酿酒酵母对Ag+的吸附特性研究

为了深入探讨酿酒酵母吸附贵金属离子Ag⁺的特性,研究了吸附时间、离子浓度、初始pH值、温度对废弃酿酒酵母吸附Ag⁺的影响,并分析了动力学、热力学以及等温吸附特性.结果表明,酵母吸附Ag⁺的过程进行得很快,当Ag⁺初始浓度为1 mmol·L^-1、细胞浓度2 g·L^-1条件下,反应10 min,Ag⁺可以达到平衡吸附量的86%以上.随后在24 h内吸附量缓慢增加,去除率基本维持在51%～55%左右.酵母吸附Ag⁺的过程可以用准一级和准二级动力学方程描述,后者模拟效果更好.酵母吸附Ag⁺的等温吸附过程可以用Langmuir方程描述,但Freundlich方程拟合效果较差.当Ag⁺初始浓度为0～8 mmol·L^-1、酵母浓度2 g·L^-1条件下,酵母吸附Ag⁺的Langmuir理论饱和生物吸附容量为0.385 mmol·g^-1.在pH 2.0～7.2范围内,吸附量随着溶液初始pH值升高而升高.10～40℃范围内,温度对酵母吸附Ag⁺的影响不如pH值的影响显著,特别是在低离子浓度下尤其如此.酵母吸附Ag⁺的较适宜温度为20～30℃.热力学分析表明,酵母吸附Ag⁺具有自发性、熵增特征.     

铁锰复合氧化物吸附去除五价锑性能研究

对比研究了铁锰复合氧化物(FMBO)、羟基氧化铁(FeOOH)和二氧化锰(MnO₂)吸附去除五价锑(Sb(V))的性能.结果表明FMBO对Sb(V)具有很好的吸附性能,在pH=5.0的条件下,最大吸附容量达到1.05 mmol·g^-1,略高于FeOOH (0.82 mmol·g^-1)及远高于MnO₂ (0.43 mmol·g^-1);采用Freundlich模型可以很好地描述Sb(V)在FMBO的吸附行为(R² = 0.98).就吸附动力学而言,假二级动力学可很好地描述Sb(V)在FMBO (R² = 0.93)和MnO₂表面的吸附过程(R² = 0.96),而Sb(V)在FeOOH表面的吸附过程可用Elovich模型拟合 (R² = 0.94).Sb(V)的吸附量随着pH值的升高而降低;磷酸盐显著抑制了Sb(V)的吸附,而硫酸盐和碳酸盐影响不大.提高体系离子强度可促进Sb(V)在FMBO表面的吸附,推断Sb(V)在FMBO表面形成内层络合物后被吸附去除.     

PEI改性生物炭的制备及对CO2吸附性能的评价

采用超声辅助-水热法将聚乙烯亚胺（PEI）成功接枝到玉米芯生物炭表面,制备了PEI改性生物炭材料（PBC）,并通过X射线衍射（XRD）、扫描电子显微镜（SEM）、比表面积分析仪和傅里叶红外光谱仪（FTIR）等方法对其表征.结果表明,虽然PEI通过CN、C-N和离子键与生物炭表面的活性基团链接,但制备的PBC材料仍保持原生炭的无定型结构和形貌,且比表面积高达928.1 m²·g^-1.同时,还研究了PBC的吸附性能和热力学行为,结果表明,吸附过程符合Langmuir等温吸附机制,属于微孔单层吸附过程,而且随温度的降低,吸附量增大,在10、20和30℃时,饱和吸附量（Q_m）分别为6.47、4.75和2.64 mmol·g^-1.此外,PBC重复利用性能良好,容易实现热再生,即使循环利用10次,吸附性能也无显著变化（p>0.05）,且穿透吸附量（Q_B）保持在2.6~2.7 mmol·g^-1.     

