某电镀厂污泥酸浸除杂提磷试验 |
| |
引用本文: | 陈茂荣,李神勇,孙家寿,李文荣,刘安.某电镀厂污泥酸浸除杂提磷试验[J].中国再生资源,2009(10):42-44. |
| |
作者姓名: | 陈茂荣 李神勇 孙家寿 李文荣 刘安 |
| |
作者单位: | 武汉工程大学环境与城市建设学院,湖北武汉430074 |
| |
摘 要: | 探讨了武汉某工业园电镀厂污泥酸浸、除杂提磷的工艺及条件。当H2SO4(浓度为72%)用量为4mL/g污泥,在液固比为5:1,常温搅拌浸出时间为1h,用碱液调节浸出液pH为4后沉淀1h,过滤,磷的浸出率为86%,铁的沉淀率达到94.2%,除铁后的浸出液进一步用NH4HCO3净化,并制取磷铵产品,总养分(N+P2O5)为52%。产品达到国家合格品的标准。
|
关 键 词: | 电镀污泥 硫酸 酸浸 提磷 |
Test of extracting phosphorus from sludge in an electroplating plant by pickling and removing impurities |
| |
Authors: | CHEN Maorong LI Shenyong SUN Jiashou LI Wenrong LIU An |
| |
Institution: | (School of Environmental and Civil Engineering, Wuhan Institute of Technology, Wuhan 430074, China) |
| |
Abstract: | The craft and conditions of refining phosphorus by pickling and removing impurities from electroplating sludge in a industrial park in Wuhan were explored .When the amount of H2SO4 (C=72%)was 4 mL/g, the liquid-solid ratio at 4:1 and stir leaching time for lh at room temperature , the phosphorus lixiviated efficiency was 86% with precipitating for lh after adjusting the leaching solution at pH 4, while ,the iron sedimentation rate was 94.2%. Purify the lixiviated liquid after removing iron with NH4HCO3, then the AP products were made ,the total nutrient (N+P2O5) was 52%.The products reach the state qualified grade. |
| |
Keywords: | electroplating sludge H2SO4 acid leaching extraction of phosphorus |