磁性微球负载光催化剂失活特性及再生方法研究

TiO2/SiO2/Fe3O4在连续使用过程中存在失活现象并表现出吸附能力的降低,在实验基础上提出了超声波在线再生的解决方案;测试结果表明,TiO2/SiO2/Fe3O4在重复使用10次及连续使用130h条件下可保持其催化活性不变。     

磁性微球负载光催化剂制备及处理造纸废水研究

采用溶胶-凝胶法,在磁性颗粒表面包覆TiO2,制备了易于固液分离的磁载光催化剂TiO2/SiO2/Fe3O4,通过XRD和TEM对产物的晶体结构、晶粒大小、形貌进行了表征,讨论了焙烧温度、焙烧时间、催化剂用量和光照时间等对TiO2光催化剂处理造纸废水的影响。结果表明:焙烧温度为500℃、焙烧时间3.5h时,光催化活性最高;催化剂用量为2.5g/L,光照时间4h时TiO2降解造纸废水的能力最强。     

石墨烯基磁性纳米吸附剂的制备及性能研究

为有效去除废水中MnO-4,采用水热法合成Fe3 O4-RGO,以乳液-凝胶法引入SiO2修饰Fe3 O4,通过接枝EDTA增强材料的吸附性能,最终制备出Fe3 O4@SiO2@EDTA-RGO纳米吸附剂.利用透射电子显微镜、X-射线衍射、磁回收对该吸附剂形貌、晶型结构及磁性能进行了表征,考察了吸附时间、吸附剂投加量和...     

纳米氧化物对斑马鱼胚胎孵化率的影响

为评价纳米氧化物的水生态毒理效应,以模式生物斑马鱼胚胎为研究对象,观察了纳米ZnO、纳米TiO2、纳米Fe2O3、纳米Fe3O4和纳米SiO2对其96h孵化率的影响.结果表明,纳米氧化物毒性与其成分有很大关系.纳米ZnO对斑马鱼胚胎孵化抑制作用明显,毒性较大,且其毒性与浓度之间存在一定的剂量-效应关系;在低浓度时,纳米ZnO抑制胚胎孵化的效应较等浓度Zn2+强,说明纳米ZnO特殊理化性质发挥了一定作用.纳米Fe2O3在低浓度下不影响胚胎孵化率,而在高浓度下抑制胚胎孵化.纳米TiO2、纳米Fe3O4、和纳米SiO2对斑马鱼胚胎96h孵化率没有明显影响.     

纳米结构Fe3O4/Y2O3磁性颗粒的制备、表征及磷吸附行为研究

采用共沉淀法制备了一种新型铁钇氧化物(Fe3O4/Y2O3)磁性吸附剂,并对其表面特性及磷吸附行为进行了初步研究.扫描电镜(SEM)与X-射线衍射仪(XRD)表征结果表明,此吸附剂具有纳米结构,初级粒子平均粒径为15.2nm.振动样品磁强计(VSM)测得比饱和磁化强度为38.7emu·g-1,磁性较强,可方便地实现固液分离.吸附剂的等电点为6.8.磷吸附实验表明,25℃时,Langmuir吸附等温线可较好地拟合Fe3O4/Y2O3对溶液中磷的吸附(R2=0.989),最大吸附量(pH=5.0)为60.6mg·g-1(以P计);吸附速率较快,在120min内可完成吸附容量的80%以上,符合准二级动力学模型(R2=0.997);溶液pH对Fe3O4/Y2O3吸附磷的影响较为明显,离子强度则影响不大;共存阴离子对吸附影响的大小顺序为Cl-相似文献   

纳米TiO2协助下As（Ⅲ）在可变电荷土壤中的光催化氧化和吸附

环境中As(Ⅲ)的毒性和活动性均大于As(Ⅴ),将A8(Ⅲ)转化为As(Ⅴ)有利于砷的固定.为此使用自制的光催化装置,采用一次平衡法研究了纳米TiO2协助下As(Ⅲ)在土壤悬液体系中的光催化氧化及土壤对氧化产物的吸附.结果表明,As(Ⅲ)的光催化氧化量随TiO2的加入量和光照时间的增加而增加,当TiO2的加入量为1.0 g·L-1,光照时间为90 min时As(Ⅲ)可以达到很好的转化效果.As(Ⅲ)在土壤中的光催化氧化及土壤对氧化产物的吸附增加了水体中砷的去除量,在Fe/Al氧化物与TiO2体系中也观察到类似的效应.实验结果还表明γ-Al2O3也可诱导As(Ⅲ)的光催化氧化.     

