La1-xCexFe0.7Co0.3O3-δ网状多层纳米纤维对碳烟催化燃烧性能研究

采用静电纺丝法制备了一系列钙钛矿催化剂La_(1-x)Ce_xFe_(0.7)Co_(0.3)O_(3-δ)(x=0、0.1、0.2、0.3和0.4),并采用XRD、SEM、FT-IR、H2-TPR和O_2-TPD等技术分析了Ce掺杂量对催化剂结构、微观形貌及理化特性的影响.同时,采用程序升温氧化(TPO)技术评价了催化剂对碳烟的催化燃烧活性,探讨了催化剂对碳烟的催化燃烧机理.结果表明:在La_(1-x)Ce_xFe_(0.7)Co_(0.3)O_(3-δ)中掺杂适宜的Ce有助于提高催化剂活性,改善催化剂比表面积和孔容积.在催化剂与碳烟松散接触条件下,当Ce掺杂量(质量百分比)为0.3时,所制备的La_(0.7)Ce_(0.3)Fe_(0.7)Co_(0.3)O_(3-δ)对碳烟的起燃温度(T_(ig))、最大燃烧温度(T_m)和燃尽温度(T_f)分别为329.5、409.8和421.1℃,呈现良好的催化氧化活性.碳烟最大转化效率为98.7%,平均活化能为123 kJ·mol~(-1),CO_2选择率为98.2%,实现了对柴油机碳烟排放污染物有效"过滤+催化燃烧"的双重目标.     

静电纺壳聚糖/聚乙烯醇纳米纤维膜对Cu~(2+)、Ni~(2+)及Cd~(2+)的吸附特性

采用SEM、FTIR、XRD、BET等技术对静电纺丝制得的吸附材料壳聚糖/聚乙烯醇(CS/PVA)纳米纤维膜进行表征,并通过对模拟重金属离子废水的吸附实验,系统考察了溶液pH、重金属离子(Cu2+、Ni2+及Cd2+)初始浓度和反应温度对吸附的影响.结果表明,在外加电压25kV、接触距离15.0 cm、纺丝速度0.15 m L·h-1的条件下,可制得CS/PVA质量比为20/80的连续无缺陷的平均直径76.31 nm、比表面积219.4m2·g-1的纤维膜.CS/PVA纳米纤维膜对重金属离子的吸附在2 h内达到平衡,其吸附容量随着温度的升高而升高,随着初始浓度的增大而增大,随着pH值的升高而提高,在pH=5.5时达到最大.在25℃和pH=5.5的条件下,用CS/PVA纳米纤维膜吸附浓度100 mg·L-1的Cu2+、Ni2+和Cd2+溶液,吸附容量分别为98.65、116.89和124.23 mg·g-1,且对重金属吸附无选择性.吸附过程符合Langmuir和Freundlich等温吸附模型,吸附动力学同时匹配准一级动力学模型和准二级动力学模型.热力学参数(ΔG、ΔH和ΔS)计算结果表明,CS/PVA纳米纤维膜对重金属离子的吸附是自发的吸热反应.     

静电纺丝制备TiO2／PAN纳米纤维毡及其性能研究

采用超声波水解技术水解TiCl4制备纳米TiO2粒子,与聚丙烯腈（PAN）的N,N-二甲基甲酰胺（DMF）溶液共混后,通过静电纺丝制得具有光催化活性的TiO2／PAN纳米纤维毡,并用其对模拟废水中苯酚进行光催化降解实验。X射线衍射（XRD）表征结果显示制备的TiO2为锐钛矿。用场发射扫描电镜（FE—sEM）观察纤维毡的形态,显示纤维的直径随纺丝液浓度增大而增大。对苯酚进行光催化降解结果表明：纺丝液浓度质量分数为5％TiO2／PAN纤维毡对苯酚的降解率最高,对100mg／L,50mg／L和20mg／L苯酚的降解率分别为51．1％,87．5％和99．6％。纤维毡循环使用5次后对于20mg／L苯酚的降解率为87．4％。     

铁改性掺氮碳纤维活化过一硫酸盐降解双酚A

通过静电纺丝制备了Fe和N掺杂改性的碳纳米纤维（Fe-N-CNF）,研究了该催化剂活化过一硫酸盐（PMS）降解双酚A（BPA）的性能.以聚丙烯腈为前驱体通过添加FeCl₃、尿素、NH₄Cl、均苯四甲酸二酐等配制溶胶进行静电纺丝,预氧化并高温碳化后获得Fe-N-CNF,研究了Fe-N-CNF投加量、PMS投加量、溶液初始pH对BPA降解效果的影响.结果表明,当Fe-N-CNF投加量为1 g·L^-1,PMS投加量为2 mmol·L^-1,初始pH为5时,30 min内对初始浓度为20 mg·L^-1 BPA的降解率可达100%.自由基淬灭实验和电子自旋共振波谱（ESR）分析证明,该体系中起主要作用的活性氧物种是O₂^·-和¹O₂.同时研究了Fe-N-CNF/PMS体系对多种有机污染物的降解效果.     

