Formic acid as an alternative reducing agent for the catalytic nitrate reduction in aqueous media

Formic acid was used for the nitrate reduction as a reductant in the presence of Pd:Cu/γ-alumina catalysts. The surface characteristics of the bimetallic catalyst synthesized by wet impregnation were investigated by SEM, TEM-EDS. The metals were not distributed homogeneously on the surface of catalyst, although the total contents of both metals in particles agreed well with the theoretical values. Formic acid decomposition on the catalyst surface, its influence on solution pH and nitrate removal efficacy was investigated. The best removal of nitrate (50 ppm) was obtained under the condition of 0.75 g/L catalyst with Pd:Cu ratio (4:1) and two fold excess of formic acid. Formic acid decay patterns resembled those of nitrate removal, showing a linear relationship between kf (formic acid decay) and k (nitrate removal). Negligible amount of ammonia was detected, and no nitrite was detected, possibly due to buffering effect of bicarbonate that is in situ produced by the decomposition of formic acid, and due to the sustained release of H2 gas.     

OMS-2负载Pt催化剂的制备及其催化氧化性能研究

采用前掺杂法、沉积-沉淀法和浸渍法制备了氧化锰八面体分子筛(OMS-2)负载Pt催化剂(Pt/OMS-2),对所制催化剂进行了结构和织构表征。并研究了不同制备方法和沉积-沉淀法中不同制备(Pt负载量和溶液的pH值)对Pt/OMS-2催化氧化CO性能的影响。结果表明,沉积-沉淀法制备的Pt/OMS-2-DP催化剂活性最好(T100=100℃)。这与Pt/OMS-2-DP催化剂中Pt颗粒大小及OMS-2载体与Pt之间存在强相互作用有关。Pt负载量明显影响Pt/OMS-2-DP催化剂的催化活性,3Pt/OMS-2-DP催化剂(Pt=3.0 wt%)催化活性最高,这是由于适当Pt负载量,Pt颗粒较小,并与载体OMS-2的相互作用较强,能较好地活化OMS-2晶格氧。pH值对Pt/OMS-2-DP催化剂催化性能影响较大,这与OMS-2的等电点和Pt在不同溶液中存在不同Pt配位体形式有关。     

非均相类Fenton试剂的制备及其在焦化废水处理中的应用研究

利用浸渍法,将Fe3＋负载在经酸碱改性后的粉状活性炭上,当浸渍液浓度为2．5％,固化温度为270℃时,制成的催化剂催化活性较高。用自制的非均相类benton试剂降解焦化废水,通过正交试验和极差分析得出,影响因素的主次顺序为催化剂用量〉初始pH值〉反应时间〉H：0：投加量。结果表明,在100ml水样中。室温条件下,初始pH值为4．0,催化剂使用量为1．5g,H20：投加量为5ml（分两次投加）,反应时间为90min时,COD去除率可达99％。采用混凝＋化学沉淀＋非均相类Fenton试剂法处理焦化废水,各主要出水水质指标为：色度lO倍;COD浓度38．5mg／L;氨氮浓度8．4mg／L,达到国家一级排放标准。     

一种新型电化学法处理硝态氮废水的初步研究

通过对Pd-Me双金属催化还原NO 3--N和折点氯化法处理NH 4+-N的相关理论分析,提出了一种基于电化学法的新型NO 3--N废水处理工艺.即利用具有电子空轨的常见金属元素修饰Ti基获得催化阴极,在电场的作用下,将NO 3--N催化还原;通过调整催化元素的配比和电解条件,控制NO 3--N还原产物主要为NH 4+-N;利用阳极氧化Cl-生成高氧化性物质HOCl,将NH 4+-N氧化为无害产物N2-N.结果表明,金属元素Co和Cu修饰Ti基制得阴极可以有效地催化还原模拟废水中的NO 3--N;按前驱物溶液金属元素摩尔比1∶1制得Ti基Co-Cu复合涂层催化阴极,可以将NO 3--N高效催化还原为NH 4+-N;电解体系中引入Cl-后,通过阳极作用可将NO 3--N还原生产的NH 4+-N有效地氧化为N2-N.在100 mg/L NO 3--N模拟废水中添加1 000 mg/L Cl-,设置极板间距6 mm、电流400 mA,电解2.5 h后出水NO 3--N、NO 2--N、NH 4+-N和TN分别为2.9、0.5、1.7和6.0 mg/L.     

