In Vivo and In Vitro Degradation Studies for Poly(3-hydroxybutyrate-<Emphasis Type="Italic">co</Emphasis>-3-hydroxyhexanoate) Biopolymer

Studies have shown that the copolymer poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) [P(HB-co-HHx)] possesses favorable mechanical properties for use in medical supplies and products (e.g., sutures, scaffolds, bone plates). One of the major under-addressed issues associated with the use of biodegradable, bio-based PHA polymers in resorbable medical products is the correlation between the mechanical properties and the in vivo material degradation over time. In this study, P(HB-co-17 mol% HHx) matrices were mechanically tested after either incubation in cultures of human embryonic kidney cells (HEK) for in vitro degradation studies for up to 4 weeks, or inserted into Danio rerio (zebrafish) tissues for in vivo degradation studies for up to 7 weeks. The mechanical properties and scanning electron microscopy (SEM) images of the degraded materials were examined and later correlated to understand the degradation phenomenon. Our results show that Young’s modulus of P(HB-co-17 mol%HHx) during in vitro studies decreased from 3.26 to 2.42 GPa within 4 weeks, and in vivo breakdown resulted in a significant decrease in Young’s modulus with a decrease from 3.26 to 0.51 GPa and a mass loss of 59 % within 7 weeks. SEM images showed the development of pores and cracks on the surface of the material over time. Plasticization and recrystallization were observed and likely play a role in the alteration of mechanical properties.     

Anti-biofilm Activity of Solvent-Cast and Electrospun Polyhydroxyalkanoate Membranes Treated with Lysozyme

Biofilms consist of groups of microorganisms that adhere to surfaces, such as wound and implant surfaces, making it difficult to prevent or remove their formation by antibiotic treatment, due to the innate resistance of the biofilm. Effective treatments of medical biofilms are limited. Polyhydroxyalkanoate (PHA) is a biodegradable and biocompatible polymer that is a suitable alternative to petroleum based polymers for use as a raw material for medical applications. In this study, membranes of the copolymer poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) [P(HB-co-HHx)] containing different HHx monomer contents were used due to its porosity and flexibility, and different sheets were prepared by solvent-casting and electrospinning methods. The sheets were loaded with lysozyme in order to measure the maximum amount of protein adsorption and to examine the ability of immobilized enzyme to inhibit biofilm formation and detach previously established biofilms. Our results have shown maximum loading of 16.1 µg enzyme per 9.5 mm³ discs, and these sheets are effective for inhibiting biofilm formation. Also, lysozyme loaded, eletrospun sheets were observed to more effectively inhibit biofilm formation, as compared to solvent-cast sheets. Based on this study, P(HB-co-HHx) sheets are a suitable material for being used as a potential raw material for fabrication of wound dressings to be used in anti-biofilm treatments.     

Municipal Wastes Treatment and Production of Polyhydroxyalkanoate by Modified Two-Stage Batch Reactor

The municipal wastes were utilized as substrate for polyhydroxyalkanoate (PHA) using two strains of Bacillus licheniformis (PHAs-007, wild type and M2-12, mutant). Municipal wastes were subjected to separate wastewater and biosolid. Municipal biosolid was digested by anaerobic bacteria thereafter only the supernatant with soluble organic compounds was subjected into the PHA-producing reactor containing municipal wastewater. The mutant strain M2-12 gave the highest value of biomass (42.0 ± 2.0 g/L) and PHA concentration (37.4 ± 1.0 g/L with 88.9 % of dry cell weight, DCW) and reduced 76.5 % of soluble chemical oxygen demand after 60 h of cultivation. The value of pH, biochemical oxygen demand and total solid of the reclaimed wastewater after PHA recovery was 7.1, 20 and 97 mg/L, respectively. Moreover, the polymers produced by both strains of B. licheniformis were characterized. The resultant polymer from B. licheniformis PHAs-007 and M2-12 cultivated in the PHA-producing reactor was identified as poly-3-hydroxybutyrate-co-3-hydroxyvalerate [P(3HB-co-3HV)] and poly-3-hydroxybutyrate-co-4-hydroxybutyrate [P(3HB-co-4HB)], respectively. The results suggesting that the production of PHA by municipal wastes is feasible thus the PHA production stage can be integrated in waste treatment to produce PHA and treated municipal wastes at the same time.     

