TiO2/陶粒光催化降解甲基橙研究

采用溶胶-凝胶法制备了以陶粒为载体的新型、高光催化活性的复合光催化剂TiO2/陶粒,使用XRD、TG-DTA、FT-IR进行表征;以甲基橙为目标降解物,考察了焙烧温度、催化剂投加量、初始pH值等因素对甲基橙去除效果的影响。结果表明:甲基橙初始浓度为100 mg/L时,最佳降解条件是pH=3,焙烧温度700℃,催化剂投加量30 g/L。     

超声强化非均相Fenton法处理甲基橙的研究

采用硅藻土负载Fe3+制备了非均相催化剂,并通过TiO2来提高催化剂的稳定性.研究了采用该催化剂的US/Fenton体系对甲基橙的降解效果.通过正交试验考察了pH值、H2O2浓度、催化剂投加量对处理效果影响的大小,分别为pH值＞H2O2＞催化剂.并通过单因素实验确定在最佳条件下:pH值=3,H2O2浓度为2 mmol/L催化剂投加量为2g/L,反应120min后,脱色率可以达到98%以上,COD的去除率也能够达到87.18%.此外Fe3+溶出实验表明TiO2可以提高催化剂的稳定性.     

纳米TiO2/硅藻土光催化降解蒽醌染料废水的研究

为提高光催化剂的稳定性,选取硅藻土为载体,以钛酸四异丙酯为前驱物,采用溶胶-凝胶法制备了TiO2/硅藻土光催化剂,并利用XRD、SEM、FT-IR等技术对其进行表征.以蒽醌染料弱酸性艳蓝RAW为目标降解物,考察了TiO2/硅藻土的光催化活性、最佳pH值范围及催化剂重复使用对光催化活性的影响.结果表明,所制备的TiO2为锐钛矿和金红石混晶型,平均粒径11nm,通过控制硅藻土加入量可以得到负载均匀的光催化剂.所制备的TiO2/硅藻土具有较强的光催化活性,对弱酸性艳蓝RAW的降解效果好于商品Degussa P25型TiO2,最佳pH值为4.0.该催化剂性质稳定,重复使用15次后,催化活性仅降低12.4%.     

多壁碳纳米管的制备与可见光催化性能

采用溶胶-凝胶法,制备了多壁碳纳米管(MWCNTs)/CdS/TiO2复合半导体光催化剂。通过扫描电镜(SEM)、X射线衍射(XRD)和紫外-可见吸收光谱(UV-vis)等分析方法对光催化剂进行了结构表征,并考察了在可见光照射条件下MWCNTs/CdS/TiO2对甲基橙(MO)降解的光催化性能。结果表明,MWCNTs/CdS/TiO2能有效降解甲基橙。低浓度MO降解效果比高浓度好,光催化剂投加量为1.2 g/L即可达到较好的催化效果,酸性条件有利于光催化,投加适宜浓度的H2O(2低于10 mmol/L)时会和催化剂产生协同效果,浓度过大,催化效果下降。阴离子对催化效果有抑制作用,其中PO43-的抑制作用最强。所制备的复合催化剂具有较好的实际应用价值。     

TiO_2/ACFs催化剂光催化降解染料废水活性研究

以活性炭纤维为载体,采用溶胶-凝胶法制备得到了活性炭纤维负载二氧化钛光催化剂(TiO2/ACFs),并且以亚甲基蓝为模型化合物模拟研究了活性炭纤维负载二氧化钛光催化剂(TiO2/ACFs)对染料废水的光催化活性。通过扫描电镜(SEM)、XRD等表征方法对活性炭纤维负载二氧化钛光催化剂(TiO2/ACFs)的结构进行了研究。SEM表征显示,大部分二氧化钛以膜的形式均匀地包裹在活性炭纤维丝上,二氧化钛膜层的厚度大约为330 nm,还有一部分TiO2是以颗粒的形式负载在活性炭纤维上。FT-IR分析可知,ACF与TiO2之间有Ti—O—C键生成,说明TiO2与ACF结合牢固,TiO2不易脱落。通过对亚甲基蓝降解可知当煅烧温度为500℃时,TiO2/ACF的光催化性能最好,通过对比发现500℃煅烧制备的催化剂也具有最好的循环使用性能,经过4次循环后该催化剂对亚甲基蓝的去除率仍达到90.2%。     

