Photocatalytic degradation of L-acid by TiO2 supported on the activated carbon

Introduction Aromatic sulfonic acid, which is produced in large amounts in chemical industry since the end of 19th century, has been widely applied in many industrial processes, including the various steps of procedure (Alonso and Barcelo, 2000). Naphthalene- sulfonic acids are of importance as dye intermediates and commonly used in the textile auxiliary industry employing many azo dyes and pigments. Among them, 1-naphthol-5-sulphonic acid (L-acid) is widely used in the printing as the raw ma…     

表面活性剂光催化降解动力学研究

为了研究光催化法对不同电荷类型表面活性剂的降解性能,在紫外光照射下,用TiO2光催化剂对阴离子表面活性剂十二烷基磺酸钠(SDS)、阳离子表面活性剂十六烷基三甲基溴化铵(CTAB)和两性表面活性剂十八烷基甜菜碱(BS18)进行降解试验.同时,探讨了TiO2光催化剂加入量、表面活性剂初始质量浓度及初始pH对光降解的影响及其动力学过程.结果表明,3种表面活性剂的降解行为符合准一级动力学规律,3种表面活性剂降解速率快慢顺序为:BS18CTABSDS.SDS和BS18的最佳TiO2催化剂用量为1 g.L-1,而CTAB的最优用量为2g.L-1;CTAB和BS18的光降解速率随着活性剂初始质量浓度的增大而线性减小,SDS的降解速率则随活性剂初始质量浓度的增加而缓慢增大;CTAB和BS18在偏碱性条件下降解最快,而SDS在弱酸条件下具有最大的动力学降解速率.     

Mn/TiO2和Mn-Ce/TiO2低温脱硝催化剂的抗硫性研究

在低温选择性催化还原(SCR)反应条件下考察了烟气残余SO2对Mn/TiO2和Mn-Ce/TiO2催化剂选择性催化还原活性的影响,同时对SO2的影响机理进行了探讨.结果发现,Mn/TiO2催化剂在SO2反应气氛中失活很快,硫铵盐的沉积和活性组分的硫酸化是催化剂失活的重要原因;Ce的加入可以有效地抑制催化剂活性组分的硫酸化,同时还能降低硫酸盐在催化剂表面的稳定性,从而可以提高催化剂的抗硫性.     

CTMAB/TiO_2表面修饰膨胀珍珠岩光催化降解水中对硝基苯酚

用溴化十六烷基三甲铵(CTMAB)和/或TiO2对膨胀珍珠岩(EP)进行表面修饰,获得不同表面修饰膨胀珍珠岩(CTMAB-EP,TiO2/CTMAB-EP,TiO2-EP和EP),研究其对水中对硝基苯酚的去除效果、吸附降解动力学以及最适条件.结果表明:膨胀珍珠岩对对硝基苯酚的吸附去除能力很小,对其用CTMAB进行表面修饰或负载TiO2均可显著提高对硝基苯酚的去除率,同时负载CTMAB和TiO2的膨胀珍珠岩对对硝基苯酚的去除率最高;环境修复材料用量、振荡时间、初始ρ(对硝基苯酚)和pH等对去除效果有一定影响.膨胀珍珠岩上负载的TiO2对对硝基苯酚的光催化降解能力受pH的影响不大,表面活性剂CTMAB在pH为8时对对硝基苯酚的吸附能力较强,pH为8时修复材料对对硝基苯酚的去除效果最好.     

纳米TiO2对气相中甲醛光催化降解的研究

采用溶胶-凝胶法制备了掺杂金属离子的纳米TiO₂光催化剂,运用透射电镜和X射线衍射手段对催化剂的结构进行了表征,并将制备的光催化剂负载于不锈钢丝网、玻璃弹簧和泡沫镍板3种不同载体上,以室内空气典型污染物甲醛气体为模型反应物,研究了3种不同改性纳米TiO₂光催化剂对甲醛气体的光催化作用,3种光催化反应器的催化效率以及环境因素对光催化效率的影响,同时考察了催化剂的失活特征.结果表明:该负载型纳米TiO₂光催化剂具有较高的光催化活性,其中掺镧1.5%(质量分数)的TiO₂对甲醛的降解率最高,60 min达到91.5%,大于掺铁和掺银;泡沫镍板作为负载载体的光催化效率大于玻璃弹簧和不锈钢丝网;循环风量和不同波长紫外光对该光催化反应影响不大,反应中催化剂存在失活现象,但在清洁后能够恢复.      

