Green Composites of Poly (Lactic Acid) and Sugarcane Bagasse Residues from Bio-refinery Processes

Twin-screw extrusion was used to prepare the composites consisting of PLA and three types of sugarcane bagasse residues (up to 30 wt%) derived from different steps of a biorefinery process. Each residue had different composition, particle size and surface reactivity due to chemical and biological (enzyme, microbes) treatments that the biomass was subjected to. The effects of different residue characteristics on properties, crystallization behaviors and morphologies of PLA composites were investigated. Besides, a small amount (2 wt%) of coupling agent, Desmodur^® VKS 20 (DVKS), was used to improve the interfacial bonding between PLA and bagasse residues. The results indicated that in the presence of 2 % DVKS, PLA composite with pretreated residue exhibited the maximum strength properties (98.94 % tensile strength and 93.91 % flexural strength of neat PLA), while PLA composite with fermentation residue exhibited the minimum strength properties (88.98 % tensile strength and 81.91 % flexural strength of neat PLA).     

Mechanical Properties of Poly (Lactic Acid)/Hemp Fiber Composites Prepared with a Novel Method

This research dealt with a novel method of fabricating green composites with biodegradable poly (lactic acid) (PLA) and natural hemp fiber. The new preparation method was that hemp fibers were firstly blending-spun with a small amount of PLA fibers to form compound fiber pellets, and then the traditional twin-screw extruding and injection-molding method were applied for preparing the composites containing 10–40 wt% hemp fibers with PLA pellets and compound fiber pellets. This method was very effective to control the feeding and dispersing of fibers uniformly in the matrix thus much powerful for improving the mechanical properties. The tensile strength and modulus were improved by 39 and 92 %, respectively without a significant decrease in elongation at break, and the corresponding flexural strength and modulus of composites were also improved by 62 and 90 %, respectively, when the hemp fiber content was 40 wt%. The impact strength of composite with 20 wt% hemp fiber was improved nearly 68 % compared with the neat PLA. The application of the silane coupling agent promoted further the mechanical properties of composites attributed to the improvement of interaction between fiber and resin matrix.     

Stiff Biodegradable Polylactide Composites with Ultrafine Cellulose Filler

Polylactide (PLA) composites with 10–30 wt% of commercial fine grain filler of native cellulose were prepared by melt-mixing, and examined. The composite films had esthetic appearance, glossy surface, creamy color and density close to that of neat PLA. Good dispersion of the filler in PLA matrix was achieved. The composites were stiffer than neat PLA; in the glassy region the storage modulus increased by approx. 30 %. The tensile strength of the composite materials in the temperature range from 25 to 45 °C was similar to that of neat PLA. No marked decrease in molar mass of PLA in the composites occurred during processing in comparison to neat PLA. Moreover, thermogravimetry experiments demonstrated good thermal stability of the composites; 5 % weight loss occurred well above 300 °C.     

Mechanical Properties and Isothermal Crystallization Behaviour of Poly(lactide)/Poly(methyl methacrylate)/α-Cellulose Composites

Polylactide (PLA)/polymethylmethacrylate (PMMA)/α-cellulose composites were fabricated using a twin-screw extruder. During fabrication, α-cellulose short fibres were incorporated for improving the toughness of the brittle PLA and a chain extender was used for reducing PLA hydrolysis. Highly transparent PLA and PMMA were blended to obtain miscible and transparent blends. For evaluating the performance of the PLA/PMMA/α-cellulose composites, a series of measurements, including tensile and Izod impact tests, light transmission and haze measurements, thermomechanical analysis, and determination of isothermal crystallisation behaviour, was conducted. Adding the chain extender considerably reduced the occurrence of hydrolytic degradation. Both the chain extender and α-cellulose short fibres increased the elongation at break and Izod impact strength of the composites. Compared with the neat PLA, including 1.0 wt% α-cellulose short fibres increased the elongation at break and Izod impact strength of the composite PLA by approximately 211 and 219 %, respectively. According to the observed mechanical performance, the optimal blending ratios for PLA and PMMA were between 90:10 and 80:20. The total light transmittance of the composites was as high as 91 %, indicating that the PLA/PMMA blend was highly miscible. The haze value of the PLA/PMMA/α-cellulose composites was lower than 32 %. Incorporating cellulose short fibres increased the number of crystallisation sites and crystallinity of the PLA/PMMA/α-cellulose composites while reducing the spherulite dimensions.     

