为研究吸附剂对正态磷酸盐、非正态磷酸盐的吸附特征,以及正态磷酸盐和非正态磷酸盐混合体系下的竞争吸附行为,制备出3种改性蒙脱石SWy-焙烧、SWy-Al、SWy-Fe,将其分别用于对不同形态的磷酸盐吸附实验中。结果表明,制备的3种改性蒙脱石对磷的吸附效果均有所提升。SWy-Fe的吸附效果最佳,对正态磷酸盐和非正态磷酸盐4 h吸附去除率分别提高了56.1%和55.3%,实验结果符合Ho拟二级吸附动力学方程。根据Langmuir吸附热力学方程,对正态磷酸盐和非正态磷酸盐的饱和吸附量分别为21.9 mg·g~(-1)和18.8 mg·g~(-1)。此外,在初始总磷浓度高于3.0 mg·L~(-1)的条件下,正态磷酸盐和非正态磷酸盐混合体系中的非正态磷酸盐吸附量显著高于正态磷酸盐,二者单位平衡吸附量之比为2.9∶1.0。改性蒙脱石对正态磷酸盐和非正态磷酸盐的吸附结果均表现为吸附外部液膜扩散、表面吸附、颗粒内扩散等多种过程的综合作用,可交换阳离子Ca~(2+)/Fe~(3+)/Al~(3+)的引入通过吸附络合作用提高了蒙脱石对磷酸盐的吸附能力。在初始总磷浓度高于3.0 mg·L~(-1)的条件下,正态磷酸盐和非正态磷酸盐混合体系存在吸附竞争现象,这为实际处理含磷废水吸附技术的发展和应用提供了理论依据。     

3-氨丙基三乙氧基硅烷改性蒙脱石的表征及其对Sr(Ⅱ)的吸附研究

3-氨丙基三乙氧基硅烷(APTES)作为偶联剂在粘土功能化方面具有特殊的研究意义.因此,本文采用X射线衍射(XRD)、扫描电镜(SEM)及红外光谱(FTIR)等方法对不同离子交换容量(1.0CEC、1.5CEC、2.0CEC、2.5CEC、3.0CEC、4.0CEC)的APTES改性蒙脱石(APTES-Mt)的结构及表面进行表征与分析,同时对Sr(Ⅱ)的吸附性能进行了研究.结果表明,改性蒙脱石对Sr(Ⅱ)的吸附平衡时间为24h,吸附量随溶液pH(1.0～10.0)的增大而增强,且改性蒙脱石的吸附量是原始蒙脱石吸附量的3倍.改性蒙脱石对Sr(Ⅱ)的吸附作用较强,吸附后的Sr(Ⅱ)不易从材料中解吸出来.XRD、SEM和FTIR等分析结果显示,APTES已经成功插入层间,改性蒙脱石对Sr(Ⅱ)的吸附机理主要为配位吸附.     

邻菲罗啉对蒙脱石吸附镍离子性能影响

利用镍离子能与邻菲罗啉反应生成螯合物的性质,研究了加与未加邻菲罗啉条件下,蒙脱石对金属镍离子的吸附行为,考察了镍离子浓度、吸附时间、温度和溶液pH值等因素对吸附性能的影响.结果表明:加入邻菲罗啉后,蒙脱石对镍的螯合离子的吸附量明显增大;吸附平衡时间约为120min;蒙脱石对[Ni(phen)n]2+的吸附性基本不受pH值的影响.动力学研究表明该吸附过程符合准二级反应动力学模型,吸附量随温度升高而增大.二级动力学参数证明加入邻菲罗啉可显著提高蒙脱石对Ni2+的吸附性.蒙脱石对简单Ni2+的吸附符合Langmuir的单层吸附等温式;而蒙脱石对镍的螯合离子的吸附则符合Freundlich等温式.蒙脱石对Ni2+和[Ni(phen)n]2+的吸附均为自发、吸热和更无序的;XRD及FTIR研究表明,蒙脱石对[Ni(phen)n]2+的吸附以层间的物理吸附为主.     

载铜蒙脱石对大肠杆菌K88吸附性能的研究

以蒙脱石(MMT)和硫酸铜为主要原料,制备了载铜蒙脱石(MMT-Cu),并对MMT-Cu吸附大肠杆菌K88的能力进行比较研究.结果表明:MMT和MMT-Cu对大肠杆菌K88均有较强的吸附作用,但载铜后蒙脱石吸附大肠杆菌的能力明显增强.细菌与吸附材料作用90min后可达到吸附平衡.介质pH值、离子强度和吸附温度对MMT和MMT-Cu吸附细菌的能力均有不同程度的影响.     

