钒基催化剂中低温SCR脱硝性能研究

为探索适用于焦化烟气的具有较高催化活性的SCR脱硝催化剂,选用纳米Ti O_2粉末P25作为载体,采用浸渍法制备一系列的V/Ce-Ti催化剂,考察催化剂的中低温脱硝和抗硫性能。结果表明,4V10Ce-Ti催化剂具有最高的脱硝效率,在250℃时脱硝效率达到99%;空速越低、氧浓度越高且氨氮比越接近1,催化剂的脱硝效率越高。进一步通过掺杂其他元素(Br、Fe、Cu等)加以改性,结果表明在4V-Ti催化剂上添加Br能提高催化剂的脱硝效率,Br的最佳掺杂比例为5%;4V5Br-Ti催化剂在有SO_2的情况下仍能长时间保持较高的脱硝效率,具有良好的抗硫性能。XRD和BET测试结果表明,V和Ce的添加没有改变催化剂的晶型,但降低了催化剂的比表面积和平均孔径。XPS结果显示,通入SO_2后催化剂表面有硫酸氢铵生成,同时V~(5+)的含量减少,以上因素导致了催化剂活性的降低。     

制备参数对Mn-Ce/TiO2催化剂脱硝性能的影响

以锐钛矿型TiO₂为载体,采用分步共混法制备了Mn-Ce/TiO₂催化剂,通过考察不同活性组分前驱体、焙烧温度以及活性组分负载量对催化剂样品脱硝性能的影响,以确定最佳制备参数;结合XRD（X射线衍射）、XPS（X射线光电子能谱分析）、BET比表积等表征手段研究制备参数对催化剂性能的影响.结果表明:无定型态MnO₂含量越多,越有利于提高催化剂的脱硝活性;催化剂样品表面原子浓度比Mn/Ti[或（Mn+Ce）/Ti]越高,催化剂表面有效活性组分越多,催化剂脱硝活性越好.以自制Mn盐（MX）为前驱体,在Mn-Ce活性组分负载量为16%时,经500℃焙烧的催化剂样品脱硝活性最高;反应空速为10000 h-1,反应温度为80℃时,其脱硝效率可达80%,150℃时脱硝效效率可达99%.      

过渡金属元素掺杂改性SCR对零价汞的催化氧化性能

为提高商用SCR催化剂对Hg0(零价汞)的催化氧化活性,研究了过渡金属对其进行掺杂改性的方法,并利用固定床反应平台考察了不同试验条件下改性催化剂对Hg0的氧化效率. 结果表明:Y、Zn、Ni和Zr等过渡金属的掺杂可明显抑制SCR催化剂的催化活性,而Fe、Cu掺杂改性SCR催化剂对Hg0的催化氧化性能有显著提升. 在反应温度为350 ℃、空速比为370 000 h-1、φ(HCl)为1×10-5的条件下,Fe、Cu掺杂改性的SCR催化剂对Hg0的氧化效率均能达到90%以上,并且Fe掺杂改性后的SCR催化剂的脱硝性能也未受到明显影响. 借助XRD和XPS等表征手段,对反应前后Fe掺杂改性SCR催化剂进行了研究,表明Fe改性SCR催化剂遵循Mars-Maessen和Langmuir-Hinshelwood机制,可明显提高对Hg0的催化氧化效率,因此,应用前景较好.      

低温脱硝催化剂的研究现状

低温SCR脱硝处理可避免中温SCR催化的堵塞、磨损等问题,减轻K、Na、Ca、As等元素对催化剂的污染和中毒,建设成本低。通过介绍各种低温脱硝催化剂体系及研究进展,全面论述形成的不同氧化物相、不同制备方法、载体改性和催化剂内部结构特征对催化剂低温活性的影响;着重分析催化剂的中毒机理和抗中毒性能提高的方法。一方面,SO2浓度对催化剂的双重影响归结为催化剂表面形成的硫酸盐数量,H2O和催化剂表面反应物的竞争吸附;另一方面,催化剂活性组分改性和制备方法改进可以提高催化剂的抗硫和抗H2O性能;最后指出低温SCR脱硝技术的未来研究方向和应用重点。     