无定形氧化铁-胡敏酸复合胶体对Cu2+的吸附特征

采用Cu2 选择电极研究了不同pH值条件下胡敏酸(HA)、无定形Fe2O3、HA-Fe2O3复合胶体对Cu2 的等温吸附规律.结果表明,随着pH值的升高,3种胶体饱和吸附量和吸附平衡常数均增大,有利于吸附的进行.HA和无定形Fe2O3等温吸附Cu2 的4种拟合方程中,Langmuir方程整体拟合效果最佳,其次为对数方程和Freundlich方程,Linear方程较差.HA-Fe2O3复合胶体等温吸附Cu2 的4种拟合方程均达到显著相关.在相同pH值条件下,无定形Fe2O3对Cu2 吸附量最小,复合胶体次之,HA胶体最大;而且,无定形Fe2O3和复合胶体的饱和吸附量之和小于HA胶体.     

四氧化三铁/聚乙烯亚胺纳米颗粒的制备及除磷性能的研究

采用化学共沉淀法,以聚乙烯亚胺(PEI)为改性剂,制备了聚乙烯亚胺改性的纳米四氧化三铁复合材料(Fe3O4/PEI).Zeta电位、透射电镜和FTIR表征结果显示,PEI修饰提高了纳米Fe3O4在水中的分散性和稳定性,同时也增强了其表面正电荷,从而提高了Fe3O4对水中磷酸根的去除能力.在磷酸根初始浓度为50 mg·L~(-1),Fe3O4/PEI投加量为200 mg,p H=3,温度为25℃的条件下,Fe3O4/PEI对100 m L磷酸根的吸附去除率达到91%.吸附过程在3 h内达到平衡.吸附等温数据表明,该吸附过程符合Langmuir吸附等温方程,可决系数R2达到0.99,最大吸附量为29.88 mg·L~(-1).Fe3O4/PEI复合材料重复利用性好,在第5次吸附-解析后还能保持对磷酸根75%以上的吸附去除率.磷的解析效率随着p H增加而增加,在p H=13时,解析效率达到65%.     

悬浮态TiO_2光催化降解苯系物的方法研究

以高压汞灯为光源 ,在TiO2 粉末悬浮体系内 ,系统地研究了光照时间、光照距离、催化剂用量、苯系物浓度和溶液pH、空气流量、H2 O2 浓度、Fe3+ 浓度等因素对模拟水样中苯系物的光催化降解效率的影响。研究结果表明 ,当光照时间为 2 0min、光照距离为 6cm ,TiO2 用量为 4 0 0mg L、pH =7、苯系物浓度为 10 0mg L ,空气流量为 4 0 0mL min,苯系物降解率可达 93% ,添加H2 O2 与Fe3+ 能增加苯系物的降解率 ,当H2 O2 浓度为 6mmol L ,Fe3+ 浓度为 0 2mmol L ,苯系物可完全降解。实验测定精密度RSD为 0 5 %。     

复合纳米Fe_3O_4的制备及其控磷效能的研究

采用氧化沉淀法在羧甲基纤维素(CMC)体系中制备了以纳米Fe3O4为核心,外包覆羧甲基纤维素的复合纳米Fe3O4.对比研究了复合纳米Fe3O4和微米Fe3O4对水中磷的吸附以及对土壤中磷的固化,并考察了添加纤维素酶在此过程中所起的作用.结果表明,在水中微米Fe3O4的平衡吸附量为3.2 mg/g,而复合纳米Fe3O4为2.1 mg/g.当将纤维素酶(用以降解包覆在氧化铁表面的羧甲基纤维素)添加到复合纳米Fe3O4吸附磷的溶液中,复合纳米Fe3O4的除磷效率(86%)接近于微米Fe3O4(90%),说明羧甲基纤维素的存在减弱了复合纳米Fe3O4的吸附能力.在土柱实验中,将2种Fe3O4悬浊液注入到10 cm高的土壤柱中,72%的复合纳米Fe3O4穿过土壤柱溢出,而微米Fe3O4完全滞留在土壤柱中没有溢出.原始土壤的固磷率为30%,注入复合纳米Fe3O4的土壤固磷率达到45%,而将纤维素酶和复合纳米Fe3O4一起注入土壤中固磷效率提高到74%.     

