In this work, xylene removal from waste gas streams was investigated via catalytic oxidation over Pd/carbon-zeolite and Pd/carbon-CeO2 nanocatalysts. Activated carbon was obtained from pine cone chemically activated using ZnCl2 and modified by H3PO4. Natural zeolite of clinoptilolite was modified by acid treatment with HCl, while nano-ceria was synthesized via redox method. Mixed supports of carbon-zeolite and carbonceria were prepared and palladium was dispersed over them via impregnation method. The prepared samples were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), Brunauer-Emmett-Teller surface area (BET), Fourier transform infrared spectroscopy (FTIR) and thermogravimetric (TG) techniques. Characterization of nanocatalysts revealed a good morphology with an average particle size in a nano range, and confirmed the formation of nano-ceria with an average crystallite size below 60 nm. BET analysis indicated a considerable surface area for catalysts (～1000 m2·g?1). FTIR patterns demonstrated that the surface groups of synthesized catalysts are in good agreement with the patterns of materials applied in catalyst synthesis. The performance of catalysts was assessed in a low-pressure catalytic oxidation pilot in the temperature range of 100° C-250°C. According to the reaction data, the synthesized catalysts have been shown to be so advantageous in the removal of volatile organic compounds (VOCs), representing high catalytic performance of 98% for the abatement of xylene at 250°C. Furthermore, a reaction network is proposed for catalytic oxidation of xylene over nanocatalysts. 相似文献
Catalytic wet air oxidation (CWAO) is one of the most promising technologies for pollution abatement. Developing catalysts with high activity and stability is crucial for the application of the CWAO process. The Mn/Ce complex oxide catalysts for CWAO of high concentration phenol-containing wastewater were prepared by coprecipitation. The catalyst preparation conditions were optimized by using an orthogonal layout method and single-factor experimental analysis. The Mn/Ce serial catalysts were characterized by Brunauer-Emmett-Teller (BET) analysis and the metal cation leaching was measured by inductively coupled plasma torch-atomic emission spectrometry (ICP-AES). The results show that the catalysts have high catalytic activities even at a low temperature (80°C) and low oxygen partial pressure (0.5 MPa) in a batch reactor. The metallic ion leaching is comparatively low (Mn<6.577 mg/L and Ce<0.6910 mg/L, respectively) in the CWAO process. The phenol, CODCr, and TOC removal efficiencies in the solution exceed 98.5% using the optimal catalyst (named CSP). The new catalyst would have a promising application in CWAO treatment of high concentration organic wastewater. 相似文献
A series of Co-La catalysts were prepared using the wet impregnation method and the synthesis of catalysts were modified by controlling pH with the addition of ammonium hydroxide or oxalic solution. All the catalysts were systematically investigated for NO oxidation and SO2 resistance in a fixed bed reactor and were characterized by Brunanuer–Emmett–Teller (BET) method, Fourier Transform infrared spectroscopy (FTIR), X–ray diffraction (XRD), Thermogravimetric (TG) and Ion Chromatography (IC). Among the catalysts, the one synthesized at pH = 1 exhibited the maximum NO conversion of 43% at 180°C. The activity of the catalyst was significantly suppressed by the existence of SO2 (300 ppm) at 220°C. Deactivation may have been associated with the generation of cobalt sulfate, and the SO2 adsorption quantity of the catalyst might also have effected sulfur resistance. In the case of the compact selective catalytic reduction (SCR), the activity increased from 74% to 91% at the highest gas hourly space velocity (GHSV) of 300000 h–1 when the NO catalyst maintained the highest activity, in excess of 50% more than that of the standard SCR.
