铁锰泥除砷颗粒吸附剂对As(Ⅴ)的吸附去除

以除铁除锰生物滤池反冲洗泥为主要原料制备除砷颗粒吸附剂(granular adsorbents for arsenic removal,GA),使用SEM、XRD与BET等技术对其进行表征,并考察了GA对As(Ⅴ)的吸附机制和性能.结果表明,GA表面粗糙且孔隙发达;XRD图谱中出现石英晶体和少量赤铁矿晶体衍射峰,内部结晶度差;比表面积为43.8 m~2·g~(-1),存在大量介孔.吸附动力学过程符合准二级动力学模型.Freundlich等温方程更符合其吸附行为(R2=0.994).最大吸附容量为5.05 mg·g~(-1).进一步分析表明,在pH为1.1~9.5的范围内,GA对As(Ⅴ)具有较好的吸附效果.H_2PO_4~-与SiO_3~(2-)能显著抑制As(Ⅴ)的吸附,而HCO_3~-、SO_4~(2-)对吸附效果影响相对较小.GA的可再生性好,3次再生后吸附量相当于初始吸附量的82%.     

基于铁锰泥的除砷颗粒吸附剂制备及其比较

地下水除铁除锰滤池反冲洗铁锰泥具有良好的除砷效果,但因其粉末形态不易固液分离,本文采用高温烘焙法和包埋法以铁锰泥为原料制备颗粒吸附剂,其中包埋法采用烘干和冻干两种干燥方法制粒.结果表明,3种颗粒吸附剂:高温烘焙颗粒吸附剂(GA)、包埋烘干吸附剂(H-GA)和包埋冻干吸附剂(D-GA),表面粗糙,比表面积分别为43. 830、110. 30和129. 18 m~2·g~(-1).吸附实验表明,H-GA和D-GA对砷的吸附远大于GA,GA、H-GA和D-GA最大吸附量分别为5. 05、14. 95和13. 45 mg·g~(-1). Langmuir模型能更好地拟合H-GA和D-GA对砷的吸附,Freundlich模型更好地拟合GA的吸附过程,准一级动力学和准二级动力学模型均能拟合3种吸附剂的动力学数据.酸性环境更有利于砷的吸附.包埋法制备的颗粒吸附剂H-GA和D-GA保留了铁锰泥原始结构,比表面积也远大于GA,因此吸附效果比GA好.两种干燥方式烘干和冻干对吸附没有明显影响.     

铁改性赤泥吸附剂的制备及其除砷性能研究

以氧化铝生产废渣--赤泥为原料,采用铁盐改性处理制备了新型羟基铁包覆型赤泥除砷吸附剂.研究考察了吸附剂吸附砷效能、投加量、吸附时间和pH值对吸附除砷效果的影响;采用扫描电镜(SEM)、红外光谱(IR)、比表面积(BET)等仪器对吸附剂进行了表征,并探讨了吸附机制.结果表明,铁盐改性赤泥吸附剂对As(V)具有显著吸附效能,在pH为7,初始砷浓度为1 mg·L-1,铁盐改性赤泥吸附剂饱和吸附容量为50.6mg·g-1时,除砷率高达99.9%,吸附后出水砷含量可达到0.01 mg·L-1以下,吸附规律符合Langmuir等温方程式;溶液pH值显著影响砷去除效果,吸附机制主要为羟基铁的表面吸附机制;吸附后的吸附剂可通过NaOH溶液再生,脱附率达到92.1%.     