黄土风化成土过程中主要元素迁移序列

主要研究了渭南黄土剖面中主要化学组分的分布特征、影响因素以及它们在风化成土过程中的迁移富集规律。结果表明：（1）在剖面中随着黄土与古土壤层的交替叠复，各组分含量由低-高或由高-低呈周期性变化。（2）碳酸盐含量的剧烈变化是影响黄土元素分布特征极为重要的因素，古土壤中一些组分的含量增高，主要是碳酸盐被强烈淋滤造成的相对富集。（3）在黄土风化成土过程中，CaCQ3、SiQ2、FeO、MgO、K2O、Na2O等本身的地球化学行为以迁移为主，而Al2O3、Fe2O3、TiO2等均以淀积为主。它们在黄土中的迁移能力有如下顺序：CaCO3＞FeO＞MgO＞Na2O＞K2O＞SiO2＞Al2O3＞TiO2＞Fe2O3。（4）除碳酸盐外，黄土风化成土过程中铁的变化比其它组分都明显，表现为价态以及形态的转化。铁的转化主要为就地完成．本身没有发生明显迁移。     

Enhancement of formaldehyde degradation by amine functionalized silica/titania films

Doping amine functional groups into SiO2/TiO2 films for enhancing the decomposition of formaldehyde has been investigated using the modified sol-gel method to prepare organic-inorganic hybrid photocatalysts via the co-condensation reaction of methyltrimethoxysilane (MTMOS) and amine functional groups. n-(2-Aminoethyl)-3-aminopropyl-trimethoxysilane (AEAPTMS) and 3-aminopropyl-trimethoxysilane (APTMS) were selected to study the e ect of amine functional groups on the enhancement of formaldehyde adsorption and degradation under a UV irradiation process. Physicochemical properties of prepared photocatalysts were characterized with nitrogen adsorption-desorption isotherms measurement, X-ray di raction (XRD) and Fourier transform infrared (FT-IR) spectroscopy. The results indicated that the APTMS/SiO2/TiO2 film demonstrated a degradation e ciency of 79% superior to those of SiO2/TiO2 and AEAPTMS/SiO2/TiO2 films due to the synergetic e ect of adsorption and photocatalytic properties. The APTMS/SiO2/TiO2 film can be recycled with about 7% decreasing of degradation e ciency after seven cycles.     

Iron-doped Mn-Ce/TiO2 catalyst for low temperature selective catalytic reduction of NO with NH3

The catalysts of iron-doped Mn-Ce/TiO 2(Fe-Mn-Ce/TiO 2) prepared by sol-gel method were investigated for low temperature selective catalytic reduction(SCR) of NO with NH 3.It was found that the NO conversion over Fe-Mn-Ce/TiO 2 was obviously improved after iron doping compared with that over Mn-Ce/TiO 2.Fe-Mn-Ce/TiO 2 with the molar ratio of Fe/Ti = 0.1 exhibited the highest activity.The results showed that 96.8% NO conversion was obtained over Fe(0.1)-Mn-Ce/TiO 2 at 180°C at a space velocity of 50,000 hr 1.Fe-Mn-Ce/TiO 2 exhibited much higher resistance to H 2 O and SO 2 than that of Mn-Ce/TiO 2.The properties of the catalysts were characterized using X-ray diffraction(XRD),N 2 adsorption,temperature programmed desorption(NH 3-TPD and NOx-TPD),and Xray photoelectron spectroscopy(XPS) techniques.BET,NH3-TPD and NOx-TPD results showed that the specific surface area and NH3 and NOx adsorption capacity of the catalysts increased with iron doping.It was known from XPS analysis that iron valence state on the surface of the catalysts were in Fe3+ state.The doping of iron enhanced the dispersion and oxidation state of Mn and Ce on the surface of the catalysts.The oxygen concentrations on the surface of the catalysts were found to increase after iron doping.Fe-Mn-Ce/TiO2 represented a promising catalyst for low temperature SCR of NO with NH3 in the presence of H2 O and SO2.     

