采用纳米四氧化三铁(Fe3O4)降解水溶液中的2,4-二氯苯氧乙酸(2,4-D),考察了2,4-D初始浓度、纳米Fe3O4投加量、溶液pH和温度等因素对2,4-D降解率的影响.结果表明,纳米Fe3O4对2,4-D有显著的降解效果,初始浓度为10 mg/L的2,4-D, 48 h内降解率可达48%.纳米Fe3O4对2,4-D的降解是一个还原脱氯过程,反应体系中氯离子浓度随2,4-D浓度降低而升高.LC/MS分析表明,2,4-D降解的主要产物是苯酚,其他中间产物是2,4-二氯苯酚(2,4-DCP)、4-氯苯酚(4-CP)和2-氯苯酚(2-CP).溶液中2,4-D的降解符合准一级反应动力学,产物4-CP、2,4-DCP和苯酚的反应速率常数K分别为0.0043、0.0026和0.0032 h -1.环境条件对降解效率有显著影响,2,4-D初始浓度在0～10 mg/L、纳米Fe3O4投加量0～300 mg/L的范围内,2,4-D降解率随初始浓度和纳米Fe3O4投加量的增加而增大;pH对2,4-D的脱氯降解有显著影响,在pH为3.0时,纳米Fe3O4对2,4-D的还原脱氯效果最好;温度升高,可以提高脱氯反应速率.     

紫外光降解水中痕量NDMA的效能研究

采用紫外光降解水中痕量亚硝基二甲胺(NDMA),研究了NDMA初始浓度、溶液pH值、光照面积、紫外光辐射强度以及水质对紫外光降解NDMA的影响.结果表明,紫外光能够有效降解水中的NDMA,紫外光解反应5min, NDMA去除率可以达到97.5%.初始浓度对NDMA的光降解去除率影响不大.随着pH值升高,紫外光解NDMA的反应速率呈现下降趋势,低pH值条件下光量子产率较高,溶液pH=2.2时NDMA具有最大光降解速率.NDMA的去除率随着有效光照面积的增大而增大,紫外光辐射强度的增加有利于NDMA的去除.水质对紫外光降解NDMA具有一定的影响,在自来水和江水为背景的2种对比体系中,光解NDMA去除率分别为96.7%和94.8%     

纳米零价铁对水中芴的去除研究

研究了实验室自制的纳米零价铁在不同投加量、初始浓度、pH及温度条件下,对芴溶液的吸附效果、吸附等温线及吸附动力学.结果表明,随着纳米铁投加量的增加,芴的去除率升高;增加芴的初始浓度,去除率则相应下降,同时平衡吸附量增加.另一方面,纳米铁对芴的吸附能力随pH的升高而下降;温度为15~35℃时,芴的平衡吸附量随温度的升高而增加,但变化不大.纳米铁对芴的吸附等温线符合Langmuir和Freundlich方程;纳米铁对芴的吸附过程很好地符合准二级速率方程,吸附速率随芴初始浓度的增大而减小,平衡吸附量随芴初始浓度的增大而增大.除上述结果以外,本文还对此反应体系的吸附机理进行了初步探讨.     

臭氧法降解水中对甲基苯磺酸的动力学研究

采用臭氧法降解对甲基苯磺酸废水,研究了对甲基苯磺酸降解的影响因素和动力学.考察了反应液初始浓度、初始pH值、臭氧投量、反应温度、常见无机离子等因素对臭氧氧化降解对甲基苯磺酸反应速率的影响.结果表明,对甲基苯磺酸初始浓度0.29mmol.L-1,pH9.0,臭氧投量3.75×10-6mol.s-1,控制温度25℃,反应6...     

纳米零价铁降解水中四氯化碳的试验研究

以四氯化碳为目标污染物,研究了不同因素对自制纳米零价铁降解水中四氯化碳的影响,并对反应产物及可能的反应路径进行了探讨.结果表明,自制纳米零价铁对四氯化碳有很好的降解效果.在pH=3和30℃的条件下,当初始四氯化碳浓度为2.0 mg·L~(-1),纳米零价铁浓度为1.0 g·L~(-1)时,去除率高达96.7%.纳米零价铁降解四氯化碳的酸碱适应范围较大(pH值3~9).随着温度升高和纳米零价铁投加量的增大,四氯化碳降解率显著提高.该反应符合一级动力学,且反应活化能较低,反应易于进行.     