污泥基吸附剂除磷及其吸附效能研究

试验通过制备的污泥基吸附剂A、B、C和市售果壳活性炭分别对磷酸二氢钾、三聚磷酸钠、甘油磷酸钠不同的磷溶液进行吸附除磷,研究吸附时间、吸附剂投加量、吸附溶液pH值以及磷溶液初始浓度对除磷效果的影响。试验结果表明:污泥基吸附剂对磷的去除率随吸附时间的增加而提高,在2h时基本达到吸附平衡;磷去除率随吸附剂投加量的增加而提高,但单位吸附剂的吸附量会降低;磷去除率随着磷溶液浓度的增加而降低,而吸附量随磷溶液浓度的增加而提高;随着污泥基吸附剂含铁量的增加,磷溶液解析pH值也越小;同时在对生活污水吸附除磷试验中发现,污泥基吸附剂A、B、C磷去除率均好于市售果壳活性炭,分别为73.4%、85.2%、93.6%、73.3%。     

磁性吸附材料CuFe2O4吸附砷的性能

根据Cu(Ⅱ)和Fe(Ⅲ)都对砷有较强的亲和性,制备了同时含有Cu(Ⅱ)和Fe(Ⅲ)的、可用磁分离方法进行分离回收的磁性吸附材料CuFe2O4,并对其进行了表征及吸附砷的性能研究.结果表明,该吸附剂对砷的吸附能力与溶液pH有关,在弱酸性及中性条件下,吸附砷的能力最强,而对As(V)的吸附能力比对As(Ⅲ)更强些,在平衡浓度为10μg/L时,其吸附容量可达10mg/g左右,可以很容易地将水中浓度为1～20mg/L的As(V)降到10μg/L以下.实验考察了几种无机阴离子对吸附砷的影响,表明较高浓度(砷浓度的20倍)的硫酸盐对As(Ⅲ)和As(V)的吸附均有一定影响,盐酸盐及磷酸盐则影响不明显;负载的As(V)可较容易地用0.1mol/L NaOH洗脱下来,使吸附剂再生,而As(Ⅲ)则难以洗脱,这与2种价态砷的吸附机理不同有关.     

金属基吸附剂除砷技术研究进展

砷污染问题由于砷的高毒性、不可降解性的特点,一直是世界普遍面临的饮用水处理难题之一,并且受到广泛关注。吸附技术由于其低能耗、无污染、操作简便而被广泛应用于水中砷的去除,如何开发出高效、易回收的砷吸附剂是吸附除砷技术的主要研究内容。该文围绕吸附剂特性、除砷性能及吸附机制,综述了近年来的研究热点金属基吸附剂除砷研究进展,并展望了金属基吸附剂除砷技术未来的研究方向,认为金属基吸附剂结构优化、限域纳米吸附剂的制备以及吸附剂孔道大小的定向调控是未来的研究热点。     

沸石负载氧化铁吸附剂吸附除磷研究

采用铁盐溶液蒸发法制备沸石负载氧化铁吸附剂,探讨其对磷的吸附性能。结果表明:随着沸石负载氧化铁吸附剂投加量的增加,单位质量吸附剂对磷的吸附量先升高后降低;磷的去除率随负载铁含量的增加而升高;p H=7时,去除率高达92.6%;吸附剂对磷的去除率受共存离子的影响较小;吸附数值可采用Freundlich等温模型拟合,相关性显著;吸附过程很好地遵循准二级动力学模型;采用Na OH为再生剂效果较好,再生率随着Na OH溶液浓度的提高而提高。     

