氮氟掺杂二氧化钛(N,F-TiO2)的制备及可见光催化活性的研究

以氨水为氮源,氢氟酸为氟源,采用溶胶-凝胶法制备了氮氟掺杂二氧化钛(N,F-TiO2)光催化剂,并通过X-射线衍射(XRD)和扫描电镜(SEM)技术对其晶型和形态进行表征.最后以酸性红B为模型污染物,探讨了N和F加入量、焙烧温度、焙烧时间、照射时间、催化剂用量、溶液初始浓度和照射功率等因素对N,F-TiO2可见光催化活性的影响.结果表明,制备的N,F-TiO2以锐钛型为主,N和F的掺杂对TiO2的晶相没有明显改变,但可以扩大TiO2的可见光响应范围.当N和F的加入量均为2.0%,且在500℃下焙烧40 min时,得到的N,F-TiO2的可见光催化活性明显高于单N或单F掺杂的TiO2(N-TiO2或F-TiO2).对于50 mL浓度为10.0 mg·L-1的酸性红B溶液,当催化剂加入量为1.5 g·L-1,128W光照3.0 h,溶液pH=5.6时,去除率为85.40%.适当延长光照时间至4.0 h,降解率几乎可达100%.另外,研究还证明了N,F-TiO2催化可见光降解过程中有.OH自由基生成.     

流化床O2/CO2气氛下添加SiO2对燃煤PM2.5的控制

采用小型流化床研究了在O2/CO2气氛下添加SiO2对PM2.5(空气动力学直径小于2.5 μm的颗粒物)的控制,试验在1123 K、O2/CO2气氛下进行,并采用荷电低压撞击器(ELPI)采集和分析燃烧后的PM2.5.结果表明,添加SiO2是燃烧过程中影响PM2.5生成的重要因素.添加SiO2后,生成PM1的质量浓度均降低,而PM1-2.5的质量浓度均略有增加;PM2.5质量粒径分布均呈双峰分布,峰值分别出现在0.2 μm和2.0μm左右.随着SiO2添加量的增加,PM2.5中的S、K、Na、Cu和Pb元素的含量呈减少的趋势;随着颗粒粒径减小,S、K、Na、Cu和Pb元素的含量有增高的趋势.     

流化床焚烧含盐苯胺废液的NOx排放特性

在流化床焚烧实验装置上进行含盐苯胺(C6H5NH2)废液的焚烧实验研究,用IMR-IMR2800P废气分析仪对焚烧尾气成分进行了在线监测,考察了焚烧工艺条件对NOx排放浓度的影响规律.结果显示:采用分级燃烧工艺和提高焚烧温度,可以降低NOx浓度;增大进料速率却导致NOx排放浓度的增加.当过剩空气系数(α)低于1.0时,NOx排放浓度随着α的增大急剧上升;大于1.1时,NOx排放浓度随α增加而减小.苯胺废液高温焚烧时添加氯化钠能降低NOx排放.     

二氧化钛复合型催化剂制备及其微波辅助催化氧化甲苯性能

实验采用溶胶凝胶法和传统浸渍法制备了TiO2-分子筛复合载体及复合载体负载过渡金属与稀土元素催化剂,通过微波辅助催化氧化甲苯的性能实验考察其催化活性.结果表明,复合TiO2明显提高了载体结构的稳定性与耐温性,并使过渡金属铜(Cu)、锰(Mn)和稀土元素铈(Ce)等活性组分在催化剂表面的分散更均匀;在复合载体吸附、吸波性能与多相活性组分催化的共同作用下,Cu-Mn-Ce/TiO2-分子筛催化剂微波辅助催化氧化甲苯的完全燃烧温度仅为175℃,此时甲苯去除率可达99％;15 h的连续性实验表明,TiO2复合型催化剂具有良好的催化活性与稳定性.由催化剂表征分析结果可知,活性组分颗粒的均匀分布与铜、锰氧化物及铜锰尖晶石固溶物等活性相的存在促进了甲苯的催化氧化,锐钛矿型TiO2较高的电子迁移速率与催化剂孔径的增大均有助于甲苯的氧化降解.     

直接大红4BE的磷钨酸均相光催化还原脱色

以磷钨酸(H3PW12O40,PW12)为光催化剂,异丙醇(Isopropanol)作为电子给体的条件下对偶氮染料直接大红4BE进行均相光催化还原脱色研究,考察PW12用量、IS浓度、直接大红4BE和盐浓度等因素的影响,结果表明杂多蓝(PW1-2)对直接大红4BE具有明显的还原脱色作用.pH=2.0,直接大红4BE初始浓度50 mg·L-1,PW12浓度为600 mg·L-1,IS浓度为0.13mol·L-1,50 min直接大红4BE的脱色率可达到90.39%.4BE的光催化还原脱色速率随PW12和IS浓度的增加而增加,最后趋于恒定;直接大红4BE初始浓度增加,其光反应一级速率常数降低;PW12、IS和4BE浓度之间存在交互影响.离子强度增加,4BE脱色速率减小,表现为负的盐效应,推测4BE与光反应生成的杂多蓝(PW1-2)进行复合,然后发生电子转移引起偶氮染料还原脱色和杂多蓝氧化复原.本研究结果表明PW12/IS/UV能够有效用于偶氮染料直接大红4BE的还原脱色处理.     