Adsorption of Crystal Violet Dye from Aqueous Solution by Poly(Acrylamide-<Emphasis Type="Italic">co</Emphasis>-Maleic Acid)/Montmorillonite Nanocomposite

Poly(acrylamide-co-maleic acid)/montmorillonite nanocomposites, were synthesized via in situ polymerization with different maleic acid and MMT content. The capability of the hydrogel for adsorption of crystal violet (CV) was investigated in aqueous solutions at different pH values and temperatures. The pseudo-second-order kinetics model could fit successfully the adsorption kinetic data. The effects of maleic acid to acrylamide molar ratio (MA_R), weight percent of MMT (MMT%), the pH of medium and the solution temperature (T) on the CV adsorption capacity (q _e ) of adsorbents were studied by Taguchi experimental design approach. The results indicated that increasing the MMT% leads to a greater q _e . The q _e value of adsorbents increased also with increasing both MA_R and pH, while reduced when the temperature of medium increased. The relatively optimum conditions to achieve a maximum CV adsorption capacity for P(AAm/MA)/MMT adsorbents were found as: 0.06 for MA_R and 5 % of MMT%, medium pH = 7 and T = 20 °C.     

Accumulation of poly(3-hydroxybutyric acid-co-3-hydroxyvaleric acid-co-4-hydroxyvaleric acid) by mutants and recombinant strains ofAlcaligenes eutrophus

Alcaligenes eutrophus accumulated a terpolyester of 3-hydroxybutyric acid (3HB), 3-hydroxyvaleric acid (3HV), and 4-hydroxyvaleric acid (4HV) during cultivation with 4HV as carbon and energy source under nitrogen starvation. The polyester accumulated by wild-type strains under these conditions contained 4HV at a molar fraction of approximately 5 mol% only. A catabolic pathway of 4HV was postulated, which included the activation of 4HV to 4HV-CoA and a conversion of 4HV-CoA to 3HV-CoA. Tn5::mob-induced mutants were isolated fromA. eutrophus HF39, which were affected in 4HV and/or valeric acid catabolism. Among 83 mutants were 27 4HV-negative or 4HV-leaky mutants; two mutants were identified which accumulated a terpolyester with a molar fraction of 10.1 to 22.7 mol% 4HV. In addition, a further increase in the molar fraction of 4HV in poly(3HB-co-3HV-co-4HV) and a two- to fourfold increase in the PHA synthase activity were monitored in these mutants or others and also in HF39, if the cells were complemented with the hybrid plasmid pHP1014::PP1, which contained the PHA biosynthesis genes ofA. eutrophus H16. Application of mutagenesis plus recombinant DNA techniques resulted in the accumulation of a terpolyester with up to 30 mol% 4HV and with approximately equimolar fractions of 3HB, 3HV, and 4HV.     

The mixing and segregation characteristics of rice straw in a cylindrical bubbling fluidized bed

In the present study, an experiment was performed to investigate the mixing and segregation characteristics of standard sand and rice straw particles in a cylindrical bubbling fluidized bed. The mass ratio (rice straw/standard sand = 0.5–1.25 %) of two particles and superficial gas velocity (0.13–0.18 m/s) were changed as experimental variables. The pressure drop curve and Kramer’s equation were used to determine the minimum fluidization velocity and mixing index, respectively. In all cases, the mixing index was the lowest at U/U _mf = 1.15. Based on the point of U/U _mf = 1.15, the segregation region and mixing region were observed. In the segregation region, mass ratio of 0.75 % showed the lowest mixing index. At the U/U _mf = 1.23 which was selected as the starting of fast pyrolysis considering residence time and the previous fast pyrolysis experiment, mass ratio of 1.25 % showed the highest mixing index which was 0.90.     

