Effect of chemical and thermal activations on the properties of rice husk ash-based solidified wastes

Strength development,leachability and microstructure of heavy metals from the solidified waste using synthesis rice husk ash (sRHA) and lime blended at the weight ratio of 1:1 were used as binders.The heavy metal-containing sludge was used at the level of 0 wt.%,30 wt.%,and 50 wt.% dry weight,respectively.The sample specimens with and without 1.5 wt.% of sodium silicate (SiO 2 /Na 2 O=1.0) were cured under the ambient condition and elevated temperature curing at 50°C for 24 hr.Experimental results showed that the introduction of sodium silicate solution and elevated temperature curing to sRHA-based solidified waste containing 30 wt.% of heavy metal sludge gave one day strength of 20 kg/cm 2 compared to 0.9 kg/cm2 for the control sample.XRD patterns indicated that most metal-sulfides present in the sludge were appeared in the solidified waste and SEM coupled with EDX techniques reveal these metal-sulfide particles were trapped within the lime-sRHA matrices.In addition,cumulative leaching behavior by tank test (EA NEN 7375:2004) showed that solidified waste containing up to 30 wt.% of heavy metal sludge was suitable to dispose in a secured landfill.     

多孔水化硅酸钙的制备及其磷回收特性

为实现磷资源的可持续利用,以环境废弃物电石渣为钙质材料,以白碳黑为硅质材料合成CSH(水化硅酸钙),以该材料为晶种,以结晶形成羟基磷灰石的形式从含磷废水中回收磷,重点研究了不同钙硅比〔c(CaO)/c(SiO₂)〕条件下制备的CSH对含磷废水中磷的回收特性. 结果表明,钙硅比为1.8∶1时所得的CSH结构更疏松、表面分布有较多的孔隙, 较大的比表面积使其具有较好的溶钙能力. 钙硅比为1.8∶1的CSH最佳磷回收工艺条件:反应时间为60min,CSH投加量为4g/L,搅拌强度为40r/min. 在该条件下重复除磷15次以后,回收产物中w(P)达到17.56%,说明CSH具有良好的磷回收性能. 对回收磷前后的CSH进行了XRD图谱分析和FTIR分析发现,溶液中的磷主要生成了羟基磷灰石并嵌入到CSH中. 基于回收磷的目的,CSH可以用于处理ρ(P)较高的工业废水,或者是生物除磷系统中的污泥厌氧释磷液中,回收磷后的产品可作为含磷矿石或者磷肥加以利用.      

聚硅氯化铝混凝剂中Al(Ⅲ)水解聚合历程及铝硅作用特性研究

采用共聚与复合两种制备工艺，制备出了系列具有不同碱化度和不同Ａｌ／Ｓｉ摩尔比的聚硅氯化铝混凝剂，分析研究了ＰＡＳＣ中Ａｌ（Ⅲ）的水解－聚合历程以及聚硅酸与铝水解聚合产物的相互作用，探讨了ＰＡＳＣ溶液的酸解聚。     

碳素纤维在近岸海洋污染物磷酸盐、硅酸盐处理中的应用

对碳素纤维进行氧化改性,利用改性后的碳素纤维处理近岸污染海水,重点研究了改性碳素纤维对海水中活性磷酸盐和活性硅酸盐的吸附作用。考察了碳素纤维液相改性时间、碳素纤维投加量、活性磷酸盐初始浓度、活性硅酸盐初始浓度、吸附时间、海况、pH值等单因素对近岸海洋污染物磷酸盐、硅酸盐吸附效果的影响。研究结果表明:改性碳素纤维对硅酸盐的吸附效果较好,去除率可达70%,对活性磷酸盐的去除率为31%左右。通过正交实验确定改性碳素纤维材料修复模拟近岸海水的优化条件为:碳素纤维改性时间为1.5 h,投加量为0.01 g,硅酸盐初始浓度为3mg/L,磷酸盐初始浓度为20 mg/L,海况为3级,pH值为8,吸附时间为3 h。在此条件下,碳素纤维对磷酸盐的去除率可达31.06%,硅酸盐去除率可达70.88%。     

Soil microbial response to waste potassium silicate drilling fluid

Potassium silicate drilling fluids (PSDF) are a waste product of the oil and gas industry with potential for use in land reclamation. Few studies have examined the influence of PSDF on abundance and composition of soil bacteria and fungi. Soils from three representative locations for PSDF application in Alberta, Canada, with clay loam, loam and sand textures were studied with applications of unused, used once and used twice PSDF. For all three soils, applying ≥ 40 m³/ha of used PSDF significantly affected the existing soil microbial flora. No microbiota was detected in unused PSDF without soil. Adding used PSDF to soil significantly increased total fungal and aerobic bacterial colony forming units in dilution plate counts, and anaerobic denitrifying bacteria numbers in serial growth experiments. Used PSDF altered bacterial and fungal colony forming unit ratios of all three soils.     

