Hybrid Composites from Waste Materials

Hybrid composites of thermoplastic biofiber reinforced with waste newspaper fiber (NF) and poplar wood flour (WF) were prepared. The weight ratio of the lignocellulosic materials to polymer was 30:70 (w:w). Polypropylene (PP) and maleic anhydride grafted polypropylene (MAPP) were also used as the polymer matrix and coupling agent, respectively. The mechanical properties, morphology and thermal properties were investigated. The obtained results showed that tensile and flexural modulus of the composites were significantly enhanced with addition of biofibers in both types (fiber and flour), as compared with pure PP. However, the increasing in WF content substantially reduced the tensile, flexural and impact modulus, but improved the thermal stability. This effect is explained by variations in fiber morphological properties and thermal degradation. Increasing fiber aspect ratio improved mechanical properties. The effect of fiber size on impact was minimal compared to the effects of fiber content. Scanning electron microscopy has shown that the composite, with coupling agent, promotes better fiber–matrix interaction. The largest improvement on the thermal stability of hybrid composites was achieved when WF was added more. In all cases, the degradation temperatures shifted to higher values after addition of MAPP. This work clearly showed that biofiber materials in both forms of fiber and flour could be effectively used as reinforcing elements in thermoplastic PP matrix.     

Rheology,Morphology, Crystallization Behaviors,Mechanical and Thermal Properties of Poly(lactic acid)/Polypropylene/Maleic Anhydride-Grafted Polypropylene Blends

The rheologies, morphologies, crystallization behaviors, mechanical and thermal properties of poly(lactic acid) (PLA)/polypropylene (PP) blends and PLA/PP/maleic anhydride-grafted PP (MAPP) blends were investigated. The results showed that the complex viscosities of PLA/PP blends were between those of neat PLA and neat PP, and MAPP had a thinning effect on those of the blends. PLA/PP blends exhibited the distinct phase separation morphologies due to the limited partial miscibility of the blend components. MAPP slightly improved the miscibility between PLA and PP. Both the cold crystallization of PLA component and melt crystallization of PP component were enhanced, probably because PLA and PP were reciprocal nucleating agents. The tensile strength and flexural modulus decreased, while the tensile strain at break and heat deflection temperature (HDT) increased with the increasing PP content. MAPP had the positive effects on the notched impact strength and HDT of PLA-rich blends and also increased the flexural modulus of the binary blends. The thermal stability of the blend was improved by PP, and the incorporation of MAPP further enhanced the thermal stability.     

Fabrication Mechanical Properties of Unidirectional Jute/PP Composites Using Jute Yarns by Film Stacking Method

This paper mainly focuses on the fabrication process of long fibre reinforced unidirectional thermoplastic composites made using both natural (untreated) treated jute yarns. Jute yarns were wound in layers onto a metallic frame. Polypropylene films were inserted between these layers and compression moulded to fabricate unidirectional jute/PP composite specimens. Static mechanical properties were evaluated from tensile three point bending tests. Pre- post-failure examination were carried out on the test specimens using optical scanning electron microscopy to analyse the test results and investigate the correlations between their impregnation state, processing conditions, mechanical performances and fracture morphologies. For the unidirectional jute/PP film-stacked composites, the results indicated that the processing condition at the moulding temperature of 160°C and moulding pressure of 2.0 MPa for 15 min was ideally suited to obtain optimized properties. Improved wettability of resin melts due to complete matrix fusion at this processing condition facilitated thorough impregnation with minimum microstructural imperfections (microvoids) being generated. Jute/PP composites that contained treated jute yarns have shown superiority in tensile bending properties. Jute yarns polished or coated with PVA/PP (polyvinyl alcohol/polypropylene) must have contributed positively to fibre/matrix interfacial interactions leading to matrix to fibre effective stress transfer, thereby improving their reinforcing effects. Tensile strength and modulus of PP resin increased by approximately 285% and 388%, respectively, due to 50 wt% reinforcement by natural jute yarns. Further improvements in strength and modulus were achieved by approximately 14% and 10%, respectively, when treated yarns were used . The maximum bending stress modulus of jute/PP composites containing untreated yarns were approximately 190% and 460% higher than those of the virgin PP materials, and bending properties were improved by further 11% and 23%, respectively, due to coating treatments on the yarn surface.     

