CuO-Ru/A_2lO_3催化臭氧化降解苯乙酮的研究

采用浸渍法制备了以活性Al2O3为载体的双组分催化剂CuO-Ru/Al2O3,利用该催化剂催化臭氧化降解了苯乙酮.结果表明,贵金属钌掺杂能显著提高CuO/Al2O3催化臭氧化苯乙酮的降解效率,如在相同条件下处理30 min后,单独臭氧氧化、CuO/Al2O3/O3和CuO-Ru/Al2O3/O3对苯乙酮水溶液的COD去除率分别为6.3%、20.0%和54.0%.pH对CuO-Ru/Al2O3催化臭氧化降解苯乙酮的效率并没有影响,但与单独臭氧化相比,该催化臭氧化体系更适合在中性或酸性条件下应用.CuO-Ru/Al2O3对水中臭氧有较好的催化分解活性,臭氧分解的速率常数达2.58×10-3s-1,高于二次水中臭氧的分解速率常数1.19×10-3s-1.叔丁醇的试验结果表明,CuO-Ru/Al2O3/O3降解苯乙酮反应遵循羟基自由基(.OH)反应机制.     

CuO-Ru/Al2O3 催化臭氧化降解苯乙酮的研究

采用浸渍法制备了以活性Al2O3为载体的双组分催化剂CuO-Ru/Al2O3,利用该催化剂催化臭氧化降解了苯乙酮.结果表明,贵金属钌掺杂能显著提高CuO/Al2O3催化臭氧化苯乙酮的降解效率,如在相同条件下处理30 min后,单独臭氧氧化、CuO/Al2O3/O3和CuO-Ru/Al2O3/O3对苯乙酮水溶液的COD去除率分别为6.3%、20.0%和54.0%.pH对CuO-Ru/Al2O3催化臭氧化降解苯乙酮的效率并没有影响,但与单独臭氧化相比,该催化臭氧化体系更适合在中性或酸性条件下应用.CuO-Ru/Al2O3对水中臭氧有较好的催化分解活性,臭氧分解的速率常数达2.58×10-3s-1,高于二次水中臭氧的分解速率常数1.19×10-3s-1.叔丁醇的试验结果表明,CuO-Ru/Al2O3/O3降解苯乙酮反应遵循羟基自由基(.OH)反应机制.     

催化湿式氧化工艺中负载型催化剂的研制

研究了过渡金属氧化物和稀土金属氧化物对乳化液废水催化湿式氧化工艺中的催化活性，得出：CuO的活性高于MnO2,Co3O4未表现出催化活性。CeO2、Nd2O3、Sm2O3均表现一定活性：制备了CuO／γAl2O3，Mn／γAl2O3负载型催化剂及其复合负载型催化剂，并对它们各自的催化活性和稳定性进行了研究。发现：Cu／γAl2O3负载型催化剂用于乳化液废水处理，200℃反应2h，CODCr去除率为88．4％，达到均相催化效果，比非催化提高13.0％，Mn／γAl2O3表现出负催化作用．复合负载型催化剂的活性低于Cu／γAl2O3。     

天然沸石负载WO_3-TiO_2复合半导体的光催化臭氧氧化性能

采用溶胶-凝胶-浸渍-焙烧法制备了负载型纳米复合半导体WO3-Ti O2/Zeolite催化剂。以偶氮染料亚甲基蓝为目标降解物,通过光催化臭氧氧化法讨论了污染物初始浓度,溶液的pH,催化剂用量等因素对催化剂光催化臭氧氧化的影响。结果表明,当亚甲基蓝初始浓度为1 400 mg/L,溶液pH=5,通氧量为2 L/min,催化剂用量为5 g/L时催化剂氧化污染物活性最好,1 h后亚甲基蓝的降解率可达99.81%。     

O_3催化氧化深度处理兰炭废水的试验研究

采用O3催化氧化法深度处理兰炭废水,提出了兰炭废水达标排放的新处理方法。以铜为活性组分,氧化铝为载体采用浸渍法制备CuO/γ-Al2O3催化剂,并采用XRD对其进行表征,利用催化剂结合O3催化氧化法去除兰炭废水中经生化处理后残留的污染物。设计了催化氧化试验装置,考察了催化剂投加量、反应时间、O3用量以及pH等因素对处理效果的影响。实验结果表明,pH在酸性条件下有利于COD去除率的提高,O3用量提高有助于COD去除率的提高,将催化剂用量和反应时间控制在一定范围内有利于污染物的去除;最佳条件下催化剂投加量300 g,反应时间1 h,O3用量0.08 m3/h,pH为7左右时COD去除率可达到95%左右。另外,催化剂在20次反应过程中表现出较高的催化活性及较强的稳定性。     

