直接大红4BE的磷钨酸均相光催化还原脱色

以磷钨酸(H3PW12O40,PW12)为光催化剂,异丙醇(Isopropanol)作为电子给体的条件下对偶氮染料直接大红4BE进行均相光催化还原脱色研究,考察PW12用量、IS浓度、直接大红4BE和盐浓度等因素的影响,结果表明杂多蓝(PW1-2)对直接大红4BE具有明显的还原脱色作用.pH=2.0,直接大红4BE初始浓度50 mg·L-1,PW12浓度为600 mg·L-1,IS浓度为0.13mol·L-1,50 min直接大红4BE的脱色率可达到90.39%.4BE的光催化还原脱色速率随PW12和IS浓度的增加而增加,最后趋于恒定;直接大红4BE初始浓度增加,其光反应一级速率常数降低;PW12、IS和4BE浓度之间存在交互影响.离子强度增加,4BE脱色速率减小,表现为负的盐效应,推测4BE与光反应生成的杂多蓝(PW1-2)进行复合,然后发生电子转移引起偶氮染料还原脱色和杂多蓝氧化复原.本研究结果表明PW12/IS/UV能够有效用于偶氮染料直接大红4BE的还原脱色处理.     

Effect of transition metal doping under reducing calcination atmosphere on photocatalytic property of TiO2 immobilized on SiO2 beads

TiO₂ immobilized on SiO₂ (TiO₂/SiO₂) have been prepared by sol-gel method and various ions of transition metals (Cr³⁺, Co²⁺, Ni²⁺, Cu²⁺, and Zn²⁺) were doped on the photocatalyst using wet impregnation method under reducing calcination atmosphere. The photocatalytic activity of metal doped TiO₂/SiO₂ towards phenol degradation under black light irradiation were investigated and compared with undoped TiO₂/SiO₂. The results showed that the photoresponse of Cu²⁺ and Zn²⁺ doped TiO₂/SiO₂ were larger than undoped TiO₂/SiO₂, indicating that the photogenerated carriers were separated more efficiently in Cu²⁺ and Zn²⁺ doped TiO₂/SiO₂. The reactivity was in the order of Cu²⁺ > Zn²⁺ > Ni²⁺ > Cr³⁺ > Co²⁺. The different photoreactivity was ascribed to combine effect of the different ionic radii and photocorrison tendency of the dopants. The sample was also characterized by surface analytical methods such as X-ray diffraction, scanning electron micrograph/electron dispersive X-ray analyzer and UV-Vis absorption spectrum.     

Homogeneous and heterogeneous reactions of anthracene with selected atmospheric oxidants

The reactions of gas-phase anthracene and suspended anthracene particles with O3 and O3-NO were conducted in a 200-L reaction chamber, respectively. The secondary organic aerosol (SOA) formations from gas-phase reactions of anthracene with O3 and O3-NO were observed. Meanwhile, the size distributions and mass concentrations of SOA were monitored with a scanning mobility particle sizer (SMPS) during the formation processes. The rapid exponential growths of SOA reveal that the atmospheric lifetimes of gas-phase anthracene towards O3 and O3-NO are less than 20.5 and 4.34 hr, respectively. The particulate oxidation products from homogeneous and heterogeneous reactions were analyzed with a vacuum ultraviolet photoionization aerosol time-of-flight mass spectrometer (VUV-ATOFMS). Gas chromatograph/mass spectrometer (GC/MS) analyses of oxidation products of anthracene were carried out for assigning the time-of-flight (TOF) mass spectra of products from homogeneous and heterogeneous reactions. Anthrone, anthraquinone, 9,10- dihydroxyanthracene, and 1,9,10-trihydroxyanthracene were the ozonation products of anthracene, while anthrone, anthraquinone, 9-nitroanthracene, and 1,8-dihydroxyanthraquinone were the main products of anthracene with O3-NO.     

Formic acid as an alternative reducing agent for the catalytic nitrate reduction in aqueous media

Formic acid was used for the nitrate reduction as a reductant in the presence of Pd:Cu/γ-alumina catalysts. The surface characteristics of the bimetallic catalyst synthesized by wet impregnation were investigated by SEM, TEM-EDS. The metals were not distributed homogeneously on the surface of catalyst, although the total contents of both metals in particles agreed well with the theoretical values. Formic acid decomposition on the catalyst surface, its influence on solution pH and nitrate removal efficacy was investigated. The best removal of nitrate (50 ppm) was obtained under the condition of 0.75 g/L catalyst with Pd:Cu ratio (4:1) and two fold excess of formic acid. Formic acid decay patterns resembled those of nitrate removal, showing a linear relationship between kf (formic acid decay) and k (nitrate removal). Negligible amount of ammonia was detected, and no nitrite was detected, possibly due to buffering effect of bicarbonate that is in situ produced by the decomposition of formic acid, and due to the sustained release of H2 gas.     