附载TiO2光催化降解咪蚜胺农药

以主波长３６５ｎｍ的黑炽荧光灯为光源,研究了由ＣＭＣ－Ｎａ附载ＴｉＯ２光催化降解咪蚜胺农药的过程。结果表明,咪蚜胺农药在３＊８Ｗ黑炽荧光灯照射下,经附载ＴｉＯ２作用３ｈ后可降解５０％以上,其光解可用假一级动力学方程表示。     

纳米二氧化钛制备与表征

通过水热反应法合成出了两种纳米二氧化钛粉体材料,通过差热分析、X衍射分析、扫描电镜分析,粉体的平均直径小于100nm,通过光催化试验分析,纳米二氧化钛的光催化性能可以达到47%.     

CuO/TiO2的疏水改性及其影响因素

采用3种制备方法对纳米TiO₂催化剂进行疏水改性,以高浓度硝基苯为处理对象,在可见光照射下,研究了催化剂的疏水改性方法及其影响因素,并进行了光催化反应影响因素研究. 结果表明,滴加法和吸附法制备的催化剂具备完整的TiO₂(锐钛矿)和CuO晶体衍射峰,共沉法制备的催化剂没有TiO₂(锐钛矿)衍射峰出现;不同方法制备的催化剂对可见光吸收阈均达到900 nm;滴加法和吸附法制备的催化剂疏水位主要是长链烷基;共沉法制备的催化剂疏水位主要是短链烷基. 降解试验发现具备长链烷基的催化剂有较佳的催化能力,滴加法氮气煅烧得到的催化剂催化性能最好,2 h硝基苯去除率可达75%.      

镍掺杂二氧化钛光催化剂的制备与光催化性能研究

利用溶胶-凝胶法制备了镍掺杂的二氧化钛,采用紫外可见分光光度计、傅里叶红外分光光度计、X衍射仪(XRD)、扫描电镜(SEM)等测试手段对结果进行了表征。表征结果表明在550℃下煅烧的产物主要是锐钛型二氧化钛,镍的掺杂使得二氧化钛的紫外可见反射光谱明显红移,且镍掺杂二氧化钛的粒度减小,团聚程度下降。以活性艳蓝KN-R为模型降解目标物,通过比较镍掺杂二氧化钛、纯二氧化钛以及标准P25二氧化钛的光催化性能发现镍掺杂二氧化钛的光催化活性最好。当钛酸正丁酯/乙醇比为1:25;钛酸正丁酯/冰乙酸比为1:1;钛酸正丁酯/硝酸镍比为1 000:3;煅烧温度为550℃,煅烧时间为2 h时,镍掺杂二氧化钛的光催化效率最高,达到73.3%。     

H2O2-固载型TiO2光催化对城市污水消毒作用研究

以泡沫镍作为载体,利用电沉积技术将纳米TiO2负载在泡沫镍上,制成固载型TiO2光催化反应器,在光催化反应器中加入H2O2,研究H2O2-固载型TiO2光催化反应系统对城市污水消毒效果。试验表明,固载型TiO2光催化反应中加入10 ppm H2O2,能大大提高紫外消毒效果,降低原水浊度对紫外消毒系统的影响,同时显著减少紫外消毒系统出水光复活现象。H2O2-固载型TiO2光催化反应系统,对降低紫外消毒投资和运行成本,提高紫外消毒效果稳定性,促进城市污水紫外消毒技术的推广具有重要意义。     

