钯离子液相催化氧化低浓度磷化氢

采用Pd^2＋液相催化氧化低浓度PH3，考察了Pd^2＋浓度、O2体积分数、PH3质量浓度、混合气流量、反应温度等因素对Pd^2＋吸收液去除低浓度PH3效果的影响。实验结果表明，采用10mL Pd^2＋浓度为0．112mol／L的水溶液作为吸收液净化含低浓度PH3的混合气，在反应温度22℃、O2体积分数5％、PH3质量浓度850mg／m^3、混合气流量190mL／min的条件下，印min之内PH3去除率保持在90％以上。Pd^2＋浓度越高、O2体积分数越大、反应温度越高，PH3去除率越高；混合气流量越大，PH3去除率越低；反应温度越低、O2体积分数越大，PH3去除率的下降速率越小。     

氮掺杂二氧化钛负载钒磷氧催化氧化NO的实验研究

以VPO为活性组分,N掺杂TiO 2为载体,采用浸渍法制备了VPO/TiN催化剂,基于单因素实验研究了其对NO的选择性催化氧化(SCO)性能以及抗硫抗水性能。研究表明:当P/V为1/5、N/Ti为1、活性组分负载量为10%、焙烧温度为350℃时,催化剂的SCO活性最好,NO氧化率达到61%;光致发光光谱(PL)表征显示N掺杂TiO 2在催化剂表面形成的氧空位可增强催化剂对O 2的吸附;VPO/TiN催化剂抗硫抗水性能较强,反应后的催化剂表面未发现硫酸根的特征峰,水蒸气主要通过与NO竞争吸附占据活性位点来抑制催化剂的SCO活性。     

钴掺杂二氧化钛的制备及光催化性能的研究

钴掺杂制备超细TiO2粒子,并进行了表征。CoO与TiO2形成固溶体抑制了TiO2晶粒的长大并促进相变。钴掺杂有利于提高TiO2光催化剂的寿命。     

Catalytic dechlorination of chlorobenzene in water by Pd/Fe bimetallic system

IntroductionChlorinatedorganiccompoundshavebeenusedonalargescaleinthechemical,petrochemical,andelectronicindustries.Inrecentyears ,worldwideattentionhasbeengiventotheenvironmentalandhealthimpactofthemasaclassofcontaminants .Severalareknowntocauseozonedepletion ,whileothersproduceadverseeffectsonthehumancentralnervoussystemandhavebeenlinkedtodiseasessuchascancer.Almostallofthechlorinatedaromaticcompoundsaretoxicandthermallystable .Oncereleasedintoenvironment,theywillaccumulateinthesurroundings…     

Promotional effect of cobalt doping on catalytic performance of cryptomelane-type manganese oxide in toluene oxidation

The cryptomelane-type manganese oxide (OMS-2)-supported Co (xCo/OMS-2; x = 5, 10, and 15 wt.%) catalysts were prepared via a pre-incorporation route. The as-prepared materials were used as catalysts for catalytic oxidation of toluene (2000 ppmV). Physical and chemical properties of the catalysts were measured using the X-ray diffraction (XRD), Fourier transform infrared spectroscopic (FT-IR), scanning electron microscopic (SEM), X-ray photoelectron spectroscopy (XPS), and hydrogen temperature-programmed reduction (H₂-TPR) techniques. Among all of the catalysts, 10Co/OMS-2 performed the best, with the T_90%, specific reaction rate at 245°C, and turnover frequency at 245°C (TOF_Co) being 245°C, 1.23 × 10⁻³ mol_toluene/(g_cat·sec), and 11.58 × 10⁻³ sec⁻¹ for toluene oxidation at a space velocity of 60,000 mL/(g·hr), respectively. The excellent catalytic performance of 10Co/OMS-2 were due to more oxygen vacancies, enhanced redox ability and oxygen mobility, and strong synergistic effect between Co species and OMS-2 support. Moreover, in the presence of poisoning gases CO₂, SO₂ or NH₃, the activity of 10Co/OMS-2 decreased for the carbonate, sulfate and ammonia species covered the active sites and oxygen vacancies, respectively. After the activation treatment, the catalytic activity was partly recovered. The good low-temperature reducibility of 10Co/OMS-2 could also facilitate the redox process accompanied by the consecutive electron transfer between the adsorbed O₂ and the cobalt or manganese ions. In the oxidation process of toluene, the benzoic and aldehydic intermediates were first generated, which were further oxidized to the benzoate intermediate that were eventually converted into H₂O and CO₂.     

