wastewater and Their Ability to Produce Medium-Co-Long-Chain-Length Polyhydroxyalkanoates

Journal of Polymers and the Environment - Newly isolated Basic Red 9-degrading bacteria were isolated from textile wastewater using a pretreatment method. Nine strains were isolated; however, only...     

RH大孔吸附树脂处理炼油厂碱渣废水的研究

在研究ＲＨ大孔吸附树脂吸附和解吸性能的基础上，以ＲＨ树脂处理炼油厂的碱渣进行了试验。结果表明，ＲＨ树脂可用于碱渣脱酚，在一定条件下，树脂的吸酚量可达１３０ｍｇ／ｍｌ，吸附饱和后的树脂，解吸后可重复使用，碱渣中的硫不会树脂中毒而降低吸酚量。     

Investigation of Synthesis of Copolymers from the Waste Products of Industrial Oil Refinement having Adhesion Properties and Strength to the Thermal Destruction

In this study, the waste products of industrial vegetable oil refinement were transformed into the glycidyl ester for preventing the effects of them to the environment, the ways for evaluating them in polymer chemistry were investigated, copolymers having high adhesion property and strength to the thermal destruction were synthesized and the area of their usage was determined. For this reason, the waste product of sunflower oil refination as a vegetable oil in the industry; soap stock (SS) was converted to the unsaturated glycidyl esters by the interaction with epichlorohidrine in the alkaline medium. After that the copolymerization of synthesized unsaturated glycidyl esters and the other waste product of oil refinement fatty acid (FA) with styrene in the radicalic initiator medium were investigated and copolymers that have high strength to the thermal destruction and adhesion property were synthesized. From the results of TGA and DTA analysis, it was determined that synthesized copolymers have low loss of weight at high temperature. The structures of copolymers were fixed by spectral and chemical analysis methods.     

Removal of Cinnamic Acid Derivatives from Aqueous Effluents by Fenton and Fenton-like Processes as an Alternative to Direct Biological Treatment

The removal of various phenolic acids (p-coumaric, caffeic and ferulic acids), typically found in wastewaters of agricultural origin, from model effluents by chemical and biological means has been investigated. Chemical oxidation processes comprising hydrogen peroxide and a homogeneous or heterogeneous copper or iron catalyst were employed over a wide range of experimental conditions. Chemical oxidation is capable of removing most of the total organic carbon initially present in the effluent at relatively mild treatment conditions (i.e. reaction times up to 120 min and temperatures up to 80°C), while removal rates generally increase with increasing temperature, H₂O₂ and catalyst concentrations. The anaerobic degradability and toxicity of p-coumaric acid has been assessed using the biochemical methane potential and anaerobic toxicity assay respectively. p-Coumaric acid, at concentrations below about 1 g/L, is not toxic against methanogens and slowly degrades over a period of about 35 days at 35°C. In light of this, chemical oxidation may provide a promising alternative to direct biological treatment for either the partial or complete removal of phenolic acids at reasonable treatment times; the implications for wastewater treatment are discussed.