Remarkable promotion effect of trace sulfation on OMS-2 nanorod catalysts for the catalytic combustion of ethanol

OMS-2 nanorod catalysts were synthesized by a hydrothermal redox reaction method using MnSO₄ (OMS-2-SO₄) and Mn(CH₃COO)₂ (OMS-2-AC) as precursors. SO₄^2 −-doped OMS-2-AC catalysts with different SO₄^2 − concentrations were prepared next by adding (NH₄)₂SO₄ solution into OMS-2-AC samples to investigate the effect of the anion SO₄^2 − on the OMS-2-AC catalyst. All catalysts were then tested for the catalytic oxidation of ethanol. The OMS-2-SO₄ catalyst synthesized demonstrated much better activity than OMS-2-AC. The SO₄^2 − doping greatly influenced the activity of the OMS-2-AC catalyst, with a dramatic promotion of activity for suitable concentration of SO₄^2 − (SO₄/catalyst = 0.5% W/W). The samples were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), inductively coupled plasma optical emission spectroscopy (ICP-OES), NH₃-TPD and H₂-TPR techniques. The results showed that the presence of a suitable amount of SO₄^2 − species in the OMS-2-AC catalyst could decrease the Mn–O bond strength and also enhance the lattice oxygen and acid site concentrations, which then effectively promoted the catalytic activity of OMS-2-AC toward ethanol oxidation. Thus it was confirmed that the better catalytic performance of OMS-2-SO₄ compared to OMS-2-AC is due to the presence of some residual SO₄^2 − species in OMS-2-SO₄ samples.