Water Absorption Kinetics and Hygrothermal Aging of Poly(lactic acid) Containing Halloysite Nanoclay and Maleated Rubber

Poly(lactic acid)/halloysite nanoclay composites (PLA/HNC) containing maleic anhydride grafted styrene-ethylene/butylene-styrene (SEBS-g-MAH) were produced using melt compounding followed by compression molding. The effects of hygrothermal aging on the thermal properties and functional groups changes of the HNC reinforced PLA (with and without SEBS-g-MAH) at three different temperatures (i.e., 30, 40 and 50 °C) were analyzed using differential scanning calorimetry and Fourier transform infrared spectroscopy techniques. The diffusion coefficient (D) of PLA was decreased by the incorporation of HNC and SEBS-g-MAH. The activation energy of water diffusion (E _a ) of PLA/HNC/SEBS-g-MAH nanocomposites was higher than that of pure PLA. The glass transition temperature (T _g ), cold-crystallization temperature (T _cc ) and melting temperature (T _m ) of the PLA sample were shifted to lower temperature and the effect was more pronounced at 50 °C. The carbonyl index values of all PLA samples increased after immersed in 40 and 50 °C, which is due to the formation of higher amount of carboxyl groups during the hydrolysis process.     

The Influence of Artificial Photodegradation on Properties of Poly(3-hydroxybutyrate-<Emphasis Type="Italic">co</Emphasis>-3-hydroxyvalerate)(PHBV)/Graphite Nanosheets (GNS) Nanocomposites

The potential use of poly(3-hydroxybutyrate-co-3-hydroxyvalerate)/graphite nanosheets (GNS) as a biodegradable nanocomposite has been explored. PHBV/GNS nanocomposites films were prepared by solution casting at various concentrations of GNS—0.25, 0.50 and 1.00 wt% GNS. The films were exposed to artificial ultraviolet radiation (UV) during 52 h. The effect of GNS on PHBV photodegradation was investigated and compared to neat PHBV film. The artificial photodegradation induced changes in physical (weight loss), chemical carbonyl index by Fourier transform infrared spectroscopy, thermal degree of crystallinity and melting temperature by differential scanning calorimetry and morphological scanning electron microscopy characteristics. Based on the results obtained from aforementioned analyzes it was verified that GNS inhibits the oxidative degradation of PHBV matrix.     

Biosynthesis and Characterization of Poly-(3-hydroxybutyrate-co-3-hydroxyvalerate) from Bacillus cereus S10

The biodegradable and biocompatible copolymer poly-(3-hydroxybutyrate-co-5 mol% 3-hydroxyvalerate), poly-(3HB-co-5 mol% 3HV), was synthesized by Bacillus cereus S10 and the highest yield was determined as 69.91 % at pH 7 and 30 °C after 48 h of incubation using a glucose as the sole carbon source. Poly-(3HB-co-5 mol% 3HV) was purified from bacterial biomass using chloroform. FTIR analysis showed absorption bands at 1,723, 1,274, 1,373, 1,453, 2,932 cm^?1 corresponding to C=O, C–O stretching, CH₃, –CH₂ and –CH groups, respectively. ¹H-NMR and ¹³C-NMR analysis confirmed that the copolymer was composed of 95 mol% of 3-hydroxybutrate and 5 mol% of 3-HV monomeric units. Poly-(3-HB-co-5 mol% 3HV) was used for nanoparticles preparation. The diameter of nanoparticles was 202 nm.     

Adsorptive Removal of Malachite Green Chloride and Reactive Red-198 from Aqueous Solutions by Using Multiwall Carbon Nanotubes-Graft-Poly (2-acrylamido-2-methyl-1-propanesulfonic acid)

