废铸砂作为建筑材料资源化再利用研究进展

废铸砂是铸造工业在金属制品的生产过程中次生出来的一种细颗粒固体废弃物。研究其作为一种资源进行合理再利用是当前处置废铸砂、保护生态环境的良好对策。本文对废铸砂的环境特征、物理性质及废铸砂作为建筑材料在多种建筑制品及工程中的资源化再利用进行了综述研究，涉及的再利用领域包括混凝土、热拌沥青混合料、低强度填料、水泥、路基、路堤、阻水帷幕（屏障）和衬垫。调查发现，次生于黑色金属（铁和钢）铸造生产线的废铸砂是一种无害固体废弃物，正确处置和科学利用，对环境不会产生二次污染，在以上建筑制品及工程中的应用能满足相关技术、性能要求，可以替代相关的材料进行资源化再利用。     

Compressive strength and resistance to chloride ion penetration and carbonation of recycled aggregate concrete with varying amount of fly ash and fine recycled aggregate

Construction and demolition waste has been dramatically increased in the last decade, and social and environmental concerns on the recycling have consequently been increased. Recent technology has greatly improved the recycling process for waste concrete. This study investigates the fundamental characteristics of concrete using recycled concrete aggregate (RCA) for its application to structural concrete members. The specimens used 100% coarse RCA, various replacement levels of natural aggregate with fine RCA, and several levels of fly ash addition. Compressive strength of mortar and concrete which used RCA gradually decreased as the amount of the recycled materials increased. Regardless of curing conditions and fly ash addition, the 28 days strength of the recycled aggregate concrete was greater than the design strength, 40 MPa, with a complete replacement of coarse aggregate and a replacement level of natural fine aggregate by fine RCA up to 60%. The recycled aggregate concrete achieved sufficient resistance to the chloride ion penetration. The measured carbonation depth did not indicate a clear relationship to the fine RCA replacement ratio but the recycled aggregate concrete could also attain adequate carbonation resistance. Based on the results from the experimental investigations, it is believed that the recycled aggregate concrete can be successfully applied to structural concrete members.     

弧叶型旋转窑烧制污泥陶粒实验研究

实验选取污水污泥、粉煤灰和港口淤泥为原辅材料,采取正交实验设计物料质量配合比与烧制工艺参数,遴选出最佳物料配比和优化的烧制工艺;依照选定物料配比和工艺参数采用弧叶型旋转窑烧制污泥陶粒并测定产品的1 h吸水率,软化系数,堆积密度,表观密度,颗粒级配,粒型系数以及产品浸出毒性等技术指标,选取制得陶粒产品替代全部天然石料配制...     

Study on the mechanical and environmental properties of concrete containing cathode ray tube glass aggregate

Cathode ray tube (CRT) glass is considered a hazardous material due to its lead toxicity. In addition, current disposal practices are being phased out due to their adverse environmental impacts. In this project, CRT glass was used as a fine aggregate replacement in concrete. Life-cycle material characterization was conducted by evaluating the durability and strength of the CRT-Concrete. Leaching tests were also conducted to investigate whether the material meets drinking water limits for Pb. Test results show that the plastic state of the CRT-Concrete was affected by the angularity of the glass particles. Moreover, the compressive strength of CRT-Concrete met and exceeded that of the control specimen. However, CRT-Concrete was susceptible to expansive alkali-silica reactions when more than 10% CRT replacement was used. Environmental leaching results show that lead concentrations from CRT-Concrete are below the drinking water limits depending on the CRT volume replacement and if biopolymers are used.     

混凝土结构使役环境中氯离子浓度控制系统设计

本文结合湖北省自然科学基金项目"混凝土结构使役环境的智能模拟(2008CDB396)",在前期"211工程"项目"单轴约束可调式混凝土温度应力试验机"研究基础上,针对现有混凝土耐久性试验机在侵蚀溶液注入与氯离子浓度控制环境的空白,采用C51单片机为控制器,设计了一种混凝土结构使役环境中氯离子浓度控制系统,用于自动调节混凝土耐久性实验,模拟实验环境箱内的侵蚀溶液氯离子浓度,保证混凝土耐久性实验试件所处环境氯离子浓度稳定在设定的范围。系统采用溶液缓冲调节与循环注入方式,控制单元采用直读式离子浓度控制器,信号采集更方便。本系统不仅结构简洁,工作可靠性高,还能减少人力浪费,提高运行经济性。     

