高分子水凝胶灭火剂黏附性改进与应用研究

为提升水系灭火剂的灭火效率,设计实验室测试方法并搭建实物模型,研究高分子水凝胶灭火剂的应用性能。首先,分析高分子水凝胶灭火剂的保水性、黏附性等基础性能;然后,在水凝胶灭火剂中添加5大类24种添加剂,在实验室分别测试其性能,并与原灭火剂做对比,筛选出黏附性、耐高温性最佳的添加剂;最后,搭建实物模型,验证改进后的水凝胶灭火剂的性能。结果表明:凹凸棒土对水凝胶灭火剂的黏附性和耐高温性的提升效果最佳;添加凹凸棒土的改进灭火剂能降低罐壁峰值温度,并延迟罐壁达到峰值温度的时间,对相邻罐的冷却效果良好。     

活化改性半焦用于烟气脱硫催化剂制备工艺优化

为研究不同制备工艺条件下的烟气脱硫催化剂吸附去除烟气中硫化物的性能,采用硝酸活化的半焦脱硫剂,通过穿透时间和硫容评价所制备催化剂的脱硫性能.采用固定床反应器考察了催化剂表面基团酸碱性、催化剂成型的制备顺序、黏结剂和催化剂尺寸及负载金属氧化物等制备工艺条件对催化剂脱硫性能的影响.结果表明:原料半焦表面呈碱性,半焦经硝酸氧化改性后,表面呈酸性,高温煅烧可以使半焦表面酸性官能团分解成碱性官能团,催化剂表面净碱量越大,脱硫性能越好;采取先将半焦成型再进行高温煅烧、水气活化的工艺,脱硫活性更高;最适合的黏结剂为煤焦油;最佳的催化剂粒径为3mm;烟气中通入O2能显著提高半焦吸附催化剂的脱硫性能,O2体积分数以5％为宜,烟气中适量H2O是脱硫必不可少的条件,水汽体积分数以8％最佳;在催化剂制备过程中添加质量分数为1％的V2O5,可以明显改善催化剂的脱硫性能.     

Ni-Cu金属氧化物改性活性炭同时脱硫脱硝性能研究

采用浸渍法改性活性炭,分析了单组份Cu和双组份Cu-Ni金属氧化物对活性炭改性后同时脱硫脱硝性能的影响。实验中用于改性的产物分为两组:x%CuO-AC,5%NiO-x%CuO/AC(x%表示负载的物质占总物质的百分比),在不同温度下测试了活性。结果表明,CuO单独改性活性炭可以提高120℃下活性炭同时脱硫脱硝性能,且6%CuO/AC效果最好;在CuO/AC上负载5%的NiO,可以进一步提高120℃下活性炭同时脱硫脱硝性能,且5%NiO-2%CuO/AC的效果最好。     

MCM-41吸附法脱除烟气中二氧化硫的研究

基于活性炭吸附剂存在再生成本高、高温吸附能力差以及在高湿高温下脱附后性能严重下降等问题,研究采用MCM-41材料作为新型烟气脱硫吸附材料,该材料具有表观均匀、比表面积大、耐高温、脱附后能高效利用等优点,该研究设计了一种基于MCM-41材料的烟气脱硫吸附装置。介绍了该烟气脱硫吸附装置的结构、工作原理,并对MCM-41材料和活性炭在烟气中二氧化硫吸附效果进行了对比实验研究。研究结果表明:MCM-41吸附剂脱硫性能优异,相比活性炭吸附剂,脱硫效率提高了4%~8.4%,基于MCM-41材料的烟气脱硫吸附装置结构紧凑、占地面积小、吸附剂更换方便、脱硫效率高,在烟气排放量较小的各类工业企业脱硫系统中具有广泛的应用前景。     

影响脱硫塔性能的因素分析与研究

湿法烟气脱硫是成熟且具有较好发展前景的工艺,其中关键是对脱硫塔的选择及通过各项参数的控制达到良好的脱硫效率.通过对脱硫塔酸碱度(PH)、气液比(L/G)、流场特性、结垢等各种性能进行分析研究,对脱硫塔的选择和实际运行具有一定的指导意义.     

含添加剂细水雾灭火性能评价方法探讨

采用正交实验设计方法,设计了含添加剂细水雾灭火有效性实验,大大减少了实验工作量;同时通过灭火时间、温度变化、烟气成分变化、火焰形状变化4个灭火有效性评价参数和添加剂的灭火效率、对环境的影响程度、价格、稳定性、对系统的腐蚀性5个主要性能参数,建立了含添加剂细水雾灭火剂性能的综合评价方法;结合具体实验运用综合评价方法对含添加剂细水雾灭火实验数据进行综合分析,得出其中的最优添加剂。提出的含添加剂细水雾灭火性能的综合评价方法,对研究细水雾灭火具有一定的理论指导意义和实际应用价值。     

