Breakthrough CO2 adsorption in bio-based activated carbons

In this work, the effects of different methods of activation on CO₂ adsorption performance of activated carbon were studied. Activated carbons were prepared from biochar, obtained from fast pyrolysis of white wood, using three different activation methods of steam activation, CO₂ activation and Potassium hydroxide (KOH) activation. CO₂ adsorption behavior of the produced activated carbons was studied in a fixed-bed reactor set-up at atmospheric pressure, temperature range of 25–65°C and inlet CO₂ concentration range of 10–30 mol% in He to determine the effects of the surface area, porosity and surface chemistry on adsorption capacity of the samples. Characterization of the micropore and mesopore texture was carried out using N₂ and CO₂ adsorption at 77 and 273 K, respectively. Central composite design was used to evaluate the combined effects of temperature and concentration of CO₂ on the adsorption behavior of the adsorbents. The KOH activated carbon with a total micropore volume of 0.62 cm³/g and surface area of 1400 m²/g had the highest CO₂ adsorption capacity of 1.8 mol/kg due to its microporous structure and high surface area under the optimized experimental conditions of 30 mol% CO₂ and 25°C. The performance of the adsorbents in multi-cyclic adsorption process was also assessed and the adsorption capacity of KOH and CO₂ activated carbons remained remarkably stable after 50 cycles with low temperature (160°C) regeneration.