TiO_2-Fenton试剂光氧化降解水中氯代有机物的研究

探讨了在光 Fenton体系中引入催化剂TiO2 对几种氯代有机物的光氧化降解效果及其影响因素。试验结果表明 ,TiO2 Fenton试剂复合体系对CH2 ClCOOH的光解脱氯速率显著高于TiO2 和Fenton试剂体系 ,TiO2 对Fenton光氧化反应有较强的催化作用 ;溶液 pH值、铁离子浓度、氯代有机物组成和结构等因素对复合体系的光氧化效果均有明显的影响     

城市生活垃圾与煤混烧灰渣的熔融特性及成分分析

根据我国城市生活垃圾熔融焚烧需要添加一定量辅助燃料进行稳燃的实际情况以及垃圾成分复杂、波动性大的特点，对配比一定煤的混合垃圾焚烧灰渣的熔融特性及熔融渣的回收利用进行实验研究．实验结果表明：垃圾的熔融特性主要与垃圾渣中的以SiO2-A12O3-CaO-Fe2O3为代表成分有关，垃圾渣中SiO2/A12O3、SiO2 Al2O3、CaO Fe2O3对灰渣熔融点T3的影响与该成分在垃圾渣中存在的化学形式及其性质有关；垃圾熔融渣的物理性能优良，渣中的重金属浸出和噁英的含量均达环保标准．可以直接对垃圾熔融渣进行回收利用。     

TiO2/PS/Fe3O4 光催化剂的低温制备及其光催化和磁回收性能

以聚苯乙烯(PS)包覆油酸修饰过的纳米Fe3O4为磁核,在低温(90℃)、中性(pH=7左右)条件下,制备了以PS为惰性隔离层的磁载TiO2光催化剂.用X射线衍射仪(XRD)、透射电子显微镜(TEM)、傅里叶红外分光光度计(FT-IR)、振动样品磁强计(VSM)对催化剂的物相组成、形貌、表面性质、磁学性质进行了表征.以苯酚为模拟污染物,考察了其光催化活性,以自制的磁回收装置,考察其回收特性.结果表明,低温制备的TiO2为锐钛矿结构,平均粒径为2～5 nm,催化剂TiO2/PS/Fe3O4[其中物质的量比为n(TiO2)∶n(St)∶n(Fe3O4)=60∶2.5∶1]具有结构完整的壳/壳/核结构,TiO2在PS/Fe3O4表面负载牢固;光催化降解苯酚遵循一级反应动力学方程,TiO2/PS/Fe3O4[n(TiO2)∶n(St)∶n(Fe3O4)=60∶2.5∶1]的反应速率常数K=0.025 8,与纯TiO2的活性接近(K=0.026 2);循环使用5次后,反应速率常数仅降低0.003 4.所制催化剂具有较强的磁感应强度,平均回收率可达到92%以上.该低温水解法制备的磁载TiO2光催化剂具有良好的应用前景.     

聚合多巴胺包覆的磁性微球吸附Cr(Ⅵ)

用聚合多巴胺(PDA)包覆溶剂热法制备Fe_3O_4磁性微球,得到Fe_3O_4@PDA复合材料,并采用红外光谱、扫描电镜、透射电镜对复合材料进行表征。同时,对Fe_3O_4@PDA吸附溶液中六价铬(Cr(Ⅵ))的性能进行研究,考察了溶液pH对其吸附性能的影响。结果表明:Fe_3O_4@PDA在溶液pH为3.0时对Cr(Ⅵ)有较好的吸附性能,其吸附动力学数据符合伪二级动力学方程,等温吸附符合Langmuir吸附模型,最大吸附容量达到108.8 mg/g,热力学实验计算出的吉布斯自由能为负值,表明Cr(Ⅵ)在Fe_3O_4@PDA的吸附为自发过程。