磁性高交联纳米吸附树脂的合成及其对酚类的吸附

采用油酸双层包覆Fe₃O₄纳米粒子,然后进行共聚和交联反应,制备出耐酸性的磁性高交联纳米吸附树脂YQ-3.YQ-3树脂的比表面积为653.5 m²·g^-1,平均孔径为4.12 nm,磁化强度为1.72 emμ·g^-1,具有超顺磁性.苯酚（PN）、对苯二酚（HN）、对硝基苯酚（PNP）在YQ-3上的吸附等温线符合Freundlich方程,主要通过疏水和 π-π作用进行吸附.3种酚的饱和吸附量顺序为PNP>PN>HN,与其疏水性顺序一致.准一级动力学和颗粒内模型适合拟合YQ-3对酚的吸附,由于YQ-3磁性树脂具有较小的粒径和丰富的中-大孔隙,其动力学速率比传统超高交联树脂更快.     

土壤中聚乙烯和聚苯乙烯微塑料对多环芳烃的吸附行为和机理分析

本研究旨在探讨微塑料对土壤基质中16种多环芳烃（PAHs）吸附的影响.通过批实验考察了PAHs在聚乙烯（PE）和聚苯乙烯（PS）微塑料上的吸附过程,系统地评价了pH和腐殖酸（HA）浓度等环境因素对微塑料吸附土壤PAHs的影响.结果表明,微塑料对土壤中PAHs的吸附动力学符合准二级动力学模型,且Freundlich模型对吸附结果的拟合程度（R²=0.9868~0.9931）明显高于Langmuir模型（R²=0.8638~0.8927）, 说明微塑料对PAHs的吸附过程主要为化学吸附.通过吸附热力学计算的ΔH均为正值,ΔG为负值,表明微塑料对土壤PAHs的吸附是自发的吸热过程.pH和HA对PE和PS微塑料吸附PAHs的影响显著,PE和PS微塑料对PAHs的吸附量分别在pH=5.0和pH=7.0时达到峰值;腐殖酸浓度的增加抑制了PAHs在PE微塑料上的吸附,吸附量从9363.95 ng·g^-1降到4877.42 ng·g^-1,但促进了PAHs在PS微塑料上的吸附,吸附量从9422.71 ng·g^-1增加到13259.73 ng·g^-1,这表明PAHs对腐殖酸的亲和力高于对PE微塑料的亲和力.微塑料对土壤PAHs的吸附主要与静电 作用、π-π作用和疏水作用有关.     

纳米磁性磷酸二氢钙对Cd的吸附、回收与再生

以Ca（H₂PO₄）₂、铁盐与亚铁盐为原料,采用共沉淀法制备成纳米磁性材料Ca（H₂PO₄）₂@Fe₃O₄（NMCDP）,研究其对Cd²⁺的吸附、回收与再生效果.透射电镜（TEM）、红外光谱（FTIR）、X射线衍射（XRD）显示,NMCDP粒径约60 nm,稳定性良好,饱和磁化强度为30.9 emu·g^-1.吸附动力学表明,NMCDP对Cd²⁺的吸附1 h之内即可达到平衡,符合准二级动力学模型.吸附热力学表明,NMCDP对Cd²⁺的吸附符合Langmuir与Freundlich等温吸附模型,最大吸附量为142.50 mg·g^-1.在pH值由2增加到3时,吸附量随溶液初始pH值的升高而增加,当pH值大于3后,逐渐保持稳定;溶液中共存离子Na⁺、Mg²⁺、Cu²⁺对材料吸附Cd²⁺均有一定的影响,影响程度Cu²⁺ > Mg²⁺ > Na⁺.采用0.01 mol·L^-1 HCl与EDTA-Na₂均可解吸出部分吸附的Cd²⁺,以EDTA-Na₂解吸率较高,达到68%,从而实现NMCDP的再生.     