镀铜铁内电解法用于甲基橙的脱色研究

采用镀铜铁内电解法对甲基橙染料废水进行了降解脱色研究,考察了pH、铁屑投加量、反应时间、初始浓度对脱色效果的影响,并对镀铜铁内电解降解甲基橙的过程进行了原位循环伏安跟踪监测。结果表明:最佳反应条件为酸性条件pH值2~4,铁屑投加量为400g/L,反应时间为100min,脱色率为96.0%;镀铜铁内电解降解甲基橙过程发生了氧化还原反应,生成了甲基橙的氧化产物与还原产物。     

吸附树脂负载铁酞菁催化降解硝基苯的研究

在可见光照射下,采用吸附树脂负载铁酞菁催化过氧化氢降解硝基苯.考察了光照、催化剂投加量、双氧水投加量、温度及pH值等因素对催化效果的影响.结果表明,在功率为50W卤钨灯照射下,硝基苯溶液初始质量浓度为200 mg/L,初始pH值为3,催化剂投加量为1.5 g/L,双氧水投加量为1.0 mL/L,温度为35℃下反应10h,硝基苯去除率可达到79.9％.     

超声波/零价铁体系降解苯胺废水的影响因素及机理研究

以苯胺为研究对象,通过试验对超声波/零价铁体系降解苯胺的过程与机理进行了研究,分别考察了零价铁投加量、废水初始pH值、废水初始浓度对苯胺污染物降解的影响规律,结果表明:超声波/零价铁体系适宜处理苯胺浓度较低的废水,零价铁的最佳投加量为2.8g/L,废水初始pH值的适宜范围为7～8;超声波/零价铁体系降解苯胺具有协同作用,对苯胺的降解以.OH自由基的氧化作用为主,其降解过程符合一级反应动力学规律;紫外可见光谱显示,苯胺在超声波/零价铁体系中发生了开环反应。     

氧化铜催化零价铁还原水中亚硝基二甲胺

为去除水中亚硝基二甲胺(NDMA)对环境的污染,研究采用氧化铜(CuO)催化零价铁还原NDMA.考察了反应效能以及CuO的投量、pH值、溶解氧、反应器转速等因素的影响,进行了产物分析并对动力学规律和反应机理进行探讨.实验结果表明:CuO可以有效地催化零价铁还原NDMA,反应18h后去除率可达99%以上.CuO投量越大,pH值越低,反应进行越快.富氧状态抑制NDMA的还原.反应器转速过快或过慢都会影响反应的进行.随着NDMA的降解,偏二甲肼(UDMH)和二甲胺(DMA)随之生成.催化加氢被提出是该反应的机理.     

超声波/铁-炭微电解协同降解苯酚

采用超声波/铁-炭微电解联用体系,以苯酚为目标污染物,考察了苯酚溶液初始pH值、初始浓度、铁屑与活性炭投加量等因素对联用体系降解苯酚效果的影响.结果表明:考察范围内,苯酚降解率随其初始浓度和溶液初始pH值的增加而降低,随铁屑与活性炭投加量的增加而升高.当苯酚初始浓度由50mg·L-1增至270mg·L-1,溶液初始pH值由3.0增至9.0时,降解率分别由91.3%和78.4%降至34.7%和50.7%;铁屑投加量为每L苯酚溶液中40g、160g和320g,铁屑与活性炭体积比均为1∶1时,降解率依次为31.8%、51.9%和72.8%.对比实验及动力学分析表明:联用体系中超声波(US)和铁-炭微电解对苯酚降解具有明显的协同作用,协同因子Ｅ＝5.12,且降解过程符合假一级动力学规律,并根据降解速率常数随各影响因素的变化关系确定了宏观动力学模型.     