Determination of Au(III) and Pd(II) ions by flame atomic absorption spectrometry in some environmental samples after solid phase extraction

A simple and sensitive solid phase extraction method was developed for simultaneous separation and preconcentration of gold and palladium ions with N-(4-methylphenyl)-2-{[(4-phenyl-5-pyridine-4-yl-4H-1,2,4-triazol-3-yl)thio]acetyl}hydrazine carbo thioamide complex on Amberlite XAD-1180 resin before their determination by flame atomic absorption spectrometry. Some analytical parameters such as HNO₃ concentration of the sample solution, amount of complexing agent, sample volume, eluent type and volume, effects of foreign ions and adsorption capacity of the resin were investigated for quantitative recovery of gold and palladium ions. The effects of some anions and cations were also examined. Under optimum conditions, the detection limits for gold and palladium ions were found to be 0.29 and 0.19 μg L^?1, respectively. The preconcentration factor for gold and palladium was 250. After being validated by standard addition and analysis of standard reference material, the procedure was successfully applied to the analysis of sea and stream water, anodic slime, gold ore, soil and electronic waste.     

La3+掺杂对吸附相反应制备TiO2复合催化剂的结晶过程及弱紫外光下活性的影响

利用吸附相反应技术制备弱紫外光响应的高效催化剂,并通过XRD、XPS以及HRTEM探索了不同焙烧温度下La3+掺杂量对TiO2结晶过程的影响.结合弱紫外光下甲基橙的降解反应,深入研究催化剂结晶过程的变化对弱紫外光下催化剂活性的影响.结果表明,La3+掺杂会抑制TiO2的结晶过程.当焙烧温度或者掺杂量较低时,La3+不能进入TiO2的晶格结构但会轻微地抑制TiO2的结晶过程;未进入晶格结构的La3+存在会引入光生载流子的浅能级捕获中心,在弱光体系中极大提升了催化剂的活性.当La3+的掺杂量为0.05%(原子分数)时,经过900℃焙烧后催化剂降解能力最高,其活性超过商用P25的2倍多.在较高La3+掺杂量(超过0.20%)时,900℃焙烧后一定量La3+进入TiO2的晶格结构而大大抑制了TiO2结晶;这种强烈的抑制作用使得催化剂中存在大量无定形结构TiO2,无定形TiO2甚至多于700℃焙烧后的催化剂,反而大大抑制了弱光体系中催化剂活性.     

Effect of transition metal doping under reducing calcination atmosphere on photocatalytic property of TiO2 immobilized on SiO2 beads

TiO₂ immobilized on SiO₂ (TiO₂/SiO₂) have been prepared by sol-gel method and various ions of transition metals (Cr³⁺, Co²⁺, Ni²⁺, Cu²⁺, and Zn²⁺) were doped on the photocatalyst using wet impregnation method under reducing calcination atmosphere. The photocatalytic activity of metal doped TiO₂/SiO₂ towards phenol degradation under black light irradiation were investigated and compared with undoped TiO₂/SiO₂. The results showed that the photoresponse of Cu²⁺ and Zn²⁺ doped TiO₂/SiO₂ were larger than undoped TiO₂/SiO₂, indicating that the photogenerated carriers were separated more efficiently in Cu²⁺ and Zn²⁺ doped TiO₂/SiO₂. The reactivity was in the order of Cu²⁺ > Zn²⁺ > Ni²⁺ > Cr³⁺ > Co²⁺. The different photoreactivity was ascribed to combine effect of the different ionic radii and photocorrison tendency of the dopants. The sample was also characterized by surface analytical methods such as X-ray diffraction, scanning electron micrograph/electron dispersive X-ray analyzer and UV-Vis absorption spectrum.     

四氨基酞菁钯/γ-Al_2O_3可见光催化降解罗丹明B

采用浸渍法制备了四氨基酞菁钯(PdTAPc)/γ-Al_2O_3负载型光催化剂,采用UV-Vis,FTIR,XRD,SEM技术对其进行了表征,并将其用于罗丹明B的可见光催化降解,考察了光催化剂加入量、溶液pH、H_2O_2加入量、反应温度对罗丹明B降解效果的影响,并对光催化剂的稳定性进行了测试。表征结果显示,PdTAPc以圆片状负载于γ-Al_2O_3上,二者的结构均未发生明显变化。实验结果表明:在光催化剂加入量1.6 g/L、溶液pH 7.0、H_2O_2加入量12 mmol/L、反应温度20℃的优化条件下反应120 min,罗丹明B(质量浓度0.05 g/L)的降解率高达95%;光催化剂具有较高的稳定性,使用4次后罗丹明B的降解率仍高于85%。     

氮掺杂TiO2可见光光催化剂的制备及性能

以尿素和钛酸丁酯为原料,通过溶胶-凝胶法低温下制备了高可见光催化活性的氮掺杂TiO2(NDT)光催化剂,采用XRD、TEM、BET和UV-Vis DRS等测试手段对其进行了表征,并在自制光催化反应器中降解甲基橙评价了样品的光催化活性。结果表明,当氮与钛的摩尔比为0.5∶1时,350℃焙烧的样品(NDT350)具有最佳的可见光光谱吸收和光催化活性,该催化剂为锐钛矿晶相,平均粒径为21 nm,比表面积为89.13 m2/g。可见光辐照下,NDT350降解甲基橙的表观反应速率常数为1.381×10-2min-1,是商业P25催化剂的16.85倍。NDT350优良的可见光催化活性与其大的比表面积和强烈的可见光光谱吸收有关。