胺硫改性生物炭对水溶液中不同重金属离子的吸附特性及吸附稳定性

以玉米秸秆为原料热裂解制备生物炭,利用二乙烯三胺和二硫化碳,通过酸化氧化,曼妮希反应胺基改性、二硫化碳巯基取代对生物炭进行胺硫双基团改性,研究胺硫改性生物炭（BC-SN）对Pb²⁺、Ni²⁺及Cd²⁺在单一和三元体系下的吸附特性和吸附稳定性.表征分析证实了生物炭表面胺硫双基团改性成功,且具有比表面积大、表面官能团丰富的特点.对吸附过程进行了pH值、吸附剂投加量和吸附平衡时间的研究.结果表明,单一体系下,吸附平衡时间为4 h,最佳投加量为1、0.8和1.2 g·L^-1,吸附满足准二级动力学方程;三元体系下,吸附平衡时间缩短到1.5h,最佳投加量为0.4、1.6和0.8 g·L^-1,选择吸附顺序为Pb²⁺ > Cd²⁺ > Ni²⁺,吸附总量为0.67 mmol·g^-1,均大于单个重金属离子的吸附量,说明BC-SN对3种重金属离子共存下的污染水体处理效果更好.Pb²⁺和Cd²⁺的吸附以重金属硫化物和螯合氨基形式稳定结合,Ni²⁺的为多种官能团的混合吸附;Pb²⁺和Cd²⁺竞争吸附时结合能更高,吸附稳定性强.     

不同类型酸修饰-磁化海泡石对水体Cd(II)的吸附研究

采用无机或有机酸修饰-磁化的方法研制海泡石吸附材料H-Sep(盐酸修饰)、N-Sep(硝酸修饰)、P-Sep(磷酸修饰)和A-Sep(醋酸修饰),并借助SEM、TEM、EDS、BET、FT-IR、VSM及XPS等手段表征分析改性前后海泡石的结构特征.同时,在不同投加量、pH、温度和溶液浓度等因素条件下,考察了酸修饰-磁化海泡石对水体Cd(II)吸附效果的影响.结果表明,改性材料取得最佳吸附效果时的投加量为5g·L^-1,pH为6.5,拟合结果更符合准二级动力学方程和Langmuir等温方程.其中,P-Sep的吸附效果最好,其最大理论吸附量为52.6 mg·g^-1.VSM结果表明,H-Sep、N-Sep和A-Sep是磁化分离效果较好的材料,而P-Sep的磁化分离效果不佳.此外,Na⁺、Cl^-等阴阳离子对酸修饰-磁改性海泡石吸附性能没有太大影响,而重金属离子如Pb(II)、Zn(II)会对其吸附过程产生抑制作用.XPS吸附机理分析表明,酸修饰-磁化改性将新的功能基团引入海泡石结构,极大地提升了吸附性能.     

磁性铁基改性生物炭去除水中氨氮

氨氮的过度排放是水体富营养化的一个重要原因.然而,随着环境法规的日益严格,传统方法处理效果难以达到要求.吸附法因高效、安全等优点近年来开始应用于去除水中的氨氮.本研究中以共沉淀法将磁性铁基材料负载到市政污泥生物炭上,结果表明其对水中氨氮有良好的去除效果.80℃下合成的材料（MB₈₀）在293 K下对氨氮的饱和吸附量可达17.52 mg·g^-1.动力学与热力学结果表明,MB₈₀吸附氨氮的过程更符合伪二级动力学和Langmuir等温线.MB₈₀对氨氮的吸附机制可归纳为静电吸引、孔隙填充、离子交换和氢键结合.且5次循环后对氨氮的吸附量仍十分理想,可达3.18 mg·g^-1.本研究的结果可以为高效去除水中氨氮提供一种行之有效的方法,并为市政污泥的处理提供新的出路.     

