功能性磁性纳米复合材料的制备及应用 |
| |
引用本文: | 叶明,王公正,宿贵梅,莫润阳,胡静.功能性磁性纳米复合材料的制备及应用[J].环境工程,2015,33(10):66-71. |
| |
作者姓名: | 叶明 王公正 宿贵梅 莫润阳 胡静 |
| |
作者单位: | 1.陕西师范大学物理学与信息技术学院 |
| |
摘 要: | 采用水热法制备了Fe3O4磁性纳米微球,进而用腐殖酸(HA)修饰,成功制备了功能性磁性纳米复合材料(Fe3O4-HA)。并通过紫外可见分光光度计对含有有机染料亚甲基蓝(MB)废水中Fe3O4-HA磁性纳米复合材料的吸附行为进行研究。Fe3O4-HA磁性纳米复合材料的结构和性能用透射电子显微镜、光学接触角测量仪、傅立叶变换红外光谱、X射线衍射仪、振动样品磁强计等手段进行表征。结果表明:Fe3O4-HA磁性纳米复合材料结构均匀,平均粒径约为300 nm,饱和磁化强度为75.3 emu/g。Fe3O4-HA磁性纳米复合材料具有良好的超顺磁性,较高的吸附效率和可重复使用性。
|
关 键 词: | PM10 PM2. 5 超标率 超标倍数 |
PREPARATION AND APPLICATION OF FUNCTIONAL MAGNETIC NANOCOMPOSITE |
| |
Abstract: | Functional magnetic nanocomposite ( Fe3O4-HA) was successfully prepared by hydrothermal method,and then
coated by humic acid ( HA) . Adsorption behavior of the Fe3O4-HA to wastewater containing organic dye methylene blue
( MB) was studied by ultraviolet and visible spectrophotometer. The structure and property of the Fe3O4-HA were
characterized by transmission electron microscopy,optical contact angle,fourier transform infrared spectroscopy,X ray
diffractometer,vibrating sample magnetometer. The results demonstrate that Fe3O4-HA has a homogeneous structure,and its
average particles size is about 300 nm and the saturation magnetization is 75. 3 emu /g. This synthetic Fe3O4-HA
nanocomposite has good superparamagnetism,high adsorption efficiency and reusability. |
| |