Phosphogypsum Waste Used as Reinforcing Fillers in Polypropylene Based Composites: Structural,Mechanical and Thermal Properties

The industrial production of wet phosphoric acid in Morocco led to controversial stockpiling of waste phosphogypsum by-products resulting in the release of significant amounts of toxic impurities in salt marshes. In the framework of fighting against global climate change and efforts to reduce toxic industrial wastes (phosphate industry), this work presents a new polymer composite based on phosphogypsum (PhG) and polypropylene (PP).The compounds were produced by twin-screw extrusion and injection molding. The morphological results show that good affinity between PhG and PP led to good particle dispersion/distribution in the polymer matrix. Thermal characterizations showed that PhG particles improved the thermal stability of PP with a 50 °C increase at 40 wt%. The optimum tensile modulus was also obtained at 40 wt% with a 74 % increase over neat PP. Dynamical mechanical analysis showed that PhG addition can improve the viscoelastic properties of PP for potential applications under dynamic stress. Overall, it can be concluded that PhG is potential reinforcing filler for the production of PP composites and represents a promising avenue for the valorization of this waste as a new raw material while resolving some environmental issues.     

Utilization of Sunflower Stalk in Manufacture of Thermoplastic Composite

Dimensional stability and mechanical performance of polypropylene thermoplastic composites filled with sunflower stalk (SS) flour at 30, 40, 50, and 60 wt% contents of the SS flour were investigated. The thickness swelling and water absorption of the specimens increased with increasing SS flour content. The modulus in the flexural and tensile improved with increasing SS flour content while the tensile and flexural strengths of the specimens decreased. The use of maleic anhydride polypropylene (3 wt%) had a positive effect on the dimensional stability and mechanical properties of the polypropylene thermoplastic composites filled with SS flour. The melting temperature of polypropylene decreased with increasing content of the SS flour. The degree of crystallinity of filled polypropylene composites between fibre loading of 0–30 % by weight was higher than that of unfilled polypropylene composites. However, further increment in the filler content decreased the degree of crystallinity. The obtained results showed that SS flour could be potentially suitable raw material in the manufacture of polypropylene composites.     

Soda-Treated Sisal/Polypropylene Composites

Treated sisal fibers were used as reinforcement of polypropylene (PP) composites, with maleic anhydride-grafted PP (MAPP) as coupling agent. The composites were made by melting processing of PP with the fiber in a heated roller followed by multiple extrusions in a single-screw extruder. Injection molded specimens were produced for the characterization of the material. In order to improve the adhesion between fiber and matrix and to eliminate odorous substances, sisal fibers were treated with boiling water and with NaOH solutions at 3 and 10 wt.%. The mechanical properties of the composites were assessed by tensile, bend and impact tests. Additionally, the morphology of the composites and the adhesion at he fiber–matrix interface were analyzed by SEM. The fiber treatment led to very light and odorless materials, with yields of 95, 74 and 62 wt.% for treatments with hot water, 3 and 10 wt.% soda solution respectively. Fiber treatment caused an appreciable change in fiber characteristics, yet the mechanical properties under tensile and flexural tests were not influenced by that treatment. Only the impact strength increased in the composites with alkali-treated sisal fibers.     

Mechanical Properties and Morphology of Polypropylene/Poly(ethylene-co-octene) Blends

The polypropylene (PP)/poly(ethylene-co-octene) (POE) blends was prepared by means of a twin screw extruder in a range of temperature from 185 to 195 °C. The mechanical properties including tensile, flexural and impact of the PP/POE blends were measured at room temperature to identify the effect of the POE content on the mechanical properties. It was found that the Young’s modulus, tensile strength and tensile elongation at break decreased nonlinearly with increasing the POE weight fraction. While the V-notched and unnotched impact fracture strength increased nonlinearly with an increase of the POE weight fraction. The flexural modulus and strength decreased roughly linearly with increasing the POE weight fraction. Furthermore, the impact fracture surface of the blends was observed by using a scanning electronic microscope and the toughening mechanisms were discussed.     

Lightweight Polypropylene Composites Reinforced by Long Switchgrass Stems

Switchgrass (SG) stems with lengths up to 10 cm have been used as reinforcement to make lightweight composites with polypropylene (PP) webs. The long SG stems, with simple cut or split and without chemical treatment, were used directly in the composites. Utilizing SG stems for composites not only increases the values of SG but also provides a green, sustainable and biodegradable material for the composites industry. Lightweight composites are preferred, especially for automotive applications due to the potential saving in energy. In this research, the effects of manufacturing parameters on the properties of composites have been studied. Although the tensile properties of SG stem are significantly worse than jute fiber, SG stem with low bulk density is found to better reinforce the lightweight composites. Compared with the jute-PP composites of the same density (0.47 g/cm³), composites reinforced by the split SG stems have 56% higher flexural strength, 19% higher modulus of elasticity, 15% higher impact resistance, 63% higher Young’s modulus, 52% lower tensile strength, and similar sound absorption property. The SG-PP composites with optimized properties have the potential to be used for industrial applications such as the support layers in automotive interiors, office panels and ceiling tiles.     

