Physical characteristics of sintered fly ash aggregate containing clay binders

A comprehensive research has been conducted to explore the influence of sintering on the properties of fly ash aggregate containing clay binders (bentonite and kaolinite). Fly ash aggregate containing clay binders, have been subjected to various sintering temperatures at different durations of 700?C1400?°C and 15?C120?min, respectively. The variation in aggregate properties, viz strength, water absorption, density and shrinkage during sintering, have been determined and discussed. In addition to these, the uniformity of sintering and rate of water absorption of sintered aggregate were also determined. No significant changes in aggregate properties were observed for aggregate sintered up to 900?°C, due to the insufficient sintering temperature range. However, the aggregate properties substantially enhanced for temperature above 1000?°C, which is attributed to the activation of liquid phase sintering. For temperatures between 1000 and 1300?°C, the aggregate with bentonite shows significant increase in shrinkage (30?%), density (density ratio 0.70), higher ten percent fines value (TPFV) (6.13?tonne), reduction in porosity (35?%), and water absorption of 4?%. However, at 1400?°C, the aggregate properties degraded due to the decomposition of mineral phases in bentonite. For aggregates with kaolinite, highest TPFV of 8.5?tonne with lowest water absorption of 2?% have been observed at 1400?°C. The presence of a higher amount of interconnected pores for aggregates sintered between 700 and 1000?°C leads to a higher rate of water absorption and then reduces to 30?% for temperatures between 1200 and 1300 and 1200 to 1400?°C for bentonite and kaolinite aggregates, respectively. This reduction is due to the reduced interconnected pores. Duration of sintering has no impact on the aggregate properties for temperatures up to 800 and 1000?°C for aggregates with bentonite and kaolinite, respectively. However, between 1000 and 1400?°C, there has been considerable improvement in the aggregate properties for increasing duration up to 60?min. In comparison, during sintering, aggregates with bentonite possessed better properties for temperature less than 1000?°C, whereas aggregates with kaolinite exhibited superior properties between 1100 and 1400?°C.     

Evaluation on the applicability of dry processed bottom ash as lightweight aggregate for construction fields

Currently, wet bottom ash is not sufficiently utilized due to its content of unburned coal, chloride and moisture. In contrast, bottom ash discharged from the recently introduced dry process spends a longer time on the clinker conveyer in the lower part of the boiler and consequently contains a significantly smaller amount of unburned coal. Consequently, it has high potential for use as a lightweight aggregate for construction material because of properties such as high porosity, low unburned coal content, non-chloride, and non-moisture. However, it is not frequently used for construction because the ash particle has a flat and thin shape, coarse surface and unfavorable structural strength. Against this backdrop, this study has conducted a range of experiments to identify the shapes, structure, density, absorption, percentage of floating particles, unit volume weight, solid volume, characteristics of air bubbles and micro pores, crushing strength of bottom ash, and the following results were observed. Though the dry bottom ash has sharp and angular edges, its flat and thin shapes lead to vulnerable structures. Dry bottom ash of the size of 0.6 mm or larger has 50–60 % of the total pore rate and 30–50 % of the closed pore rate. Considering these qualities, by removing the relatively fragile surface parts and making the particles more globular, dry bottom ash can be used as a lightweight aggregate for construction field having outstanding performance in terms of light weight and insulation.     

Evaluation of bioaccessible arsenic in fly ash by an in vitro method and influence of particle-size fraction on arsenic distribution

A huge amount of fly ash is produced by coal-fired power plants every year in China and leads to increasing environmental problems associated with disposal and treatment. It will be very helpful for the study of management and disposal of solid waste to understand the bioaccessibility and environmental behaviors of arsenic in fly ash. In this paper, an in vitro physiologically-based extraction test was applied to estimate the solubility and bioaccessibility of arsenic in fly ash in the human gastrointestinal tract. The fly ash samples were sieved into different fractions with different particle sizes (100–60, 60–10, 10–2.5, <2.5 μm). The influence of particle size on both total and bioaccessible arsenic was also investigated. The results demonstrated that arsenic concentrations in fly ash were significantly correlated with particle size. The proportion of bioaccessible arsenic (gastric and intestinal arsenic) accounting for the total arsenic was in the range of 36–67 %. The statistic analysis indicated that total arsenic in fly ash was linearly correlated with bioaccessible arsenic. The results illustrated that bioaccessible arsenic was dominated by total arsenic.     