双氧水敏化二氧化钛的制备及表征

利用超声分散法,以钛酸丁酯为主要原料,以双氧水为敏化剂,无水乙醇作为溶剂,冰醋酸作为抑制剂,制备双氧水敏化的二氧化钛粉体。并通过X射线衍射(XRD)和透射电镜(TEM)对产品进行表征。同时研究不同影响因素对甲基橙去除率的影响。实验结果显示,当焙烧温度为550℃,H2O2浓度为0.3%,催化剂投加量为0.5 g/L时,可制备出降解甲基橙溶液效果较好的二氧化钛。     

磷钨酸光催化降解甲基橙溶液的研究

以磷钨酸为光催化剂,在紫外灯照射下,对模拟染料废水甲基橙溶液进行光催化降解反应;研究了催化剂加入量、甲基橙初始质量浓度、外加TiO2和氧化剂H2O2、KIO4对甲基橙溶液光催化脱色效果的影响。结果表明:100mL20mg/L甲基橙溶液光催化剂最佳用量80m g;在较低浓度下,甲基橙溶液的光催化降解反应符合一级动力学方程;在特定条件下,(TiO2+H3PW12O40)/UV、(H2O2+H3PW12O40)/UV和(KIO4+H3PW12O40)/UV光催化体系对甲基橙溶液光催化脱色效果优于H3PW12O40/UV光催化体系。     

微波干燥制备Ag/TiO2的光催化活性试验研究

利用钛酸丁酯溶胶—凝胶法制备TiO2凝胶,通过光化学沉积法在TiO2凝胶表面负载Ag,采用微波对凝胶进行干燥制备TiO2光催化剂。以甲基橙为模拟污染物进行光催化降解试验,结果表明该方法制备的Ag/TiO2催化剂光催化活性明显提高。     

活性炭负载纳米TiO_2电催化氧化处理染料废水

用溶胶凝胶—动态吸附法制备颗粒活性炭(GAC)负载纳米二氧化钛(TiO2)催化剂,以甲基橙的脱色率为考察指标,研究TiO2/GAC电催化反应体系对甲基橙染料废水的电催化氧化性能。实验结果表明,在甲基橙废水pH为4,TiO2/GAC催化剂用量为0.5g,Fe2+浓度为250mg/L,电解电压为16V时,电催化氧化30min的条件下,甲基橙脱色率达99.2%,COD去除率达93.1%。     

钙钛矿La_(1-x)B_xCoO_3光催化降解SDBS的研究

文章采用了溶胶-凝胶法制备了钙钛矿催化剂La1-x Bx CoO3(B=Mg、Ca、Sr;x=0,0.1,0.3,0.5,0.7,0.9,1)并以X衍射线对其结构进行表征,以甲基橙光催化降解率来评价所制备的催化剂的活性。结果表明SrCoO3对甲基橙的降解有较高的活性。在紫外光下,催化剂的量为2.5 g/L、pH=8.0、30%H2O2的量为2 mL/L,SrCoO3对SDBS溶液有较好的降解效果,降解率达到96%。     

Sonocatalytic degradation of methyl orange in the presence of (nanometer and ordinary) anatase TiO2 powders

The nanometer and ordinary anatase titanium dioxide(TiO2 ) powders were adopted as the sonocatalysts for the degradation of methyl orange used as a model compound for the first time. It was found that the sonocatalytic degradation effect of methyl orange in the presence of TiO2 powder were much better than that without TiO2, but the sonocatalytic activity of the nanometer anatase TiO2 particle was obviously higher than that of ordinary anatase TiO2 particle. Although there are many factors influencing sonocatalytic degradation of methyl orange, the experimental results showed that the best degradation ratio of methyl orange could be obtained when the experimental conditions were: initial concentration 15 mg/L, nanometer anatase TiO2 adding amount 750 mg/L, ultrasonic frequency 40 kHz, output power 50 W, pH = 3.0 and temperature 40℃ within 150 min. In addition, the catalytic activity of reused nanometer anatase TiO2 catalyst was also studied and found to decline gradually comparing with initial nanometer anatase TiO2 catalyst. All experiments indicated that the method of the sonocatalytic degradation of organic pollutants in the presence of TiO2 powder was an advisable choice for non-or lowtransparent organic wastewaters.     