植物角质层的蜡质组分对甲萘酚的吸附作用

采用批量平衡法,比较研究了苹果角质结合蜡质、分离蜡质和重建蜡质对极性有机污染物甲萘酚的吸附作用,并探讨了不同负载量的重建蜡质的吸附性能,以期为准确预测有机污染物在不同状态蜡质组分上的吸附行为提供依据.结果表明,甲萘酚在苹果角质层、脱蜡角质层、分离蜡质(IW)、重建蜡质(BW)上的等温吸附线呈非线性,符合Freundlich方程.植物蜡质对甲萘酚的吸附作用与蜡质所处状态密切相关,吸附能力(Koc)大小顺序为:重建蜡质(321.2) > 分离蜡质(190.4) > 角质结合蜡质(128.4),表明植物角质层进入土壤后发生演化过程中,其中不易降解的蜡质的吸附能力逐渐增大.重建蜡质(BW)的吸附系数(Kd)与甲萘酚的浓度呈负相关,与蜡质的负载量呈正有关.在低浓度时,甲萘酚的有机碳标化吸附系数Koc值随有机碳含量(foc)增大先增大后减小,存在一些强的特殊作用;而高浓度时, Koc-基本为一常数,不随蜡质负载量而变化,主要吸附机理为分配作用.角质结合蜡质(CW)对角质层的总吸附作用的贡献较小,但随甲萘酚平衡浓度的增大而逐渐增大,并于高浓度时, CW的吸附能力与IW相当.     

Adsorptive property of Cu^2＋-loaded montmorillonite clays for Escherichia coli K_（88） in vitro

The Cu²⁺-loaded montmorillonite clays (MMT-Cu) may be a good material for the adsorbed and eliminated pathogenic bacteria from aqueous solution.     

Remediation of copper polluted red soils with clay materials

Attapulgite and montmorillonite were utilized to remediate heavy metal polluted red soils in Guixi City, Jiangxi Province, China. The e ects of clay minerals on availability, chemical distribution, and biotoxicity of Cu and Zn were evaluated. The results provided a reference for the rational application of clay materials to remediate heavy metal contaminated soils. From the sorption experiment, the maximum adsorbed Cu2+ by attapulgite and montmorillonite was 1501 and 3741 mg/kg, respectively. After polluted red soil was amended with attapulgite or montmorillonite and cultured at 30 and 60 days, soil pH increased significantly compared to the control. An 8% increase in the amount of montmorillonite in soil and 30 days incubation decreased acid exchangeable Cu by 24.7% compared to the control red soil. Acid exchangeable Cu decreased with increasing amounts of attapulgite and montmorillonite, with best remediation e ect reached at a dose of 8%. Results also showed that the Cu poisoning e ect on earthworms was reduced with the addition of attapulgite and montmorillonite. Montmorillonite showed the best e ect, with the addition of a 2% dose the mortality of earthworms decreased from 60% to zero compared to the control. Our results indicated that the bioavailability of Cu in soils was reduced more e ectively with the application of montmorillonite than attapulgite.     

一种改性柱撑蒙脱石的制备及其对废水中SO2-4吸附效率研究

蒙脱石具有较大的比表面积和阳离子交换容量,吸附性能较好.但其不能有效地吸附疏水性物质,应用中常将一些聚合羟基金属阳离子引入到蒙脱石层间制成柱撑蒙脱石以提高其孔道特性和热稳定性.为了进一步提高其吸附效率,在柱撑蒙脱石中加入了物料A,高温焙烧,对其进行了一系列的改性,并确定了改性条件,制备了一种新型的SO2-4高效吸附剂,并应用于煤矿矿井废水的治理,改性后的吸附剂较柱撑蒙脱石对水中SO2-4的吸附率提高了54.6%.最佳焙烧温度为800℃,焙烧时间为4 h,焙烧的最佳物料配比为1:4.     

左氧氟沙星在蒙脱石存在条件下对大肠杆菌的毒性效应

采用批实验研究了蒙脱石对左氧氟沙星的吸附机理及对左氧氟沙星抗菌作用的影响。结果表明,中性条件下存在培养基时,左氧氟沙星在蒙脱石上前2 h即达到吸附平衡,吸附等温线符合Langmuir吸附方程,吸附率达90%以上;蒙脱石吸附左氧氟沙星存在阳离子交换作用、氢键作用、疏水作用、阳离子键桥作用、静电吸附作用等物理化学过程;蒙脱石本身不具有抑菌、杀菌活性,且由于蒙脱石增大了微生物附着的比表面积,在特定情况下可以促进微生物的生长;扣除其对微生物生长的促进作用后,蒙脱石吸附左氧氟沙星降低了后者的毒性效应,其抑菌率降低约25%。上述结果为进一步研究抗生素在环境中的毒理效应提供了基础依据。     

有机蒙脱石负载纳米铁去除溶液中四溴双酚A的研究

研究了改性蒙脱石负载纳米铁材料(NZVI-CMT)在甲醇-水体系中对四溴双酚A(TBBPA)的去除作用,并确定了反应温度、TBBPA初始浓度以及材料投加量等因素对去除效果的影响.结果表明,在25℃条件下,0.02 g NZVI-CMT对初始浓度为10 mg·L-1TBBPA溶液的去除率可达97.5%,而且NZVI-CMT对TBBPA的去除率明显高于两种单一材料即纳米零价铁(NZVI)及有机蒙脱石(CMT)的去除率(18.3%、67.3%),同时也大于两者之和(85.6%).利用NZVI-CMT对TBBPA进行重复去除实验时,前3次的去除率均可达到90%以上.通过检测降解产物并分析材料对TBBPA去除过程的特性,发现NZVI-CMT对TBBPA的去除以吸附为主,并伴有少量还原脱溴反应发生,而且较高的反应温度对降解反应有利.