Preparation and performance of novel APP/NaY–Fe suppressant for coal dust explosion

Coal dust explosion occurs easily in the coal chemical industry. To ensure safety in industrial production, NaY zeolite was used as carrier modified with Fe ions and combined with ammonium polyphosphate (APP) to prepare a novel composite suppressant for coal dust explosion. The explosion suppression performance of novel APP/NaY–Fe suppressant was investigated by flame propagation inhibition experiments. The results show that Fe ion modification can effectively improve the explosion suppression performance. By increasing content, the explosion suppression performance of the explosion suppressant increases. The maximum explosion pressure P_max of coal dust drops to 0.13 MPa when 50 wt% explosion suppressants were added, and the coal dust explosion cannot continue to expand. Complete suppression of explosion could be achieved by adding 66 wt% explosion suppressants. Combined with XRD, SEM and TG results, the explosion suppression mechanism was proposed. The novel explosion suppressant has high thermal stability, good dispersity and its explosion suppression components distribute uniformly. It shows good explosion suppression performance by the synergistic effect among explosion-suppression components.     

石墨烯材料去除重金属及放射性核素的研究

石墨烯及其改性材料具有比表面积大、吸附能力强、抗辐射性能好、耐高温、耐酸碱等优点,近年来在去除重金属和放射性核素领域得到了广泛关注.本文简要介绍了石墨烯的合成及改性方法,综述了石墨烯材料去除水中重金属离子和放射性核素的研究进展,包括吸附容量、影响因素、吸附动力学、吸附热力学模型和吸附机理,分析了该研究领域目前存在的问题,探讨了今后的研究方向.     

改性活性炭纤维吸附炸药废水中TNT实验研究

本文研究了改性活性炭纤维对炸药废水中TNT的吸附行为。研究表明:1 mol/L HNO3改性的活性炭纤维吸附效果最好,其对炸药废水中TNT的最佳吸附条件为:吸附剂用量为0.6 g/25 m L,吸附平衡时间为60 min,升温有利于吸附进行。Langmuir和Freundlich吸附等温线均能较好地描述活性炭纤维对TNT的吸附,吸附动力学分析表明,吸附过程遵循准二级动力学规律。     

改性糠醛渣吸附脱硫废水中钙离子

石灰石-石膏法烟气脱硫技术中石灰石利用率低导致钙流失严重,为实现脱硫废水中Ca2+的资源化利用,进行糠醛渣改性和Ca2+的吸附特性研究。实验结果表明,利用H3PO4改性后的糠醛渣对脱硫废水中Ca2+具有较高的吸附率;在振荡的前30 min吸附率上升极快,至90 min时基本达到平衡吸附量;对Ca2+浓度对吸附率影响研究结果表明,平衡吸附量与平衡浓度关系符合Langmuir等温吸附方程;在初始Ca2+浓度为300 mg/L的溶液中加入3 g吸附剂,温度30℃条件下振荡90 min,平衡吸附量为8.41 mg/g。     

改性粉煤灰合成沸石对甲基橙的吸附动力学

以粉煤灰(FA)为原料,采用水热晶化一步法制备了Na P1型沸石(ZFA),对合成产物的结构进行了表征,并采用阳离子表面活性剂十六烷基三甲基溴化铵(CTAB)对其进行改性。通过静态吸附实验,研究了改性后Na P1型沸石(MZFA)对水溶液中甲基橙的吸附特性,从动力学角度探讨了吸附机理。结果表明,在所研究的浓度条件下,改性Na P1型沸石对甲基橙的吸附符合Langmuir等温吸附方程,在25℃时,静态饱和吸附量(Qm)为64.76 mg/g。动力学分析表明,改性Na P1型沸石对溶液中甲基橙的吸附符合准二级动力学模型。     

