催化剂Ru/ZrO2-CeO2催化湿式氧化苯酚

催化剂Ru/ZrO₂-CeO₂催化湿式氧化苯酚的过程表明,Ru/ZrO₂-CeO₂可以显著提高COD和苯酚去除效果,当反应温度为170℃,压力为3 MPa,反应120 min后,COD和苯酚的去除率分别达到了99％和100％.试验还考察了不同反应条件对苯酚溶液COD去除的影响,并获得了最优的反应条件：温度为170℃,压力为3 MPa,催化剂的投加量为5　g/Ｌ,搅拌速度为500 r/min.通过对中间产物的分析,本研究提出了催化湿式氧化苯酚的简单路径图,认为苯酚首先被氧化成小分子有机酸,接着小分子有机酸被氧化成二氧化碳和水.前一个过程是快速反应,后一个过程中的乙酸氧化是慢速过程,需要在高温下才能完成.乙酸的氧化主要是自由基攻击α碳上的C—H键,先生成甲酸,并最终生成二氧化碳和水.     

粉煤灰催化H2O2氧化水中对硝基酚研究

采用粉煤灰做催化剂,研究了在常温常压下对H₂O₂氧化对硝基酚（PNP）的催化性能.在分析粉煤灰理化性质的基础上,考察了粉煤灰种类,不同预处理方法以及粉煤灰投加量、pH、反应时间、H₂O₂浓度等因素对PNP去除率的影响.结果表明,比表面积大,未燃炭含量高的粉煤灰催化效果好;经过350℃预处理可以有效提高其催化性能;在pH=2,反应时间为60 min, H₂O₂起始浓度为200 mg/L, 粉煤灰投加量为60 g/L的条件下,热处理粉煤灰对PNP的去除率为62.38%.其中,粉煤灰的比表面积、未燃炭以及活性金属氧化物均是影响其催化活性的重要因素.在催化氧化对硝基苯酚过程中,吸附占有重要作用,为总去除率的65.97%.粉煤灰可以重复使用,随使用次数增加,粉煤灰催化性能提高.第2次、第3次对PNP的去除率分别为82.47%和98.72%,之后的9次实验中去除率均保持在99%左右,在使用12次后催化性能降低.     

以堇青石蜂窝陶瓷为载体的新型钒氧化物脱氮催化剂研究

以TiO₂/Al₂O₃/堇青石蜂窝陶瓷为载体,以V₂O₅-MoO₃-WO₃为活性组分,用于氨法选择性催化还原烟气中NO的新型催化剂,并对该催化剂的活性性能和微观结构进行了评价和表征.同时,将该催化剂的活性性能与其它几种活性组分相同但载体、制备方法、结构不同的催化剂进行了对比.对比结果表明,该新型催化剂能取得最好的选择性催化还原氮氧化物催化性能BET、FT IR、XPS表征实验结果表明,其高催化活性得益于大比表面积及大孔体积,而TiO₂/Al₂O₃/堇青石蜂窝陶瓷载体及其制备方法对获得好的催化剂构型起了至关重要的作用.     

化学反硝化去除硝酸盐的试验研究

在间歇式完全混合反应器中,以Pd-Cu/γ-Al₂O₃为催化剂,对催化还原硝酸盐进行了实验研究.结果表明:在负载型金属催化剂作用下,硝酸盐能有效地被还原生成N₂,总氮的去除率达80%以上.催化剂的活性和对氮气的选择性受催化剂量、pH值、H₂的流量和压力、初始硝酸盐浓度等反应条件的影响,适当增加催化剂量和提高H₂的流量和压力都有利于提高催化剂的活性;而对于选择性,前者提高,后者则会导致降低,即控制反应扩散性能有利于提高催化选择性.在试验的浓度范围内,其催化还原硝酸盐的反应为一级反应.     

