Biodegradation of Polycaprolactone Powders Proposed as Reference Test Materials for International Standard of Biodegradation Evaluation Method

Polycaprolactone (PCL) powders were prepared from PCL pellets using a rotation mechanical mixer. PCL powders were separated by sieves with 60 and 120 meshes into four classes; 0–125 μm, 125–250 μm, 0–250 μm and 250–500 μm. Biodegradation tests of PCL powders and cellulose powders in an aqueous solution at 25°C were performed using the coulometer according to ISO 14851. Biodegradation tests of PCL powders and cellulose powders in controlled compost at 58°C were performed by the Mitsui Chemical Analysis and Consulting Service, Inc. according to ISO 14855-1 and by using the Microbial Oxidative Degradation Analyzer (MODA) instrument according to ISO/DIS 14855-2. PCL powders were faster biodegraded than cellulose powders. The reproducibility of biodegradation of PCL powders is excellent. Differences in the biodegradation of PCL powders with different class were not observed by the ISO 14851 and ISO/DIS 14855-2. An enzymatic degradation test of PCL powders with different class was studied using an enzyme of Amano Lipase PS. PCL with smaller particle size was faster degraded by the enzyme. PCL powders with regulated sizes from 125 μm to 250 μm are proposed as a reference material for the biodegradation test.     

Sexual selection on mature male parr of masu salmon (Oncorhynchus masou): does sneaking behavior favor small body size and less-developed sexual characters?

In many salmonid species, males exhibit morphological dimorphism associated with alternative mating behaviors. ”Precocious males” have a small body size with little or no development of sexual characters and adopt sneaking to gain access to females, while ”migratory males” of large body size and well-developed secondary sexual characters fight. We quantified selection on precocious male parr of masu salmon (Oncorhynchus masou) under simulated natural conditions to examine the contribution of morphology to sneaking success. In contrast to the prediction that sneaking behavior favors small body size, we detected selection favoring relatively large body size for sneaking success. This selection pressure was caused by the dominance hierarchy within parr and may have been facilitated by indifference of dominant migratory males to parr. Unlike the secondary sexual characters exhibited by migratory male salmon, such as the hooked snout and humped back, no morphological characters other than body size contributed to the reproductive success of masu salmon parr. This non-contribution may have been responsible for the lack of development of sexual characters in precocious males. Received: 15 November 1999 / Accepted: 20 May 2000     

Paternal expenditure is related to brood sex ratio in polygynous great reed warblers

In many polygynous animals, parents invest more heavily in individual sons than in daughters. However, it is unclear if these differences in investment are a consequence of sex differences in the demand of offspring related to sexual size dimorphism or a consequence of parental manipulation. Here, we report on parental food delivery frequency in relation to brood size and brood sex ratio in a wild population of polygynous great reed warblers Acrocephalus arundinaceus. We used the polymorphic microsatellite loci on the Z chromosome to sex chicks. We found that paternal feeding frequency (times/h per nest) increased not with brood size, but with the proportion of males in the brood, although the demand per nest was more closely related to brood size than to brood sex ratio. Additionally, the increase in rate of paternal feeding frequency in relation to the brood sex ratio was much higher than the increase in rate of nestling food demands. Maternal feeding frequency was independent of both brood size and brood sex ratio. These results strongly suggest that fathers preferentially invest in their sons. We propose that parents can afford sex-biased parental care in animals in which food provisioning is enough for all offspring to survive. Received: 22 January 1996/Accepted after revision: 30 June 1996     

阶梯形鱼道中的滚动流研究

最近,小型倾斜河流中的阶梯形鱼道建筑以它的简易与实用而变得日益重要。在这种鱼道中出现的滚动流将产生波涌,并继续向下传播,而且它的周期性滚动可能会严重危害鱼道,因此,我们着手研究了它的严重性以便设计者在设计鱼道时能考虑这些因素。由实验证实滚动流源于阶梯形鱼道的上游。滚动流在稳定流与半平滑流间转变,它在一定时间间隔内不断地从稳定流变成半平滑流,又从半平滑流变成稳定流。它的流量值随着阶梯形水道的几何形状变形而呈现上下限。流量值和时间间隔均随着水池长度的增加而增加。     

Extraction of arsenic in a synthetic arsenic-contaminated soil using phosphate

An environment-friendly and cost-effective extraction method has been studied for the removal of arsenic from contaminated soil. A yellow-brown forest soil was contaminated with arsenic(V) and used as a model soil. Among various potassium and sodium salts, potassium phosphate was most effective in extracting arsenic, attaining more than 40% extraction in the pH range of 6–8 with minimum damage to the soil properties. Exchange mechanism is proposed for the extraction of arsenic from soil by phosphate. Sequential extraction shows that phosphate is effective in extracting arsenic of Al- and Fe-bound forms. Arsenic of residual form was not extracted. Arsenic was efficiently extracted by phosphate solution of pH 6.0 at 300 mM phosphate concentration and at 40°C.     