新型纳米材料光催化反应器研究

为了充分发挥纳米材料的光催化性能,研制了一种带有旋转叶片且可负载光催化纳米材料的光催化反应器.并以制备的纳米TiO2/硅藻土复合材料作为光催化剂、TNT生产废水为处理对象,考察了催化材料附载量、废水浓度和多次重复使用对反应器催化降解效率的影响.结果表明:附载有光催化纳米材料的反应器经过6次6h重复使用,对TNT生产废水催化降解效率仍然保持在75%以上,远高于直接分散在废水中纳米材料的处理效率(47.25%),即多次重复使用并保持高降解效率;而且可较好地避免纳米光催化材料的团聚.避免因回收造成的纳米材料光催化效率降低以及回收不完全造成的水体二次污染等现象.     

掺杂镧硼TiO_2光催化剂的制备及可见光活性研究

采用溶胶一凝胶法,制备新型La3+/B/TiO2光催化剂,使用氙灯为光源研究了催化剂光降解甲基橙溶液的催化活性。结果表明,当掺杂0.05%La3+,2.0%B,在500℃下焙烧2 h时,所得催化剂对甲基橙具有最高的光催化活性,与单一的TiO2和单独La3+或者B掺杂的光催化剂比较,La3+/B/TiO2具有相对较高的催化活性。     

Mn~(2+)-WO_3-TiO_2光催化降解甲基橙的研究

溶胶-凝胶和浸渍相结合的方法制备Mn2+-WO3-TiO2光催化剂,进行甲基橙的光催化降解实验,考察WO3和Mn2+掺入量、焙烧温度及时间对光催化性能的影响。结果表明,500℃焙烧2h,掺杂量n(Mn2+)∶n(WO3)∶n(TiO2)=0.8∶1∶100时,光催化活性最高,光催化降解甲基橙溶液,120min后,降解率达84%,比单纯TiO2的光催化活性提高83%。     

吸附树脂/铁酞菁对甲基橙的光催化降解

针对铁酞菁在水溶液中易于聚合而降低催化活性,同时在均相光催化体系中分离困难、难以重复利用的问题,将铁酞菁负载在吸附树脂上,制得多相催化剂。该催化剂在可见光的照射下能有效地催化H2O2降解偶氮染料甲基橙。考察了催化剂用量、H2O2投加量、pH值、温度等因素对甲基橙去除效果的影响。结果表明,甲基橙初始浓度为50 mg/L,卤灯功率为100 W,催化剂投加量为1.0 g/L,H2O2用量为0.2 mol/L,pH为3,温度为35℃时,反应10 h,甲基橙去除率达到91%,且催化剂所含铁离子无流失,具有很好的稳定性,可重复使用。     

Degradation of dyestuff wastewater using visible light in the presence of a novel nano TiO2 catalyst doped with upconversion luminescence agent

IntroductionEvery year ,the dyeing processes and dye productionbring large amounts of wastewaters containing highconcentration poisonous organic compounds ( Neppolian,2002 ; An, 2002) . If not being treated properly andbetimes , the wastewaters will serio…     

活性炭负载TiO2催化剂对直接耐酸大红4BS溶液的光催化降解研究

采用溶胶-凝胶法制备了活性炭负载型TiO2催化剂,采用了XRD、BET和SEM对催化剂进行表征。研究了催化剂对直接耐酸大红4BS的紫外光催化降解,比较了活性炭、P25和TiO2／AC对4BS溶液的降解能力,探讨了催化剂煅烧温度和投加量以及染料溶液的初始浓度对光催化降解率的影响,并对催化剂进行了回收再生实验。结果表明,500℃下煅烧的TiO2／AC催化剂比表面积为1147．88m^2／g、TiO2粒径为21．9nm、晶相组成以锐钛矿为主,具有良好的光催化活性和稳定性;90min后2g／L催化剂对150mg／L的4BS溶液紫外光催化降解率达到99．8％。