颗粒Ru催化剂催化湿式氧化乙酸和苯酚

采用湿式成型法制备了Ru/ZrO₂-CeO₂颗粒催化剂,对乙酸和苯酚进行湿式氧化,研究反应条件对苯酚氧化过程中COD去除的影响,并对催化剂的稳定性进行评价.结果表明,向CeO₂中添加Zr能提高催化剂抗热性能,使用湿式成型法能降低焙烧温度,两者都可以提高比表面积和催化剂活性.Ru/ZrO₂-CeO₂催化湿式氧化苯酚的COD去除率随着反应温度的升高、压力的增大和催化剂使用量的增加而升高,最优反应条件为温度150℃,压力3MPa,催化剂用量35g/L.在110h的动态试验中,COD和苯酚的去除率高于90%,催化剂具有较高活性和良好的稳定性.     

添加原水改善SBR工艺处理猪场废水厌氧消化液性能

采用序批式反应器(SBR)工艺直接处理猪场废水厌氧消化液,处理系统的效率较低,COD去除率仅有10%左右,NH₄⁺-N去除率70%左右;处理出水水质较差,出水COD高于1 000mg/L,出水NH₄⁺-N在200mg/L左右;处理系统的工作不稳定,效能逐渐恶化.在猪场废水厌氧消化液中添加部分未经厌氧消化的猪场废水(原水),处理系统的处理效率明显提高,COD去除率高于80%,出水COD降到250～350mg/L;NH₄⁺-N去除率高于99%,出水NH₄⁺-N小于10mg/L;处理系统的稳定性也得到增强.添加原水后,猪场废水厌氧消化液的BOD₅/COD比值从0.19上升到0.54,BOD₅/TN比值从0.28上升到2.04,增加了微生物生长和反硝化所需的碳源,强化了反硝化作用,不仅提高了总氮去除效率,而且通过回补碱度,维持了处理系统的pH值稳定.     

电化学氧化与厌氧技术联用处理垃圾渗沥水

采用电化学氧化与上流式厌氧污泥床(UASB)结合技术,提出了处理香港垃圾渗沥水的二步法工艺.对含COD和NH₃-N分别为4750mg/L和1310mg/L的垃圾渗沥水,首先进行UASB预处理(消化温度37℃,COD负荷0.78g/(L·d),HRT为6.1d),获得了66%的COD去除率;UASB的出水被引入电化学氧化反应器进行深度处理.在外加Cl 2000mg/L,电流密度为32.3mA/cm²的条件下,经6h的电解间接氧化,COD和NH₃-N的去除率分别达到87%和100%,出水的COD为209mg/L,并且不含NH3-N,此过程的COD电能消耗＜55kW·h/kg.本文讨论了电化学氧化过程中电极反应原理,各实验参数对COD和NH₃-N去除率的影响,以及电能消耗与运行成本评估等.     

载Pt石墨催化臭氧化降解水中草酸的研究

以石墨为催化剂载体,以H₂PtCl₆·6H₂O为贵金属活性组分前驱物,采用等体积浸渍法制备了Pt/石墨催化剂.对Pt/石墨催化臭氧化、石墨催化臭氧化以及单独臭氧氧化降解草酸的效果进行了研究.结果表明,在本实验条件下,单独臭氧氧化、石墨催化臭氧化和Pt/石墨催化臭氧化草酸的去除率分别为3.0%、47.6%和99.3%.Pt的负载可以显著地提高石墨催化臭氧化的效果.以草酸的去除效率为催化活性指标对Pt/石墨催化剂的制备条件进行了优化.结果表明,石墨载体的预处理没有提高Pt/石墨催化剂的活性.Pt/石墨催化剂最佳制备条件为：以水为溶剂,浸渍时间24　h,活性组分Pt的负载量为1.0%,氢还原温度为350℃.所制备催化剂经重复使用5次,草酸去除率仍超过90％.     