The Effects of Additives on the Biodegradation of Polycaprolactone Composites

Because environmental pollution caused by plastic waste is a major problem investigations concerning biodegradable packaging are important and required. In this study, the biodegradation of PCL composite films with organic (glycerol monooleate and oleic acid) and inorganic additives (organo nano clay) was investigated to understand which additive and the amount of additive was more effective for biodegradation. The relationship between the degree of crystallinity and the effect of additives on the biodegradability of polycaprolactone (PCL) was examined. PCL composite films were prepared using organo nano clay (0.1–0.4–1–3 wt%) and oleic acid (1–3–5 wt%) or GMO (1–3–5 wt%). The 35 films prepared with PCL (P), clay (C), oleic acid (O), or glycerol monooleate (G) are coded as P_C#wt%_O (or G)#wt%. The composite films, P_C0.4_O5 contains 0.4 wt% clay and 5 wt% oleic acid and the P_C3_G1 contains 3 wt% clay and 1 wt% glycerol monooleate. The biodegradation of PCL films in simulated soil was studied for 36 months. The films were periodically removed from the simulated soil and film thicknesses, weight losses, visual changes, crystal structures, and a functional group analyses were performed. PCL composite films are separated into three groups, depending on degradation time, (1) films that degraded before 8 months (fast degradation), (2) films that degraded around 24 months (similar to neat PCL), and (3) films that take longer to degrade (slow degradation). The films in the first group are PCL films with 1 and 3 wt% clay additive and they begin to biodegrade at the 5th month. However, a composite film of PCL with only 0.4 wt% clay and 5 wt% GMO addition has the shortest degradation time and degraded in 5 months. The films in the last group are; P_G3, P_G5, P_C0.1, P_C0.1_O1, and P_C0.1_O5 and they took around 30 months for biodegradation. It was observed that increasing the organo nanoclay additive increases the biodegradability by disrupting the crystal structure and causing a defective crystal formation. The addition of GMO with organo nano clay also accelerates biodegradation. The addition of organo nano clay in an amount as small as 0.1 wt% acts as the nucleating agent, increases the degree of crystallinity of the PCL composites, and slows the biodegradation period by increasing the time.     

Recycling of combined coal-biomass ash from electric power plant waste as a cementitious material: characteristics and improvement

Combined coal-biomass ash has an enormous impact on environmental quality near electric power plants. This paper describes an alternative to disposal in which the ash is used to produce cementitious materials. Ash was obtained from combustion of coal and biomass containing four mass ratios of anthracite, bitumen, rice husks, and eucalyptus bark. The cement-forming properties were systematically characterized including compressive strength development, durability, and expansion in water. The ash samples were ground to increase the specific surface area, and then used to partially replace ASTM Type I Portland cement in mixtures containing 15, 30, or 45 % ash by mass. The water-binder material's (Portland cement with or without combined coal-biomass ash) ratios (w/c) were held constant at 45, 55, or 65 % by mass. Types A, B, and D ash behaved similarly, while the properties of type C ash were slightly different. Increasing the ash fraction in Portland cement mixtures increased the water requirement and resulted in lower compressive strength. Thorough mechanical grinding reduced the porosity and significantly enhanced the material properties.     

