C/C复合材料不同碳基体的纳米压痕行为研究

目的研究碳基体微观结构对材料整体性能的影响。方法用酚醛浸渍-碳化、中温煤沥青浸渍-碳化、甲烷为碳源前驱体,经化学气相沉积制备得到不同碳基体C/C复合材料。采用偏光显微镜对C/C复合材料不同碳基体的显微结构进行观察分析,采用XRD和Raman光谱对C/C复合材料的树脂碳基体、沥青碳基体和热解碳基体的微晶尺寸进行表征,以玻璃碳作为参比样品,通过纳米压痕测试不同碳基体试样的弹性模量和硬度。结果碳基体为热解碳和沥青碳的石墨微晶缺陷少,完整度较好,石墨化程度高。玻璃碳和树脂碳基体中石墨微晶排列紊乱,有序度低,石墨化程度低。酚醛浸渍-碳化得到的树脂碳的微晶尺寸Lc最小,为1.69 nm,弹性模量和硬度最大,分别为(23.17±0.54) GPa和(3.26±0.10) GPa;光滑层热解碳和粗糙层热解碳的弹性模量和硬度次之;沥青碳的微晶尺寸最大,Lc为9.36nm,而弹性模量和硬度最小,分别为(12.53±2.29) GPa和(0.72±0.14) GPa。结论不同碳基体的C/C复合材料中,碳基体的石墨化度越高,微晶尺寸越大,各向异性越显著,材料的弹性模量和硬度越低。     

Emissions of C2 – C12 hydrocarbons in the Hsuehshan tunnel, Taiwan

The concentrations of 56 hydrocarbons from C2 to C12 were measured simultaneously in the southbound bore, the northbound bore and the exhaust air shafts of the Hsuehshan tunnel near Yilan, Taiwan for 12 days during 2007 and 2008. A total of 60 integrated air samples were collected using stainless steel canisters and analyzed using GC/FID and GC/MS. The five most abundant species in all samples were ethylene, acetylene, isopentane, propylene and toluene. The exit/entrance ratios of total non-methane hydrocarbons (NMHC) concentration were 7.8 and 4.8 for the southbound and northbound bores, respectively. Furthermore, the exhaust from the vertical shafts affects air quality in the neighborhood. The most abundant species of emission rate (ER) was toluene (21.93–42.89 mg/sec), followed by isopentane, ethylene, propylene and 1-butene, with ER ranging from 2.50 to 9.31 mg/sec. The species in the three exhaust air shafts showed that the reactivities of these emissions are similar to those of vehicle emissions. Notably, the control of emissions in the vertical shafts of the vehicle tunnel will be important in the future.     

Airborne C1- and C2-halocarbons at four representative sites in Europe

Air concentratiions of trichlorofluoromethane, trichloromethane, tetrachloromethane, 1,1,2-trichloro-1,2,2-trifluoroethane, 1,1,1-trichloroethane, trichloroethene and tetrachloroethene have been determined at four sites: a medium-sized (80, 000 inhabitants), moderately industrialized city in southwest Germany, a mountain forest site in the northern Black Forest, a suburb south of Lisbon at the Atlantic coast of Portugal, and a truly remote oceanic site, the island of Madeira. As expected, there are large differences in the concentrations of those halocarbons which find wide technical applications and have relatively short atmospheric lifetimes; moderate or small differences are found for those with small anthropogenic sources—chloroform and tetrachloromethane. Chloroform tends to be higher at the marine sites, suggesting that it arises from natural sources.