The multiwall carbon nanotubes (MWCNTs) were modified by 2-acrylamido-2-methyl-1-propanesulfonic acid (AMPS) via grafting reaction and γ-rays of ⁶⁰Co source was used as initiator. The outcome product was called hydroxyethylated (HOEt-MWCNTs) graft poly(AMPS) and abbreviated as HOEt-MWCNTs-g-PAMPS. The parameters that affected the grafting yield were optimized. The maximum grafting obtained was ~20 %. HOEt-MWCNTs-g-PAMPS were characterized by Fourier transform infra red, scanning electron microscopy, high resolution transmission electron microscopy, thermal gravimetric analysis. The adsorptive removals of malachite green chloride (MGC) and reactive red 198 (RR-198) onto HOEt-MWCNTs-g-PAMPS were studied at variable conditions. The adsorption isotherms were analyzed using Langmuir, Redlich–Peterson, Freundlich, Khan and Sips models. The results referred that Sips model is the best fitting to adsorption of MGC and Freundlich model is the best fitting to RR-198 adsorption. The monolayer coverage capacities of HOEt-MWCNTs-g-PAMPS for MGC and RR-198 dyes were found 172 and 323 mg g^?1, respectively. The rate of kinetic adsorption processes of MGC and RR-198 onto HOEt-MWCNTs-g-PAMPS were described by using pseudo-first order, pseudo-second order and intraparticle diffusion models. The pseudo-first order and pseudo-second order models were the best choice among the kinetic models to depict the adsorption behaviors of MGC and RR-198 dyes onto HOEt-MWCNTs-g-PAMPS, respectively. Further, the effect of temperature on the adsorption isotherms was investigated and the thermodynamic parameters were obtained. The results indicated that the adsorption process is spontaneous and endothermic. The values of ΔG° varied in range with the mean values showing a gradual increase from ?3.17 to ?3.64 kJ mol^?1 for MGC and ?3.36 to ?3.73 kJ mol^?1 for RR-198. The reusability and regeneration of adsorbent were investigated. The outcome data referred to that the efficiency of adsorbent >98 %. The outline results declared that there is a good potentiality for the HOEt-MWCNTs-g-PAMPS to be used as an adsorbent for the removal of MGC and RR-198 from aqueous solutions.     

Distribution of inorganic bromine and metals during co-combustion of polycarbonate (BrPC) and high-impact polystyrene (BrHIPS) wastes containing brominated flame retardants (BFRs) with metallurgical dust

This study focused on the thermal degradation of polycarbonate (BrPC) and high-impact polystyrene (BrHIPS), containing different brominated flame retardants. The evolved inorganic bromine was utilized for the separation of metals present in electric arc furnace dust (EAFD). The thermal degradation of BrPC generated inorganic gaseous HBr (69%) and condensable Br₂ (31%). The bromine evolved from BrHIPS was detected almost entirely in a condensed phase as SbBr₃. When mixed with EAFD, the evolved inorganic bromine reacted immediately with the metallic components of zinc and lead, but not with iron. The best bromination efficiencies were obtained during the isothermal heating (80 min at 550 °C) of the mixtures at mass ratios of 6:1 and 9:1 w/w under oxidizing conditions. The achieved brominating rates reached 78 and 81% for zinc and 90 and 94% for lead in 6:1 and 9:1 BrPC:EAFD, respectively, and 47 and 65% for zinc and 67 and 63% for lead in 6:1 and 9:1 BrHIPS:EAFD, respectively. The oxidizing condition favored complete vaporization of the formed bromides.     

Comparison of three ornamental plants for phytoextraction potential of chromium removal from tannery sludge

Based on pre-experimentation, three ornamental plants, Mirabilis jalapa, Impatiens Balsamin (I. Balsamin) and Tagetes erecta L., were selected as target plants to study the phytoextraction of chromium (Cr) in tannery sludge irrigated with four treatments according to Cr concentration gradient [Control (CK); 20.50 × 10³ mg kg^?1 (T1); 51.25 × 10³ mg kg^?1 (T2); 102.50 × 10³ mg kg^?1 (T3)]. Results of pot experiments showed that the biomass of Mirabilis jalapa and Tagetes erecta L. had no significant differences among the four treatments, while I. Balsamin showed a decline trend in the biomass with the increase of Cr concentration, probably due to some extent to the poisoning effect of Cr under treatment T2 or T3. Mirabilis jalapa accumulated Cr concentration, with 408.97, 124.97, 630.16 and 57.30 mg kg^?1 in its roots, stems, leaves and inflorescence, respectively. The translocation factor and the bioaccumulation coefficient of Mirabilis jalapa are each greater than 1, indicating that Mirabilis jalapa has the strong ability to tolerate and enrich Cr by biological processes. Comparing accumulation properties of the three ornamental plants, in the amount and allocation, Mirabilis jalapa showed the highest phytoextraction efficiency and could grow well at the high Cr concentration. Our experiments suggest that Mirabilis jalapa is the expected flower species for Cr removal from tannery sludge.     