光助纳米铁还原Cr(VI)的研究

采用液相还原法制备了纳米铁,并用X射线衍射仪(XRD)、扫描电镜(SEM)对其晶体结构、形貌特征进行了表征.以Cr(Ⅵ)为模拟污染物,中压汞灯作为光源,考察了不同投加量、不同pH值等条件下光照对纳米铁还原Cr(Ⅵ)的影响.结果表明:制备的纳米铁具有很高的反应活性,粒径约为7.6nm,呈球形,可在空气中自燃.在25℃、Cr(Ⅵ)浓度为20mg/L、pH=7±0.5,加入0.1g的纳米铁,光照60min后Cr(Ⅵ)的还原率达到62.3%,而无光照时Cr(Ⅵ)的还原率仅为27.6%,说明光照对Cr(Ⅵ)的还原具有明显的促进作用.当纳米铁投加量较大时,纳米铁对Cr(Ⅵ)的还原速率大于光照对其产生的影响.反应液pH值对Cr(Ⅵ)还原速率的影响较光照对其产生的影响显著.在紫外光的照射下,纳米铁中电荷可能在诱导下作受迫振荡,与吸附分子发生电荷传递是光照促进纳米铁还原Cr(Ⅵ)的主要原因.     

有机膨润土负载纳米铁去除废水中硝基苯

用具有良好吸附能力的有机膨润土作载体,通过FeSO4与NaBH4反应制得负载型的纳米铁(NZVL/CTMAB-Bent),用XRD、BET对其性能进行了表征.以硝基苯为目标污染物,试验了 -NZVI/CTMAB-Bent对不同起始浓度硝基苯的去除作用,考察了介质PH对其去除效率的影响,并与相同铁含量的纳米铁(NZVI)进行了比较.此外.还对NZVI/CTMAB-Bent还原硝基苯的机理进行了探讨.结果表明,NZVI/CTMAB-Bent对硝基苯的去除能力远高于相同铁含量的NZVI.也明显优于相同含量的有机膨润土和相同铁含量的NZVI对硝基苯去除率的加和.     

Factors influencing the photodegradation of N -nitrosodimethylamine in drinking water

In order to provide basic data for practical application, photodegradation experiment of N-nitrosodimethylamine (NDMA) in aqueous solution was carried out with a low-pressure Hg lamp. Effects of the initial concentration of NDMA, solution pH, dissolved oxygen, and the presence of humic acid on NDMA photodegradation were investigated. NDMA at various initial concentrations selected in this study was almost completely photodegraded by UV irradiation within 20 min, except that at 1.07 mmol/L, NDMA could be photodegraded almost completely in the acidic and neutral solutions, while the removal efficiency decreased remarkably in the alkaline solution. Dissolved oxygen enhanced the NDMA photodegradation, and the presence of humic acid inhibited the degradation of NDMA. Depending on the initial concentration of NDMA, NDMA photodegradation by UV obeyed the pseudo-first-order kinetics. Dimethylamine, nitrite, and nitrate were detected as the photodegradation products of NDMA. ¹O₂ was found to be the reactive oxygen species present in the NDMA photodegradation process by UV, based on the inhibiting experiments using tert-butanol and sodium azide.     

NZVI/Na2S2O8/超声复合法降解污染土壤PCB-29

多氯联苯（polychlorinated biphenyls,PCBs）是一类具有高毒性、难降解的有机化合物,为了研发土壤中多氯联苯（PCBs）污染物高效处理技术,本研究采用PCBs中的2,4,5-三氯联苯（PCB-29）作为研究对象,以纳米零价铁（NZVI）活化Na₂S₂O₈,再辅以超声氧化对土壤中PCB-29进行降解试验,结果表明,NZVI/Na₂S₂O₈/超声复合法对污染土壤中PCB-29具有很好的去除效果,降解反应时间为1h时,去除率最高可达86.37%;NZVI/Na₂S₂O₈/超声复合法对PCB-29最佳降解条件为土壤初始pH值为5.0,Na₂S₂O₈浓度为12mmol/L,Na₂S₂O₈/NZVI物质的量比1：1.     

氧化石墨烯负载零价纳米铁吸附水中环丙沙星的研究

通过溶液还原法制备了氧化石墨烯负载零价纳米铁NZVI16-GO1(F16G1),并将其用于水中环丙沙星的去除.同时,采用X射线衍射仪(XRD)、场发射扫描电镜(FE-SEM)、能谱仪(EDS)和热重分析仪(TG)等手段表征了F16G1的结构、化学组成和微观形貌.结果发现,F16G1对水中环丙沙星具有良好的吸附性能;氧化石墨烯的引入可以有效降低零价纳米铁的自身团聚;F16G1与环丙沙星的吸附作用很大程度上受静电引力的影响.实验同时考察了p H值、反应时间、初始浓度、投加量等因素对F16G1吸附环丙沙星的影响.结果表明,在p H=4~5之间,溶液的p H值对吸附量没有明显影响;F16G1对环丙沙星的最大吸附量是656.66 mg·g-1;Langmuir等温吸附模型可以用来描述吸附平衡过程.零价纳米铁的磁性使复合材料便于回收.     