Preparation and coagulation efficiency of polyaluminium ferric silicate chloride composite coagulant from wastewater of high-purity graphite production

The aim of the present work was to produce a polyaluminium ferric silicate chloride (PAFSiC) coagulant from acidic and alkaline wastewater of purifying graphite by roasting, and subsequently to evaluate coagulation efficiency of the reagent by treating surface water from the Yellow River as well as municipal wastewater in comparison with the conventional coagulant polyaluminium chloride (PAC). The PAFSiC coagulant was prepared by co-polymerization. The effects of (Al+Fe)/Si molar ratio, OH/(Al+Fe) molar ratio (i.e., value), coagulant dosage and pH value of test suspension on the coagulation behavior of FAFSiC and the stability of the PAFSiC were also examined. Results showed that PAFSiC performed more efficiently than PAC in removing turbidity, chemical oxygen demand (COD), and total phosphate (TP). The PAFSiC with a value of 2.0 and (Al+Fe)/Si ratio of 5 (PAFSiC 2.0/5) showed excellent coagulation effect for both turbidity and COD, while PAFSiC 1.0/5 was the best for TP. The optimum coagulation pH range of PAFSiC 2.0/5 was 5.0–9.0, slightly wider than that of PAC (6.0–8.0). The process can be easily incorporated into high-purity graphite production plants, thereby reducing wastewater pollution and producing a valuable coagulant.     

硅酸盐细菌解钾兼拮抗活性菌株的筛选

从紫色土壤中分离筛选出具有解钾拮抗双重活性的硅酸盐细菌CS1和CS29菌株。接菌处理,其水溶性钾分别增加75％和65％,转化率达0．82％和0．72％。两株菌对革兰氏阳性的蜡样芽孢杆菌,金黄色葡萄球菌,藤黄八叠球菌等和革兰氏阴性的大肠杆菌均有较强的抑菌活性。筛选菌株中91．2％具有解钾活性,但拮抗活性菌株只占总数的11．6％,表明二性状之间无相关关系。表4参7     

Influences of Magnesium <Emphasis Type="Italic">tri-</Emphasis>Silicate on the Physical,Mechanical, and Degradable Properties of Ultraviolet (UV) Radiation Cured Plain Board Surface

A series of formulations were prepared with different percentages of oligomer, epoxy diacrylate (EA-1020 ), monomer, 1,6 Hexane diol diacrylate,(HDDA) and different percentages of filler (Magnesium tri-silicate, Mg₂Si₃O₈). Irgacure 369 [2-Benzyl-2-dimethyl-amine-1 (4-morpholinophenyl) butanone-1] was used in the formulations as photoinitiator. Ultraviolet (UV) cured thin polymer films were prepared from these formulating solutions on clean glass plates. Pendulum hardness (PH), gel content and macro scratch hardness (MSH) of the UV cured films were studied. One percent Mg₂Si₃O₈ containing formulation showed the premium properties. The substrates (plain board) were coated by these formulating solutions and cured under the same UV lamp at different intensities of radiation. Various properties of the coated surface such as PH, gloss, adhesion, abrasion and MSH were investigated. The base coat containing 1% Mg₂Si₃O₈ and top coat containing 48% HDDA produced the best performance among all the formulations inspected. The degradable properties in different weathering conditions on PH, gloss, adhesion, abrasion and MSH were measured. The surface cured with the optimized formulation (E) again yielded the minimum loss of the properties.     

Changing nutrient levels in Lake Maurepas following human population shifts in response to Hurricane Katrina

Following Hurricane Katrina in August 2005, as many as 57% of residents in some parishes in the Lower Lake Pontchartrain Basin were displaced from their homes. Concurrently, the population in the Upper Lake Pontchartrain Basin, which drains into Lake Maurepas, increased by 62,000 residents, leading to increased residential and urban land use. These changes led to significant increases in phosphate and silicate concentrations in Lake Maurepas that are likely caused by non-point source pollution through erosion from new construction sites, fertilisation of new lawns and stress to existing wastewater treatment facilities. Average phosphate concentrations at three sites in Lake Maurepas increased by 76–205% and silicate levels increased by 60–83% compared with data collected in 2003 prior to the hurricane. Discharge-weighted averages increased even more dramatically, with phosphate and silicate concentrations increasing up to 161 and 394%, respectively. Discharge-weighted silicate and phosphate concentrations were 2.5 and 3.4 times greater than in 2003, respectively. Discharge-weighted silicate levels were 3.9 times greater than similar measurements from 1963. These large increases in nutrient and discharge-weighted nutrient concentrations are indicative of increased human population in the Upper Lake Pontchartrain Basin following Hurricane Katrina.     

Decomposition of silicate minerals by Bacillus mucilaginosus in liquid culture

The extraction of K⁺ and SiO₂ from silicate minerals by Bacillus mucilaginosus in liquid culture was studied in incubation experiments. B. mucilaginosus was found to dissolve soil minerals and mica and simultaneously release K⁺ and SiO₂ from the crystal lattices. In contrast, the bacterium did not dissolve feldspar. B. mucilaginosus also produced organic acids and polysaccharides during growth. The polysaccharides strongly adsorbed the organic acids and attached to the surface of the mineral, resulting in an area of high concentration of organic acids near the mineral. The polysaccharides also adsorbed SiO₂ and this affected the equilibrium between the mineral and fluid phases and led to the reaction toward SiO₂ and K⁺ solubilization. These two processes led to the decomposition of silicate minerals by the bacterium.