Mechanical Properties of Microcrystalline Cellulose (MCC) Filled Engineering Thermoplastic Composites

In this study, engineering thermoplastic composites were prepared from microcrystalline cellulose (MCC)-filled nylon 6. MCC were added to nylon 6 using melt mixing to produce compounded pellets. The MCC-filled nylon 6 composites with varying concentrations of MCC (from 2.5 to 30 wt%) were prepared by injection molding. The tensile and flexural properties of the nylon 6 composites were increased significantly with the addition of MCC. The maximum strength and modulus of elasticity for the nylon 6 composites were achieved at a MCC weight fraction of 20 %. The Izod impact strength of composites decreased with the incorporation of MCC without any surface treatments and coupling agent. This observation is quite expected for filled polymer systems and has been commonly observed. There was a strong correlation between density and tensile (r = 0.94) and flexural modulus of elasticity (r = 0.9). MCC filled composites manufactured by injection method had highly uniform density distribution through their thickness. The higher mechanical results with lower density demonstrate that MCC can be used as a sufficient reinforcing material for low cost, eco-friendly composites in the automotive industry especially for under-the-hood applications (engine covers, intake manifolds and radiator end tanks) as well as in other applications such as the building and construction industries, packaging, consumer products etc.     

Mechanical Properties of Poly (Lactic Acid)/Hemp Fiber Composites Prepared with a Novel Method

This research dealt with a novel method of fabricating green composites with biodegradable poly (lactic acid) (PLA) and natural hemp fiber. The new preparation method was that hemp fibers were firstly blending-spun with a small amount of PLA fibers to form compound fiber pellets, and then the traditional twin-screw extruding and injection-molding method were applied for preparing the composites containing 10–40 wt% hemp fibers with PLA pellets and compound fiber pellets. This method was very effective to control the feeding and dispersing of fibers uniformly in the matrix thus much powerful for improving the mechanical properties. The tensile strength and modulus were improved by 39 and 92 %, respectively without a significant decrease in elongation at break, and the corresponding flexural strength and modulus of composites were also improved by 62 and 90 %, respectively, when the hemp fiber content was 40 wt%. The impact strength of composite with 20 wt% hemp fiber was improved nearly 68 % compared with the neat PLA. The application of the silane coupling agent promoted further the mechanical properties of composites attributed to the improvement of interaction between fiber and resin matrix.     

Effect of Thermo-Mechanical Degradation of Polypropylene on Hygroscopic Characteristics of Wood Flour-Polypropylene Composites

In this research, the influence of thermo-mechanical degradation of polypropylene (PP) on water absorption and thickness swelling of beech wood flour–PP composites were studied. For this purpose, a virgin PP was thermo-mechanically degraded by two times extrusion under controlled conditions. The results showed that the melt flow index, water absorption and thickness swelling of PP significantly increase by extrusion and re-extrusion. The virgin PP and degraded polypropylene were compounded with wood flour (at 60% by weight wood flour loading) in a counter-rotating twin-screw extruder in presence or absence of MAPP to produce wood flour–PP composites. From the results, the composites containing recycled PP exhibited higher water absorption and thickness swelling. The use of MAPP decreased water absorption and thickness swelling in composites made of virgin or recycled PP.     

Effect of High Content of Deinking Paper Sludge (DPS) on the Reinforcement of HDPE

Deinking paper sludge (DPS)/high density polyethylene (HDPE) composites with and without coupling agent (3 % of maleated polyethylene (MAPE)) were manufactured by twin-screw extrusion followed by injection molding with high percentages of DPS (0, 20, 30 and 40 %). The effects of DPS content and MAPE on the mechanical, thermal, and morphological properties of the DPS/HDPE composites were investigated. Increasing DPS content in composites increased the tensile and flexural modulus (E; MOE), tensile and flexural strength (Rm; MOR), while decreased elongation at break and Un-notched impact resistance due to a poor adhesion between the DPS and HDPE. The addition of DPS also improved the thermal stability and increased the composites crystallinity. High content of DPS (40 %) and 3 % MAPE achieved good interfacial adhesion between fibres of DPS and HDPE. Therefore, an increase is observed for Rm, MOR, ductility, and impact toughness.     