Application of ameliorated wood pulp to recover Cd(II), Pb(II), and Ni(II) from e-waste

In this study, dl-malic acid and hydrogen peroxide were used as leaching agents to remove metals from e-waste (printed-circuit boards) and itaconic acid-grafted poly(vinyl alcohol)-encapsulated wood pulp (IA-g-PVA-en-WP) to uptake metals from leachate with high proficiency [11.63 mg g^?1; 93.03 % for Cd(II), 11.90 mg g^?1; 95.18 % for Pb(II), and 12.14 mg g^?1; 97.08 % for Ni(II)]. Metals were recovered from the loaded biosorbent by desorption studies. The standard analytical techniques, such as elemental analysis, Fourier-transform-infrared spectroscopy, scanning electron microscopy, atomic force microscopy, and thermogravimetric analysis, were used to characterize the recovering agent (biosorbent). At equilibrium, the metal uptake data were fitted to Langmuir and D–R isotherms (R ² > 0.99) significantly, revealing, the homogeneous distribution of active sites on biosorbent’s backbone. The possible mechanism appeared to be ion exchanges of metal ions with H⁺ together with binding over functionalities (COO^?). Dimensionless equilibrium parameter (R _L) showed the favourability of metal uptake at lower concentration, while mean adsorption energy (E) certified the physical binding of metal on functionalities which was further confirmed by sticking probability and activation energy parameters. Reusability studies were also conducted to state the performance of biosorbent.     

Polyvinyl Alcohol (PVA)/Starch Bioactive Packaging Film Enriched with Antioxidants from Spent Coffee Ground and Citric Acid

The bioactive packaging polyvinyl alcohol (PVA)/starch films were prepared by incorporating combined antioxidant agents i.e. extracted spent coffee ground (ex-SCG) and citric acid. Effect of citric acid content on chemical compatibility, releasing of antioxidant, antibacterial activities, and physical and mechanical properties of PVA/starch incorporated ex-SCG (PSt-E) films was studied. The results of ATR-FTIR spectra showed that antioxidant agents of ex-SCG can penetrate into the film and the ester bond of blended films by citric acid was also observed. The presence of ex-SCG increased efficiency of antioxidant release and antimicrobial activity. The PSt-E film incorporated 30 wt% citric acid showed minimum inhibitory concentration against Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus). The incorporation of ex-SCG and citric acid into film showed a synergistic effect on antibacterial activity. The water resistance and kinetic moisture sorption improved with incorporation of citric acid. The tensile strength and biodegradability of samples were in range of 5.63–7.44 MPa and 65.28–86.64%, respectively. Based on this study, PSt-E film incorporated 30 wt% citric acid can be applied as novel food packaging materials.     

New Poly(aniline-<Emphasis Type="Italic">co</Emphasis>-<Emphasis Type="Italic">o</Emphasis>-phenylenediamine)/Kaolinite Microcomposites for Water Decontamination

Copolymers of aniline and o-phenylenediamine/kaolinite composites were synthesized by 5:1 molar ratios of the respective monomers with different percentages of nanoclay via modified in situ chemical co-polymerization. The results were verified by measuring the FT-IR and UV–vis absorption spectra for PANI-o-PDA/kaolinite composites. The thermal behaviour of the copolymer and composites was studied. PANI-o-PDA/kaolinite composites were thermally more stable than pure copolymer. Surface morphology of copolymer composites was recorded at different magnification power by SEM which revealed whitish micrometric beads distributed all over the field with particle size in the range of 0.122–0.233 μm. This work demonstrates that the PANI-o-PDA/kaolinite composites particles can be considered as potential adsorbents for hazardous and toxic metal ions of water from lake El-Manzala, Egypt. All of Cd(II), Cu(II), and Pb(II) posed dangerous health risk to the local population via fish consumption.     