烟气组分对活性炭脱硫性能的影响

活性炭应用于烟气脱硫技术具有脱硫效率高、原料来源广泛、工艺适应范围广、环保性能好、脱硫过程不耗水等优点,受到人们的高度重视。简要介绍了我国SO2的污染现状及目前各种脱硫技术,采用干法脱硫工艺,着重对影响脱硫效率的反应温度、烟气中O2体积分数、SO2体积分数和活性炭粒径等因素进行了研究。结果表明:1)温度的降低有利于提高脱除SO2的效率;2)烟气中O2体积分数越高,活性炭脱硫效果越好,活性炭脱硫能力与烟气中O2体积分数成正比;3)烟气中SO2体积分数越低,活性炭脱硫效果越好,活性炭脱硫能力随SO2体积分数增加而降低;4)活性炭粒径对活性炭的脱硫能力没有明显影响。     

文丘里旋风水膜除尘器利用废碱液脱硫的试验研究

试验研究了文丘里旋风水膜除尘器利用废碱液进行烟气脱硫时,主要参数对脱硫效率的影响,并运用双膜理论对试验结果进行了分析,结果表明该方法可达７０％－８０％的脱硫效率,本研究的除尘脱硫一体化的设计及利用废碱液除尘脱硫的运行操作提供依据。     

基于双循环多级水幕塔的有机酸强化烟气脱硫性能研究

双循环多级水幕塔在传统双循环脱硫反应器基础上进行了改进,采用不同pH值对上、下循环进行控制,以多级水幕代替传统的多层喷淋,因而可增强气液传质效果。石灰石溶解特性试验发现,甲酸、己二酸和柠檬酸浓度分别为10 mmol/L、5 mmol/L和5 mmol/L时,石灰石的溶解效果最佳。其中,加入10 mmol/L的甲酸时,0.5~1.5 h内石灰石溶解速率约提高10%;加入5 mmol/L己二酸,2 h内石灰石的转化率达95.02%,比空白试验缩短3 h,石灰石溶解率提高约15%;加入5 mmol/L柠檬酸时,石灰石溶解率增加3%~15%,达到平衡的反应时间缩短2 h。显然5 mmol/L己二酸的促溶效果最好。以促溶效果最好的己二酸进行强化脱硫试验,己二酸浓度为3 mmol/L时的脱硫效率比无添加剂时提高了7%以上。研究表明,双循环多级水幕塔己二酸强化脱硫效果显著,在相同脱硫效率前提下,双循环多级水幕塔己二酸强化脱硫L/G的运行经济性明显低于无添加剂脱硫L/G的。     

脱硫塔气流均布数值模拟

针对湿法脱硫塔内部流场不均匀等问题,提出一种用于气流均布的倒“V”字形气流均布板,运用CFX软件分别对装有孔隙率为40％、50％和60％的气流均布板的脱硫塔在引入2层喷淋的情况下进行流场数值模拟,并与无气流均布板的情况进行对比.结果表明,未加气流均布板时,脱硫塔内烟气分布不均匀,横截面的烟气速度标准方差最高达到2.024;加装倒“V”字形气流均布板后,脱硫塔内烟气流场改善效果明显,横截面速度标准方差可减小到约1.1.综合分析脱硫塔内流场、温度场和压力场,发现安装孔隙率约50％的气流均布板时效果较为理想.研究表明,脱硫塔内加装倒“V”字形气流均布板可提高脱硫效率,应用在氨法脱硫系统中可有效减少氨逃逸.     

燃煤电厂非颗粒态汞的捕集技术概述

基于燃煤电厂现有设备,根据不同形态汞的特殊物化性质,分别介绍了湿法脱硫系统和选择性催化还原脱硝装置对元素态汞的氧化、湿法脱硫系统固定氧化态汞等技术的研究现状。文章分析了WFGD中氧气、SCR催化剂组分等因素对氧化Hg~0的影响,阐述了不同添加剂对于抑制脱硫浆液中Hg~(2+)再还原的效果。最后根据燃煤电厂烟气脱汞技术的发展需要,提出发展设备分工式脱除非颗粒态汞的研究方向。     

循环流化床锅炉脱硫对尾部电除尘器的影响

分析了循环流化床锅炉添加石灰石、生石灰和熟石灰脱硫对尾部除尘器的影响 ,主要从烟气含尘浓度和粉尘比电阻两个方面进行计算分析。     

Effects of typical additives on the thermal stability of ammonium peroxydisulfate

Ammonium peroxydisulfate (APS), one of the most widely used inorganic peroxides in the process industries, is a thermally unstable peroxide and potent oxidizer due to the presence of peroxy bond in the molecule and is incompatible with most substances. To investigate the effect of typical additives on the thermal decomposition of APS, in this paper, diamine phosphate (DAP), monoamine phosphate (MAP), and aluminum hydroxide (AH) were selected as additives; pure APS and samples with 10 wt% and 20 wt% of additives were first tested by differential scanning calorimetry (DSC). The experiments and analysis showed that the samples with 10 wt% of additive had better thermal stability than those with 20 wt% of additive. After screening, the three groups of 10 wt% AH, 10 wt% MAP, and 20 wt% MAP additive conditions could be considered to have a better thermal stability effect on the thermal decomposition of APS. Four groups of samples were, in turn, tested by Phi-Tec II. The adiabatic results showed two discontinuous exothermic processes; 10 wt% AH promoted the weak exothermic effect in the first stage. In contrast, the three groups of additives in the main exothermic stage showed different degrees of inhibition, and the inhibiting effect was ranked as 10 wt% AH, 10 wt% MAP, and 20 wt% MAP in order. Finally, the self-accelerated decomposition temperature (SADT) was calculated under the 25 kg standard package. The adiabatic results, including SADT, were combined to render feasible recommendations for the use of additives, which provides references for the packaging and transportation of additives and their applications.     