Al2O3催化臭氧化处理邻苯二甲酸二甲酯

'Al₂O₃催化剂对邻苯二甲酸二甲酯(DMP)溶液臭氧化过程的影响结果表明:Al₂O₃可以显著提高臭氧氧化的效果,反应120min后,TOC的去除率从单独臭氧氧化的23.9%提高到55.1%.实验中还考察了制备条件对Al₂O₃催化剂活性的影响并确定了反应的最佳工艺条件.在实验考察的范围内:焙烧温度600℃,Al₂O₃粒径为0.5～1.0mm时催化活性最高;最佳反应工艺条件为:催化剂投加量20g/L,混和气体流速200mL/min,反应温度15℃.通过单独臭氧氧化,单独臭氧氧化后再进行催化剂吸附,催化臭氧化的对比实验证明了Al₂O₃催化剂对体系TOC的去除主要是基于催化作用.     

FCR多级接触氧化系统处理乳品工业废水的研究

为提高乳品工业废水生物处理的去污脱氮能力,以新型螺旋状纤维填料作为载体,采用多级氧化槽内不同种类微生物形成的食物链系统（food chain reactor）,详细考察了不同水力停留时间COD、TN、NH^＋₄-N、TP等的去除率及其去除机理,并对污泥减量化效果进行了初步探讨.结果表明,当进水COD为842～1 843 　mg/L、TN为36.3～92.2 　mg/L、NH^＋₄-N为30.1～52.1 　mg/L,HRT=6　h时,系统COD的平均去除率达到93.3%;TN和NH⁺₄-N的去除效果显著,其平均去除率分别达到73.3%和80.7%,出水COD、TN、NH⁺₄-N平均值分别为79.4　mg/L、9.6 　mg/L、6.1　mg/L,均低于《污水综合排放标准》（GB 8978-2002）的一级标准.该系统不仅具有较高的去污脱氮效果,而且产生的剩余污泥量极少,其污泥产率的平均值为7.7%.该系统运行费用低,操作管理方便,长期运行稳定,可应用于城市污水、中高浓度有机废水（如餐厅污水、食品工业废水）等的处理.     

丙烯腈生产废水的催化湿式氧化

在高压反应釜中采用Mn-Ce和Co-Bi复合催化剂通过催化湿式氧化法处理丙烯腈废水。试验结果表明Mn-Ce和Co-Bi复合氧化物催化剂的活性强烈的依赖于Mn-Ce和Co-Bi的组成。Co-Bi复合催化剂对丙烯腈废水的氧化活性最高,且在酸性溶液中无金属离子溶出问题。在反应温度190～200℃,氧气的分压1.5～1.8MPa,反应时间为90min,丙烯腈废水的COD去除率超过90%。     

Catalytic wet air oxidation for the treatment of emulsifying wastewater

The wet air oxidation (WAO) and catalytic WAO(CWAO) of the high strength emulsifying wastewater containing nonionic surfactants have been investigated in terms of COD and TOC removal. The WAO and homogeneous CWAO processes were carried out at the temperature from 433 K to 513 K, with initial oxygen pressure 1.2 MPa. It was found that homogeneous catalyst copper(Cu(NO3)2) had an fairly good catalytic activity for the WAO process, and the oxidation was catalyzed when the temperature was higher than 473K. Moreover, several heterogeneous catalysts were proved to be effective for the WAO process. At the temperature 473 K, after 2h reaction, WAO process could achieve about 75% COD removal and 66% TOC removal, while catalysts Cu/Al2O3 and Mn-Ce/Al2O3 elevated the COD removal up to 86%-89% and that of TOC up to 82%. However, complete elimination of COD and TOC was proved to be difficult even the best non-noble catalyst was used. Therefore, the effluent from WAO or CWAO process need to be further disposed. The bioassay proved that the effluent from WAO process was amenable to the biochemical method.     