Pd/Fe0双金属复合催化纤维降解水中痕量亚硝基二甲胺

存在于环境水体中的亚硝基二甲胺(NDMA)是一种强致癌性有机物,采用零价铁催化还原技术可以将其降解转化为低毒性物质,针对水中痕量NDMA的去除,需要深入开展基于高效零价铁材料、还原性能及还原机制方面的研究.以聚丙烯(PP)纤维为基材,采用紫外辐射接枝-金属离子配位-化学还原方法制备了含Pd/Fe~0双金属的复合催化纤维(Pd/Fe~0-PP-gAA),开展水中亚硝基二甲胺的去除研究.通过SEM、ICP-AES和XPS分析等对Pd/Fe~0/PP-g-AA进行表征.研究了不同制备条件和反应条件下,复合催化纤维对NDMA的降解性能.结果表明,丙烯酸单体质量分数为20%时,通过配位还原制备的复合催化纤维对NDMA的催化降解效果最佳,降解过程符合准一级反应动力学模型.在痕量浓度范围,NDMA初始浓度和溶液pH对复合纤维还原NDMA的性能影响不大.CO_3~(2-)和NO_3~-的存在显著抑制NDMA的降解,SO_4~(2-)、HCO_3~-和腐殖酸的存在对NDMA降解影响较小.     

Cysteine-enhanced reductive degradation of nitrobenzene using nano-sized zero-valent iron by accelerated electron transfer

As an aliphatic amino acid, cysteine (CYS) is diffuse in the living cells of plants and animals. However, little is known of its role in the reactivity of nano-sized zero-valent iron (NZVI) in the degradation of pollutants. This study shows that the introduction of CYS to the NZVI system can help improve the efficiency of reduction, with 30% more efficient degradation and a reaction rate constant nine times higher when nitrobenzene (NB) is used as probe compound. The rates of degradation of NB were positively correlated with the range of concentrations of CYS from 0 to 10 mmol/L. The introduction of CYS increased the maximum concentration of Fe(III) by 12 times and that of Fe(II) by four times in this system. A comparison of systems featuring only CYS or Fe(II) showed that the direct reduction of NB was not the main factor influencing its CYS-stimulated removal. The reduction in the concentration of CYS was accompanied by the generation of cystine (CY, the oxidized form of cysteine), and both eventually became stable. The introduction of CY also enhanced NB degradation due to NZVI, accompanied by the regeneration of CYS. This supports the claim that CYS can accelerate electron transfer from NZVI to NB, thus enhancing the efficiency of degradation of NB.     

CMC改性纳米Fe/Cu双金属模拟PRB去除地下水中2,4-二氯苯酚

使用羧甲基纤维素钠（CMC）对纳米零价铁（NZVI）改性,并将铜（Cu）作为复合金属,制得改性纳米Fe/Cu双金属.同时采用模拟反应柱模拟可渗透反应墙（PRB）去除地下水中2,4-二氯苯酚（2,4-DCP）的反应过程.改性前后材料的表征以及沉降实验结果表明,改性后的材料有更强分散性.通过考察污染物浓度、材料投加量、Cu的负载率、pH值、流量等因素对降解2,4-DCP的影响,结果表明：反应过程符合一级动力学模型,较低的pH值与较小的流速以及10%的Cu负载率有利于2,4-DCP脱氯,过多的材料投加量和过高的初始2,4-DCP浓度不利于其脱氯.     

零价纳米铁处理水中Cr(Ⅵ)的实验研究

采用NaBH4还原Fe3+制备纳米级零价铁(NZVI).运用X射线衍射(XRD)、扫描电镜(SEM)对样品进行表征.以Cr(Ⅵ)为研究对象,批实验考察了初始浓度、纳米铁投加量、温度对去除效果的影响,研究NZVI对Cr(Ⅵ)离子的吸附动力学.结果表明,NZVI加入量0.15 gL,水体中20 mg/L的Cr(Ⅵ)的去除率...