Removal kinetics of phosphorus from synthetic wastewater using basic oxygen furnace slag

Removal kinetics of phosphorus through use of basic oxygen furnace slag (BOF-slag) was investigated through batch experiments. Effects of several parameters such as initial phosphorus concentration, temperature, BOF-slag size, initial pH, and BOF-slag dosage on phosphorus removal kinetics were measured in detail. It was demonstrated that the removal process of phosphorus through BOF-slag followed pseudo-first-order reaction kinetics. The apparent rate constant (k_obs) significantly decreased with increasing initial phosphorus concentration, BOF-slag size, and initial pH, whereas it exhibited an opposite trend with increasing reaction temperature and BOF-slag dosage. A linear dependence of k_obs on total removed phosphorus (TRP) was established with k_obs = (3.51 ± 0.11) × 10^− 4 × TRP. Finally, it was suggested that the Langmuir–Rideal (L–R) or Langmuir–Hinshelwood (L–H) mechanism may be used to describe the removal process of phosphorus using BOF-slag.     

Removal kinetics of phosphorus from synthetic wastewater using basic oxygen furnace slag

Removal kinetics of phosphorus through use of basic oxygen furnace slag(BOF-slag)was investigated through batch experiments. Effects of several parameters such as initial phosphorus concentration, temperature, BOF-slag size, initial p H, and BOF-slag dosage on phosphorus removal kinetics were measured in detail. It was demonstrated that the removal process of phosphorus through BOF-slag followed pseudo-first-order reaction kinetics. The apparent rate constant(kobs) significantly decreased with increasing initial phosphorus concentration, BOF-slag size, and initial p H, whereas it exhibited an opposite trend with increasing reaction temperature and BOF-slag dosage.A linear dependence of kobson total removed phosphorus(TRP) was established with kobs=(3.51 ± 0.11) × 10- 4× TRP. Finally, it was suggested that the Langmuir–Rideal(L–R)or Langmuir–Hinshelwood(L–H) mechanism may be used to describe the removal process of phosphorus using BOF-slag.     

Preparation of steel slag porous sound-absorbing material using coal powder as pore former

The aim of the study was to prepare a porous sound-absorbing material using steel slag and fly ash as the main raw material, with coal powder and sodium silicate used as a pore former and binder respectively. The influence of the experimental conditions such as the ratio of fly ash, sintering temperature, sintering time, and porosity regulation on the performance of the porous sound-absorbing material was investigated. The results showed that the specimens prepared by this method had high sound absorption performance and good mechanical properties, and the noise reduction coefficient and compressive strength could reach 0.50 and 6.5 MPa, respectively. The compressive strength increased when the dosage of fly ash and sintering temperature were raised. The noise reduction coefficient decreased with increasing ratio of fly ash and reducing pore former, and first increased and then decreased with the increase of sintering temperature and time. The optimum preparation conditions for the porous sound-absorbing material were a proportion of fly ash of 50% (wt.%), percentage of coal powder of 30% (wt.%), sintering temperature of 1130°C, and sintering time of 6.0 hr, which were determined by analyzing the properties of the sound-absorbing material.     

锰渣填埋场渗滤液及周边水体的水化学特征和质量评价

本文在分析锰渣填埋场区渗滤液及周边水体水化学组成的基础上,运用改进的水质量指数(WQI)进行了水质评价,阐述了填埋场渗滤液对下游水体的影响过程。结果表明,研究区渗滤液pH呈中性偏酸性,EC在1 780~44 500μS/cm之间,渗滤液中NH4-N、Mn2+、Mg2+、SO2-4、NO-3的浓度较高,并呈现SO2-4Mn2+Mg2+NH+4-N的特征,并且浓度与堆存时间呈负相关性。填埋场下游水体的重金属浓度微量,但NH4-N和Mn2+浓度较高,均超过GB 3838—2002和GB/T 14848—93规定的限值,其中2014年5月份某地下水的这两个参数分别超标243倍和488倍。改进的WQI指数评价结果显示,地表水的渗滤液水污染指数(LWPI)值在2.89~7.83之间,受影响的地下水为172,说明渗滤液已对锰渣填埋场下游水体造成严重影响。     