Adsorption Efficiency of Polyaspartate-Montmorillonite Composite Towards the Removal of Pb(II) and Cd(II) from Aqueous Solution

The selective modification of sodium montmorillonite (Na⁺-Mt) surface with polyionene followed by poly (succinimde-co-aspartate) has been considered. Na⁺-Mt was allowed to react with well characterized polyionene in two fold excess. The resulting polyionene/Mt (IC) was further modified with poly (succinimide-co-aspartate) through an ion exchange process. The obtained polyaspartate/Mt (IPS) composite was characterized by elemental analysis, X-ray diffraction, FTIR spectroscopy, thermogravimetric analysis (TGA), scanning electron microscopy (SEM), and BET surface analyzer. The adsorption efficiency of IPS composite was investigated for the removal of Pb(II) and Cd(II) from aqueous solution under different experimental conditions including initial metal ions concentration, temperature and single and binary mixture systems of metal ions. The experimental data were analyzed by Langmuir, Freundlich, Temkin, and Dubinin-Radushkevich models. Langmuir model reveals that the monolayer adsorption capacity of IPS was 92.59 and 67.57 mg/g for Pb(II) and Cd(II), respectively. The modification of parent Na⁺-Mt enhanced their adsorption capacity by about 87.91 and 29.84% for Pb(II) and Cd(II), respectively, due to inclusion of extra active sites of polyaspartate. The mean sorption energy, E calculated from Dubinin–Radushkevich isotherm were 2.75 and 1.98 kJ/mol for the adsorption of Pb(II) and Cd(II), respectively, indicating physical adsorption process. Also, The thermodynamic parameters were calculated and indicated that the adsorption was spontaneous and exothermic process. The mechanism of cation exchange and complexation of metal ions was suggested. IPS composite has a considerable potential for the removal of heavy metal ions from aqueous solution and wastewater stream.     

Selective Lead(II) Adsorption and Flocculation Characteristics of the Grafted Sodium Alginate: A Comparative Study

Synthesis of sodium alginate-g-poly(acrylamide-co-N-methylacrylamide) [S-III], sodium alginate-g-poly(N-methylacrylamide-co-N,N-dimethylacrylamide) [S-II], sodium alginate-g-poly(acrylamide-co-N,N-dimethylacrylamide) [S-I]. Sodium alginate-g-poly(N,N-dimethylacrylamide) [SAG-g-PDMA] and sodium alginate-g-poly(acrylamide) [SAG-g-PAM] were prepared by solution polymerization technique using potassium peroxydisulfate as the initiator at 70?°C in water medium. The graft copolymers were characterized by FTIR and NMR (¹H and ¹³C) spectroscopy, SEM and XRD studies. All the five graft copolymers were used to remove Pb(II) ions from the aqueous solution and also in flocculation studies of kaolin clay (1.0 wt%), silica (1.0 wt%) and iron ore slime (0.25 wt%) suspensions. A comparative studies of all the five graft copolymers were also made in both the two cases. The Pb(II) ion removal capacity of all the graft copolymers follows the order S-III?>?SAG-g-PAM?>?S-II?>?SAG-g-PDMA?>?S-I. But the flocculation performance of the graft copolymers follows the order S-II?>?S-I?>?S-III?>?SAG-g-PDMA?>?SAG-g-PAM. S-III was also used for the competitive metal ion removal with Hg(II), Cd(II), Cu(II) and Zn(II). Pb(II) adsorption of S-III (the best Pb(II) ion adsorber) follows pseudo second order rate equation and Langmuir adsorption isotherm.     