Comparative study on the characteristics of fly ash and bottom ash geopolymers

This research was conducted to compare geopolymers made from fly ash and ground bottom ash. Sodium hydroxide (NaOH) and sodium silicate (Na(2)SiO(3)) solutions were used as activators. A mass ratio of 1.5 Na(2)SiO(3)/NaOH and three concentrations of NaOH (5, 10, and 15M) were used; the geopolymers were cured at 65 degrees C for 48 h. A Fourier transform infrared spectrometer (FT-IR), differential scanning calorimeter (DSC), and scanning electron microscope (SEM) were used on the geopolymer pastes. Geopolymer mortars were also prepared in order to investigate compressive strength. The results show that both fly ash and bottom ash can be utilized as source materials for the production of geopolymers. The properties of the geopolymers are dependent on source materials and the NaOH concentration. Fly ash is more reactive and produces a higher degree of geopolymerization in comparison with bottom ash. The moderate NaOH concentration of 10 M is found to be suitable and gives fly ash and bottom ash geopolymer mortars with compressive strengths of 35 and 18 MPa.     

Porous materials produced from incineration ash using thermal plasma technology

This study presents a novel thermal plasma melting technique for neutralizing and recycling municipal solid waste incinerator (MSWI) ash residues. MSWI ash residues were converted into water-quenched vitrified slag using plasma vitrification, which is environmentally benign. Slag is adopted as a raw material in producing porous materials for architectural and decorative applications, eliminating the problem of its disposal. Porous materials are produced using water-quenched vitrified slag with Portland cement and foaming agent. The true density, bulk density, porosity and water absorption ratio of the foamed specimens are studied here by varying the size of the slag particles, the water-to-solid ratio, and the ratio of the weights of the core materials, including the water-quenched vitrified slag and cement. The thermal conductivity and flexural strength of porous panels are also determined. The experimental results show the bulk density and the porosity of the porous materials are 0.9–1.2 g cm^?3 and 50–60%, respectively, and the pore structure has a closed form. The thermal conductivity of the porous material is 0.1946 W m^?1 K^?1. Therefore, the slag composite materials are lightweight and thermal insulators having considerable potential for building applications.     

New technology and application of brick making with coal fly ash

China has ranked first in the coal fly ash emission in the world. The multipurpose use of the fly ash from power plant waste is always an important topic for the Chinese environmental protection, which has drawn the concern of the government, scientific research departments, manufacturing enterprises and industry experts. This paper introduces an experimental research on how to recycle fly ash effectively, a kind of new technology of making bricks by which fly ash content could be amounted to 50–80 %. The article introduces raw materials of fly ash brick, production process and key control points. It introduces how to change the technical parameters of the existing brick-making mechanical device, optimize the parameters combination and improve the device performance. High-content fly ash bricks are manufactured, which selects wet fly ash from power plants, adding aggregate with reasonable ratio and additives with reasonable dosage, and do the experimental research on manufactured products for properties, production technology and selection about technology parameters of production equipment. All indexes of strength grade, freezing-thawing resisting, and other standards of the studied bricks reached the national standards for building materials industry.     

Fly ash of mineral coal as ceramic tiles raw material

The aim of this work was to evaluate the use of mineral coal fly ash as a raw material in the production of ceramic tiles. The samples of fly ash came from Capivari de Baixo, a city situated in the Brazilian Federal State of Santa Catarina. The fly ash and the raw materials were characterized regarding their physical chemical properties, and, based on these results; batches containing fly ash and typical raw materials for ceramic tiles were prepared. The fly ash content in the batches varied between 20 and 80 wt%. Specimens were molded using a uniaxial hydraulic press and were fired. All batches containing ash up to 60 wt% present adequate properties to be classified as several kinds of products in the ISO 13006 standard () regarding its different absorption groups (pressed). The results obtained indicate that fly ash, when mixed with traditional raw materials, has the necessary requirements to be used as a raw material for production of ceramic tiles.     