Tensile and Combustion Properties of PP/IFR/POE/nano-CaCO<Subscript>3</Subscript> Composites

The tensile and combustion properties of polypropylene/polyolyaltha olefin composites filled with intumescent flame retardant (IFR) and nanometer calcium carbonate (nano-CaCO₃) were measured. It was found that the values of the Young’s modulus of the composites increased almost linearly, while the values of the tensile yield strength and tensile fracture strength of the composites decreased with increasing the IFR weight fraction; the values of the elongation at break of the composites decreased quickly when the IFR weight fraction was lower than 10 wt%, and then varied slightly when the IFR weight fraction was higher than 10 wt%. Moreover, the morphology of the specimens after combustion was observed and the frame retardant mechanisms of the composites were discussed.     

Mechanical Properties of Kenaf/Polypropylene Nonwoven Composites

With an industrial trend of going green, the use of natural fibers in polymer composites is growing rapidly, especially in the automotive industry. The objectives of this research are to investigate mechanical performance of kenaf/polypropylene nonwoven composites (KPNCs) in production of automotive interior parts, and to develop preliminary linear models for quantifying elastic range of the KPNCs under various loading conditions. Using polypropylene (PP) fiber as bonding fiber, the KPNCs were fabricated with 50/50 blend ratio by weight. Unlike the manufacturing method of fiber reinforced plastics, all KPNCs were produced by carding and needle-punching techniques and thermally bonded by a panel press with 3-mm thickness gauge. Mechanical properties of the KPNCs in terms of uniaxial tensile, open-hole tensile, tensile at different strain rates, flexural, and in-plane shear were measured instrumentally. It was found that sample which was processed at higher temperature (230?°C) but shorter time (60?s) had the best mechanical performance. KPNCs were relatively insensitive to the notch but sensitive to strain rates. The linear elastic finite element model of KPNCs agreed well with the experimental results in the valid strain range of 0?C0.5?% for uniaxial tensile test and 0?C1?% for flexural test.     

Synthesis,Characterization and Nanocomposite Formation of Poly(glycerol succinate-co-maleate) with Nanocrystalline Cellulose

A novel biodegradable polymer based on glycerol, succinic anhydride and maleic anhydride, poly(glycerol succinate-co-maleate), poly(GlySAMA), was synthesized by melt polycondensation and tested as a matrix for composites with nanocrystalline cellulose. This glycerol-based polymer is thermally stable as a consequence of its targeted cross-linked structure. To broaden its range of properties, it was specifically formulated with nanocrystalline cellulose (NCC) at concentrations of 1, 2 and 4 wt%, and showed improved mechanical properties with NCC. Specifically, the effect of reinforcement on mechanical properties, thermal stability, structure, and biodegradability was evaluated, respectively, by tensile tests and thermogravimetric analyses, X-ray diffraction and respirometry. The neat poly(GlySAMA) polymer proved flexible, exhibiting an elongation-to-break of 8.8 % while the addition of nanowhiskers (at 4 wt%) caused tensile strength and Young’s modulus to increase, 20 and 40 %, respectively. Stiffness improved without significantly decreasing thermal stability as measured by thermogravimetric analysis. Biodegradation tests indicated that all samples were degradable but NCC reduced the rate of biodegradation.     

Synergistic Effect of Oil Palm Based Pozzolanic Materials/Oil Palm Waste on Polyester Hybrid Composite

This research work aims to investigate the synergistic effect of pozzolanic materials such as oil palm ash (OPA) and oil palm empty fruit bunch (OPEFB) on the developed hybrid polymer composites. The OPEFB and OPA fillers of different particle sizes (250, 150, and 75 µm) were mixed at OPEFB:OPA ratios of (0:100; 20:80; 40:60; 60:40; 80:20 and 100:0) and incorporated into an unsaturated polyester resin. Furthermore, both mechanical and morphological properties of the composites were analyzed and it was found that tensile, flexural, and impact properties were significantly improved at OPEFB:OPA of 75 µm particle size hybridization of the polymer. The increase of OPEFB to OPA filler ratio up to 80:20 significantly improved the tensile properties of the composites while 40:60 ratio of 75 µm gave the optimum filler ratio to obtain the highest flexural and impact properties of the composites among all studied samples. Scanning electron micrograph images showed strong particle dispersion of the embedded fillers with resin which explained the excellent mechanical strength enhancement of the composite.     

