Fabrication of bulk materials with zeolite from coal fly ash |
| |
Authors: | Hayami Takeda Shinobu Hashimoto Tomoya Iwata Sawao Honda Yuji Iwamoto |
| |
Institution: | 1. Department of Environmental and Materials Engineering, Nagoya Institute of Technology, Gokiso-cho, Showa-ku, Nagoya, 466-8555, Japan
|
| |
Abstract: | After packing a compact of coal fly ash mixed with 3.5?M (mol/L) sodium hydroxide solution into a cylindrical plastic mold at 80?°C and 50?% relative humidity for 24?h, the plastic mold was released and the compact was immersed in 3.5?M sodium hydroxide solution at 80?°C for 48?h. When the resultant compact was removed from the solution and cured at 80?°C and 50?% relative humidity for 7?days, a bulk material with zeolite was formed. The strength of the resultant bulk material was a result of the formation of geopolymer (alkali-activated cement). The specific surface area and the compressive strength of the bulk body sample were 21.4?m2/g and 29.0?MPa, respectively. According to a quantitative analysis conducted using the X-ray diffraction (XRD) technique, the content of the formed Na-P type zeolite was estimated to be approximately 28.2?% in mass ratio. The pore size of the resultant bulk materials with zeolite ranges from sub-nanometer to several tens of nanometers, so the resultant bulk material with zeolite exhibited excellent water vapor retention characteristics. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|