治理催化超临界水氧化处理1,5-萘二磺酸

采用Mn2O3γAl2O3和V2O5γAl2O3为催化剂,在一连续流固定床反应器中进行了超临界水氧化1,5萘二磺酸实验。实验结果表明,在380～440℃,24MPa条件下,Mn2O3γAl2O3和V2O5γAl2O3催化剂对1,5萘二磺酸的氧化降解具有显著的促进作用,TOC去除率达到90%以上;催化剂的催化效果随反应温度的升高而增强,随pH值的降低而增强,随停留时间的延长先增强后趋于平缓。     

纳米TiO2/沸石/UV催化臭氧化水中硝基苯的研究

设计了O3/纳米TiO2/沸石（体系A）和O3/纳米TiO2/沸石/UV（体系B）2种催化臭氧化体系并将其用于处理水中的硝基苯,研究了影响处理效果的主要因素,并对2种方法进行了比较。结果表明,2种催化臭氧化体系都能产生大量的羟自由基,加速硝基苯的降解,其中体系B对硝基苯的降解效果最好。随着进气流量的增加、温度的升高硝基苯的降解速率都会加快。催化臭氧化反应速率遵循一级反应规律,与苯酚的初始浓度和催化剂的用量关系不大。pH值对苯酚去除率有重要的影响,随pH值的升高,苯酚去除率显著提高。叔丁醇对硝基苯的降解有很强的抑制作用。     

超声气升式环流反应器降解乐果水溶液的动力学研究

采用超声气升式环流反应器(UALR),以臭氧气体为氧化剂,以有机磷农药乐果为典型污染物,研究其降解反应动力学规律.通过对乐果降解过程的表观动力学研究,发现乐果在单独超声辐射(不通入气体,即臭氧)、臭氧(O3)氧化和超声气升式环流反应器(UALR/O2)协同下的降解均符合表观一级动力学.在乐果初始质量浓度为50 mg/L、溶液初始pH为6.0、反应液体积80 mL、超声声强0.5W/cm2、O3流量200 L/h、温度20℃、处理时间4h的条件下,采用超声(US)、O3和UALR/O3工艺,乐果的去除率分别为27%、15%和90%,乐果降解的速率常数增强因子可达到4.816.进一步从UALR/O3系统中存在US、O3和羟基自由基(·OH)协同作用的降解机理,推导出了简化的机理动力学模型.     

O_3/Mn_2O_3对钻井废水多相催化臭氧化试验研究

通过静态试验,探讨了Mn2O3催化剂对钻井废水催化臭氧化处理效果.分别考察了催化剂加量、pH值、反应时间、反应温度和强化剂对钻井废水COD去除率的影响,通过正交试验得到了最佳工艺条件,对钻井废水氧化过程中的产物进行了分析,并探讨了Mn2O3催化剂的稳定性能.结果表明:Mn2O3加量从25 mg·L-1增加到50 mg·L-1时,COD去除率由43.6%增加到54.3%;pH分别为5、11时,COD去除率分别为45.4%和64.3%;反应温度为20℃时,COD去除率最高达到59.1%;随着反应时间的延长,COD去除率也随之增加,反应时间为40 min时,COD去除率达到85.3%;由正交试验得知影响因素的主次关系为催化剂加量反应pH反应温度反应时间,最佳处理工艺条件为催化剂加量50mg·L-1、pH值11,反应温度25℃、反应时间35 min;在25 min时,Ca2+的引入使COD去除率增大了7.1%;钻井废水中的有机物得到降解和矿化;Mn2O3催化剂重复使用10次后,对钻井废水COD降解率影响不大,锰离子的溶出量在反应15 min后稳定在3 mg·L-1,Mn2O3催化剂稳定性能较好.     