Solidification and recycling of incinerator bottom ash through the addition of colloidal silica (SiO2) solution

The possibility of using incinerator bottom ash as a substitute for natural aggregates was investigated. Rough, porous surface of bottom ash, which diminishes the strength of solidified products, was improved by colloidal silica solution. As a result, a significant increase of mechanical strength was accomplished by a slight amount of silica (<1 wt% to total). Moreover, pozzolanic reaction was induced in initial cement hydration due to the nano-particle size of about 20 nm in colloidal silica solution. Cylindrical specimens and bricks were prepared from bottom ash added to a colloidal silica (SiO2) solution and cement, and then their compressive strengths were evaluated. Cylindrical specimens showed an increase of approximately 60% in compressive strength when colloidal solution containing 4 wt% silica particles was sprayed onto the bottom ash. The strength of bricks containing colloidal silica was in excess of 20 MPa, which meets the requirement of construction materials. Results of leaching tests based on Toxicity Characteristic Leaching Procedure (TCLP) proved that the solidified bottom ash possessed good chemical stability.     

Thermocatalytic Degradation of High Density Polyethylene into Liquid Product

Thermocatalytic degradation of high density polyethylene (HDPE) was carried out using acid activated fire clay catalyst in a semi batch reactor. Thermal pyrolysis was performed in the temperature range of 420–500 °C. The liquid and gaseous yields were increased with increase in temperature. The liquid yield was obtained 30.1 wt% with thermal pyrolysis at temperature of 450 °C, which increased to 41.4 wt% with catalytic pyrolysis using acid activated fire clay catalyst at 10 wt% of catalyst loading. The composition of liquid products obtained by thermal and catalytic pyrolysis was analyzed by gas chromatography-mass spectrometry and compounds identified for catalytic pyrolysis were mainly paraffins and olefins with carbon number range of C₆–C₁₈. The boiling point was found in the range of commercial fuels (gasoline, diesel) and the calorific value was calculated to be 42 MJ/kg.     

Glass–ceramic from mixtures of bottom ash and fly ash

Along with the gradually increasing yield of the residues, appropriate management and treatment of the residues have become an urgent environmental protection problem. This work investigated the preparation of a glass–ceramic from a mixture of bottom ash and fly ash by petrurgic method. The nucleation and crystallization kinetics of the new glass–ceramic can be obtained by melting the mixture of 80% bottom ash and 20% fly ash at 950 °C, which was then cooled in the furnace for 1 h. Major minerals forming in the glass–ceramics mainly are gehlenite (Ca₂Al₂SiO₇) & akermanite (Ca₂MgSiO₇) and wollastonite (CaSiO₃). In addition, regarding chemical/mechanical properties, the chemical resistance showing durability, and the leaching concentration of heavy metals confirmed the possibility of engineering and construction applications of the most superior glass–ceramic product. Finally, petrurgic method of a mixture of bottom ash and fly ash at 950 °C represents a simple, inexpensive, and energy saving method compared with the conventional heat treatment.     

The application and evaluation research of coffee residue ash into mortar

Coffee residue is usually regarded as a kind of agriculture waste; as its quantity increases the treatment of coffee residue will become an environmental problem. This research is innovative in that it derives the possibility of recycle application using coffee residue ash for cement replacement. In this research, coffee residue is burned in an electronic oven to three kinds of coffee residue ash at 500, 600 and 700 °C, and then appropriate apparatus is used to check the chemical and physical properties of these three types of coffee residue ash. After a general comparison, this study selected 500 and 600 °C coffee residue ashes with 2, 3, 5, 10 and 15 % cement replacements to make 5 cm³ cube mortar specimen to test different curing ages’ compressive strength. Through measurement and experiment, this research found that the compressive strength decreased by adding 500 or 600 °C coffee residue ash into the mortar. By considering waste reduction and practice application, this research derives that using the 600 °C coffee residue ash with 10 % replacement is better than others application, such using result also can get valuable efficiencies of financial and CO₂ reduction.     