Processing Stability and Biodegradation of Polylactic Acid (PLA) Composites Reinforced with Cotton Linters or Maple Hardwood Fibres

Polylactic acid (PLA) composites comprising up to 25 wt% cotton linter (CL) or up to 50 % maple wood fibre (WF) were prepared by compounding and injection moulding. A reduction of crystallinity in the PLA matrix was observed as a result of the thermal processing method. These PLACL and PLAWF composites provided excellent improvements in both stiffness (with increases in tensile and flexural modulus) and toughness (increases in notched impact strength) properties over the neat PLA resin, while the tensile and flexural strengths of the composites were generally unchanged, while the strain at break values were reduced in comparison to the neat PLA. DMA results indicated incorporating these fibres caused the mechanical loss factor (tan δ) to decrease, suggesting better damping capabilities were achieved with the composites. SEM analysis of the impact fractured surfaces of the PLACL composites showed debonding-cavitation at the matrix-fibre interface while the PLAWF composites showed good wetting along its matrix-fibre interface. The composting of these composites up to 90 days showed that the degradation onset time was increased when increasing the fibre loadings, but the maximum degree of degradation and the maximum daily rates of degradation were decreased compared to neat PLA. On a weight basis of fibre loading, the PLACL composites had a quicker onset of biodegradation, a higher maximum daily rate of biodegradation and, overall, a higher degree of biodegradation at 90 days than the PLAWF composites, possibly due to the quicker thermal hydrolysis observed in the PLA matrix of the PLACL composites during processing and composting.     

Polylactic Acid (PLA) Biocomposites Filled with Waste Leather Buff (WLB)

A large amount of leather waste is generated from tanning industries and most of which are disposed of landfill or discharged into the natural water bodies without any treatment, causing environmental problems. The aim of this study is to develop eco-biocomposites using waste leather buff (WLB) as filler in Polylactic acid (PLA) matrix to reduce the environmental issues and provide sustainable solution. WLB/PLA composites were prepared by twins-screw micro extruder varying the WLB content from 2% to 30 wt%. These composite were extensively characterise by several techniques. Tensile properties of the composites showed addition of WLB resulted in improvement of tensile property of composite and reduction in percentage crystallinity of PLA matrix observed with increase in WLB content. The effect of WLB on properties of interfacial adhesion and dispersion in WLB/PLA composites were studied by SEM. Wettability of composites was tested by contact angle and water absorption studies. WLB/PLA composite showed increase in water absorption with WLB loading. These WLB/PLA composite could be used to develop low cost eco-friendly product material.     

High Toughness and Fast Crystallization Poly(Lactic Acid)/Polyamide 11/SiO<Subscript>2</Subscript> Composites

A poly(lactic acid) (PLA)/polyamide 11 (PA11)/SiO₂ composite was mixed from PLA, PA11, and nanosilica particles through twin-screw extrusion. The PLA/PA11/SiO₂ composite was evaluated with tensile and Izod impact tests, light transmission and haze measurement, and isothermal and nonisothermal crystallization behavior determinations. The PLA/PA11/SiO₂ (97.0/3.0) composite had approximately 10.8% less ultimate tensile strength than neat PLA, but it had greater ductility and approximately ninefold greater elongation at break. A dimple morphology was observed on the fractural surface of the PLA/PA11/SiO₂ composite, indicating that the incorporation of PA11 and nanosilica particles increased the ductility of the PLA matrix. PLA with less than 3 wt% of PA11 and 0.5 phr of nanosilica particles had an Izod impact strength of 8.72 kJ/m². PA11 and nanosilica particles effectively toughened this PLA polymer; they accelerated both isothermal and nonisothermal crystallization rates and increased the crystallinities of the resulting composites under isothermal and nonisothermal crystallization processes.     