高效除磷渗滤床填料筛选及连续流动态运行特性

磷是造成水体富营养化的重要因素之一,深度去除污染水体中的磷,具有重要的环保意义.为此,本研究比较了多种填料包括海绵铁及其改性填料、钢渣、活性氧化铝、活性炭的吸附除磷特性及动力学,探究了除磷机理,构建了高效除磷渗滤床,考察了动态连续流运行条件下的除磷特性.结果表明酸改性海绵铁具有最高的饱和磷吸附容量,为19.45 mg·g^-1,碱改性海绵铁、活性氧化铝、钢渣、未改性海绵铁及活性炭的饱和磷吸附容量分别为10.91、8.70、7.73、3.39和1.34 mg·g^-1.在此基础上,利用高效除磷填料酸改性海绵铁和钢渣构建了除磷渗滤床,开展了连续240 d的连续流实验,在磷容积负荷为6 g·d^-1·m^-3条件下,渗滤床累积磷吸附量达到10215 mg,单位容积吸附量达到1.62 kg·m^-3.总之,利用酸改性海绵铁和钢渣构建的除磷渗滤床具有较高的除磷效率和性能,可以作为除磷单元与现有的水污染治理及净化工艺耦合,提高或拓展系统除磷功能.     

Kinetics of enhanced adsorption by polarization for organic pollutants on activated carbon fiber

The adsorption kinetics for model pollutants on activated carbon fiber (ACF) by polarization was investigated in this work. Kinetics data obtained for the adsorption of these model pollutants at open-circuit, 400 mV, and −400 mV polarization were applied to the Lagergren equation, and adsorption rate constants (K _a) were determined. With the anodic polarization of 400 mV, the capacity of sodium phenoxide was increased from 0.0083 mmol/g at open-circuit to 0.18 mmol/g, and a 17-fold enhancement was achieved; however, the capacity of p-nitrophenol was decreased from 2.93 mmol/g at open-circuit to 2.65 mmol/g. With the cathodal polarization of −400 mV, the capacity of aniline was improved from 3.60 mmol/g at open-circuit to 3.88 mmol/g; however, the capacity of sodium dodecylbenzene sulfonate was reduced from 2.20 mmol/g at open-circuit to 1.59 mmol/g. The enhancement for electrosorption changed with different groups substituting. Anodic polarization enhances the adsorption of benzene with the electron-donating group. But whether anodic or not, cathodal polarization had less effect on the adsorption of electron-accepting aromatic compounds, and decreased the adsorption capacity of benzene-bearing donor-conjugate bridge-acceptor, while increasing its adsorption rate. Electrostatic interaction played a very important role in the electrosorption of ion-pollutants. Translated from Environmental Science, 2006, 27(6): 1111–1116 [译自: 环境科学]     

石墨烯凝胶电极的制备及电吸附Pb2+的性能

电吸附去除水中重金属离子具有吸附容量高和电极可再生的优点.本文采用高温水热法还原氧化石墨烯(GO)得到石墨烯水凝胶(GS)并经压片制得GS电极.本文对GS电极的电化学性能进行了测试,考察了GS电极电吸附Pb~(2+)的动力学和热力学特性,以及电极的脱附和循环使用情况.结果表明,GS电极的电化学性能优异,其单位质量比电容高达200.4 F·g~(-1)(1 A·g~(-1));提高电压有利于GS电极电吸附Pb~(2+),电压为-1.2 V时,GS电极对Pb~(2+)的去除率达96.4%;GS电极电吸附Pb~(2+)的饱和吸附量达461.20 mg·g~(-1),是不加电时饱和吸附量的2倍;施加反向电压可以实现Pb~(2+)的脱附和电极再生,电吸附-脱附15次后,电极对Pb~(2+)的去除率保持在95%以上.     

