Inhibiting effects by Fe2O3 on combustion and explosion characteristics of ABS resin

The global increase in the use of, and reliance on, plastics has prompted the demand for acrylonitrile-butadiene-styrene (ABS) resin in various fields. With this increased requirement, numerous failures have occurred in the ABS process. Those incidents, resulting from electrostatic discharge, powder accumulation, heat accumulation, construction sparks, and plant fires, have caused dust fire and explosions.In this study, the ABS resin was gleaned from the site and tested for its explosion parameters, including minimum ignition temperature of dust cloud (MIT_C), minimum ignition energy (MIE), and minimum explosion concentration (MEC). To improve loss prevention in the manufacturing process, ferric oxide (Fe₂O₃) as an inert additive was added in the ABS powder. According to the MIE test, Fe₂O₃ has an apparent inhibiting effect on dust explosion for the ABS dust. With the proportion of Fe₂O₃ increased from 25 to 50 mass% in ABS, the MIE increased from 67 to 540 mJ. The explosion tests via 20-L apparatus indicated that Fe₂O₃ mixed with ABS could not increase the MEC significantly. However, the explosion pressure dropped by increasing in the ratio of Fe₂O₃ in ABS. This inerting strategy of ABS was deemed to substantially lessen the probability and severity of fire and explosion.