低温磁性铁基SCR烟气脱硝的实验研究

在流化床反应器中,以磁性铁氧化物(Fe3O4、γ-Fe2O3)颗粒为床料,氨为还原剂,进行了中低温SCR烟气脱硝实验研究,然后对反应辅加磁场,初步研究磁场对磁性γ-Fe2O3催化剂SCR脱硝的影响,并对床料进行了XRD分析.结果表明,Fe3O4的SCR活性较差,γ-Fe2O3的SCR活性较佳,在250℃其催化脱硝效率能达到90%,但在250℃以上Fe2O3会对氨的氧化起作用,因而在250℃及以下的邻近温度区间是最佳催化温度区间.此外,在150~290℃,外加磁场能促进γ-Fe2O3对NO的吸附,提高脱硝效率,使250℃时的脱硝效率达到95%左右,但在290℃以上,则会降低脱硝效率.为了抑制氨的氧化,发挥磁场对γ-Fe2O3脱硝的作用,适合在200~250℃低温区间内采用γ-Fe2O3催化剂进行SCR脱硝.     

碱土金属钙沉积对Mn-Ce/TiO2低温SCR催化剂脱硝性能的影响

本研究采用浸渍法分别制备CaCl2、CaCO3和CaSO4这3种钙盐前驱体沉积的Mn-Ce/TiO2催化剂,通过分析催化剂活性与催化剂理化特性之间的关系,考察碱土金属钙沉积对Mn-Ce/TiO2低温SCR催化剂脱硝性能的影响.结果表明,钙的加入会导致催化剂中毒,且不同钙前驱体掺杂对催化剂中毒效应不同.CaCO3的沉积对Mn-Ce/TiO2催化剂脱硝效率的影响最小,而CaCl2沉积对催化剂活性抑制作用最为强烈.通过比表面积测试(BET)、X射线光电子能谱(XPS)、X射线晶体衍射(XRD)、程序升温脱附(TPD)等方法对不同催化剂进行表征发现,催化剂的晶型变化、孔道结构破坏、表面活性元素及酸性点位的减少是催化剂中毒的主要原因.     

Fe掺杂对MnO_x催化剂结构性质及低温SCR反应机制的影响

采用Fe对MnOx催化剂的低温选择性催化还原（SCR）活性进行改性,并通过N2吸附、X射线衍射（XRD）、X射线光电子能谱（XPS）及原位漫反射傅里叶红外（insituDRIFTS）重点探讨了Fe引入后催化剂结构性质的变化及对低温SCR反应机制的影响.结果表明,Fe的掺杂能显著提高催化剂的低温SCR性能,Fe/（Fe＋...     

SCR催化剂对汞的催化氧化研究进展

文章综述了目前国内外选择性催化还原(SCR)催化剂催化氧化燃煤烟气中汞的研究现状。介绍了钒基、铜基、铁基、锰基、铈基以及贵金属SCR催化剂对汞的催化氧化性能;分别分析了烟气温度、烟气组分(Cl2、HCl、SO2、NH3等)、空速等因素对各催化剂汞氧化性能的影响;最后运用文献对比方法综合概括了燃煤烟气条件对汞氧化的影响,并结合我国燃煤电厂现状,对SCR催化脱汞技术的发展方向提出建议:利用SCR催化剂实现燃煤烟气中汞的氧化,结合现有污染物控制设备实现汞的脱除,是一种经济、高效的燃煤烟气脱汞技术;当前应深入研究SCR催化剂对汞的催化氧化机理,开发能够实现NOx与汞协同控制的,稳定、高效、普适性强的低温SCR催化剂。     

