Modification of ferrite–manganese oxide sorbent by doping with cerium oxide

Fe–Mn oxide and Ce-doped Fe–Mn oxide sorbents were studied on the structural and desulfurization behavior in COS removal from syngas. The effects of cerium oxide on the Fe–Mn oxides have been investigated by XRD, BET, TPR, XPS and TEM methods. Analysis data show that the Ce-doped sorbent has larger specific surface area and better particles’ dispersion compared with non-modified Fe–Mn sorbent. The addition of Ce improves the reduction performance of Fe–Mn species. The desulfurization experiments show that the desulfurization activity of sorbent can be increased because of the promotion of the structural and redox properties by ceria doped. The Ce-doped sorbent can reduce COS from 15,000 ppmv to less than 0.1 ppmv at 325 °C and a space velocity of 1000 h⁻¹.     

PHBV表面疏水改性用作吸油材料的研究

利用多种表面改性剂对生物可降解材料PHBV进行了表面改性实验研究，测定了不同改性剂改性后PHBV的吸油率以及温度对其吸油效果的影响，并探讨了改性机理，研究结果表明：不同改性剂对PHBV的改性效果有所差异，从疏水和吸油的共同效果来看，最佳疏水改性剂为添加量5％时的硅油，温度对未改性PHBV和改性PHBV的吸油率及吸油速度均有影响。     

绿色木霉改性玉米秸秆溢油吸附剂的制备及其性能研究

利用绿色木霉对玉米秸秆进行固态发酵,通过单因素改性实验(改性时间、固液比和改性温度)制备溢油吸附剂TCS(Trichoderma viride modified corn stalk),并模拟溢油环境测定TCS的吸油量.研究表明,25℃下,改性6 d、固液比1∶4时,制得的TCS吸油量最大,达到13.84 g.g-1,相对原材料RCS(Raw corn stalk,吸油量为6.58 g.g-1)提高了110.33%.对RCS和TCS进行扫描电子显微镜(SEM)分析显示制得的TCS表面变得更加粗糙;傅里叶红外光谱分析(FT-IR)表明玉米秸秆纤维素组分被部分降解;X射线衍射分析(XRD)得到改性后的材料结晶度降低;纤维素、半纤维素和木质素等组分测定进一步表明生物改性降低了玉米秸秆中纤维素及半纤维素的含量,这些均说明改性后材料吸油量增加的原因.吸附动力学及保油性能测试表明,TCS具有快速的吸油速率,80 r.min-1条件下振荡1 h后即达到吸附平衡;且在吸附饱和后滴淌10 min仍能保持最初吸油量的74.87%,具有良好的保油性能.     

吸附剂烟气脱砷的研究现状

大气砷污染问题日益引起人们的重视,吸附剂能够在去除烟气中砷的同时去除其他有害气体,是控制烟气砷含量、防止砷污染的有效途径.文章分析了砷在废气中的形态及分布,总结了近年来氧化钙、活性炭、飞灰和金属氧化物作为吸附剂用于烟气脱砷的最新研究进展,重点分析了各自的吸附机理及不同因素对脱砷过程的影响.指出吸附过程通常以化学吸附为主...     

流化床O2/CO2气氛燃煤痕量元素的排放特性及控制

通过平顶山烟煤在小型流化床中的燃烧实验,采用X-射线荧光光谱仪(XRF)对低压撞击器(LPI)收集到的细颗粒物元素组成进行定量测定,研究了O2/CO2气氛下硅藻土对煤粉燃烧痕量元素的排放控制.结果表明,Zn、Mn和Ni的含量随粒径呈双峰分布,峰值分别在0.1μm和2μm附近,Hg和Co的含量在0.1μm附近有一峰值;Hg和Zn在亚微米颗粒上有一定程度的富集,Mn、Ni和Co在亚微米和超微米颗粒上的含量基本相当;当颗粒物粒径一定时,随着硅藻土含量的增加,5种元素的富集因子呈减小的趋势;随着添加剂粒径的减小,颗粒物中Hg、Mn、Zn、Ni和Co的含量呈减少的趋势;当颗粒物粒径一定时,5种元素含量顺序为MnZnNiCoHg.     

Modification of Fe–Mn mixed oxide COS removal sorbent by rare-earth oxides addition

In order to develop highly active sorbent for COS removal, Fe–Mn mixed oxides doped with CeO₂, La₂O₃ or Sm₂O₃ were studied. The effects of these promoters on the structural properties of Fe–Mn oxides were investigated by XRD, BET, TPR and TEM techniques. XRD results revealed that the degree of crystallinity of Fe–Mn oxide phase decreased due to the addition of rare-earth oxides. Doping with CeO₂, La₂O₃ or Sm₂O₃ led to an increase in BET surface area of the sample. TPR studies showed that the reactivity of the reduction of doped samples increased in the temperature range of 300–450 °C. In addition, the desulfurization test was performed at 325 °C with a gas hourly space velocity of 1000 h⁻¹. It was found that the addition of 3% La₂O₃ greatly improved the absorption sulfur capacity of the sorbent, while the sorbent doped 3% CeO₂ achieved a sufficiently high purifying degree before breakthrough.     

Effect of steam hydration on performance of lime sorbent for CO2 capture

Lime is considered a feasible sorbent for the capture of CO₂ from large stationary sources. The positive attributes of a natural source material, low cost and lack of harmful by-products are offset by rapid deterioration in performance and high regeneration temperature. Performance can be improved by hydrating the lime using steam. We investigate a steam hydration process wherein lime is hydrated for 5 min at 300 °C and atmospheric pressure in a mixture of steam and CO₂. The experiments consisted of 10 capture cycles with 60% of the lime active at the end. Extrapolation using a decay model suggests a residual carbonation level of 48%, significantly higher than the 8% achieved by dry lime cycles. The cost of replacement sorbent under these conditions is less than $1/t of CO₂ captured. The hydrated lime process also reduces the thermal load, for heating and cooling, by half as well as the inventory, and therefore solids handling, by a factor 5 over dry lime. The introduction of the hydration reaction provides another exothermic reaction for heat management.     

分子吸附器在光学相机污染控制中的应用研究

分子吸附器作为一种新型的在轨污染控制手段,具有使用方便、重量轻、无功耗和成本低等特点,可以为航天器光学相机提供在轨污染控制。从在轨分子污染物和分子吸附器特点两方面进行分析,描述了光学相机在轨污染物来源及特点,分析了污染物成分及对光学相机的危害,阐述了分子吸附器(包括吸附剂和基底)的组成及吸附特点。结合相机结构,提出了分子吸附器在光学相机污染控制中的应用方案,并明确了今后的研究方向。     

钙基脱硫剂孔隙中SO2气体非线性扩散的研究

以动态生成的CaO孔隙网络为骨架，按照不退行随机行走模型（NRRW），模拟气体分子在CaO孔隙中的扩散过程，计算了SO2分子的扩散系数和行走维数，并在SO2非线性扩散反应方程基础上，分析了CaO颗粒孔隙中SO2浓度的分布特性。     

再生条件对钾基CO_2吸附剂吸附性能的影响

通过固定床实验研究了再生条件对钾基CO2吸附剂吸附性能的影响。深入分析了再生温度和气氛对吸附穿透时间和饱和吸附量的影响。研究发现,当再生温度为200℃,N2气氛下再生时效果最佳,在此条件下再生后钾基CO2吸附剂循环性能良好,10次循环后仍然能有很好的吸附效果;再生气氛中有H2O或CO2时会影响再生反应的进行,不利于吸附剂的再生。