高效除砷分子筛新型材料制备及其吸附特性研究

为提高4A分子筛(MS)对水溶液中砷的吸附性能,以MS为载体,采用浸渍法制备载铁分子筛(FMS)和铁锰分子筛(FMMS)作为除砷吸附剂,利用扫描电镜(SEM)、傅里叶红外光谱(FT-IR)、比表面积测试法(BET)等手段对MS和FMS微观结构特点进行表征,并开展批次试验考察FMS和FMMS对水中五价砷(As5+)和三价砷(As3+)的吸附效果,对FMS吸附As5+过程进行吸附动力学、等温吸附试验和吸附热力学等拟合.结果表明:①铁盐浸渍改性能有效提高MS比表面积、改善其表面结构,改性后FMS是一种窄孔径、尺寸均匀的介孔材料,比表面积和孔体积分别从27.38 m2/g和0.068 cm3/g增至281.25 m2/g和0.16 cm3/g,平均孔径由9.93 nm减至2.21 nm;MS微观结构由密实粗糙颗粒转变为疏松多孔隙结构.②FT-IR表明,铁盐浸渍形成的铁氧化物主要与MS结构中O—H、Al—O和Si—O结合;批次试验设定ρ(As5+)为4 mg/L,与MS相比FMS对As5+的去除率约提高70%.③吸附动力学结果显示,FMS对As5+的吸附过程符合准二级动力学模型,相关系数(R2)达0.99,反应过程中化学吸附起主要作用.④等温吸附试验表明,FMS对As5+吸附过程与Freundlich等温吸附模型拟合程度较高,相关系数(R2)达0.98,计算最大吸附容量为9.9 mg/g.⑤热力学参数ΔG、ΔH和ΔS计算表明,温度升高有利于FMS吸附砷,反应过程中FMS表面固体与溶液的混乱度上升.⑥与FMS相比,FMMS对As3+吸附性能有效提高,ρ(As3+/As5+)(As3+与As5+共存条件下溶液质量浓度)分别为2.0、4.0、6.0 mg/L下,FMMS去除率分别约提高26.34%、28.06%和28.09%.研究显示,利用铁盐浸渍法对MS改性可有效提升其对As5+和As3+的吸附容量,发挥材料的实际运用价值.      

不同载体的除砷吸附剂研究进展

在众多除砷方法中,吸附法以方便、安全、不产生二次污染、不添加大量化学试剂被广泛应用,因此制备价格低廉,吸附再生效果好,能应用于实际含砷废水处理的吸附材料尤为重要。一般的纳米金属材料极易溶于水,不易于二次分离和重复再利用,因此通过负载合适的载体来改善此问题。本文主要对矿物,树脂,碳质类,及其他吸附材料的研究进展进行综合概述,为除砷吸附剂的实际应用打下基础。     

粘土吸附剂的除铅性能及热力学研究

本文报道了粘土吸附剂自溶液中吸附铅的吸附性能及热力学性能．该吸附剂吸附铅的最佳处理条件为：用３ＭＨ２ＳＯ４振荡处理４ｈ，然后在２００℃下培烧２ｈ，该吸附为放热过程．饱和吸附量为１６．８ｍｇ／ｇ，符合Ｌａｎｇｍｕｉｒ吸附等温线，其吸附热为－６０９．６Ｊ／ｍｏｌ．     

壳聚糖海藻酸钠铁锰泥吸附剂制备与除As(V)研究

将生物除铁除锰水厂反冲洗铁锰泥包埋在壳聚糖海藻酸钠水凝胶中,成功制备了一种具有高机械强度和稳定性的复合除砷吸附剂（CAFB）.表征结果显示,其表面粗糙,铁锰元素含量为69.31%,比表面积达117.20m²/g,且具有介孔结构.吸附动力学数据更符合准二级动力学模型（R²=0.963）.Langmuir等温吸附模型能更好地描述As （V）吸附过程（R²=0.969）,25℃时最大吸附容量为15.80mg/g.酸性条件有利于As （V）的吸附,在pH=3~7范围内As （V）去除率能达到80%以上.H²PO₄^-,SiO₃^2-离子对吸附过程抑制作用明显.用0.1mol/L的NaOH溶液再生4次后吸附量能达到初始值的70.68%,具有在工程上运用的前景.     

污泥吸附剂的制备及其对含Pb2+模拟废水的吸附特性研究

以污水处理站脱水污泥和煤为原料,通过共热解法制备污泥吸附剂,并将其用于吸附含Pb2+的模拟废水.同时,考察了污泥吸附剂制备过程中热解温度、配比、热解时间、粒径对碘吸附值及产率的影响,以及吸附时间、温度、pH值、污泥吸附剂投加量对吸附效果的影响,并对其吸附动力学和热力学特性进行了探讨.结果表明,制备污泥吸附剂的最佳条件为...     