FeSAPO-34和CuFeSAPO-34分子筛的可控制备、表征及其低温NH3-SCR活性

采用一锅水热法制备了一系列不同铁前驱体的FeSAPO-34分子筛催化剂和元素掺杂的分子筛催化剂,考察了铁源和元素掺杂对分子筛催化剂的可控合成和低温催化还原NO_x性能的影响,并采用ICP、XRD、FESEM、BET、H2-TPR、XPS、NH₃-TPD、EPR及UV-Vis DRS等表征技术进行分析.活性结果表明,不同铁前驱体对所制备的FeSAPO-34分子筛催化剂的可控合成产生较大影响且对应分子筛催化剂的NH₃-SCR活性也存在较大差别.3种分子筛催化剂的低温活性顺序为：Fe_0.1SAPO-34-C>Fe_0.1SAPO-34-S>Fe_0.1SAPO-34-N. Cu掺杂的Cu_0.01Fe_0.1SAPO-34催化剂在200℃时NO_x转化率即可达82%,这反映出Cu掺杂能大大提高分子筛催化剂的低温选择性催化还原（SCR）活性.表征结果表明,不同铁源导致所制备催化剂的晶相结构、Fe物种...     

CTAB改性蒙脱石负载锰氧化物催化剂的原位生长法制备及其低温SCR脱硝活性研究

以十六烷基三甲基溴化铵（CTAB）改性的有机蒙脱石（OMMT）为载体,采用原位生长法一步合成负载型锰氧化物催化剂（MnO_x/OMMT-SP）,并应用于低温NH₃-SCR脱硝反应.考察了表面有机官能团对催化剂脱硝活性的影响,发现载体表面有机官能团对催化剂的低温SCR活性具有显著的抑制作用.对有机蒙脱石载体负载锰氧化物前后分别进行热处理以去除表面有机官能团,可有效提高催化剂活性.同时,通过XRD、SEM、TEM、BET、XPS、TG、NH₃-TPD和H₂-TPR等表征手段对催化剂的结构和及理化特性进行了表征.结果表明,在原位生长法制备催化剂的过程中,有机官能团的存在主要影响了前驱体物种在载体表面的原位反应,从而影响了活性物种的化学性质;其次,有机官能团本身也对SCR反应具有抑制作用,但影响较小.分析发现,有机官能团的存在抑制了原位生长过程中Mn⁴⁺的生成,而将催化剂在氧气氛围下进行煅烧 处理,不但使催化剂的比表面积大幅提升,而且增加了其Mn⁴⁺比例,可显著增强催化剂的酸中心数量及氧化还原能力.     

铈钛掺杂促进铁氧化物低温SCR脱硝性能的机理

利用X射线晶格衍射（XRD）、N₂吸附和X射线光电子能谱仪（XPS）等对铈和钛掺杂后的铁氧化物晶相、孔隙结构及表面活性组分的分散度等物性进行表征分析,得到了铈和钛掺杂对铁氧化物低温NH₃-SCR脱硝性能的促进机理.结果表明：铈和钛掺杂会抑制铁氧化物中Fe₂O₃的结晶,细化其孔径,增大其比表面积和比孔容;铈掺杂会促使铁氧化物表面形成Ce⁴⁺/Ce³⁺氧化还原电子对;进一步掺杂钛会提高铁铈复合氧化物形成更多吸附氧,增强其表面低温催化氧化NO为NO₂的性能;且铈和钛掺杂增强了铁氧化物表面的吸附性能,尤其提高了对NH₃的低温吸附,从而促进了铁基氧化物催化剂的低温NH₃-SCR脱硝性能.     

Effect of preparation methods on the performance of CuFe-SSZ-13 catalysts for selective catalytic reduction of NOx with NH3

CuFe-SSZ-13 catalyst showed excellent performance in the selective catalytic reduction of NO_x with NH₃ (NH₃-SCR) for diesel engine exhaust purification. To investigate the effect of preparation methods on NH₃-SCR performance, Fe was loaded into one-pot synthesized Cu-SSZ-13 catalysts through solid-state ion-exchange (SSIE), homogeneous deposition precipitation (HDP) and liquid ion-exchange (IE), respectively. Three CuFe-SSZ-13 catalysts showed similar SO₂ resistance, which was better than that of Cu-SSZ-13. The improvement was attributed to the protection of Fe species. Hydrothermal stability of three CuFe-SSZ-13 catalysts was significantly different, which was attributed to the state of active species caused by different preparation methods. Compared with the other two catalysts, more active species existed inside the zeolite pores of CuFe-SSZ-13_SSIE. During hydrothermal aging, the aggregation of these active species in the pores caused the collapse of catalyst structure, ultimately leading to the deactivation of CuFe-SSZ-13_SSIE. In contrast, Fe species was dispersed better on the surface over CuFe-SSZ-13_IE, enhancing the hydrothermal stability of catalysts. Consequently, Fe loading effectively improved the resistance of SO₂ and H₂O over Cu-SSZ-13. For CuFe-SSZ-13, large amounts of active species located inside the zeolite pores are not beneficial for the hydrothermal stability.     

