Catalytic degradation of toxic organic dye using an aluminum-doped Cu0.4Zn0.6-xAlxFe2O4 (x = 0.0, 0.2, 0.4, 0.6) spinel ferrite in a photo-Fenton system

Catalytic activity of spinel ferrite in breaking down toxic dye materials are promising due to their uniqueness. In this study, aluminum-doped copper zinc ferrite, Cu_0.4Zn_0.6-xAl_xFe₂O₄ (x = 0.0, 0.2, 0.4, 0.6), a catalyst for toxic dye degradation is synthesized through chemical co-precipitation route. The formation of the spinel ferrite catalyst is initially confirmed by Fourier transform infrared spectra, which shows the frequency of metal-oxygen bond vibration at 539 and 427 cm⁻¹ attributed to the tetrahedral and octahedral sites respectively. Higher intensity sharp peak of X-ray diffraction for (311) plane is the evidence for the phase purity and the formation of spinel ferrite. The crystallite size is found to decrease with the increase of Al³⁺ ion. The surface structure of the obtained particles is investigated using a scanning electron microscope. Analyses of the material's magnetic characteristics using a vibrating sample magnetometer (VSM) revealed that it is, in fact, a soft magnet, as evidenced by the loop of its hysteresis, which is narrow. The catalytic degradation of methylene blue dye under the mechanism of the photo-Fenton process is studied with the obtained spinel ferrites and the result is found to be as high as 96.5%. The process follows pseudo-second order kinetics and the Langmuir isotherm.     

含氮生物降解促进剂对土壤吸附正十六烷的影响

选用正十六烷模拟润滑油,通过振荡平衡实验,考察了两种含氮脂肪酸型生物降解促进剂（甲基二乙醇胺油酸酯（MDEAO）和油酸二乙醇酰胺（ODEA））对水土体系中正十六烷吸附行为的影响。实验结果表明：正十六烷在水土体系中的有机质标化分配系数与土壤种类无关,与生物降解促进剂种类有关;土壤对正十六烷的吸附过程更符合Freundlich等温吸附模型;MDEAO的临界胶束浓度为2.0 mg/L,对土壤吸附正十六烷有一定的促进作用,ODEA的临界胶束浓度为0.7 mg/L,形成的胶束对正十六烷的增溶效果明显,促进了正十六烷在土壤中的解吸。     

聚苯乙烯/CdS/TiO_2双壳层核壳纳米颗粒可见光催化降解甲基橙

采用溶胶-凝胶法,在聚苯乙烯(PS)/CdS核壳纳米颗粒表面包覆致密TiO_2层,制备出具有双壳层结构的PS/CdS/TiO_2纳米复合颗粒,考察了制备条件对材料结构的影响,并利用甲基橙溶液对其光催化性能进行了评价。SEM、TEM、XRD和FTIR分析结果表明,制得的微球单分散性良好,壳层包覆完整,厚度均匀。PS/CdS/TiO_2制备的适宜反应时间为12~18 h,适宜反应pH为7~9。PS/CdS/TiO_2较PS/CdS具有更为优异的可见光催化性能。     

Effects of EGR on performance and emissions of a diesel engine fuelled with balanites aegyptiaca/diesel blends

In this study, balanites Aegyptiaca (L.) Del biodiesel was blended in proportions of 10% and 20% on the volume basis with diesel fuel and tested in a single cylinder, VCR diesel engine under measured load conditions with varied EGR rates (0, 10 and 20%). The results showed that B10 and B20 blends shown a significant reduction rate in terms of NO_x emissions that were familiar with biodiesel blends. At peak load conditions, BTE increased slightly for test fuel blends compared with pure diesel fuel while the BSFC rate and EGT suffered from increasing and decreasing nature with respect to blending percentage. From the emissions point of view, with the increase in blends percentage, a significant reduction rate is observed in terms of CO and HC concentrations (up to 12.34 and 17.5%, respectively) while NOx emissions decreased at peak load conditions (up to 24.34%). HC and CO emissions decreased with increase in blends percentage. However, lower levels of NO_x and EGT (up to 21.37 and 8.47%, respectively) and the average increase in terms of BTE and BSFC (up to 2.83 and 2.9%, respectively) can be realised with B20 test fuel blend under 20% EGR rate.     

不同培养条件下锰过氧化物酶(MnP)的合成及其对甲基橙的降解

高效、大规模、低成本合成木质素降解酶是直接采用其降解难降解有机污染物所必须解决的问题.对锰过氧化物酶(MnP)降解甲基橙和在非灭菌的反应器中连续合成MnP的可行性进行考察.结果表明,在采用2 mmol H2O2和1.5 mmol MnSO4的降解体系中,获最大脱色效果,且100、200和300 U/L的MnP可在8h内将甲基橙分别脱色18％、23％和35％;在非灭菌的反应器水平上实现了固定化培养的P.chrysosporium连续23 d合成MnP,但MnP酶活仅为2～ 23 U/L,难以酶解甲基橙;然而,在摇瓶培养条件下固定化的P.chrysosporium合成的MnP却能达1 152 U/L.因此,直接采用MnP对污染物进行降解以及在非灭菌的反应器中持续合成MnP是可行的,但就在非灭菌条件下如何提高MnP的合成量还有待开展深入的研究.     