LNAPLs污染物在层状非均质多孔介质中的运移试验研究

文章通过室内试验研究层状非均质多孔介质中轻非水相液体(Light Non-Aqueous Phase Liquid,LNAPL)的运移机制与分布特性。首先,在二维砂槽上进行LNAPL的入渗试验,试验过程中用数码相机进行拍照,把LANPL的扩散过程以图像的形式记录下来;然后,用AutoCAD对图片进行分析处理,得出不同时刻LNAPL的入渗锋面变化图。结果发现,介质结构突变面改变了LNAPL的迁移模式。在LNAPL由中砂进入细砂层后,由于受到毛细作用的增强,其运移速度加快;而由中砂进入粗砂,受粗砂介质阻滞作用增强的影响,LNAPL运移速度变小。当LNAPL由干砂进入湿润砂体时,由于孔隙水浮托力增大,LNAPL先产生纵向运移,随后以横向迁移的形式在地下水位上部聚积。当达到一定厚度后,LNAPL的压头足以克服浮托力,驱替孔隙水进入砂土孔隙。另外,LNAPL的厚度足够大时,方可克服饱水层受到的浮托力,在地下水位上形成LNAPL池,并因孔隙水向周围砂体排泄,LNAPL池周围的水位上升。     

OMS-2负载Pt催化剂的制备及其催化氧化性能研究

采用前掺杂法、沉积-沉淀法和浸渍法制备了氧化锰八面体分子筛(OMS-2)负载Pt催化剂(Pt/OMS-2),对所制催化剂进行了结构和织构表征。并研究了不同制备方法和沉积-沉淀法中不同制备(Pt负载量和溶液的pH值)对Pt/OMS-2催化氧化CO性能的影响。结果表明,沉积-沉淀法制备的Pt/OMS-2-DP催化剂活性最好(T100=100℃)。这与Pt/OMS-2-DP催化剂中Pt颗粒大小及OMS-2载体与Pt之间存在强相互作用有关。Pt负载量明显影响Pt/OMS-2-DP催化剂的催化活性,3Pt/OMS-2-DP催化剂(Pt=3.0 wt%)催化活性最高,这是由于适当Pt负载量,Pt颗粒较小,并与载体OMS-2的相互作用较强,能较好地活化OMS-2晶格氧。pH值对Pt/OMS-2-DP催化剂催化性能影响较大,这与OMS-2的等电点和Pt在不同溶液中存在不同Pt配位体形式有关。     

非均相类Fenton试剂的制备及其在焦化废水处理中的应用研究

利用浸渍法,将Fe3＋负载在经酸碱改性后的粉状活性炭上,当浸渍液浓度为2．5％,固化温度为270℃时,制成的催化剂催化活性较高。用自制的非均相类benton试剂降解焦化废水,通过正交试验和极差分析得出,影响因素的主次顺序为催化剂用量〉初始pH值〉反应时间〉H：0：投加量。结果表明,在100ml水样中。室温条件下,初始pH值为4．0,催化剂使用量为1．5g,H20：投加量为5ml（分两次投加）,反应时间为90min时,COD去除率可达99％。采用混凝＋化学沉淀＋非均相类Fenton试剂法处理焦化废水,各主要出水水质指标为：色度lO倍;COD浓度38．5mg／L;氨氮浓度8．4mg／L,达到国家一级排放标准。     

一种新型电化学法处理硝态氮废水的初步研究

通过对Pd-Me双金属催化还原NO 3--N和折点氯化法处理NH 4+-N的相关理论分析,提出了一种基于电化学法的新型NO 3--N废水处理工艺.即利用具有电子空轨的常见金属元素修饰Ti基获得催化阴极,在电场的作用下,将NO 3--N催化还原;通过调整催化元素的配比和电解条件,控制NO 3--N还原产物主要为NH 4+-N;利用阳极氧化Cl-生成高氧化性物质HOCl,将NH 4+-N氧化为无害产物N2-N.结果表明,金属元素Co和Cu修饰Ti基制得阴极可以有效地催化还原模拟废水中的NO 3--N;按前驱物溶液金属元素摩尔比1∶1制得Ti基Co-Cu复合涂层催化阴极,可以将NO 3--N高效催化还原为NH 4+-N;电解体系中引入Cl-后,通过阳极作用可将NO 3--N还原生产的NH 4+-N有效地氧化为N2-N.在100 mg/L NO 3--N模拟废水中添加1 000 mg/L Cl-,设置极板间距6 mm、电流400 mA,电解2.5 h后出水NO 3--N、NO 2--N、NH 4+-N和TN分别为2.9、0.5、1.7和6.0 mg/L.     

蜂窝陶瓷催化臭氧化降解水中微量硝基苯的动力学研究

实验表明单独臭氧氧化和臭氧/蜂窝陶瓷氧化在温度20℃、初始pH值6.87条件下对硝基苯的降解均遵循一级反应动力学模型,该条件下单独臭氧氧化和臭氧/蜂窝陶瓷氧化工艺对硝基苯的降解主要来源于高活性羟基自由基的氧化作用,同时证明了不同体系温度（10～40℃）和溶液初始pH值（3.00～10.96）下硝基苯的降解同样符合一级反应动力学.2种工艺对硝基苯的降解反应速率都随着温度的升高而增加,单独臭氧氧化的反应速率常数由0.37×10^-3 s^-1升高到1.49×10^-3 s^-1,臭氧/蜂窝陶瓷氧化的反应速率常数由0.56×10^-3 s^-1升高到2.46×10^-3 s^-1,温度越高反应速率提高的幅度却越小.随着pH的升高,单独臭氧氧化对硝基苯降解的反应速率常数从0.15×10^-3 s^-1增加到2.69×10^-3 s^-1,在pH值3.00～9.23范围内,臭氧/蜂窝陶瓷氧化工艺反应速率常数从0.17×10^-3 s^-1增加到1.90×10^-3 s^-1,在pH为10.96时反应速率常数下降到1.64×10^-3 s^-1.