Pollutant emission characteristics of rice husk combustion in a vortexing fluidized bed incinerator

Rice husk with high volatile content was burned in a pilot scale vortexing fluidized bed incinerator. The fluidized bed incinerator was constructed of 6 mm stainless steel with 0.45 m in diameter and 5 m in height. The emission characteristics of CO, NO, and SO2 were studied. The effects of operating parameters, such as primary air flow rate, secondary air flow rate, and excess air ratio on the pollutant emissions were also investigated. The results show that a large proportion of combustion occurs at the bed surface and the freeboard zone. The SO2 concentration in the flue gas decreases with increasing excess air ratio, while the NOx concentration shows reverse trend. The flow rate of secondary air has a significant impact on the CO emission. For a fixed primary air flowrate, CO emission decreases with the secondary air flowrate. For a fixed excess air ratio, CO emission decreases with the ratio of secondary to primary air flow. The minimum CO emission of 72 ppm is attained at the operating condition of 40% excess air ratio and 0.6 partition air ratio. The NOx and SO2 concentrations in the flue gas at this condition are 159 and 36 ppm, which conform to the EPA regulation of Taiwan.     

Formic acid as an alternative reducing agent for the catalytic nitrate reduction in aqueous media

Formic acid was used for the nitrate reduction as a reductant in the presence of Pd:Cu/γ-alumina catalysts. The surface characteristics of the bimetallic catalyst synthesized by wet impregnation were investigated by SEM, TEM-EDS. The metals were not distributed homogeneously on the surface of catalyst, although the total contents of both metals in particles agreed well with the theoretical values. Formic acid decomposition on the catalyst surface, its influence on solution pH and nitrate removal efficacy was investigated. The best removal of nitrate (50 ppm) was obtained under the condition of 0.75 g/L catalyst with Pd:Cu ratio (4:1) and two fold excess of formic acid. Formic acid decay patterns resembled those of nitrate removal, showing a linear relationship between kf (formic acid decay) and k (nitrate removal). Negligible amount of ammonia was detected, and no nitrite was detected, possibly due to buffering effect of bicarbonate that is in situ produced by the decomposition of formic acid, and due to the sustained release of H2 gas.     

OMS-2负载Pt催化剂的制备及其催化氧化性能研究

采用前掺杂法、沉积-沉淀法和浸渍法制备了氧化锰八面体分子筛(OMS-2)负载Pt催化剂(Pt/OMS-2),对所制催化剂进行了结构和织构表征。并研究了不同制备方法和沉积-沉淀法中不同制备(Pt负载量和溶液的pH值)对Pt/OMS-2催化氧化CO性能的影响。结果表明,沉积-沉淀法制备的Pt/OMS-2-DP催化剂活性最好(T100=100℃)。这与Pt/OMS-2-DP催化剂中Pt颗粒大小及OMS-2载体与Pt之间存在强相互作用有关。Pt负载量明显影响Pt/OMS-2-DP催化剂的催化活性,3Pt/OMS-2-DP催化剂(Pt=3.0 wt%)催化活性最高,这是由于适当Pt负载量,Pt颗粒较小,并与载体OMS-2的相互作用较强,能较好地活化OMS-2晶格氧。pH值对Pt/OMS-2-DP催化剂催化性能影响较大,这与OMS-2的等电点和Pt在不同溶液中存在不同Pt配位体形式有关。     

流化床污泥干燥器床料的颗粒度对流化情况的影响

以上海白龙港污水处理厂流化床污泥干燥系统为研究对象,针对流化床污泥干燥器流化情况的好坏分析,在确定其它变量（流化风量、给料分配器转速、料层压差、运行负荷等）不变的情况下,对床料颗粒度的工艺参数进行研究实验,总结颗粒度的工艺参数对流化情况的运行变化规律,从而提高了流化床污泥干燥系统的稳定性、连续性和高效性。     

非均相类Fenton试剂的制备及其在焦化废水处理中的应用研究

利用浸渍法,将Fe3＋负载在经酸碱改性后的粉状活性炭上,当浸渍液浓度为2．5％,固化温度为270℃时,制成的催化剂催化活性较高。用自制的非均相类benton试剂降解焦化废水,通过正交试验和极差分析得出,影响因素的主次顺序为催化剂用量〉初始pH值〉反应时间〉H：0：投加量。结果表明,在100ml水样中。室温条件下,初始pH值为4．0,催化剂使用量为1．5g,H20：投加量为5ml（分两次投加）,反应时间为90min时,COD去除率可达99％。采用混凝＋化学沉淀＋非均相类Fenton试剂法处理焦化废水,各主要出水水质指标为：色度lO倍;COD浓度38．5mg／L;氨氮浓度8．4mg／L,达到国家一级排放标准。