Recycling MSWI bottom and fly ash as raw materials for Portland cement

Municipal solid waste incineration (MSWI) ash is rich in heavy metals and salts. The disposal of MSWI ash without proper treatment may cause serious environmental problems. Recently, the local cement industry in Taiwan has played an important role in the management of solid wastes because it can utilize various kinds of wastes as either fuels or raw materials. The objective of this study is to assess the possibility of MSWI ash reuse as a raw material for cement production. The ash was first washed with water and acid to remove the chlorides, which could cause serious corrosion in the cement kiln. Various amounts of pre-washed ash were added to replace the clay component of the raw materials for cement production. The allowable limits of chloride in the fly ash and bottom ash were found to be 1.75% and 3.50% respectively. The results indicate that cement production can be a feasible alternative for MSWI ash management. It is also evident that the addition of either fly ash or bottom ash did not have any effect on the compressive strength of the clinker. Cement products conformed to the Chinese National Standard (CNS) of Type II Portland cement with one exception, the setting time of the clinker was much longer.     

Development of lightweight aggregate from dry sewage sludge and coal ash

In this study, dry sewage sludge (DSS) as the principal material was blended with coal ash (CA) to produce lightweight aggregate. The effects of different raw material compositions and sintering temperatures on the aggregate properties were then evaluated. In addition, an environmental assessment of the lightweight aggregate generated was conducted by analyzing the fixed rate of heavy metals in the aggregate, as well as their leaching behavior. The results indicated that using DSS enhanced the pyrolysis–volatilization reaction due to its high organic matter content, and decreased the bulk density and sintering temperature. However, the sintered products of un-amended DSS were porous and loose due to the formation of large pores during sintering. Adding CA improved the sintering temperature while effectively decreasing the pore size and increasing the compressive strength of the product. Furthermore, the sintering temperature and the proportion of CA were found to be the primary factors affecting the properties of the sintered products, and the addition of 18–25% of CA coupled with sintering at 1100 °C for 30 min produced the highest quality lightweight aggregates. In addition, heavy metals were fixed inside products generated under these conditions and the As, Pb, Cd, Cr, Ni, Cu, and Zn concentrations of the leachate were found to be within the limits of China’s regulatory requirements.     

High fire resistance in blocks containing coal combustion fly ashes and bottom ash

Fire resistance recycled blocks, containing fly ash and bottom ash from coal combustion power plants with a high fire resistance, are studied in this paper by testing different compositions using Portland cement type II, sand, coarse aggregate and fly ash (up to 50% of total weight) and bottom ash (up to 30% of total weight). The fire resistance, physical-chemical (density, pH, humidity, and water absorption capacity), mechanical (compressive and flexural strength), and leaching properties are measured on blocks made with different proportions of fly ash and bottom ash. The standard fire resistance test is reproduced on 28 cm-high, 18 cm-wide and 3 cm-thick units, and is measured as the time needed to reach a temperature of 180 °C on the non-exposed surface of the blocks for the different compositions.The results show that the replacement of fine aggregate with fly ash and of coarse aggregate with bottom ash have a remarkable influence on fire resistance and cause no detriment to the mechanical properties of the product. Additionally, according to the leaching tests, no environmental problems have been detected in the product. These results lead to an analysis of the recycling possibilities of these by-products in useful construction applications for the passive protection against fire.     

The effect of the addition of fly ash to municipal digested sludge on its electroosmotic dewatering

Effective handling of municipal digested sludge requires that the product cake have low water content. To this end, we investigated the change in sludge dewaterability after the addition of fly ash to municipal digested sludge, dewatering of which is difficult because of its high organic content. The performance of the dewatering is compared with that of electroosmotic dewatering (EDW) and conventional mechanical dewatering (CMD). Fly ash classified by sieving to the size of 25–75 μm and >75 μm is added to the municipal digested sludge by 10, 20, and 50 wt% by wet base. When adding fly ash particles to municipal digested sludge, dewatering efficiency improved with smaller fly ash particle size and with increase in the amount. When sludge was dewatered using an electroosmotic dewatering method, the dewatering efficiency is improved about 40% by adding fly ash of 25–75 μm particle size with 20 wt% when compared with conventional mechanical dewatering method without adding the fly ash. It is concluded that fly ash particles rich in inorganic material are helpful in the dewatering process when added to municipal digested sludge and EDW is more effective than CDW.     

