| 电渗析法深度处理铜冶炼废水研究 |
| |
| 引用本文： | 肖莹莹,张麟,章北平,叶恒朋,吴国珉,杜冬云.电渗析法深度处理铜冶炼废水研究[J].环境科学与技术,2012(8):181-184. |
| |
| 作者姓名： | 肖莹莹 张麟 章北平 叶恒朋 吴国珉 杜冬云 |
| |
| 作者单位： | 中南民族大学,武汉市重金属废水处理与回用工程技术研究中心,化学与材料科学学院/催化材料科学教育部-国家民委重点实验室;大冶有色金属公司;华中科技大学环境科学与工程学院 |
| |
| 基金项目： | 湖北省自然科学基金(2010CDZ045);湖北省科技攻关重点项目(2009CDA010);武汉市科技攻关重点项目(201160638173) |
| |
| 摘 要： | 文章研究建立了一套电渗析法深度处理铜冶炼废水的小试装置,以某铜冶炼厂废水处理站出水为原水,通过实验,确定了电渗析法的极限电流密度,研究了电压、进水流量、进水浓度等参数对电渗析深度处理工艺出水水质的影响,并通过对比测试不同的阻垢剂对自来水、电渗析进水、电渗析出水的阻垢率,探讨电渗析出水回用后的结垢问题。结果表明:该电渗析装置的极限电流为0.42 A,极限电流密度为1.3 mA/cm2;最佳操作电压为20 V,适宜的进水流量为20 L/h,进水浓度对淡水水质影响不大;采用浓水循环工艺,淡水产率可提高至约80%,浓室TDS超过15 000 mg/L,对浓水的后续处理处置创造了条件;各阻垢剂对电渗析出水的阻垢率为72.0%~76.9%,远大于对电渗析进水的阻垢率,也显著大于对常规自来水的阻垢率。
|
| 关 键 词： | 电渗析 铜冶炼废水 废水回用 总溶解性固体 硬度 |
Advanced Treatment of Copper Smelting Wastewater by Electrodialysis Process |
| |
| XIAO Ying-ying,ZHANG Lin,ZHANG Bei-ping,YE Heng-peng,WU Guo-min,DU Dong-yun.Advanced Treatment of Copper Smelting Wastewater by Electrodialysis Process[J].Environmental Science and Technology,2012(8):181-184. |
| |
| Authors: | XIAO Ying-ying ZHANG Lin ZHANG Bei-ping YE Heng-peng WU Guo-min DU Dong-yun |
| |
| Institution: | 1(1.Wuhan Research Centre for Heavy Metal Wastewater Treatment and Reuse Engineering and Technology,School of Chemistry and Material Science/Key Laboratory for Catalysis and Materials Science of the State Ethnic Affairs Commissions & Ministry of Education,Central South Nationalities University,Wuhan430074,China;2.Deye Nonferrous Metal Company,Huangshi 435005,China;3.School of Environmental Science and Engineering,Huazhong University of Science and Technology,Wuhan 430074,China) |
| |
| Abstract: | A small scale experiment was done for advanced treatment of copper smelting wastewater by electrodialysis process.The run characteristics such as limiting current density,voltage,inflow rate and inflow concentrations were studied.The fouling inhibition rates were discussed by comparing the inflow water,effluent water and tap-water with various fouling inhibitors.Results indicated that the limiting current was 0.42 A,and limiting current density was 1.3 mA/cm2.The optimum run voltage was 20 V,and proper inflow rate was 20 L/h.Effect of inflow concentration of TDS on effluent water quality was slightly.The output rate of fresh water was increased to 80% by circling the condensing water.TDS of condensing room was over 15 000 mg/L,which was advantageous to the proceeding treatment.The fouling inhibition rates of the effluent water were 72.0%~76.9%,which were much greater than that of the inflow water and tap-water. |
| |
| Keywords: | electrodialysis copper smelting wastewater wastewater reuse total dissolved solid hardness |