化学工业废物处理与综合利用

X780.31200603018Al2O3催化臭氧化处理邻苯二甲酸二甲酯/周云瑞…(清华大学环境科学与工程系)∥环境科学/中科院生态环境研究中心.-2006,27(1).-51~56环图X-5Al2O3催化剂对邻苯二甲酸二甲酯(DMP)溶液臭氧化过程的影响结果表明:Al2O3可以显著提高臭氧氧化的效果,反应120min后,TOC的去除率从单独臭氧氧化的23.9%提高到55.1%。实验中还考察了制备条件对Al2O3催化剂活性的影响并确定了反应的最佳工艺条件。在实验考察的范围内:焙烧温度600℃,Al2O3粒径为0.5~1.0mm时催化活性最高;最佳反应工艺条件为:催化剂投加量20g/L,混和气体流速200m…     

Treatment of phenol wastewater by microwave-induced ClO2-CuOx/Al2O3 catalytic oxidation process

The catalyst of CuOx/Al2O3 was prepared by the dipping-sedimentation method using γ-Al2O3 as a carrier. CuO and Cu2O were loaded on the surface of γ-Al2O3, characterized by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). In the presence of CuOx/Al2O3, the microwave-induced chlorine dioxide (ClO2) catalytic oxidation process was conducted for the treatment of synthetic wastewater containing 100 mg/L phenol. The relationships between removal percentage and initial ClO2 concentration, catalyst dosage, microwave power, contact time, initial phenol concentration and pH were investigated and the results showed that microwave-induced ClO2-CuOx/Al2O3 process could effectively degrade contaminants in a short reaction time with a low oxidant dosage, extensive pH range. Under a given condition (ClO2 concentration 80 mg/L, microwave power 50 W, contact time 5 min, catalyst dosage 50 g/L, pH 9), phenol removal percentage approached 92.24%, corresponding to 79.13% of CODCr removal. The removal of phenol by microwave-induced ClO2-CuOx/Al2O3 catalytic oxidation process was a complicated non-homogeneous solid/water reaction, which fitted pseudo-first-order by kinetics. Compared with traditional ClO2 oxidation, ClO2 catalytic oxidation and microwave-induced ClO2 oxidation, microwave-induced ClO2 catalytic oxidation system could significantly enhance the degradation efficiency. It provides an effective technology for the removal of phenol wastewater.     

粉煤灰基催化臭氧处理亚甲基蓝催化剂的制备

以粉煤灰作为载体,用等体积浸渍法负载NiO,CuO,Fe2O3等不同的活性组分,制备出不同单组分和双组分的催化剂,从中选择出最佳的催化剂为NiO/粉煤灰。通过正交试验确定制备NiO/粉煤灰催化剂的最佳条件为:负载量为1wt%,浸渍时间为15 h,煅烧温度为300℃,煅烧时间为2 h。将NiO/粉煤灰催化剂投加到臭氧氧化处理亚甲基蓝模拟废水体系中,处理效果有显著的提高,去除率由单独臭氧处理的88.04%提高到99.12%。     

油田作业废水臭氧化处理技术的实验研究

针对油田作业废水(COD)高、难降解的特点,探讨了废水的pH、COD初始浓度、臭氧投加量和臭氧化时间等因素对油田作业废水的COD去除效果的影响。结果表明,臭氧化对油田作业废水COD去除效果影响的主要因素为废水pH、废水的COD和臭氧投加量;当废水的COD为1064.0mg/L、pH为3.0、臭氧投加量为10g/L时,废水的COD去除率达到69.1%;臭氧化处理对低浓度油田作业废水的COD去除效果低于其对高浓度废水的处理效果。     

催化湿式氧化处理造纸废水的研究

以过渡金属氧化物CuO为活性组分,采用催化湿式氧化法处理造纸废水,考察Cu负载量、催化剂用量、反应温度对废水COD去除率的影响。结果表明:固定氧气分压在2.5MPa和反应时间3h,催化剂用量为3g,Cu负载量为4%,反应温度为220℃,500mL浓度为3250mg/L造纸废水的COD去除率为90%,色度去除率为89%,pH值由9.6变为7.8。另外,对催化剂进行再生处理和稳定性测试。结果表明:450℃下活化3h,在上述相同反应条件下,对原废水的COD去除率降低为88%,重复使用9次后对废水的COD去除率仍能保持在85%左右。     