Iron-doped Mn-Ce/TiO2 catalyst for low temperature selective catalytic reduction of NO with NH3

The catalysts of iron-doped Mn-Ce/TiO 2(Fe-Mn-Ce/TiO 2) prepared by sol-gel method were investigated for low temperature selective catalytic reduction(SCR) of NO with NH 3.It was found that the NO conversion over Fe-Mn-Ce/TiO 2 was obviously improved after iron doping compared with that over Mn-Ce/TiO 2.Fe-Mn-Ce/TiO 2 with the molar ratio of Fe/Ti = 0.1 exhibited the highest activity.The results showed that 96.8% NO conversion was obtained over Fe(0.1)-Mn-Ce/TiO 2 at 180°C at a space velocity of 50,000 hr 1.Fe-Mn-Ce/TiO 2 exhibited much higher resistance to H 2 O and SO 2 than that of Mn-Ce/TiO 2.The properties of the catalysts were characterized using X-ray diffraction(XRD),N 2 adsorption,temperature programmed desorption(NH 3-TPD and NOx-TPD),and Xray photoelectron spectroscopy(XPS) techniques.BET,NH3-TPD and NOx-TPD results showed that the specific surface area and NH3 and NOx adsorption capacity of the catalysts increased with iron doping.It was known from XPS analysis that iron valence state on the surface of the catalysts were in Fe3+ state.The doping of iron enhanced the dispersion and oxidation state of Mn and Ce on the surface of the catalysts.The oxygen concentrations on the surface of the catalysts were found to increase after iron doping.Fe-Mn-Ce/TiO2 represented a promising catalyst for low temperature SCR of NO with NH3 in the presence of H2 O and SO2.     

新型铈钨钛复合氧化物催化还原脱硝机理

利用水热共沉淀法制备了铈钨钛复合氧化物催化剂,考察了H₂O₂络合修饰对其催化脱硝转化频率（TOF）的影响;并借助傅里叶原位红外光谱仪研究了H₂O₂络合修饰后铈钨钛复合氧化物的催化脱硝机理.结果表明：H₂O₂络合修饰可增强铈钨钛复合氧化物表面Brønsted酸位强度,提高其表面NH₃低温吸附和中低温NH₃-SCR脱硝性能,400℃时其NO_x催化脱除频率TOF高达0.658s^-1;NH₃和NO_x在H₂O₂络合修饰后铈钨钛复合氧化物表面存在竞争吸附,其表面催化脱硝反应主要为吸附态NH₃、NH₂和NH₄⁺与气态NO+O₂的反应,其低温NH₃-SCR反应机理遵循Eley-Rideal（E-R）机理.     

Simultaneous removal of NO and dichloromethane（CH2Cl2） over Nb-loaded cerium nanotubes catalyst

Herein, a series of niobium oxide supported cerium nanotubes（Ce NTs） catalysts with different loading amount of Nb₂O₅（0–10 wt.%） were prepared and used for selective catalytic reduction of NOxwith NH₃（NH₃-SCR） in the presence of CH₂Cl₂. Commercial V₂O₅-WO₃-TiO₂ catalyst was also prepared for comparison. The physcial properties and chemical properties of the Nb₂O₅ lo...     

Removement of thiocyanate from industrial wastewater by microwave-Fenton oxidation method

The microwave radiation oxidation process, Fenton as catalytic agent, was used to remove the thiocyanate from the industrial wastewater. The effects of microwave power, radiation time, pH and the feeding in ways of catalyst on the degradation rate of synthetic wastewater were investigated using the microwave radiation oxidation process by orthogonal experiment. The results show Fenton catalyst ratio was 1:20, the microwave radiation power was 900 W, the microwave radiation time was 7 min and the value of pH was 3. Under the optimum conditions, the removal of KSCN can reach over 90%. The apparent kinetics of removal was studied, which conformed to kinetics first-class reaction. In short, for the thiocyanate from the industrial wastewater, microwave-Fenton oxidation method is feasible and effective.     

