Selective separation and preconcentration studies of chromium(VI) with Alamine 336 supported liquid membrane

Chromium compounds have received considerable attention because these are used extensively in such industrial applications as electroplating, steelmaking, tanning of leather goods, and corrosion inhibition. The use of supported liquid membranes (SLMs) to remove metals from wastewaters has actively been pursued by the scientific and industrial community. In the present work, the selective separation and preconcentration of Cr(VI) ions has been studied by using a commercial amine as the membrane liquid on the porous polypropylene support. Permeation experiments were conducted on a laboratory scale batch reactor made up of perspex, with a memberane fixed amid the two chambers. The flux of Cr(VI) ions was found to be maximum (3.15?×?10^?5?mol?cm^?2?s^?1) around pH 1. Above and below this pH the flux decreases. Distribution studies show that an increase in the amine concentration leads to higher distribution coefficients at fixed pH values. At pH around unity, the distribution of Cr(VI) ions into the organic phase was found to be maximum, of the order of 56.3. The Cr(VI) transport through the membrane increases with rise in temperature. In order to check the long-term efficiency of the flat sheet SLM, an experiment was conducted with higher Cr(VI) concentration (5000?ppm) for 24?h, at optimised parameters. It was observed that in 24?h, about 1/5th of the feed Cr(VI) is left over while the rest is transported. However, minute organic droplets were also seen in the feed and strip compartments, after 1 day. This observation suggested the loss of membrane liquid. The feasibility of preconcentration of Cr(VI) by using the proposed SLM parameters, was also studied by using the hollow fibre (HF) system. Highest enrichment factor (E.F) value was obtained for 50?mg?L^?1 whereby all of the metal was transported to the stripping phase and the resulting Cr concentration was 688?mg?L^?1 (E.F?=?13.8). It was observed that while treating more diluted solutions, the enrichment factor decreases. The values of E.F equal to 8.9 and 11.3 were found for initial Cr concentration of 10 and 30?mg?L^?1.