铈掺杂Ru/Al2O3催化臭氧氧化降解邻苯二甲酸二甲酯

考察了铈(Ce)的掺杂对Ru/Al2O3催化臭氧氧化邻苯二甲酸二甲酯(DMP)溶液过程的影响.结果表明,Ce的掺杂可以显著提高臭氧氧化的效果,反应100min后,TOC的去除率可以由原催化剂的61.3%提高到75.1%,而单独臭氧氧化仅有14.0%.在实验范围内,Ru和Ce同时浸渍催化效果较好,且活性组分的溶出最少,Ce的最佳掺杂量为1.0%.通过催化剂吸附试验、单独臭氧氧化试验、Ce的均相催化试验及Ru-Se/Al2O3催化剂的非均相催化实验,证明Ru-Ce/Al2O3催化剂对DMP溶液臭氧氧化体系TOC的去除率达到50%,这是基于Ru-Ce/A12O3催化剂的非均相催化作用.     

[Cu—γ—Al2O3]催化剂处理染料废水工艺条件研究

采用「Ｃｕ－γ－Ａｌ２Ｏ３」催化剂对由活性艳红Ｘ－３Ｂ配制的ＣＯＤｃｒ为５７００ｍｇ／Ｌ色度３１００倍的实际染料废水进行了催化氧化试验，试验表明，在控制ｐＨ＝４－５，Ｈ２Ｏ２用量为５．０ｍｇ／Ｌ，催化剂用量为３．０ｇ／Ｌ，ｔ＝７０℃和反应时间为２ｈ条件下，可获得ＣＯＤｃｒ去除率为７７％－７８％，脱色率为９９％的良好效果，且催化剂可再生使用。     

Al2O3催化臭氧化处理邻苯二甲酸二甲酯

'Al₂O₃催化剂对邻苯二甲酸二甲酯(DMP)溶液臭氧化过程的影响结果表明:Al₂O₃可以显著提高臭氧氧化的效果,反应120min后,TOC的去除率从单独臭氧氧化的23.9%提高到55.1%.实验中还考察了制备条件对Al₂O₃催化剂活性的影响并确定了反应的最佳工艺条件.在实验考察的范围内:焙烧温度600℃,Al₂O₃粒径为0.5～1.0mm时催化活性最高;最佳反应工艺条件为:催化剂投加量20g/L,混和气体流速200mL/min,反应温度15℃.通过单独臭氧氧化,单独臭氧氧化后再进行催化剂吸附,催化臭氧化的对比实验证明了Al₂O₃催化剂对体系TOC的去除主要是基于催化作用.     

微波耦合类Fenton处理水中对硝基苯酚

针对对硝基苯酚环境危害大、难生物降解的特点,为克服传统Fenton适用pH范围窄的缺点,制备了CuO催化剂,并对微波耦合类Fenton氧化对硝基苯酚溶液进行了实验研究,考察了H2O2投加量、催化剂投加量、微波功率、辐照时间、溶液初始pH对PNP去除效果的影响.结果表明,在H2O2和催化剂投加量分别为0.06mol/L和0.3g/L,微波功率125W,不调节溶液初始pH(约为6)的条件下,初始浓度为50mg/L的PNP溶液反应6min去除率达92%, TOC去除63%.比较不同氧化体系,得到微波能够增大微波耦合类Fenton体系中?OH的生成量,从而提高对PNP的去除率.实验表明,CuO催化微波耦合类Fenton作为一种新型类Fenton反应,能克服传统Fenton适用pH范围窄的局限性,并且显著提高反应效率,拓展了Fenton反应在废水处理中的应用.     

负载型金属氧化物催化剂分解臭氧的研究

用浸渍法制备了活性炭、γ-氧化铝和分子筛负载的MnO2,CuO,Fe2O3催化剂,并考察了它们对臭氧分解的催化性能。结果表明,MnO2催化剂优于CuO,Fe2O3,催化剂,活性炭为载体的催化剂优于γ-氧化铝和分子筛为载体的催化剂。温度对臭氧催化分解影响很大,在90℃时,MnO2／AC催化剂对臭氧的去除率可达80％以上。当存在一定浓度的水蒸气时,湿度越大,催化性能越差。当臭氧初始质量浓度低于50mg／L时,随着臭氧初始浓度的增加,催化性能有一定的下降。