Optimization of Carbon Dioxide and Valeric Acid Utilization for Polyhydroxyalkanoates Synthesis by Cupriavidus necator

The utilization of captured CO₂ as a part of the CO₂ capture and storage system to produce biopolymers could address current environmental issues such as global warming and depletion of resources. In this study, the effect of feeding strategies of CO₂ and valeric acid on cell growth and synthesis of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) [P(3HB-co-3HV)] in Cupriavidus necator was investigated to determine the optimal conditions for microbial growth and biopolymer accumulation. Among the studied CO₂ concentrations (1–20 %), microbial growth and poly(3-hydroxybutyrate) accumulation were optimal at 1 % CO₂ using a gas mixture at H₂:O₂:N₂ = 7:1:91 % (v/v). When valeric acid was fed together with 1 % CO₂, (R)-3-hydroxyvalerate synthesis increased with increasing valeric acid concentration up to 0.1 %, but (R)-3-hydroxybutyrate synthesis was inhibited at >0.05 % valeric acid. Sequential addition of valeric acid (0.05 % at Day 0 followed by 0.025 % at Day 2) showed an increase in 3HV fraction without inhibitory effects on 3HB synthesis during 4 d accumulation period. The resulting P(3HB-co-3HV) with 17–32 mol  % of 3HV is likely to be biocompatible. The optimal concentrations and feeding strategies of CO₂ and valeric acid determined in this study for microbial P(3HB-co-3HV) synthesis can be used to produce biocompatible P(3HB-co-3HV).     

Molecular Structure and Crystallization Dynamics of Poly(3-hydroxyl alkanoate) with Medium-Chain Length Biosynthesized from <Emphasis Type="Italic">Pseudomonas putida</Emphasis>

The molecular structure of poly(3-hydroxyalkanoate) (P3HA) with medium-chain length, biosynthesized from Psuedomonas putida (P. putida), was investigated by thermal analysis, X-ray diffraction, and infrared spectrum. Cultivation in a medium of nonanoic acid and a mixed substrate of nonanoic acid and glycerin as carbon sources provided P3HA with monomer units of 7 and 9 carbons (P3HA_n) and 5, 6, 7, 8, 9, and 10 carbons (P3HA_mix). Since these P3HA has comparatively long side chains, the crystallinity was as low as about 10%. It was suggested that the hydrogen bonding plays an important role in constructing the crystal. The lamellar thickness was 1.20 nm, estimated from the melting temperature depression. This lamellar thickness corresponds to two repeating units. Crystallinity depending on time was observed by the CO stretching mode in the infrared spectrum, and then Avrami’s theory was applied to analyze the crystallization mechanism. The crystallization rate of P3HA_n was very low, on the order of a few hours. An Avrami exponent of 1.45 was estimated from the slope of the Avrami plot. This shows that the conformational arrangement is presumably promoted along the chain axis. The slow crystallization is attributed to the long side chain, which prevents aggregation of the polymer chains.     

Degradation of Poly(3-hydroxybutyrate) and Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) by Some Soil Aspergillus spp.

Systematic screening of 45 soil fungi for degradation polyhydroxyalkanoic acids (PHAs) has led to the selection of 6 potent Aspergillus isolates belonging to A. flavus, A. oryzae, A. parasiticus, and A. racemosus. Degradation of PHAs as determined by tube assay method revealed that these Aspergillus spp. were more efficient in degrading poly(3-hydroxybutyrate) [P(3HB)] compared to copolymer of 3-hydroxybutyric acid and 3-hydroxyvaleric acid (P3HB-co-16% 3HV). Moreover, the extent of degradation in mineral base medium was much better than those in complex organic medium. For all the Aspergillus spp. tested, maximum degradation was recorded at a temperature of 37°C with significant inhibition of growth. The optimum pH range for degradation was 6.5–7.0 with degradation being maximum at pH 6.8. The extent of polymer degradation increased with increase in substrate concentration, the optimum concentration for most of the cultures being 0.4% and 0.2% (w/v) for P(3HB) and P(3HB-co-16%3HV) respectively. Supplementation of the degradation medium with additional carbon sources exerted significant inhibitory effect on both P(3HB) and P(3HB-co-16%3HV) degradation.