2,6-二氨基蒽醌/石墨烯复合电极强化电吸附Pb2+

电吸附高效去除水中重金属离子的关键在于开发性能优异的电极材料.采用2,6-二氨基蒽醌(DA)修饰还原氧化石墨烯(r GO),通过溶剂热法成功制备了DA@rGO复合电极,考察了复合电极的电化学性质及电吸附Pb~(2+)性能.循环伏安测试表明,复合电极电化学性质优异,比电容在电流密度为1 A·g-1时达到304. 4 F·g-1,DA修饰显著提高了复合电极的赝电容.电吸附Pb~(2+)测试表明,施加电压为-1. 2 V时电吸附效果最优,反应60 min后Pb~(2+)去除率达94. 8%.电吸附过程符合一级动力学方程,Langmuir模型拟合得到Pb~(2+)的饱和吸附量为356. 66 mg·g-1,明显高于r GO电极(319. 40 mg·g-1),DA修饰引起的电容增加是复合电极Pb~(2+)吸附量提高的重要原因.使用0. 5 mol·L-1硝酸处理可使电极吸附的Pb~(2+)在5 min内脱附完全,实现吸附剂再生.经过10次电极吸附-脱附循环后,DA@rGO复合电极对Pb~(2+)的吸附去除率保持在88%左右,电极循环性能稳定.     

紫外辐照改性生物炭对VOCs的动态吸附

采用365 nm紫外光辐照改性椰壳生物炭,以提升对挥发性有机污染物(VOCs)的吸附性能.选取苯和甲苯两种典型的VOCs为吸附质,考察了改性前后生物炭的吸附穿透曲线.结果表明,紫外辐照改性后的生物炭其吸附性能显著增加,对苯和甲苯的饱和吸附量分别由7.27 mg·g~(-1)和7.98 mg·g~(-1)提升至122.80 mg·g~(-1)和236.36 mg·g~(-1),吸附穿透时间也由1 min和2 min大大延长至390 min和620 min.生物炭表面理化特征分析表明,紫外辐照增大了生物炭表面含氧官能团的含量和外比表面积,这可能是改性生物炭吸附性能提升的关键因素.Yoon-Nelson、Thomas和BDST模型均能很好地模拟改性生物炭对不同浓度苯和甲苯的吸附过程,其相关系数大于0.992.热重分析结果表明,紫外辐射对生物炭的热稳定性影响甚微.改性生物炭吸附饱和后,可经热再生后重复利用,对甲苯的吸附重复利用5次后仍有较高的吸附能力.     

CTAC改性膨润土吸附去除水体中高氯酸盐的离子交换性能研究

选用阳离子表面活性剂十六烷基三甲基氯化铵(CTAC)改性膨润土以提高膨润土对ClO4-的吸附能力.试验结果表明,CTAC改性能显著提高膨润土对ClO4-的吸附能力,在0.1～l mmol·L-1的C1O4-溶液中,6h内能迅速达到吸附平衡.有机膨润土对ClO4-的吸附最符合Langmuir等温吸附模型,其吸附容量可达0.48 mmol·g-1.pH值在4～10范围内变化对ClO-的吸附几乎没有影响.高的分配系数(Kd＞1.5×103cm3·g-1)表明有机膨润土对ClO4-有很高的选择性,各阴离子的分配系数从小到大的顺序为HPO42-＜ SO42-＜ NO3-＜ ClO4-,这与阴离子的自由水合能大小相一致.1 mol·L-1 HCl溶液对吸附剂的再生效率在96％左右,可直接使用,不用再改性.     

高分子固体废物基活性炭对有机染料的吸附解吸行为研究

分别以3种高分子固体废物,即轮胎橡胶、聚氯乙烯(PVC)和聚对苯二甲酸乙二酯(PET)为原料,利用KOH活化法制备高比表面积活性炭.通过吸附实验研究了活性炭对2种有机染料(亚甲基蓝和甲基橙)的吸附、解吸行为,同时探讨了溶液pH值、离子强度和表面活性剂对吸附的影响.结果表明,PVC和PET基活性炭比表面积分别为2 666和2 831 m2.g-1,中孔容积分别为1.06和1.30 cm3.g-1,15 min内对亚甲基蓝和甲基橙的去除率分别高达98.5%和97.0%、99.5%和95.0%,且Langmuir模型拟合的染料最大吸附量均超过2 mmol.g-1,显著高于商业活性炭F400.Langmuir模型比Freundlich模型能更好地描述2种染料的吸附行为,说明吸附以表面单层覆盖为主.溶液pH值、离子强度和表面活性剂对染料吸附均有较大影响.制备的高分子基活性炭对亚甲基蓝的吸附强于甲基橙,2种染料均不容易发生解吸.实验结果可为高分子固体废物的资源化利用、制备经济高效的碳质吸附材料提供科学依据.     

