Polymerization of l-lactide with SnCl2: A Low Toxic and Eco-friendly Catalyst

Polymerizations of l-lactide catalyzed either by neat SnCl₂ or by SnCl₂?+?difunctional cocatalysts were conducted in bulk at 180, 160 and 140 °C with variation of the Lac/Cat ratio and time. With neat SnCl₂ poly(L-lactide) having weight average molecular weights (uncorrected M_w’s) up to 190 000 g mol^?1 were obtained mainly consisting of linear chains. Addition of salicylic acid or 1,1-bisphenol yielded a higher fraction of cyclic polylactides but lower molecular weights. Furthermore, SnCl₂ was compared with Bu₂SnCl₂ and various other metal chlorides and the best results were obtained with SnCl₂. With ethyl L-lactate as initiator SnCl₂-catalyzed ROPs were performed at 120 °C and the lac/initiator ratio was varied. All these experiments were conducted under conditions allowing for comparison with ROPs catalyzed with neat Sn(II)-2-ethyhexanoate. Such a comparison was also performed with ε-caprolactone as monomer.