Kinetics study on catalytic wet air oxidation of phenol by several metal oxide catalysts

Four metal oxide catalysts composed of copper (Cu), stannum (Sn), copper-stannum (Cu-Sn) and copper-cerium(Cu-Ce) respectively were prepared by the co-impregnation method, and γ-alumina(γ-Al2O3 ) is selected as support. A first-order kinetics model was established to study the catalytic wet air oxidation of phenol at different temperature when these catalysts were used. The model simulations are good agreement with present experimental data. Results showed that the reaction rate constants can be significantly increased when catalysts were used, and the catalyst of 6% Cu-10% Ce/γ-Al2 O3 showed the best catalytic activity. This is consistent witht he result of catalytic wet air oxidation of phenol and the COD removal can be arrived at 98.2% at temperature 210℃, oxygen partial pressure 3 MPa and reaction time 30 rain. The activation energies of each reaction with different catalysts are nearly equal, which is found to be about 42 kJ/mol and the reaction in this study is proved to be kinetics control.     

非均相Fenton处理有机磷农药污染场地抽出地下水效能及影响因素

比较了不同非均相Fenton催化剂处理高浓度有机磷农药污染场地抽出地下水的COD、TP去除率以及污泥产率的差异,探究了H₂O₂投加量、非均相催化剂装填量、pH对反应效能的影响,并利用扫描电子显微镜(SEM),X射线能谱(EDS)等技术,分析了反应前后非均相催化剂表面结构特征与成分组成。结果表明:Fe₂O₃/Al₂O₃非均相催化剂具有较高的比表面积与负载Fe含量,反应后材料表面有Fe元素沉积。以Fe₂O₃/Al₂O₃、Al₂O₃、Fe₂O₃/SiO₂-Al₂O₃作为催化剂的非均相Fenton反应,其COD、TP去除率分别可达到84.72%、74.10%、75.98%与88.48%、82.80%、85.83%,均高于无固体催化剂的均相Fenton反应。ρ(H₂O₂)/ρ(COD)=0.5~2.0时,COD与TP去除率随H₂O₂投加量的增加而提升,并与非均相催化剂装填量呈正相关。同时,非均相催化剂的投加可显著降低污泥产率,扩大反应体系有效pH范围。     

催化湿式氧化处理造纸废水的研究

以过渡金属氧化物CuO为活性组分,采用催化湿式氧化法处理造纸废水,考察Cu负载量、催化剂用量、反应温度对废水COD去除率的影响。结果表明:固定氧气分压在2.5MPa和反应时间3h,催化剂用量为3g,Cu负载量为4%,反应温度为220℃,500mL浓度为3250mg/L造纸废水的COD去除率为90%,色度去除率为89%,pH值由9.6变为7.8。另外,对催化剂进行再生处理和稳定性测试。结果表明:450℃下活化3h,在上述相同反应条件下,对原废水的COD去除率降低为88%,重复使用9次后对废水的COD去除率仍能保持在85%左右。     

催化超临界水氧化技术处理香料废水研究

采用催化超临界水氧化(CSCWO)技术对香料废水进行氧化处理,研究了催化剂浓度、反应温度、压力、停留时间等因素对废水COD、TN去除效果的影响.结果表明:在超临界水中添加cu2+催化剂后有机物的去除效率与无催化剂时相比有显著的提高.香料废水中COD、TN的去除率随催化剂浓度、反应温度和压力的升高,停留时间的延长而提高....     

