Preparation of glass-ceramics from molten steel slag using liquid-liquid mixing method |
| |
| Authors: | Zhang Kai Liu Jianwen Liu Wanchao Yang Jiakuan |
| |
| Institution: | a School of Environmental Science & Engineering, Huazhong University of Science & Technology, Wuhan, China
b School of Energy & Environment, Inner Mongolia University of Science & Technology, Baotou, China |
| |
| Abstract: | A novel approach to prepare glass-ceramics from molten steel slag (MSS) was proposed. In laboratory, the water-quenched steel slag was melted at 1350 °C to simulate the MSS. A mixture of additive powders in wt.% (55 quartz powder, 5 Na2O, 16 emery powder, 15 CaO, 8 MgO, 1 TiO2) were melted into liquid at 1350 °C separately. Then the MSS and the molten additives were mixed homogeneously in order to obtain parent glass melt. The proportion of MSS in the melt was 50 wt.%. The melt was subsequently cast, annealed, heat-treated and transformed into glass-ceramics. Their microstructure and crystallization behavior were analyzed. The samples exhibited excellent properties and displayed bulk crystallization. The major crystallized phase was diopside ((Fe0.35Al0.20Mg0.44)Ca0.96(Fe0.08Si0.70Al0.20)2O6.12), which was uniformly distributed in the microstructure. The novel approach may help iron and steel industry achieve zero disposal of steel slag with utilization of the heat energy of the MSS. |
| |
| Keywords: | Steel slag Glass-ceramics Energy recovery Zero disposal |
| 本文献已被 ScienceDirect PubMed 等数据库收录！ |
|