Evaluation of the adsorption potential of titanium dioxide nanoparticles for arsenic removal

The adsorption potential of titanium dioxide (TiO2) nanoparticles for removing arsenic from drinking water was evaluated. Pure and iron-doped TiO2 particles are synthesized via sol-gel method. The synthesized TiO2 nanoparticles were then immobilized on ordinary sand for adsorption studies. Adsorption isotherms were conducted on the synthesized nanoparticles as well as the sand coated with TiO2 nanoparticles under varying conditions of air and light, namely, the air-sunlight (A-SL), air-light (AL), air-dark (AD) and nitrogen-dark (ND). X-Ray diffraction (XRD) analysis showed that the pure and the iron-doped TiO2 nanoparticles were in 100% anatase crystalline phase with crystal sizes of 108 and 65 nm, respectively.Adsorption of arsenic on the three adsorbents was non-linear that could be described by the Freundlich and Langmuir adsorption models. Iron doping enhanced the adsorption capacity of TiO2 nanoparticle by arresting its grain growth and making it visible light responsive resulting in a higher affinity for arsenic. Similarly, the arsenic removal by adsorption on the sand coated with TiO2 nanoparticles was the highest among the three types of sand used. In all cases, As(V) adsorbed more compared with As(III). Solution pH appeared to be the most important factor in controlling the amount of arsenic adsorbed.     

Novel Fe/glass composite adsorbent and its property for arsenic(V) removal

An effective adsorbent for arsenic removal was synthesized by hydrothermal treatment of waste glass powder (HGP), followed by loading iron(III) oxyhydorxide on the surface of waste glass powder (GP). The ?Si-O-H group was formed on the surface of GP and the specific surface area of GP powder was slightly increased after hydrothermal treatment. FeOOH was loaded on the surface of HGP by the hydrolysis of FeCl3. The formation conditions of FeOOH were also investigated. The ability of this new adsorbent for arsenic removal was tested. The results indicate that the highest arsenic removal efficiency is about 97% for 1 mg/L As(V) solution at pH 6 and keeping time 2h.     

给水厂污泥颗粒制备及对铜离子的吸附行为

将给水厂污泥和粘土以质量比1：2制备了一种新型污泥颗粒,考察其对溶液中铜离子的吸附行为.结果发现,污泥颗粒对水中铜离子具有良好的吸附效果,对铜的吸附量随时间增加而增大,180min时可达最大吸附量的85%左右,吸附过程符合准二级吸附动力学方程;Langmuir等温吸附方程式可较好拟合不同温度时的吸附数据,且温度越高,平衡吸附量越大.多种重金属离子共存时,污泥颗粒仍优先吸附铜离子.pH值可显著影响污泥颗粒对铜离子的吸附,pH<5时,污泥颗粒对铜离子的吸附去除率随pH值升高而增大,pH=5时吸附去除效果最好.采用扫描电镜、红外光谱等对吸附铜离子前后的污泥颗粒进行表征,发现污泥颗粒表面粗糙、孔隙发达,含丰富表面基团,能够通过静电吸引、羟基取代和表面络合吸附铜离子.     

ANAMMOX颗粒污泥吸附氨氮特性及其影响因素

为了解析ANAMMOX颗粒污泥对氨氮的吸附特性及机理,分别考察了不同初始氨氮浓度和污泥浓度下的ANAMMOX颗粒污泥吸附氨氮特性,以及温度、pH、盐度和金属阳离子对氨氮吸附的影响;并采用了吸附等温式、动力学和热力学对吸附过程进行解析.结果表明,ANAMMOX颗粒污泥对氨氮的吸附在20min左右基本达到吸附平衡,吸附容量随着氨氮初始浓度的增加而增加,随ANAMMOX颗粒污泥浓度的升高而减少.低温有利于ANAMMOX颗粒污泥对氨氮的吸附,其最佳pH为7.0.盐度和金属阳离子显著影响ANAMMOX颗粒污泥对氨氮的吸附,在NaCl浓度为5g/L时,吸附作用已不明显.在质量浓度相同的条件下,Fe³⁺对吸附作用抑制最强,Mg²⁺与Ca²⁺次之,而Cu²⁺相对最弱.ANAMMOX颗粒污泥吸附氨氮过程更符合Freundlich等温式,吸附过程符合准二级动力学模型,并且是由表层扩散和内部扩散共同作用的结果.热力学研究表明,该吸附过程是一个自发的放热过程.     

