Effect of Al2O3 particle size reduction on aluminium dust explosion

To investigate the effect of Al₂O₃ particle size on an aluminum explosion, the overpressure and flame velocity in a vertical duct were evaluated. The results show that the inhibitory effect of submicron Al₂O₃ is best, while the inhibitory effect increases with increasing inerting ratio. However, the inhibitory effect of micron Al₂O₃ does not increase significantly after the inerting ratio exceeds 40%. For high-concentration aluminum powder, 0.8 μm Al₂O₃ with an inerting ratio less than 20% promotes aluminum explosion. As the inerting ratio increases beyond 20%, however, the overpressure decreases. Furthermore, Al₂O₃ inhibits the formation of the intermediate product AlO and decreases the flame brightness. As the inerting ratio of 0.8 μm Al₂O₃ reaches 50%, the white patches in the flame image disappear. The results of scanning electron microscopy showed that the explosion products agglomerate and some dot-like protrusions appear on the surface of the unburned aluminum particles. The inhibition mechanism was qualitatively investigated. Physical heat absorption is proven to play a limited role. Thermal radiation and chemical inhibition play a key role. The chemical effect mainly influences the surface reaction energy source.