Removement of thiocyanate from industrial wastewater by microwave-Fenton oxidation method

The microwave radiation oxidation process, Fenton as catalytic agent, was used to remove the thiocyanate from the industrial wastewater. The effects of microwave power, radiation time, pH and the feeding in ways of catalyst on the degradation rate of synthetic wastewater were investigated using the microwave radiation oxidation process by orthogonal experiment. The results show Fenton catalyst ratio was 1:20, the microwave radiation power was 900 W, the microwave radiation time was 7 min and the value of pH was 3. Under the optimum conditions, the removal of KSCN can reach over 90%. The apparent kinetics of removal was studied, which conformed to kinetics first-class reaction. In short, for the thiocyanate from the industrial wastewater, microwave-Fenton oxidation method is feasible and effective.     

微波催化氧化法预处理垃圾渗滤液的研究

采用微波-活性炭-Fenton催化氧化预处理垃圾渗滤液,研究了不同因素对垃圾渗滤液处理效果的影响.结果表明,COD和氨氮去除率随活性炭用量、微波辐射时间和微波功率增加而增加;随Fe2+用量和H2O2用量增加,COD和氨氮去除率先增加而后下降;随pH值增加,氨氮去除率显著增加,COD去除率变化不明显.在微波功率为300W,pH值为8,活性炭9g/L,Fe2+用量为0.02mol/L,H2O2用量为7mL/L,辐射时间6min条件下,垃圾渗滤液中COD和氨氮去除率分别达到68.22%和78.08%,SS去除率达到78.55%,浑浊度去除率达到99.02%,颜色由黑褐色去除为接近无色,BOD5/COD由0.21提高到0.45;研究比较了不同处理对垃圾渗滤液的处理效果.结果显示,微波催化氧化对垃圾渗滤液中COD和氨氮去除率明显高于其他处理.     

微波加热下苯的催化氧化性能研究

研究考察了微波加热与传统电炉加热两种不同加热方式下苯的催化氧化性能,同时考察了微波加热下铜锰质量比,铈掺杂量及焙烧温度变化对铜-锰-铈/分子筛催化剂催化氧化苯性能的影响,并对催化剂进行了SEM和XRD表征.结果表明,微波加热下苯的催化氧化性能优于电炉加热,微波的"局部热点"效应、偶极极化作用与稳定的床层反应温度保证了苯的高效催化氧化;铜∶锰∶铈质量比1∶1∶0.33和焙烧温度500℃下催化剂的活性最高,苯的起燃温度与完全燃烧温度分别为165℃和230℃.催化剂表征分析可知,铜、锰氧化物及铜锰尖晶石固溶物等活性相的存在保证了催化剂的高活性;稀土元素铈的掺杂促进了活性组分在催化剂表面的分散与规整化;高温焙烧可导致催化剂表面的烧结与活性组分的团聚,从而降低其催化氧化苯的活性.     

Mn基金属氧化物催化剂常温催化氧化甲醛

以硝酸铈和高锰酸钾为原料,采用络合法制备了一系列Mn-Ce-O混合氧化物催化剂,并通过正交实验设计方案,考察了Mn/Ce摩尔比、水化热温度、焙烧温度及焙烧时间对Mn-Ce-O混合氧化物催化剂常温催化氧化甲醛性能的影响,并采用X射线衍射仪（XRD）、扫描电镜（SEM）、透射电镜（TEM）和红外光谱（IR）等技术对催化剂进行微观表征与分析.结果表明：当Mn/Ce摩尔比1：1,水化热温度为180℃,焙烧温度为350℃时,催化剂表现出最佳的常温氧化活性,36h甲醛降解率可达94.2%,且稳定性良好.催化剂氧化活性的高低与材料比表面积并非正相关,而与材料结构形态存在密切关联,而材料结构主要取决于水化热温度,其次是Mn/Ce摩尔比.