O_3催化氧化深度处理兰炭废水的试验研究

采用O3催化氧化法深度处理兰炭废水,提出了兰炭废水达标排放的新处理方法。以铜为活性组分,氧化铝为载体采用浸渍法制备CuO/γ-Al2O3催化剂,并采用XRD对其进行表征,利用催化剂结合O3催化氧化法去除兰炭废水中经生化处理后残留的污染物。设计了催化氧化试验装置,考察了催化剂投加量、反应时间、O3用量以及pH等因素对处理效果的影响。实验结果表明,pH在酸性条件下有利于COD去除率的提高,O3用量提高有助于COD去除率的提高,将催化剂用量和反应时间控制在一定范围内有利于污染物的去除;最佳条件下催化剂投加量300 g,反应时间1 h,O3用量0.08 m3/h,pH为7左右时COD去除率可达到95%左右。另外,催化剂在20次反应过程中表现出较高的催化活性及较强的稳定性。     

Ti-Ce系列催化剂上乙酸的催化湿式氧化反应

采用Ti-Ce系列湿式氧化催化剂,研究模型反应物乙酸在催化湿式氧化反应中的动力学影响因素以及反应过程产物.结果表明,乙酸的催化湿式氧化受到催化剂用量、反应温度、反应体系酸度以及氧分压的影响较大.当反应温度230℃,氧分压2～2.5MPa,催化剂量5g/L,反应液初始pH3.0时,反应1h后即可使乙酸浓度(以COD计)去除率在90%以上.通过离子色谱,检测了反应过程中的甲酸中间体,结果表明,催化剂的存在不仅加速了湿式氧化反应速率,而且也改变了反应历程.     

ACF负载金属氧化物及尿素低温去除NO

以活性炭纤维(ACF)负载NiO以及NiO-CeO2制备了一系列催化剂,并在催化剂上负载尿素作为还原剂,研究其在30～120℃范围内的催化还原NO的活性.通过SEM、BET、XRD等表征实验选择性地对催化剂进行了理化特征研究.结果表明,3种不同质量分数的NiO催化剂中,5%NiO/ACF效率较低,10%NiO的催化剂活性以及活性稳定性较好,在90℃即可达到50%左右的NO净化效率,15%NiO/ACF的催化活性稳定性较差.在3种不同质量分数的NiO-CeO2/ACF催化剂中,5%NiO-5%CeO2/ACF的活性以及活性稳定性最好,在110℃可达到55%以上的NO净化效率.10%CeO2-5%NiO/ACF活性高于5%CeO2-10%NiO/ACF;活性金属的最佳负载量为10%,过多的负载量会引起催化剂比表面积的减少从而导致催化剂活性下降;金属氧化物是催化反应的活性中心.对10%CeO2/ACF、10%NiO/ACF和5%CeO2-5%NiO/ACF的研究显示,5%CeO2-5%NiO/ACF的催化活性最好,CeO2和NiO的协同作用使催化剂的活性优于2种单独负载的催化剂.本研究还对催化剂的低温催化机制进行了分析和讨论.     

催化湿式共氧化降解内分泌干扰物双酚A的研究

以NaNO2为催化剂、2,4,6-三氯苯酚(TCP)为共氧化物质对内分泌干扰物双酚A(BPA)进行了催化湿式共氧化(CWCO)降解,研究发现,在NaNO2存在的条件下,TCP的加入极大地促进了BPA的降解:在170℃、0.5MPa氧气压力条件下反应6h后,催化湿式共氧化体系中COD去除率达到了71.2%,而BPA单独氧化降解时,COD去除率仅为24.7%.在此基础上考察了反应温度、氧气压力、反应时间、TCP浓度和NaNO2浓度对BPA降解效率的影响,筛选出了最优反应条件(170℃的反应温度、0.5MPa的氧气压力、6h的反应时间、0.5mmol/L BPA、0.5mmol/L TCP和0.1mmol/L NaNO2).在优化条件下,BPA和TCP去除率分别达到了100%和96.4%,同时反应后溶液的可生化性大大提高,BOD5/COD值从反应前的0.08增加到了0.95.另外,GC-MS结果表明,BPA和TCP降解的产物主要为小分子有机酸,分别是乙酸,2-甲基戊二酸,丁二酸,3-甲基己二酸,己三酸以及1-丙烯基-1,2,3-三羧酸.该共氧化技术为污染水体中BPA和TCP的同时去除提供了一种可能性.