基于改性凹凸棒土的强化混凝处理高藻低浊原水工艺

针对水厂低浊高藻水的处理难题,研究了改性凹凸棒土(改性凹土)联合聚合氯化铝(PAC)强化混凝的除藻除浊效果。设计实验原水条件为叶绿素a(chl-a)浓度为98.58~110.35μg/L,浊度(5.6±0.5)NTU。考察了PAC和改性凹土的复配投加量、混凝沉淀时间、pH、投加顺序、搅拌速率等工艺参数对Chl-a和浊度耦合去除效果的影响。结果表明,"PAC+改性凹土"对Chl-a和浊度的去除效果明显优于单投PAC的效果。当PAC投药量12 mg/L,改性凹土投药量10 mg/L,沉淀时间20 min时,对Chl-a和浊度的去除率可分别达到92.5%和89.2%,可至少减少40%的PAC投量,且形成的矾花密实,沉降速度快,去除效率高。最适pH范围为7~8。投加顺序应为先投加改性凹土,混合搅拌转数宜慢速,可控制为50 r/min。     

磷酸活化-微波热解改性污泥对镉的吸附性能

以城市污水处理厂剩余污泥为原料,利用磷酸活化-微波热解制取改性污泥。以此污泥作为吸附剂,对含Cd2+废水进行了吸附实验研究。考察了溶液反应时间、Cd2+浓度、pH值和吸附剂用量对镉吸附去除效果的影响;利用等温吸附实验作出吸附等温线,并考察了改性污泥吸附剂吸附Cd2+的动力学方程。实验结果表明,改性污泥对Cd2+有良好的吸附性能,吸附最佳pH值为6.0,吸附较好地符合一级动力学吸附模型和Langmuir-Freundlich等温吸附方程,吸附为物理吸附,吸附反应发生12 h后达到吸附平衡。     

改性氧化铝微波诱导催化氧化处理高浓度苯酚废水的研究

采用微波诱导催化氧化技术，以改性氧化铝为催化剂，对高浓度模拟苯酚废水进行氧化处理。考察了微波功率、催化剂投加量、H202投加量、废水pH值和微波反应时间等因素对苯酚去除效果的影响。实验结果表明，处理30mL质量浓度为1 100mg/L的苯酚模拟废水，在微波功率500W，催化剂加入量1 g(液固比30∶1)，30％双氧水...     

改性生物炭负载纳米零价铁去除水体中头孢噻肟

抗生素对环境的危害已经引起了人们的广泛重视.本实验以改性生物炭(MB)为载体制备了负载纳米零价铁的功能生物炭(Fe/MB).以头孢噻肟(CFX)为目标抗生素,研究了该材料对头孢噻肟的降解特性及影响因素,并探讨了去除机理.实验结果表明,50 min内头孢噻肟的去除率为92%(Fe/MB用量为0.4 g·L~(-1),溶液p H=5.0,头孢噻肟浓度为20 mg·L~(-1),振荡速率为200 r·min~(-1),柠檬酸浓度为1.47 mmol·L~(-1)).头孢噻肟的去除过程存在改性生物炭的吸附和纳米零价铁还原降解的协同作用,数据符合伪二级反应动力学方程(R20.99).采用紫外可见光谱结合质谱分析了降解产物的结构并提出头孢噻肟的降解途径.     

硅藻土负载型非均相芬顿催化剂制备及其降解苯酚的实验研究

以硅藻土为载体,采用直接蒸发法负载铁的氧化物,制备了一种新型负载型非均相芬顿催化剂,通过SEM、EDS和XRD等对催化剂进行了表征,并以苯酚去除率考察了催化剂性能。结果表明:铁氧化物可成功负载于硅藻土上;催化剂制备时最优铁离子浓度和固液质量比分别为0.5 mol/L和1∶10;催化剂重复使用性高,耐酸碱性良好,对苯酚的去除率可达99%以上。催化剂利用了硅藻土优异的物化性质,对难降解有机废水具有良好的应用前景。