利用含铬废水和含铅废水制备铬黄

利用净化后的含铬废水和含铅废水制备铬黄.采用沉淀法对废水进行净化预处理,最佳工艺条件:100mL含铬废水中加入20 g Na_2CO_3,及10 mL H_2O_2,用NaOH调节含铬废水pH为10.00;用NaOH调节含铅废水pH为2.65.将净化后的10 mL含铬废水和25 mL含铅废水混合,在55-60℃条件下反应10 min,合成的铬黄达到GB/T 3184-2008<铬酸铅颜料和钼铬酸铅颜料>的质量标准.经重金属吸附剂处理Pb~(2+)后铬黄合成滤液中的Cr~(6+)和Pb~(2+)质量浓度均达到GB8978-1996<污水综合排放标准>的指标.     

利用高炉水淬渣制作多孔吸声材料的研究

为了促进高炉炼铁水淬渣的二次利用,研究了以高炉炼铁水淬渣为原料,以硅微粉或水泥为粘结剂,采用压制成型方法制作的多孔吸声材料的吸声性能及力学性能。结果表明:用颗粒状的高炉炼铁水淬渣制作的多孔吸声材料具有良好的吸声性能,其平均吸声系数可以达到0.70以上;材料的抗压强度可以达到3.0 MPa以上。     

锶盐废渣含硫状态分析及硫含量的测定

锶盐废渣中硫的状态及含量不同其作用大不相同,有的呈现活性导致膨胀破坏,而有的则表现为惰性,因此有必要了解硫的存在状态及含量。分析表明锶盐废渣中硫主要以硫酸盐硫(SO3)和硫化物硫(S2-)两种形式存在。选择硫酸钡重量法和碘量法进行化学测定,然后用X-射线能谱仪进行元素定性分析;并将化学分析和仪器测定两种方法进行对比。结果表明,X-射线能谱法可以快捷、方便地探测锶渣所含各种元素,但不能确定元素的价态;化学分析方法可得到相对准确的元素含量;用硫酸钡重量法和碘量法联合测定锶渣中的硫含量,与X-射线能谱法相比,偏差仅为0.37%。     

新型钢渣水处理剂去除水体污染物的研究现状

钢渣是炼钢生产过程中产生的固体废弃物,具有较高的碱度、机械强度和比表面积。钢渣化学成份较复杂,直接排放会对环境造成严重的污染,加强钢渣的处置及综合利用具有重大意义。作为一种新型的水处理剂,钢渣用于去除水体污染物不仅减少了水体、土壤等生态环境的污染,而且达到了以废治废的目的。文章分析了钢渣水处理剂去除水体污染物的作用机理,认为钢渣水处理剂对水体中污染物的去除主要通过吸附和沉淀两种作用,而还原作用和离子交换作用相对较小。阐述了钢渣水处理剂处理重金属废水、有机废水和无机废水的研究现状,提出了在开发液态钢渣新型处理工艺的基础上,实现钢渣水处理剂的应用。     

配碳还原回收铜渣中铁、铜的影响因素探讨

采用配碳还原和熔融造渣方法回收铜渣中铁和铜,研究了CaO、Al2O3、CaF2、Na2CO3成分对铁和铜回收效果的影响。在碳氧比1.5和1 450℃条件下,CaO加入量约30%时,铁和铜的回收率较高,分别是93.85%和92.73%。实验表明:添加Al2O3、Na2CO3均降低铁和铜的回收效果,使渣中含铁量增加;CaF2添加量小于2%时,有利于铜渣中铁的回收,CaF2添加量较大时不利于铁和铜的回收。     

电石渣-石膏湿法烟气脱硫废水处理工艺研究

电石渣-石膏湿法脱硫废水与石灰石-石膏湿法脱硫废水存在差异,主要体现在悬浮物与COD较难去除,采用在中和池添加助凝剂与曝气池添加氧化剂的方法,可在沿用石灰石法脱硫废水处理工艺设计的前提下达到对电石渣法脱硫废水的良好处理效果。