质子化交联壳聚糖对水中高氯酸根的吸附特性研究

通过合成质子化交联壳聚糖,采用静态试验方法对水中高氯酸根(ClO4-)的吸附效果及机制进行了研究,考察了pH、温度和初始浓度对吸附过程的影响以及吸附剂的重复使用性能.结果表明,质子化交联壳聚糖吸附ClO4-过程属放热反应;当pH在3.0~6.0之间时,对ClO4-均有较好的吸附作用;随着ClO4-初始浓度的增加,吸附容量增加,当初始浓度为100 mg.L-1时,吸附容量在34.39~37.98 mg.g-1之间;当ClO4-为400 mg.L-1时,吸附容量达128.78 mg.g-1.质子化交联壳聚糖对水中ClO4-的吸附过程符合Langmuir和Freundlich等温吸附模型,ClO4-在质子化交联壳聚糖小球上的吸附过程中化学吸附为速率控制步骤.质子化交联壳聚糖小球可在pH为12.8的NaOH溶液中再生,反复使用10次其吸附容量无明显变化,表现出较好的吸附/解吸性能,这为有效地去除水中的ClO4-提供了新的方法.     

3种吸附剂对污水磷污染去除性能与机制比较

为探索高效利用膨润土、红壤和炉渣去除农业污水磷污染的可行性,对比分析了3种吸附剂对人工合成含磷污水的吸附去除特性,结合SEM、XDS和BET等测试结果以及等温吸附、吸附动力学及Ca2+释放量探讨了3种材料对磷的吸附机制.结果表明,炉渣对磷的吸附能力高于膨润土和红壤,吸附过程均适合Langmuir等温吸附方程(R2 0. 96),对磷的理论饱和吸附量为:炉渣(16. 87 mg·g~(-1))红壤(1. 21 mg·g~(-1))膨润土(0. 92 mg·g~(-1)).炉渣对磷的吸附动力学特征符合Elovich方程(R2=0. 966),而膨润土和红壤对磷的吸附特征则更适合准二级动力学方程(R2为0. 982和0. 959).炉渣的Ca2+释放量(10. 46 mg·g~(-1))显著大于膨润土(0. 31 mg·g~(-1))和红壤(0. 03 mg·g~(-1))(P 0. 05).红壤对磷的吸附量随着p H的升高而降低;膨润土在初始p H为7. 0时,吸附量最低;但初始p H值对炉渣去除磷的影响不大.相比红壤和炉渣,膨润土解吸较快,易于进行重复利用.综上所述,吸附材料的磷吸附能力主要与其结构、化学组成、Ca2+释放能力及溶液初始p H值等有关,炉渣较膨润土和红壤对磷酸盐有着更强的去除能力,适合处理农村污水磷污染.     

MnO2/CFP复合电极的制备及电吸附Pb2+特性的研究

电极材料的形貌结构与电化学性能等将直接影响着电吸附效果.本研究将二氧化锰(Mn O2)通过电沉积的方法负载于碳纤维纸(CFP)材料上,制备获得了Mn O2/CFP复合电极.所制得的Mn O2/CFP复合电极电化学性质稳定、电容量高,复合电极的单位质量比电容量可高达360 F·g-1.用此电极对初始浓度为6 mg·L-1左右的Pb2+溶液进行电吸附,考察了电沉积时间、电压、p H值等因素对复合电极电吸附效果的影响.结果表明,沉积时间为500 s、电压值为1.0 V、p H值为5.0的条件下可获得最佳的电吸附效果,电吸附3 h后原溶液中残留Pb2+达到0.01 mg·L-1以下,去除效率高达99%以上.本研究为水中重金属离子的去除提供了新的技术选择.