废旧混凝土用作水泥稳定基层的实验研究

随着城市建设的发展,城市道路改建时产生的大量的废弃混凝土块的有效利用成了一个亟待解决的问题。结合宜昌市东山大道改建项目,将废弃的混凝土面板加工形成再生集料用作水泥稳定碎石基层,达到节约资源和保护环境的目的。实验分析了再生集料的颗粒级配、压碎值、针片状颗粒含量、表观密度和吸水率等工程性质指标,同时对水泥稳定再生碎石的级配、最佳水泥掺量进行了设计,并对水泥稳定再生碎石的无侧限抗压强度指标进行了研究。研究表明,废旧混凝土经加工形成的再生集料具有良好的路用性能,其颗粒级配、压碎值以及主要指标均达到了路面基层材料的要求;掺3%、5%和7%水泥稳定再生集料7 d浸水抗压强度均达到路面基层的要求,水泥稳定再生集料用作路面基层是可行的;掺3%水泥稳定的再生集料可以用在公路的底基层,掺5%及7%水泥稳定的再生集料可以分别用作路面下基层和上基层。     

煤矿采空区充填用煤矸石泡沫混凝土发泡剂的研究

为防止地表沉陷,煤矿采空区需要充填,目前采用的充填方法为胶结充填、高水速凝充填等.泡沫混凝土具有质轻、流动性好的特点,可作煤矿采空区的充填材料.制备低水泥用量、含粗颗粒煤矸石的泡沫混凝土对发泡剂的泡沫稳定性要求较高,目前市售的发泡剂难以满足要求.在探讨发泡剂发泡、稳泡原理的基础上,研究了稳泡剂(D)的加入量对发泡液黏度、发泡倍率和泡沫稳定性的影响,以D与十二烷基硫酸钠(SDS)复配,研制出了高泡沫稳定性的发泡剂KD-1,该发泡剂的发泡倍率为21.3,开始泌水时间为7 min,90 min后沉降距为38 mm,并且考察了KD-1与混凝土早强剂的相容性.用此发泡剂制备出了最大粒径为5 mm、煤矸石掺量为63％(质量分数)、体积密度分别为800 kg/m3、900 kg/m3和1000 kg/m3的煤矸石泡沫混凝土,其90d单轴抗压强度分别为0.4 MPa、0.63 MPa和1.75 MPa.     

中远船务构筑特色安全文化的探索与实践

本文主要阐述了在企业核心价值理念孵化牵引下生发的安全文化理念,总结和提炼了具有企业特色的“严、细、真、实、慎”的安全文化,并从制度建设、行为规范以及体现执行力的十大主要措施上,进行了比较系统的论述,对进一步促进企业安全文化建设提出了4个方面的对策。     

钢筋混凝土结构抗火研究进展与趋势

火灾高温对钢筋混凝土结构材性有显著影响，极易造成结构损伤、破坏甚至倒塌。在大量阅读国内外文献的基础上，从建筑火灾发展过程研究、钢筋混凝土结构在火灾中的行为研究、钢筋混凝土结构抗火设计方法的研究、火灾后钢筋混凝土结构的损伤评估和加固方法的研究等4个方面对钢筋混凝土结构抗火研究进行了论述；总结了目前国内外钢筋混凝土结构抗火研究的主要进展及成果；指出了结构抗火研究尚存在的一些问题；最后，对结构抗火研究趋势进行了展望。     

混凝土结构使役环境中温度智能模拟LabVIEW软件设计

本项目结合湖北省科技计划自然科学基金项目“混凝土结构使役环境的智能模拟”，在WTST-150试验机硬件平台基础上，以LabVIEW8．5为开发平台，设计了一套混凝土结构使役环境中温度智能模拟LabVIEW软件，主要包括能初始化程序、温度采集与显示子程序、温度PID控制子程序、温度存储和查询子程序。经投入实验验证，该软件能实现实时曲线显示、温度控制、试验状态和保存试验数据、数据查询、手动加热、分配温度通道、PID控制参数整定、制冷、读入温度曲线等功能。具有实时在线循环检测、采集数据、响应快速等优点，并具有良好的故障诊断能力和可维护性以及超强的纠错能力。本软件完善了WTST-150试验机的温度控制系统，使其更加符合实际工况。