MoS_2/Bi_2S_3异质结光催化剂的制备及其光催化性能

以五水硝酸铋为铋源、钼酸钠为钼源、硫脲为硫源,采用简单的一步水热法合成了MoS_2/Bi_2S_3异质结光催化剂,采用XRD,SEM,TEM,BET,UV-Vis DRS技术对其进行了表征。表征结果显示,MoS_2纳米片在Bi_2S_3微棒表面生长,增加了比表面积和活性位点,并形成异质结构,促进了光生载流子的迁移,抑制了电子-空穴对的再复合。实验结果表明:钼酸钠与五水硝酸铋的质量比为1∶2时制备的复合光催化剂性能最好,反应180min时对亚甲基蓝的去除率可达96.4%,明显高于MoS_2和Bi_2S_3,且具有较高的稳定性;该催化剂对罗丹明B、甲基橙和4-硝基苯酚的去除率分别为97.1%、93.1%和90.5%,表明其对污染物具有普适性。     

石墨相氮化碳协同UV-H_2O_2光催化降解亚甲基蓝

以三聚氰胺为前驱体,经热解—回流法制备了石墨相氮化碳(g-C3N4),采用XRD、FTIR、SEM、EDS、PL等技术对g-C_3N_4进行了表征。研究了g-C_3N_4在UV-H_2O_2体系中对废水中亚甲基蓝(MB)的光降解效果。实验结果表明,UV+g-C_3N_4催化剂+H_2O_2体系能协同降解MB,在初始MB质量浓度为20 mg/L、初始废水p H为5、废水体积为250 mL、g-C_3N_4加入量为0.10 g、H_2O_2浓度为0.4 mmol/L、反应温度为25℃的优化工艺条件下,紫外光照射70 min时MB脱色率达98.32%。g-C_3N_4催化剂具有较好的重复使用性能,使用5次后MB脱色率仍保持在95.10%。     

层状氧化物NaCo_2O_4热催化H_2O_2降解亚甲基蓝

采用固相烧结法制备了NaCo_2O_4催化剂,构建了NaCo_2O_4-H_2O_2热催化体系降解亚甲基蓝(MB)。XRD和SEM表征结果显示,合成的NaCo_2O_4催化剂具有良好的稳定性。NaCo_2O_4对H_2O_2具有良好的热催化性能,反应温度越高,反应速率常数k越大,该催化反应符合一级动力学方程。NaCo_2O_4-H_2O_2体系对MB具有较好的降解效果,在反应温度为50℃、NaCo_2O_4加入量为50 mg、MB溶液加入量为100 mL、MB初始质量浓度为30 mg/L、H_2O_2加入量为1.00 mL的最优条件下,反应340 min时,MB降解率达87.00%;催化剂重复使用三次,MB降解率仍可达85%以上;经捕获剂效果对比实验发现,催化反应体系中存在h~+、·OH等催化活性物种。     

废水中甲基橙的电化学降解

以FTO导电玻璃作为阳极、石墨电极作为阴极电解模拟甲基橙废水,优化了工艺条件,并对甲基橙的降解机理进行了初步探究。实验结果表明,在NaCl投加量5 g/L、电压8 V、废水pH 6、初始甲基橙质量浓度6.0 mg/L的优化条件下电解30 min,废水的脱色率达91.3%,COD降低了62%。机理研究结果表明,电解产生的羟基自由基与甲基橙发生氧化还原反应,破坏了甲基橙的显色基团,使其内部某些化学键发生断裂,从而达到脱色的目的。     

PW_(12)/g-C_3N_4光催化降解甲基橙

采用浸渍法制备了磷钨酸(PW12)/g-C3N4复合光催化剂,并将其用于溶液中甲基橙的光催化降解,运用IR技术对使用前后的光催化剂进行了表征。表征结果显示,PW12和g-C3N4的结构未在浸渍负载中发生改变,且PW12和g-C3N4结合牢固。实验结果表明:最佳的PW12负载量(光催化剂中PW12的质量分数)为50%;光催化降解甲基橙的优化反应条件为初始甲基橙质量浓度5 mg/L、光催化剂加入量0.6 g/L、初始溶液p H=7;在优化条件下,分别采用紫外光、模拟太阳光、可见光照射120 min后,甲基橙的降解率分别为96.59%,82.23%,42.78%;该光催化剂固载良好,使用中不易发生溶脱,稳定性好,可重复使用。