Effects of synthesis methods on catalytic activities of CoOx–TiO2 for low-temperature NH3-SCR of NO

A series of cobalt doped TiO_2(Co-TiO_2) and Co Oxloaded TiO_2(Co/TiO_2) catalysts prepared by sol–gel and impregnation methods respectively were investigated on selective catalytic reduction with NH_3(NH_3-SCR) of NO. It was found that Co-TiO_2 catalyst showed more preferable catalytic activity at low temperature range. From characterization results of XRD,TEM, Raman and FT-IR, Co species were proved to be doped into TiO_2 lattice by replaced Ti atoms. After being characterized and analyzed by NH_3-TPD, PL, XPS, EPR and DRIFTS, it was found that the better NH_3-SCR activities of Co-TiO_2 catalysts, compared with Co/TiO_2 catalyst, were ascribed to the formation of more oxygen vacancies which further promoted the production of more superoxide ions(O-2). The superoxide ions were crucial for the formation of low temperature SCR reaction intermediates(NO-3) by reacting with adsorbed NO molecule. Therefore, these aspects were responsible for the higher low temperature NH_3-SCR activity of Co-TiO_2 catalysts.