Preparation of Fe–Co based MOF-74 and its effective adsorption of arsenic from aqueous solution

To obtain a cost-effective adsorbent for the removal of arsenic in water,a novel nanostructured Fe–Co based metal organic framework(MOF-74)adsorbent was successfully prepared via a simple solvothermal method.The adsorption experiments showed that the optimal molar ratio of Fe/Co in the adsorbent was 2:1.The Fe_2Co_1MOF-74 was characterized by various techniques and the results showed that the nanoparticle diameter ranged from60 to 80 nm and the specific surface area was 147.82 m~2/g.The isotherm and kinetic parameters of arsenic removal on Fe_2Co_1MOF-74 were well-fitted by the Langmuir and pseudo-second-order models.The maximum adsorption capacities toward As(III)and As(V)were 266.52 and 292.29 mg/g,respectively.The presence of sulfate,carbonate and humic acid had no obvious effect on arsenic adsorption.However,coexisting phosphate significantly hindered the removal of arsenic,especially at high concentrations(10 mmol/L).Electrostatic interaction and hydroxyl and metal–oxygen groups played important roles in the adsorption of arsenic.Furthermore,the prepared adsorbent had stable adsorption ability after regeneration and when used in a real-water matrix.The excellent adsorption performance of Fe_2Co_1MOF-74 material makes it a potentially promising adsorbent for the removal of arsenic.

Preparation of Fe-Co based MOF-74 and its effective adsorption of arsenic from aqueous solution