Study on recycled asphalt concrete for use in surface course in airport pavement

This research investigated the possibility of using recycled asphalt concrete as surface course in airport pavement. The basic properties of recycled asphalt binder after short- and long-term aging were firstly tested and compared with those of the virgin asphalt. Then, a series of laboratory tests were performed to evaluate the performance of recycled asphalt concrete (containing 40% and 70% RAP), in which the HMA mixture without RAP was used as a control. Furthermore, an experimental pavement consisting of three sections (corresponding to 0%, 40% and 70% RAP content) was constructed to verify the laboratory test results. These results indicated that the recycled asphalt could achieve the similar properties against long-term aging as virgin asphalt. Recycled asphalt concrete containing 40% RAP could be used as surface course in airport pavement as it exhibited similar performance as control mixture both from the laboratory and experimental pavement test results. On the contrary, recycled asphalt concrete containing 70% RAP was not recommended as its fatigue property was much poorer compared with that of virgin asphalt mixture.     

Biomass Carbon Ratio of Polymer Composites Measured by Accelerator Mass Spectrometry

The evaluation method of biomass carbon ratio of polymer composite samples including organic and inorganic carbons individually was investigated. Biodegradable plastics and biobased plastics can have their mechanical properties improved by combining with inorganic fillers. Polymer composites consisting of biodegradable plastics and carbonate were prepared by two different methods. Poly(lactic acid) (PLA) composite was prepared by synthesis from l-lactide with catalyst and calcium carbonate (CaCO₃) powders from lime. Poly(butylene succinate) (PBS) composite was prepared by hot-pressing the mixture of PBS powder and CaCO₃ powders from oyster shells. The mechanical properties of composite samples were investigated by a tensile test and a compression test using an Instron type mechanical tester. Tensile test with a dumbbell shape specimen was performed for PBS composite samples and compression test with a column shape specimen for PLA composite samples. Strength, elastic modulus and fracture strain were obtained from the above tests. Biomass carbon ratio is regulated in the American Standards for Testing and Materials (ASTM). In ASTM standards on biomass carbon ratio, it is required that carbon atoms from carbonates, such as CaCO₃, are omitted. Biomass carbon ratio was evaluated by ratio of ¹⁴C to ¹²C in the samples using Accelerator Mass Spectrometry (AMS). The effect of pretreatment, such as oxidation temperature and reaction by acid, on results of biomass carbon ratio was investigated. Mechanical properties decrease with increasing CaCO₃ content. The possibility of an evaluation method of biomass carbon ratio of materials including organic and inorganic carbons was shown.     

Nitrogen and phosphorus removal for swine wastewater by ammonium crystallization and intermittent aeration process

Abstract

A process on crystallized precipitation of ammonium by adding magnesium salt and phosphate was carried out to improve C/N ratio in swine wastewater. After completion of crystallized precipitation of ammonium, an intermittent aeration process with aeration and non‐aeration periods alternated at interval of 1:1 hr day^‐1 is used for the improved swine wastewater (T‐N/BOD=0.14: BOD=8200 mg/liter and T‐N=1166 mg/liter). The results obtained from the experiment show that the removal ratios of T‐N and NH₄‐N are 91% and 99%, respectively. T‐P is not removed, while the removal ratio of PO₄‐P is 60% as 3% of CaCl₂ liquid is added. The results also indicate that dilution with water is effective to improve the removal of phosphorus even if raw swine wastewater contains high concentrations of T‐N, T‐P, BOD, and TOC.     

Biobased Contents of Organic Fillers and Polycaprolactone Composites with Cellulose Fillers Measured by Accelerator Mass Spectrometry Based on ASTM D6866

The biobased contents of raw materials such as starches, sugar, chitin, or wood powders for biomass plastics were measured using Accelerator Mass Spectrometry (AMS) based on ASTM D6866. AMS measures the isotope carbon ratio of ¹⁴C to ¹²C and ¹³C in graphite derived from sample powders. The biobased contents of starches, sugar or chitin were almost 100% which means that they are fully biobased. The biobased contents of the wood powders were over 140% due to the effect of the post 1950s ¹⁴C injection due to nuclear testing. Poly(ε-caprolactone) (PCL) composite samples were prepared using the polymerization and direct molding method. The starting compound was the ε-caprolactone monomer liquid combined with cellulose and inorganic fillers using aluminum triflate as a catalyst at 80 °C for 6 or 24 h. PCL cylinder-shaped composite samples with a homogeneously dispersed cellulose filler were prepared with M_n = 4,600 (M_w/M_n = 2.9). The biobased content of the PCL composite with 50 wt% cellulose filler (51.67%) measured using AMS was slightly higher than the carbon ratio of cellulose in the starting powder samples (41.3 mol%). This is due to the higher biobased content (112.70%) of the cellulose filler used in this study. The biobased content of the polymer composite powders by AMS was found not to be affected by the presence of inorganic fillers, such as talc.     

淮河流域可持续发展研究的重点问题

以可持续发展的基本理论为指导 ,本研究选定淮河流域为研究的典型区域 ,试图通过对淮河流域社会、经济、资源、环境的系统分析 ,提出实现大河流域可持续发展战略的基本思路与框架