Feather Fiber Reinforced Light-Weight Composites with Good Acoustic Properties

Three to four billion pounds of chicken feathers are wasted in the United States annually. These feathers pose an environmental challenge. In order to find a commercial application of these otherwise wasted feathers, composites have been prepared from feathers. Flexural, impact resistance, and sound dampening properties of composites from chicken feather fiber (FF) and High Density Polyethylene/Polypropylene (HDPE/PP) fiber have been investigated and compared with pulverized chicken quill-HDPE/PP, and jute-HDPE/PP composites. Sound dampening by FF composites was 125% higher than jute and similar to quill although mechanical properties were inferior to the latter two. In ground form, FF and jute composite properties were similar except for 34% higher modulus of jute; under the same formulation and processing conditions, ground FF composites had nearly 50% lower mechanical properties compared with ground quill composites. It was found that voids and density of composites have effect on mechanical and sound dampening properties; however, no direct relationship was found between mechanical properties and sound dampening.     

Preparation and Characterization of Clay Nanocomposites of Plasticized Starch and Polypropylene Polymer Blends

Plasticized starch (PLS) is a renewable, degradable, and inexpensive polymer, but it suffers from poor mechanical properties. The mechanical properties can be improved by blending PLS with polyolefins, nonetheless, at high PLS content, the mechanical properties remain poor. Here we show that addition of clay can greatly improve the mechanical properties of PLS/polypropylene blends at high starch content. Unmodified and organically modified montmorillonite clays, MMT and Cloisite 30B respectively, were added to blends of glycerol-plasticized starch and polypropylene, compatibilized using maleated polypropylene. TEM indicates that MMT is well dispersed in the PLS phase of the blends, while Cloisite 30B is located both within the PLS phase as well as at the interface between PLS and PP. At high PLS content, the addition of clay increased the tensile strength and tensile modulus by an order of magnitude, while reducing the ultimate elongation only slightly. Such improvements are attributable to both the addition of clay as a reinforcing component, as well as to the change in the two phase morphology due to addition of clay.     

Mechanical, Thermal and Water Absorption Properties of Kenaf-Fiber-Based Polypropylene and Poly(Butylene Succinate) Composites

The use of composites made from non-biodegradable conventional plastic materials (e.g., polypropylene, PP) is creating global environmental concern. Biodegradable plastics such as poly(butylene succinate) (PBS) are sought after to reduce plastic waste accumulation. Unfortunately, these types of plastics are very costly; therefore, natural lignocellulosic fibers are incorporated to reduce the cost. Kenaf fibers are also incorporated into PP and PBS for reinforcing purposes and they have low densities, high specific properties and renewable sourcing. However without good compatibilization, the interfacial adhesion between the matrix and the fibers is poor due to differences in polarity between the two materials. Maleic anhydride-grafted compatibilizers may be introduced into the system to improve the matrix-fiber interactions. The overall mechanical, thermal and water absorption properties of PP and PBS composites prepared with 30 vol.% short kenaf fibers (KFs) using a twin-screw extruder were being investigated in this study. The flexural properties for both types of composites were enhanced by the addition of compatibilizer, with improvements of 56 and 16 % in flexural strength for the PP/KF and PBS/KF composites, respectively. Good matrix-fiber adhesion was also observed by scanning electron microscopy. However, the thermal stability of the PBS/KF composites was lower than that of the PP/KF composites. This result was confirmed by both DSC and TGA thermal analysis tests. The water absorption at equilibrium of a PBS composite filled with KFs is inherently lower than of a PP/KF composite because the water molecules more readily penetrate the PP composites through existing voids between the fibers and the matrix. Based on this research, it can be concluded that PBS/KF composites are good candidates for replacing PP/KF composites in applications whereby biodegradability is essential and no extreme thermal and moisture exposures are required.     

Rheological, Mechanical and Thermal Behaviour of Wood Polymer Composites Based on Recycled Polypropylene

The aim of this paper was to investigate the effect of recycled polypropylene (PP) on the rheological, mechanical and thermal properties of wood flour polypropylene composites. Beforehand, the influence of wood flour treated with a coupling agent on the rheological behaviour had been looked at. By analysing moduli and viscosity curves and studying the thermal and mechanical properties of samples with 10% filler it was possible to see that the recycled PP that was added change in either its physical properties or its rheology. In the other wood plastic composites (WPC) studied, slight changes in the rheology behaviour were observed. However, the same processing parameters may be used with and without recycled PP. Recycled PP is appropriate for these kinds of composites to maintain the optimal rheological properties that make it easier to process the material by extrusion. Furthermore, it is also possible to maintain the thermal and mechanical properties in comparison with the behaviour of virgin PP/wood flour composites.