The Effect of Acetylation on the Hydrolytic Degradation of PLA/Clay Nanocomposites

In this study, the hydrolytic degradation of Poly(lactic acid) (PLA) and acetylated PLA (PLA-Ac)–clay nanocomposites were investigated. The organo clay was obtained by ion exchange reaction using cetyl tri methyl ammonium bromide (CTAB). Nanocomposites containing 2, 5 and 8% mass ratio of organo clay (CTAB-O) were prepared. PLA and its organo clay nanocomposites were characterized by scanning electron microscope (SEM), thermo gravimetric analysis (TGA) and X-ray diffraction (XRD) to determine the morphology before and after hydrolytic degradation. Fourier transform infrared (FTIR) analyses of PLA and PLA-Ac were also obtained. The hydrolytic degradation of polymers and their composites were investigated in the phosphate buffered saline solution (PBS). The results showed that controlled hydrolytic degradation was observed in the samples with end group modification of PLA. While weight loss of PLA films was 28%, that of PLA-Ac films was 18% after 60 days degradation time. The weight loss was obtained as 29.5 and 25.5% for PLA-5 wt% organo clay (PLA/5CTAB-O) and PLA-Ac-5 wt% organo clay (PLA-Ac/5CTAB-O) nanocomposites films, respectively. It was also observed that thermal degradation of PLA-Ac was much more than that of PLA. Hydrolytic degradation increased depending on organo clay content. The end group modificated PLA results in controlled hydrolytic degradation. While hydrolytic degradation in polymer films occurred as surface erosion, bulk erosion was observed in composite films.     

Characterization of Sorghum Bran/Recycled Low Density Polyethylene for the Manufacturing of Polymer Composites

The objective of the study was to investigate the suitability of using sorghum bran in recycled low density polyethylene (R-LDPE) composites manufacturing. In response to the disposal of environmental problematic agricultural and polymer waste, composite sheets using recycled low density polyethylene and sorghum bran of different loadings (5, 10, 15 and 20 wt%) were prepared by melt compounding and compression molding. The effects of sorghum bran loadings on the mechanical, thermal, water absorption, swelling and crystalline properties of the composites were determined. Characterization of composites was carried out using X-ray diffraction (XRD), differential scanning calorimetry (DSC), thermo gravimetric (TGA/DTG) and mechanical analyses. It was found that increasing fiber loadings resulted to increased moduli and tensile strength while hardness was decreased. XRD indicated that fiber addition to R-LDPE did not change characteristic peak position. DSC results showed that the R-LDPE had significantly larger peak heat flow during cooling run than the blank R-LDPE, showing higher crystallization rates for R-LDPE. The results obtained confirmed that sorghum bran particles showed some potential as a good reinforcement in polymer matrix composites and indicate its thermal stability for possibly future composite applications.     

Novel Tough Crystalline Blends of Polylactide with Ethylene Glycol Derivative of POSS

Blending of polylactide (PLA) with low stereoregularity and polyhedral oligomeric silsesquioxane grafted with arms of poly(ethylene glycol) methyl ether, acting as a plasticizer, allowed us previously to obtain a novel stable elastomeric-like material. The present contribution focuses on the properties of semi-crystalline PLA plasticized with this compound. Melt blends of PLA with 5–15 wt% of the plasticizer, were compression molded, quenched and annealed, which enabled cold-crystallization. The glass transition temperature of the blends and their drawability depended on their crystallinity and plasticizer content. The best ductility was reached at the plasticizer content of 15 wt%; the achieved strain at break was 6.5 (650%) and 1.3 (130%), for the quenched and annealed material, respectively. The latter value exceeded 20 times the strain at break of neat crystalline PLA. The tensile toughness of the annealed 15 wt% blend was 12 times larger than that of crystalline PLA. Moreover, annealing of 15 wt% blend improved its yield strength by 40%. Despite the two peaks of the loss modulus, indicating the two glass transitions in this blend, no heterogeneities were found by scanning electron microscopy, indicating that the plasticizer enriched phase formed instead of distinct inclusions of the plasticizer.     