湿法烟气脱硫机理与工程对策

烟气脱硫关注的是对流扩散.脱硫工艺根据双膜理论的基本概念所确定的相际传质速度关系,为传质设备设计的主要依据.烟气脱硫技术中大量采用化学吸收法.合理提高吸收塔内烟气流速,有利于提高系统传质速率,减少传质阻力;通过对塔局部优化设计,可增强系统传质性能.对石灰石-石膏法而言,液气比决定了石灰石的消耗量.烟气中的飞灰既在液相膜表面结壳,阻碍石灰石的溶解,又影响脱硫系统含尘量排放指标,降低石膏品质.石灰石粒径确定原则为在保证一定脱硫率的前提下,获取最优的经济指标.浆液的pH值是影响脱硫效率的重要因素.通过对系统操作、运行和设计中几个重要参数的分析,提出相应工程对策.     

浅谈顶吹氧气转炉炼钢湿法除尘的脱硫功能

立足鞍钢生产实际,肯定了氧气转炉炼钢湿法除尘的降温功能与作用、除尘功能与作用,揭示了氧气转炉炼钢湿法除尘装置在碱性洗涤溶液(pH=12.0～13.5)作用下的潜在脱硫功能与作用(脱硫率99.56%),为“分体组合”选型湿法“降温除尘脱硫”设备处理高温含硫气体提供了科学依据。     

不同添加剂对聚氨酯泡沫材料阻燃性能的影响

为研究不同添加剂对聚氨酯泡沫材料阻燃性能的影响,对磷酸、硼酸、杨梅单宁阻燃剂3种添加剂处理后的聚氨酯泡沫材料与标准样分别测定氧指数、热值、烟密度等级和热稳定性,并以层次分析法评价阻燃性能优劣。结果表明:4种材料PUF STD、PUF PA、PUF BA、PUF FR的OI、CV依次分别为34.71%、38.59%、35.88%、37.86%,17.4023、16.7037、15.3197、15.0397kJ/g,燃烧时均少烟,热稳定性排序为:TS PA>TS STD>TS FR>TS BA;采用层次分析法分析3种添加剂对聚氨酯泡沫材料阻燃性能的影响顺序由优到劣为:PUF PA>PUF FR>PUF BA>PUF STD。该结论可为聚氨酯材料阻燃添加剂的选择提供参考方向。     

含NaCl超细水雾抑制甲烷爆炸实验研究

为研究含NaCl添加剂超细水雾对甲烷爆炸的影响,在自制的半封闭透明管道内,进行含NaCl添加剂超细水雾抑制甲烷爆炸试验,通过检测和分析在不同NaCl浓度情况下超细水雾的粒径和甲烷爆炸的平均火焰传播速度、爆炸超压以及平均升压速率,探究NaCl浓度对超细水雾粒径及其对抑制甲烷爆炸有效性的影响。研究结果表明:NaCl浓度对超细水雾粒径影响较小;对于体积分数为9.5%的甲烷,相比于纯甲烷爆炸,其平均火焰传播速率、最大爆炸超压以及平均升压速率分别下降了53.7%,63.4%和60.7%,相比于超细纯水雾,其平均火焰传播速率、最大爆炸超压以及平均升压速率分别下降了38.6%,58%,56%;在通雾量相同的条件下,浓度为2.5%NaCl超细水雾对体积分数为9.5%的甲烷爆炸抑制性能最佳;含NaCl添加剂超细水雾的物理化学共同作用可以有效抑爆甲烷。     

尼龙的阻燃研究进展

综述了近年来对尼龙阻燃的最新研究进展，尼龙是相对易燃材料，因此在应用中要进行阻燃处理。主要讨论了关于含卤、含磷、含氮、含硫、含硅、含溴化合物的尼龙的阻燃性研究，也讨论了一些无机添加剂和成炭有机物。可以认为尚未有理想的方法对尼龙阻燃而又不损失其物理性能。低卤和非卤阻燃剂以及多种阻燃剂共同作用的复合型阻燃聚酰胺会越来越得以发展。     

[HPMo][OTAC]2/SiO2的制备及其催化柴油氧化脱硫的研究

采用溶胶-凝胶法制备不同负载量的[HPMo][OTAC]2/SiO2,通过红外光谱、比表面积和孔结构分析对[HPMo][OTAC]2/SiO2进行表征,考察负载量、催化剂用量、氧化剂用量、反应温度和反应时间对模拟柴油脱硫效果的影响。结果表明,掺杂后的催化剂保持了Keggin结构,[HPMo][OTAC]2/SiO2在最佳反应条件下,苯并噻吩的脱除率达到48.3%,二苯并噻吩的脱除率达到67.2%。