Preparation and application of amino functionalized mesoporous nanofiber membrane via electrospinning for adsorption of Cr3+ from aqueous solution

Novel amino (-NH₂) functionalized mesoporous polyvinyl pyrrolidone (PVP)/SiO₂ composite nanofiber membranes were fabricated by a one-step electrospinning method using poly (vinyl alcohol) and tetraethyl orthosilicate (TEOS) mixed with cationic surfactant, cetyltrimethyl ammonium bromide (CTAB) as the structure directing agent. Ureidopropyltriethoxysilane was used for functionalization of the internal pore surfaces. The membranes were characterized by scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM) images, X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FT-IR), element analyzer and N2 adsorption-desorption isotherms. The nanofiber diameters, average pore diameters and surface areas were 100-700 nm, 2.86 nm and 873.62 m²/g, respectively. These mesoporous membranes functionalized with -NH₂ groups exhibited very high adsorptions properties based on the adsorption of Cr³⁺+ from an aqueous solution. Equilibrium adsorption was achieved after approximately 20 min and more than 97% of chromium ions in the solution were removed. The membrane could be regenerated through acidification.     

Preparation, characterization and performance of an electrospun carbon nanofiber mat applied in hexavalent chromium removal from aqueous solution

Hexavalent chromium, Cr(VI), a highly toxic oxyanion known as a carcinogen and mutagen,is an issue of concern due to its adverse impact on human health. Therefore, development of effective technologies and/or materials for Cr(VI) removal from water has been of great interest for researchers. In this study, an electrospun carbon nanofiber(CNF) mat was prepared via electrospinning polyacrylonitrile(PAN), followed by thermal pre-oxidation and carbonization. Scanning electron microscopy(SEM) observation showed that the fiber diameter of the CNF with carbonization temperature of 950°C(CNF_(950)) was about 266 nm.Potentiometric titration analysis demonstrated that the point of zero charge p H(pHpzc) of CNF_(950) was around 7.93. CNF_(950) demonstrated high adsorption capacity and fast adsorption kinetics for Cr(VI) at pH 3. Langmuir isotherm calculations showed that the maximum adsorption capacity of Cr(VI) on CNF_(950) was 118.8 mg/g at pH 2. The adsorption isotherm of Cr(VI) on CNF_(950) was well described by the Redlich–Peterson model, revealing that Cr(VI)adsorption was the result of a combination of monolayer and multilayer adsorption,depending on the initial Cr(VI) concentration. Solution pH greatly affected Cr(VI) adsorption onto CNF_(950) due to the electrostatic interaction, and the adsorption capacity was relatively high when pH was below 3. X-ray photoelectron spectroscopy(XPS) analysis revealed that the removal of Cr(VI) might be the result of a combination of redox reaction and electrostatic adsorption. The adsorption-saturated CNF_(950) could be regenerated by NaOH solution. This study extends the potential applicability of electrospun CNF mats for Cr(VI)-contaminated water purification.     

尼龙6纳米纤维膜富集/固相表面荧光法快速检测水体痕量多环芳烃研究

以静电纺丝法自制的尼龙6纳米纤维膜为吸附材料,建立了快速测定水体痕量多环芳烃(PAHs)的固相表面荧光光谱法(SSF)。将直径为5 cm的尼龙6纳米纤维膜作为滤膜用于抽滤菲、芘、荧蒽的水溶液,将膜自然晾干后置于可变角粉末样品池上,利用荧光分光光度计测量膜表面PAHs的三维固相表面荧光光谱特征,确定最佳激发发射波长,考察荧光强度随溶液初始质量浓度的线性变化关系。结果表明,菲、芘、荧蒽的最大激发发射荧光中心分别位于Ex/Em=255nm/368 nm、Ex/Em=340 nm/376 nm和Ex/Em=290 nm/437 nm处。当抽滤水样体积为500 m L时,菲、芘、荧蒽荧光强度与初始质量浓度之间的标准曲线分别为y=9432.4x+261.1,线性范围为5~500ng/m L;y=753480x+805.51,线性范围为0.2~10 ng/m L;y=9946.06x+603.48,线性范围为10~400 ng/m L,检出限分别为0.973 ng/m L、0.016 2 ng/m L和0.089 6 ng/m L。当质量浓度分别为100 ng/m L、10ng/m L和50 ng/m L时,7次测量的相对标准偏差(RSD)分别为7.1%、2.6%和5.1%,平均值相对误差分别为1%、2%和-0.2%。自来水低中高3个质量浓度的平均加标回收率分别为87.2%~98.2%、101%~120%、85.8%~92.3%。本方法具有简便、经济、灵敏度高等优点,适合于水体痕量PAHs的快速测定。     

聚苯乙烯电纺纳米纤维对水中苯系物的吸附性能

采用高效液相色谱法研究了静电纺聚苯乙烯纳米纤维对水中苯系物有机污染物的吸附性能,探究了纳米纤维对苯、对氯苯、硝基苯的吸附容量随浓度和时间的变化规律.通过实验得到静电纺纳米纤维对苯、对氯苯、硝基苯的平衡吸附容量平均值分别为9.82,5.57和4.4mg.g-1,静态吸附4h后基本达到平衡.实验结果表明,静电纺聚苯乙烯纳米纤维能够较好地吸附苯类物质,并能多次重复利用,对水中较低浓度的苯类物质吸附是一种比较合适的吸附材料.     

静电纺丝过氯乙烯纳米纤维膜对PM10去除效果的研究

静电纺丝纳米纤维膜是一种新型空气净化过滤材料.为了解该材料对PM10的去除效果,以滑石粉粉尘和香烟烟雾为代表研究了静电纺丝过氯乙烯纳米纤维膜对PM10的去除率.结果表明:供试的2类静电纺丝过氯乙烯纳米纤维膜对粉尘的平均去除率分别为93.2%和97.8%,明显高于同类非静电纺丝纤维过滤材料的去除效果;对香烟烟雾有一定的去除效果,4 h的去除率为82.4%.静电纺丝过氯乙烯纳米纤维膜对PM10的过滤作用主要发生在表层,过滤机理以拦截和惯性碰撞为主.