Effect of Fiber Surface Treatments on Thermo-Mechanical Behavior of Poly(Lactic Acid)/Phormium Tenax Composites

In the present study, Phormium Tenax fiber reinforced PLA composites were processed by injection molding and twin screw compounding with a fiber content ranging from 10 to 30 wt%. Three surface treatment methods have been used to improve the Phormium Tenax fiber-matrix interfacial bonding that are as follows: (1) aqueous alkaline solution, (2) silane coupling agent, and (3) a combination of alkaline and silane treatment. The mechanical, thermal and morphological properties of the resulting composites were investigated. The results have shown that the moduli of surface treated fiber reinforced composites are lower than the ones obtained for untreated composites (as a consequence of the decrease in fiber modulus caused by the chemical treatments) and no significant increase in strength was observed for any of the composites compared to neat PLA. SEM micrographs of composite fractured surfaces confirmed an improvement in the interfacial strength, which was insufficient nonetheless to significantly enhance the mechanical behavior of the resulting composites. Results from thermogravimetric analysis and differential scanning calorimetry suggest that surface treatment of Phormium affects the ability of PLA to cold crystallize, and the thermal stability of the composites at the different fiber contents was reduced with introduction of alkali and silane treated Phormium fibers.     

Effect of Nano-SiO<Subscript>2</Subscript> and Bark Flour Content on the Physical and Mechanical Properties of Wood–Plastic Composites

The aim of this study is to evaluate the impact of nano-SiO₂ and bark flour (BF) on the natural fiber–plastic composites engineering properties made from high density polyethylene (HDPE) and beech wood flour (WF). For this purpose, WF and BF in 60 mesh size and weight ratio of (50, 0 %), (30, 20 %), (10, 40 %) and (0, 50 %) respectively were mixed with HDPE. In order to increase the interfacial adhesion between the filler and the matrix, the maleic anhydride grafted polyethylene was constantly used at 3 wt% for all formulations as a coupling agent. The nano-SiO₂ particles with weight ratio of 0, 1, 2, and 4 % were also utilized to enhance the composites properties. The materials were mixed in an internal mixer (HAAKE) and then the bark and/or wood–plastic composite samples were made utilizing an injection molding machine. The physical tests including water absorption and thickness swelling, and mechanical tests including bending characteristics and un-notched impact strength were carried out on the samples based on ASTM standard. The results indicated that as the BF content increased in the composite, mechanical and physical properties were reduced, but the given properties were increased with the addition of nano-SiO₂. The addition of nano-SiO₂ had a negative impact on the physical properties, but when it was up to 2 %, it increased the impact strength.     

Effect of Glycerin and Starch Crosslinking on Molecular Compatibility of Biodegradable Poly(lactic acid)-Starch Composites

Poly(lactic acid) (PLA) is a biodegradable material. However, PLA is relatively cost effective. Blending starch with PLA is one of the promising efforts because starch is a widely distributed and inexpensive product. PLA and starch were blended using a rheometer to form composites in this report. Glycerin was added into the blends to make the mixture molecular compatible and more homogeneous. The starch was crosslinked using epichlorohydrin to improve the compatibility of starch with PLA. Two series of composite were fabricated. One was PLA and the crosslinked starch containing 32 wt% glycerin. In this group, the crosslinking degree of the modified starch was varied. The second group was PLA and non-crosslinked starch with varied amount of glycerin added. Micro-structure of the blending composites was observed using a SEM to view the homogeneity of the mixture. The SEM pictures indicated that the compatibility of PLA and starch molecules was poor. The addition of glycerin can change the compatibility of PLA and starch. The higher the glycerin content in the composites, the better the compatibility between PLA and starch. Furthermore, when the starch was crosslinked by epichlorohydrin, the compatibility of PLA and starch can be greatly improved. The compatibility increases with the increase of crosslinking degree. This is due to the change of hydrophilicity of starch because the hydroxyl groups on the starch molecules were crosslinked into ether groups by the epichlorohydrin molecules.     

Preparation and Properties of Poly (Lactic Acid) Nanocomposites Filled with Functionalized Single-Walled Carbon Nanotubes

This work prepared poly (lactic acid) (PLA)/single-walled carbon nanotubes (SWCNTs) composites using a solution blend method, and investigated the influence of the physical properties of PLA/SWCNTs composites. In order to enhanced interfacial interactions between PLA and SWCNTs, the purified SWCNTs were given functionalisation treatments with a nitric acid/sulfuric acid mixture. These acid-treated SWCNTs (A-SWCNTs) were then grafted with 3-isocyanatopropyl triethoxysilane (A-SWCNTs-Si). When these functionalized SWCNTs were used to fill the PLA matrix, the fractured surface of composite does not present the pullout phenomenon. The dimensional stability obviously increased by a factor of approximately 72. The storage modulus was also significantly improved. The surface resistivity of the PLA/SWCNTs composites decreased from 1 × 10¹⁶ to 2.22 × 10⁴ Ω/cm².     

