Enhancement of UV and chromate mutagenesis by nickel ions in the Chinese hamster HGPRT Assay †

1. The HGPRT (Hypoxanthine‐Guanine‐Phospho‐Ribosyl‐Transferase) assay with Chinese Hamster V79 cells was used to measure the mutagenic effects of UV irradiation, potassium dichromate and nickel chloride. The agents were tested separately and in the combinations of UV plus nickel and dichromate plus nickel.

2. UV, Cr(VI) and Ni(II) were confirmed to be mutagenic in the V79 cell assay. The combination of UV(5J/m²) and Ni(II) (0.5 mM) caused a mutation rate 11.2 times above that corresponding to the sum of the individual mutation rates of these agents. The combined action of Cr(VI) (0.1 mM) and Ni(II) (0.5 mM) produced a mutation rate 2.8 fold above that corresponding to the sum of the individual rates of the separate agents.

3. The enhancing effect of nickel chloride on the mutagenicity of UV or Cr(VI) is interpreted by an interference of Ni(II) with the repair of DNA lesions.     

电解法处理含镍废水及纯镍的回收

采用电解回收法处理Ni2+含量为2g/L的废水,在阴极回收纯镍。研究了电解电流、极距、NH4Cl浓度、pH值等因素对Ni2+去除率、槽压、阴极能耗的影响,得出最优工艺参数为:温度20℃,电解时间20min时、电解电流300mA,极距15mm,NH4Cl浓度5g/L,pH值8.0,该条件下Ni2+去除率为96.926%,槽压16.21V,阴极能耗22.418kW.h/kg,在阴极可得到沉积6.45μm厚的镍板。     

镍的作物效应及临界值研究

在三种紫色土（酸性，中性，石灰性）上添加Ｎｉ（０，１０，３０，６０，１００，２００ｍｇ／ｋｇ土）进行莴笋盆栽试验，结果表明：低浓度的Ｎｉ能刺激作物生长，而高浓度的Ｎｉ则阻碍作物生长，使叶片黄化。三种土因性质及本身肥力水平的差异，使酸性紫色土上作物Ｎｉ最敏感，石灰性紫色土上次之，中性紫色土上最不敏感，且Ｎｉ在作物体内分配规律也有所不同，比较了土壤全Ｎｉ，有效Ｎｉ，植株根Ｎｉ作为的临界值的优越性，结果     

含镍废催化剂的回收利用

介绍了从含镍废催化剂中以硝酸镍形式加收镍的方法，镍回收率为70％，硝酸镍纯度为96．6％。该工艺简单，具有较好的经济效益和环境效益。     

THE IMPACT OF URBANIZATION ON THE DISTRIBUTION OF HEAVY METALS IN BOTTOM SEDIMENTS OF THE SADDLE RIVER1

ABSTRACT: A three-year study has been conducted on a 4.6 mile stretch of the Saddle River near Lodi, New Jersey. The primary objectives of this investigation were (1) to provide baseline information on the concentration and distribution of heavy metals in bottom sediments of the Saddle River; (2) to qualitatively evaluate which parameters affect this distribution; and (3) to determine the effect of urbanization on the concentration and distribution of these materials. Significant enrichments of several heavy metals were observed in bottom sediments of the lower Saddle River near Lodi, New Jersey, as compared to the upper Saddle River. Attempts to correlate metal concentrations in bottom sediments with chemical-oxygen demand were not successful in demonstrating a relationship between these two factors. Metal concentrations were found to be strongly dependent upon particle size. In general, metal concentrations in bottom sediments increased with decreasing partical diameter. However, metals enrichment was observed to be considerably greater in the larger sediment fractions studied (>420μ) than the smaller sediment fractions as one proceeded downstream through the urban area. Since the larger sediment fractions are least effected by scour and transport they may best reflect the effect of urbanization on the distribution of heavy metals over an extended period of time at a given location.     

新疆阜康冶炼厂无污染工艺及环境治理

介绍了阜康冶炼厂无污染新工艺和环境治理的有关情况 ,从理论上阐述了无污染工艺和污水治理的技术原理 ,对有色金属冶炼工业逐步采用湿法精炼清洁工艺有一定的指导作用     

Simultaneous photocatalytic treatment of Cr(VI), Ni(II) and SDBS in aqueous solutions: Evaluation of removal efficiency and energy consumption

Simultaneous photocatalytic reduction of poisonous Cr(VI) and Ni(II) ions, coupled with photocatalytic oxidation of sodium dodecyl benzene sulfonate (SDBS) were studied with a trace amount of commercial titania nanoparticles and by means of a direct-photo-irradiation reactor. The co-presence of metal ions and SDBS causes metal ions reduction as well as SDBS oxidation to enhance and energy efficiency to improve. XRD, XPS and FTIR analysis were used to characterize TiO₂ particles before and after usage with the aim of evaluating the mechanism of reactions. The effect of major operating parameters, pH and temperature, was investigated. Under conditions of [Cr(VI)]₀ = [Ni(II)]₀ = 5 mg/L, [SDBS]₀ = 10 mg/L, [TiO₂] = 40 mg/L, pH 6 and T = 35 °C; the removal efficiencies of 55.4%, 71.2% and 57.2% were obtained, respectively, for Cr(VI) and Ni(II) reduction, as well as for SDBS oxidation, after 110 min operation. The relevant kinetic model jointed with the Arrhenius equation was introduced. Pseudo-first-order reactions are relevant. Energy consumption (electrical and thermal) evaluations revealed that operations at higher temperatures provide significant cost reduction. Meantime, a criterion was proposed for a consistent assessment of this kind of processes.     

NiO-CuO/ZSM-5催化剂对催化裂化烟气的脱硫脱硝性能

采用浸渍法制备了不同NiO和CuO质量分数的NiO-CuO/ZSM-5催化剂，并以CH4为还原剂研究了NiO-CuO/ZSM-5催化剂对催化裂化烟气的脱硫脱硝活性。XRD分析结果表明，NiO质量分数为4%、CuO质量分数为6%的催化剂4%NiO-6%CuO/ZSM-5中的ZSM-5结构完好，CuO和NiO高度分散在ZSM-5骨架中，表明具有较好的催化活性。4%NiO-6%CuO/ZSM-5的脱硫脱硝起活温度均较低，无氧条件下最高NO转化率和SO2转化率分别为94.7%和95.9%，O2体积分数为1.0%时的NO转化率和SO2转化率分别为97.7%和89.0%。     

EDTA直接滴定测定镍

参考磷酸在345~356℃时有强腐蚀性的特点,采有硫磷混合酸消解矿样,能使样品消解完全。本方法经加标校核证明,检测结果重现性好,准确度高。     

镍渣制备建筑用微晶玻璃的初步研究

对从镍渣中提取铁同时制备建筑用微晶玻璃的进行了研究.结果表明,熔渣中铁的质量分数可以降到0.5%左右,满足制备微晶玻璃的要求.对微晶玻璃样品进行了显微镜、X射线衍射、扫描电镜分析.其主晶相是透辉石(CaO·MgO·2SiO2),晶体的形貌为短柱状,分布均匀.本文所介绍的制备工艺是可行的.