Remediation of fly ash landfills through plantation

In India, a significant area of land is occupied by preexisting coal‐fired thermal power plants (TPPs) for the storage of fly ash slurry in ash ponds. However, the area available for storage of fly ash at these TPPs is limited. In addition, this type of fly ash disposal poses a problem due to restricted land availability and potential contamination issues. A viable alternative is the reclamation of fly ash ponds by plantation. A study at the Ramagundam Super Thermal Power Station (RSTPS) in Andhra Pradesh, India, on reclamation of a portion of an ash‐filled, low‐lying area has been performed. This article describes the characteristics of the RSTPS pond ash, ash leachates, and improvements in the fertility status of the reclaimed area over a three‐year period. Furthermore, morphometric observations of different planted species indicate that these types of ash‐filled, low‐lying areas can be suitably reclaimed and the nutrient‐rich leachate from ash‐filled areas potentially can be used for irrigation purposes. © 2008 Wiley Periodicals, Inc.     

双掺粉煤灰再生骨料对混凝土强度影响研究

通过试验研究再生骨料混凝土中粉煤灰和再生骨料对混凝土强度的影响。采用粉煤灰替代部分水泥、再生骨料替代部分天然粗骨料的方法,通过正交试验测定混凝土立方体抗压强度的方法,来研究粉煤灰对再生骨料混凝土强度的影响。试验得出:当再生骨料掺量为20%~30%时,粉煤灰的最佳掺量为20%左右;当再生骨料掺量高于40%、粉煤灰掺量高于20%时,其混凝土拌合物搅拌时间不小于240 s,且当粉煤灰在20%~30%时,可获得较理想的混凝土抗压强度;当粉煤灰的掺入量分布在20%~30%、再生骨料的最佳掺量为50%时,可获得较理想的混凝土抗压强度。由此得出,合理的再生骨料、粉煤灰掺量对混凝土的抗压强度影响并不明显且有提高的趋势,对降低混凝土成本,提高建筑垃圾的再生利用,有一定的经济效益和社会效益。     

Gypsum treated fly ash as a liner for waste disposal facilities

Fly ash has potential application in the construction of base liners for waste containment facilities. While most of the fly ashes improve in the strength with curing, the ranges of permeabilities they attain may often not meet the basic requirement of a liner material. An attempt has been made in the present context to reduce the hydraulic conductivity by adding lime content up to 10% to two selected samples of class F fly ashes. The use of gypsum, which is known to accelerate the unconfined compressive strength by increasing the lime reactivity, has been investigated in further improving the hydraulic conductivity. Hydraulic conductivities of the compacted specimens have been determined in the laboratory using the falling head method. It has been observed that the addition of gypsum reduces the hydraulic conductivity of the lime treated fly ashes. The reduction in the hydraulic conductivity of the samples containing gypsum is significantly more for samples with high amounts of lime contents (as high as 1000 times) than those fly ashes with lower amounts of lime. However there is a relatively more increase in the strengths of the samples with the inclusion of gypsum to the fly ashes at lower lime contents. This is due to the fact that excess lime added to fly ash is not effectively converted into pozzolanic compounds. Even the presence of gypsum is observed not to activate these reactions with excess lime. On the other hand the higher amount of lime in the presence of sulphate is observed to produce more cementitious compounds which block the pores in the fly ash. The consequent reduction in the hydraulic conductivity of fly ash would be beneficial in reducing the leachability of trace elements present in the fly ash when used as a base liner.