Compatibilization Improves Performance of Biodegradable Biopolymer Composites Without Affecting UV Weathering Characteristics

With growing interest in the use of eco-friendly composite materials, biodegradable polymers and composites from renewable resources are gaining popularity for use in commercial applications. However, the long-term performance of these composites and the effect of compatibilization on their weathering characteristics are unknown. In this study, five types of biodegradable biopolymer/wood fiber (WF) composites were compatibilized with maleic anhydride (MA), and the effect of accelerated UV weathering on their performance was evaluated against composites without MA and neat biopolymers. The composite samples were prepared with 30 wt% wood fiber and one of the five biodegradable biobased polymer: poly(lactic) acid (PLA), polyhydroxybutyrate (PHB), poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV), Bioflex (PLA blend), or Solanyl (starch based). Neat and composite samples were UV weathered for 2000 h (hours), and characterized for morphological, physical, thermal, and mechanical properties before and after weathering. Compared to composites without MA, composites containing MA grafted polymers exhibited improved properties due to increased interfacial adhesion between the fiber and matrix. Upon accelerated weathering, thermal and mechanical properties of 70% of the samples substantially decreased. Surfaces of all the samples were roughened, and drastic color changes were observed. Water absorption of all the samples increased after weathering exposure. Even though the compatibilization is shown to improve composite properties before weathering, it did not affect weathering of samples, as there were no considerable differences in properties exhibited by the composites with MA and without MA after weathering. The results suggest that compatibilization improves properties of biodegradable biobased composites without affecting its UV degradation properties.     

End-Of-Life Textiles as Reinforcements in Biocomposites

A number of attempts have been made to recycle cotton/polyester blend woven fabrics after use; however, most of these fabrics are disposed of in landfills. Major part of these blend fabrics are not recycled due to complexity of the fibre arrangement and cannot be separated economically. This study shows that these discarded woven fabrics could be directly used as reinforcements in composites without fibre separation. Uniform alignment in the woven fabric provided consistent properties to the composites. The fabrics were reinforced by soybean-based-bioresins to produce biocomposites. The composites were analysed for mechanical, thermal, viscoelastic and morphological properties. Porosity and wettability of the composites were also evaluated. Results demonstrate that the tensile strength and modulus of over 100 and 10 MPa, respectively, can be obtained without any fibre treatment. Furthermore, impact strength over 70 kJ/m² was obtained without any chemical treatment on fibres. The porosity of the composites produced was less than 9 vol%. Additionally, the fabrics were treated with alkali in order to improve the fibre–matrix interface and the composite properties were studied. From the economical perspective, these composites can be produced at a low cost as the major component is available for free or low cost.     

Phosphogypsum Waste Used as Reinforcing Fillers in Polypropylene Based Composites: Structural,Mechanical and Thermal Properties

The industrial production of wet phosphoric acid in Morocco led to controversial stockpiling of waste phosphogypsum by-products resulting in the release of significant amounts of toxic impurities in salt marshes. In the framework of fighting against global climate change and efforts to reduce toxic industrial wastes (phosphate industry), this work presents a new polymer composite based on phosphogypsum (PhG) and polypropylene (PP).The compounds were produced by twin-screw extrusion and injection molding. The morphological results show that good affinity between PhG and PP led to good particle dispersion/distribution in the polymer matrix. Thermal characterizations showed that PhG particles improved the thermal stability of PP with a 50 °C increase at 40 wt%. The optimum tensile modulus was also obtained at 40 wt% with a 74 % increase over neat PP. Dynamical mechanical analysis showed that PhG addition can improve the viscoelastic properties of PP for potential applications under dynamic stress. Overall, it can be concluded that PhG is potential reinforcing filler for the production of PP composites and represents a promising avenue for the valorization of this waste as a new raw material while resolving some environmental issues.     

