钯金属具有较高的催化加氢性能,钯催化还原降解水体中污染物的研究一直是国内外研究的热点。为了制备催化性能稳定、催化活性高且易于回收利用的Pd催化剂,实验以聚丙烯腈(PAN)聚合物分离膜作为基材,采用层层自组装方法将聚乙烯亚胺/钯配合物(PEI-Pd(II))和聚苯乙烯磺酸钠(PSS)交替组装在基膜表面,制备了(PEI-Pd(0)/PSS)n复合催化膜,并采用膜分离装置通过对硝基苯酚催化加氢反应来评价催化膜的催化性能。实验结果表明,荷电化处理时间、NaOH溶液浓度、PEI和Pd(II)摩尔比、自组装层数影响着膜的催化性能。当荷电化处理时间为1.5 h,NaOH溶液浓度为1.5 mol/L,PEI和Pd(II)摩尔比为60∶4,自组装层数为5层时,复合催化膜有最佳的催化性能,其对对硝基苯酚的去除率能达到90%以上。     

纳米Pd／Fe双金属颗粒对单氯酚及二氯酚的还原脱氯

采用改进液相化学还原法制备纳米Pd／Fe双金属颗粒,研究其钯化率为0．045％和0．135％的条件下分别对3种单氯酚（2-CP、3-CP和4-CP）和3种二氯酚（2,3-DCP、2,4-DCP和2,6-DCP）的脱氯反应。结果表明,合成的纳米Pd／Fe颗粒分散性良好,粒径分布介于25～40nm。纳米Pd／Fe双金属颗粒对单氯酚及二氯酚具有良好的去除效果,3种单氯酚和3种二氯酚的脱氯难易程度分别为2-CP〉4-CP〉3-CP和2,6-DCP〉2,4-DCP〉2,3-DCP,脱氯反应均符合拟一级反应动力学方程。通过还原脱氯实验揭示了分子中氯原子的化学环境对还原脱氯过程具有明显影响。     

Relationship between Pd oxidation states on TiO2 and the photocatalytic oxidation behaviors of nitric oxide

This study has been undertaken to investigate the relationship between Pd oxidation states on TiO₂ photocatalysts and their photocatalytic oxidation behaviors of NO. Three types of Pd-modified TiO₂ with different Pd oxidation states were prepared by wet impregnation method, neutralization method and photodeposition method, respectively. And these Pd-modified photocatalysts were characterized by X-ray diffraction analysis, X-ray photoelectron spectrum analysis (XPS), UV–Vis diffuse reflectance spectra and temperature programmed desorption (TPD). It was found from XPS results that the dominant oxidation states of Pd on these Pd-modified TiO₂ catalysts were Pd²⁺, PdO, and Pd⁰, respectively. NO-TPD results showed that the NO adsorption capacity was improved greatly by the modification of Pd²⁺ ions. The activity tests showed that Pd-modified TiO₂ by a wet impregnation method increased photocatalytic activity compared to pure TiO₂ (Degussa P25). It was concluded that Pd²⁺ ions on as-prepared TiO₂ catalysts provided key contributions to the improvement of photocatalytic activity. However, Pd⁰ and PdO deposits on TiO₂ almost had no positive effect on NO oxidation. The mechanism of photocatalytic oxidation of NO in gas phase over Pd-modified TiO₂ was also proposed.     

Pd/Fe催化脱氯水中PCE的动力学研究

以GC-MS为分析方法,采用Pd／Fe双金属对水溶液中四氯乙烯（PCE）进行了催化还原脱氯处理,考察了PCE初始浓度、钯含量、Pd／Fe用量和溶液初始pH值等各因素对脱氯效果影响及还原动力学规律。结果表明,Pd／Fe双金属对PCE有较好的还原脱氯效率,反应遵循准一级反应动力学规律,以反应物PCE浓度为参照的反应速率常数K变化范围为0．019min^-1～0．16min^-1,对应的PCE半衰期从6min到36min,揭示反应有可能是在过量的Pd／Fe双金属表面进行。当PCE溶液初始浓度为1mmol／L,投加1．2g钯含量为0．03％的Pd／Fe双金属,在25℃下反应60min,PCE的脱氯率达到95％以上。增大钯含量和Pd／Fe用量可有效提高脱氯率,在初始pH值为弱酸性条件下有利于还原脱氯反应进行。