In vitro and in vivo studies of lead immobilization by synthetic hydroxyapatite

Apatite appears a useful compound for removing lead from water, due to its ability to immobilize the metal by precipitation. In dilute solution, dissolved hydroxyapatite HA, Ca1O(P04)6(OH)2] provided phosphates that were reactive with aqueous lead (molar ratio HA/Pb= 1/10) forming precipitates at around pH 6. These dissolved at a more acidic pH (3). Solid HA in contact with Pb2+ions, led to the formation of pyromorphite Pblo(P04)6(OH)2], identified by X-ray diffraction and insoluble at pH tested (3-8). The amount of pyromorphite increased with the weight ratio of HA/Pb. When this one increased from 1 to 1000, lead precipitated as pyromorphite rose from 19 to 99%. In vivo experiments on rats confirmed the in vitro results. In fact, lead bioavailability assessed by intestinal perfusion was unchanged in the presence of dissolved HA, whereas it was significantly lower in the presence of solid HA, evaluated by gastric intubation, at a weight ratio equal to 10 (amount of lead absorbed decreased by 60%). Apatite could bean effective means of immobilizing lead in drinking or sewage, since accidental pyromorphite ingestion does not yield bioavailable lead.