ZnOOH/O3催化臭氧化体系去除水中痕量对氯硝基苯

以实验室制备的羟基化锌（ZnOOH）为催化剂,考察了其催化臭氧化去除水中痕量对氯硝基苯（ppCNB能力.本实验条件下,蒸馏水中反应20　min时,催化臭氧化比单独臭氧化对pCNB的去除率提高了51 .3个百分点;催化过程遵循自由基反应机理,催化剂表面结合的羟基基团有利于催化反应;pCNB的去除效果随催化剂投量的增加而更佳,催化剂重复使用3次后,催化效果基本没有变化,水中的重碳酸盐以及缓冲溶液中的磷酸盐可以明显降低催化活性,中性条件下,催化作用最佳.     

催化剂Ru/ZrO2-CeO2催化湿式氧化苯酚

催化剂Ru/ZrO₂-CeO₂催化湿式氧化苯酚的过程表明,Ru/ZrO₂-CeO₂可以显著提高COD和苯酚去除效果,当反应温度为170℃,压力为3 MPa,反应120 min后,COD和苯酚的去除率分别达到了99％和100％.试验还考察了不同反应条件对苯酚溶液COD去除的影响,并获得了最优的反应条件：温度为170℃,压力为3 MPa,催化剂的投加量为5　g/Ｌ,搅拌速度为500 r/min.通过对中间产物的分析,本研究提出了催化湿式氧化苯酚的简单路径图,认为苯酚首先被氧化成小分子有机酸,接着小分子有机酸被氧化成二氧化碳和水.前一个过程是快速反应,后一个过程中的乙酸氧化是慢速过程,需要在高温下才能完成.乙酸的氧化主要是自由基攻击α碳上的C—H键,先生成甲酸,并最终生成二氧化碳和水.     

Kinetics of selective catalytic reduction of NO by NH3 on Fe-Mo/ZSM-5 catalyst

The catalyst of Fe-Mo/ZSM-5 has been found to be more active than Fe-ZSM-5 and Mo/ZSM-5 separately for selective catalytic reduction (SCR) of nitric oxide (NO) with NH3. The kinetics of the SCR reaction in the presence of O2 was studied in this work. The results show that the observed reaction orders were 0.74-0.99, 0.01-0.13, and 0 for NO, O2 and NH3, respectively, at 350-450℃. And the apparent activation energy of the SCR was 65 kJ/mol on the Fe-Mo/ZSM-5 catalyst. The SCR mechanism was also deduced. Adsorbed NO species can react directly with adsorbed ammonia species on the active sites to form N2 and H2O. Gaseous O2 might serve as a reoxidizing agent for the active sites that have undergone reduction in the SCR process. It is also important to note that a certain amount of NO was decomposed directly over the Fe-Mo/ZSM-5 catalyst in the absence of NH3.     

非均相催化臭氧处理高浓度制药废水的研究

非均相催化臭氧是一种对高浓度制药废水进行预处理的有效方法.本研究采用单一活性炭吸附、单一臭氧氧化和臭氧/活性炭联用3种体系对实际制药废水进行预处理,并对处理过程中的工艺参数进行优化.结果表明,相比单一活性炭吸附和单一臭氧降解体系,臭氧/活性炭联用体系能显著提高COD、TOC的去除率及BOD5/COD值,并显示出良好的协...     

Effect of manufacturing methods of AgCl/Al2O3 catalyst on selective catalytic reduction of NOx

The AgCl/Al2O3 catalyst has potential for use in the selective catalytic reduction (SCR) of NOx. A compound hydrocarbon, following oxygenation is used as a type of reducing agent. In this experiment, the AgCl/Al2O3 catalyst was produced by four different methods, and the differences among their reduction catalysis of NOx were compared. Ethanol was used as a type of reducing agent. X-ray diffraction analysis was performed to study the crystalline structure and scanning electron microscope and transmission electron microscope (TEM) were applied to determine the microindentation. The results indicated that, in the range of 350–400°C, there was no significant difference on the NOx reduction rate; however, there was dispersion at high and low temperature ranges. The size of the AgCl particles was about 20–100 nm.