Grafting of Glycidyl Methacrylate onto Poly(lactide) and Properties of PLA/Starch Blends Compatibilized by the Grafted Copolymer

Poly(lactide)-graft-glycidyl methacrylate (PLA-g-GMA) copolymer was prepared by grafting GMA onto PLA in a batch mixer using benzoyl peroxide as an initiator. The graft content was determined with the ¹H-NMR spectroscopy by calculating the relative area of the characteristic peaks of PLA and GMA. The result shows that the graft content increases from 1.8 to 11.0 wt% as the GMA concentration in the feed varies from 5 to 20 wt%. The PLA/starch blends were prepared by the PLA-g-GMA copolymer as a compatibilizer, and the structure and properties of PLA/starch blends with or without the PLA-g-GMA copolymer were characterized by SEM, DSC, tensile test and medium resistance test. The result shows that the PLA/starch blends without the PLA-g-GMA copolymer show a poor interfacial adhesion and the starch granules are clearly observed, nevertheless the starch granules are better dispersed and covered by PLA when the PLA-g-GMA copolymer as a compatibilizer. The mechanical properties of the PLA/starch blends with the PLA-g-GMA copolymer are obviously improved, such as tensile strength at break increasing from 18.6 ± 3.8 MPa to 29.3 ± 5.8 MPa, tensile modulus from 510 ± 62 MPa to 901 ± 62 MPa and elongation at break from 1.8 ± 0.4 % to 3.4 ± 0.6 %, respectively, for without the PLA-g-GMA copolymer. In addition, the medium resistance of PLA/starch blends with the PLA-g-GMA copolymer was much better than PLA/starch blends.     

Fabrication of Admicelled Natural Rubber by Polycaprolactone for Toughening Poly(lactic acid)

Natural rubber (NR) with polycaprolactone (PCL) core–shell (NR-ad-PCL), synthesized by admicellar polymerization, was acted as an impact modifier for poly(lactic acid) (PLA). PLA and NR-ad-PCL were melt-blended using a co-rotating twin screw extruder. The morphology of PLA/NR-ad-PCL blends showed good adhesion as smooth boundary around rubber particles and PLA matrix. Only 5 wt% of rubber phase, NR-ad-PCL was more effective than NR to enhance toughness and mechanical properties of PLA. The contents of the NR-ad-PCL were varied from 5, 10, 15 and 20 wt%. From thermal results, the incorporation of the NR-ad-PCL decreased the glass transition temperature and slightly increased degree of crystallinity of PLA. Mechanical properties of the PLA/NR-ad-PCL blends were investigated by dynamic mechanical analyser, pendulum impact tester and universal testing machine for tension and flexural properties. The increasing NR-ad-PCL contents led to decreasing Young’s and storage moduli but increasing loss modulus. Impact strength and elongation at break of the PLA/NR-ad-PCL blends increased with increasing NR-ad-PCL content up to 15 wt% where the maximum impact strength was about three times higher than that of pure PLA and the elongation at break increased to 79%.     

Effect of Hexadecyl Lactate as Plasticizer on the Properties of Poly(<Emphasis Type="SmallCaps">l</Emphasis>-lactide) Films for Food Packaging Applications

In this study, poly(l-lactide) (PLA) films were fabricated by melt processing and the plasticizing effect of hexadecyl lactate (HL) (0, 5, 7.5, 10, and 12.5 wt% on PLA were investigated by scanning electron microscopy (SEM), differential scanning calorimetry, thermogravimetric analysis, tensile, transparency, and water vapor permeability tests. The SEM analysis revealed that PLA with 10 wt% HL appeared uniform with extra small bumps, confirmed the interaction between PLA and HL. The thermal analysis revealed a glass transition temperature of 57.4 °C for neat PLA film, but the addition of HL elicited a decrease in the temperature of the peak (43.8 °C). The incorporation of plasticizer into PLA resulted in the increase of elongation at break, as well as the decrease of tensile strength and tensile modulus. Even though a decrease in transparency was recorded, the PLA/HL blend films appeared transparent by visually observation. The water vapor permeability of PLA/HL blend films increased with the increase of HL. The PLA/HL blend films could effectively extend the shelf-life of fresh-cut pears as the commercial low density polyethylene films. The results indicated that the properties of PLA films can be modified with the addition of HL and PLA/HL blend films could serve as an alternative as food packaging materials to reduce environmental problems associated with synthetic packaging films.