Preparation and Fundamental Characterization of Cellulose Nanocrystal from Oil Palm Fronds Biomass |
| |
| Authors: | Rudi Dungani Abdulwahab F Owolabi Chaturbhuj K Saurabh H P S Abdul Khalil Paridah M Tahir C I C M Hazwan Kamoldeen A Ajijolakewu M M Masri E Rosamah P Aditiawati |
| |
| Institution: | 1.School of Life Sciences and Technology, Gandung Labtex XI,Institut Teknologi Bandung,Bandung,Indonesia;2.School of Industrial Technology,Universiti Sains Malaysia,Penang,Malaysia;3.Federal Institute of Industrial Research Oshodi,Lagos,Nigeria;4.Laboratory of Biocomposite Technology, Institute of Tropical Forestry & Forest Products,University Putra Malaysia,Selangor,Malaysia;5.Department of Microbiology,University of Ilorin,Ilorin,Nigeria;6.Faculty of Forestry,Mulawarman University,Samarinda,Indonesia |
| |
| Abstract: | The objective of this work was to isolate cellulose nanocrystal (CNC) from oil palm fronds (Elaeis guineensis) and its subsequent characterization. Isolation involves sodium hydroxide/anthraquinone pulping with mechanical refining followed by total chlorine free bleaching (includes oxygen delignification, hydrogen peroxide oxidation and peracetic acid treatment) before acid hydrolysis. Bleaching significantly decreased kappa number and increased α-cellulose percentage of fibers as confirmed by Technical Association of the Pulp and Paper Industry standards. Transmission electron microscopy (TEM), X-ray diffraction, Fourier transform infrared spectroscopy and thermogravimetric analysis revealed that acid hydrolysis along with bleaching improved crystallinity index and thermal stability of the extracted nanocrystals. It was observed that CNC maintained its cellulose 1 polymorph despite hydrolysis treatment. Mean diameter as observed by TEM and average fiber aspect ratio of obtained CNC was 7.44 ± 0.17 nm and 16.53 ± 3.52, respectively making it suitable as a reinforcing material for nanocomposite. |
| |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ |
|