聚合氯化铝污泥吸附除磷的改性研究

研究了聚合氯化铝污泥(PACS)的酸和热改性及吸附动力学理论模型.结果表明,在酸处理过程中,经0.075mol/L盐酸在20℃下改性12h后所得酸改性PACS对磷的去除率最高,可达97.0%;在热处理过程中,经300℃煅烧温度下改性1h后所得热改性PACS对磷的去除能最高可达97.8%;相同静态吸附条件下,两种改性后PACS比原PACS对磷的去除率分别提高了21.4%及22.2%;吸附动力学拟合数据显示,PACS及酸、热改性PACS对磷的吸附行为可以用Simple Elovich模型较好的进行描述(R2≥0.97).     

氢氧化铁对砷的吸附与沉淀机理

研究了吸附反应时间为50d和1120d时,As(V)初始浓度和pH值对氢氧化铁吸附砷的影响,并利用傅利叶红外光谱(FTIR)和粉末X射线衍射技术对吸附砷后的氢氧化铁固体进行了表征.结果表明,氢氧化铁对砷的吸附能力与pH有关,在弱酸性到弱碱性条件下,吸附砷的能力最强;在低初始砷浓度(0.01～1 mmol·L-1)和相同pH条件下,吸附率随砷浓度增高而增大.当pH=3、7和12时,吸附等温线都可用Freundlich公式来进行拟合,低初始砷浓度下(0.001～1 mmol·L-1),R2>0.99,高初始砷浓度下(5～1000 mmol·L-1),R2>0.93,吸附反应时间对吸附能力影响不大.红外光谱分析表明,在pH=3条件下,初始砷浓度为50mmol·L-1和500mmol·L-1时,吸附后氢氧化铁固体的红外光谱图上As-O键的伸缩振动谱带分别位于806.11cm-1和821.54cm-1;表明吸附后的氢氧化铁表面有少量的砷酸铁晶体沉淀存在,砷在氢氧化铁表面的平均密度对砷在氢氧化铁表面存在形态有影响.X射线衍射分析表明.在中性和酸性条件下,砷可能是以双配位表面络合的质子化的=FeO2As(O)(OH)-和非质子化的=FeO2As(O)2-形态存在于氢氧化铁表面.     

SBR工艺污泥颗粒化对生物脱氮除磷特性的研究

采用模拟配制的生活污水，研究循序间歇反应器（SBR）工艺的脱氮除磷效果和污泥沉降性能，试验结果表明，通过了状态调控阶段，反应器中形成了同时具有脱氮除磷能力的好氧颗粒化污泥，其中，反应器对COD和P的去除率分别为90％和85％左右；NH3－N和TN去除率分别达到90％和80％；颗粒污泥的SVI值约为50，出水水质好，这些良好的运行性能比好氧颗粒污泥形成前大大改善。     

砷(Ⅲ)离子印迹聚合物的制备及吸附性能研究

以磁性氧化石墨烯为载体,砷离子(As(Ⅲ))为模板离子,3-巯基丙基三甲氧基硅烷(MPTS)为功能单体,正硅酸乙酯(TEOS)为交联剂合成了As(Ⅲ)离子印迹磁性氧化石墨烯纳米材料(MGO-IIP),并使用扫描电子显微镜、傅里叶变换红外光谱(FTIR)、X-射线衍射仪(XRD)和振动样品磁强计对合成材料进行了表征.同时,考察了MGO-IIP对As(Ⅲ)的吸附特性.结果表明:318 K下MGO-IIP对As(Ⅲ)的最大吸附量为148.1 mg·g~(-1),仅20 min即可达到吸附平衡,印迹因子为2.35;吸附过程服从Langmuir模型和准二级动力学模型,说明是自发的吸热过程;在其他干扰离子存在的情况下,MGO-IIP对As(Ⅲ)仍然具有良好的吸附效果,且能够重复使用4次,在含砷废水处理中具有应用价值.MGO-IIP材料对As(Ⅲ)的吸附机制为表面络合作用及物理吸附.