H_2O和SO_2对Cr-Ce/TiO_2催化氧化NO性能的影响

采用浸渍法在最佳制备条件下制备了新型Cr-Ce/TiO2催化剂,并对催化剂进行了BET和XRD表征.同时,考察了反应温度、H2O和SO2对该催化剂催化氧化NO性能的影响,并对中毒催化剂进行了FT-IR分析,讨论了中毒机理.结果表明,Cr-Ce/TiO2催化剂具有良好的NO氧化活性,在空速为10000h-1、O2体积分数8%(φ)、NO进口体积分数700×10-6条件下,反应温度250℃时NO转化率可达到59.7%,330℃时NO转化率可达到最大值80.7%.单独加入10%(φ)H2O或300×10-6(φ)SO2都可使催化剂活性降低,但在较高温度时影响较小.330℃下单独通入SO2和同时通入H2O与SO210h后,由于催化剂表面生成了少量硫酸盐和亚硫酸盐,活性下降并维持在62.4%左右,能够满足对NOx进行高效吸收的要求;停止通入H2O和SO2后,催化剂活性恢复到71.6%,加热处理后活性能进一步恢复到78.5%.该催化剂具有比文献中报道的其它NO氧化催化剂更强的抗H2O和SO2毒化能力.     

Fe(Ⅲ)/苹果酸/H_2O_2体系对有机物的光降解特性研究

系统研究了可见光照射下染料橙黄Ⅱ在Fe(Ⅲ)/苹果酸/H2O2体系中的脱色情况,考查了光源、pH值、Fe(Ⅲ)、苹果酸、H2O2及染料初始浓度等因素对橙黄Ⅱ脱色效率的影响.结果表明,Fe(Ⅲ)/苹果酸/H2O2体系在可见光照射下能有效实现橙黄Ⅱ的脱色,在pH为5.0的条件下仍然具有较强的降解有机物的能力.该体系对橙黄Ⅱ的脱色率高于Fe(Ⅲ)/H2O2体系或Fe(Ⅲ)/苹果酸体系,光反应符合表观一级反应动力学规律.随着光强的增加,橙黄Ⅱ的脱色率增大.太阳光是该体系的有效光源,本体系具有利用太阳光的潜力.     

二氧化钛光催化降解双酚AF研究

系统研究了双酚AF在二氧化钛溶液中的光催化降解行为。就溶解氧、二氧化钛投加量、氟离子浓度和双酚AF的初始浓度等因素对双酚AF降解的影响进行了详细讨论。研究重点是双酚AF的降解动力学以及在降解过程中所产生的氟离子浓度。当双酚AF的初始浓度是40μmol/L时,经过540 min的光催化降解,反应体系的总有机碳去除率超过97%,此时溶液中氟离子的浓度为0.98 mg/L。双酚AF在二氧化钛溶液中的降解符合Langmuir-Hinshelwood动力学模型,其降解动力学常数是1.21μmol/(L·min)。结果表明,二氧化钛光催化可以有效的去除双酚AF,并且不产生其它二次污染物。     

Promotional effect of Si-doped V2O5/TiO2 for selective catalytic reduction of NOx by NH3

TiO2 supports doped with different amounts of Si were prepared by a sol-gel method, and 1 wt% vanadia (V2O5) loaded on Si-doped TiO2 was obtained by an impregnation method. The mole ratio of Si/Ti was 0.2, NOx conversion exceeds 94% at 300℃ and GHSV of 41,324 hr-1 , which is about 20% higher than pure V2O5/TiO2 . The catalysts were characterized by XRD, BET, TEM, FT-IR, NH3-TPD, XPS, H2-TPR, Raman and in situ DRIFTS. The results of FT-IR and XPS indicated that Si was doped into the TiO2 lattice successfully and a solid solution was obtained. V2O5 active component could be dispersed well on the support with the increasing of surface area of the catalyst, which was confirmed by Raman and XRD results. Above all, the numbers of acid sites (especially the Br nsted-acid) and oxidation properties were enhanced for Si-doped V2O5/TiO2 catalysts, which improved the deNOx catalytic activity.     

TiO2光催化净化城市隧道中NOx的行为及经济性

考察了TiO₂光催化降解模拟城市隧道尾气中NO_x的催化行为,并以一个长度为1km和高度为5m的双向两车道城市隧道为研究对象,分析了其应用的经济性.结果表明,煅烧温度为400℃制备的TiO₂-400催化剂的NO吸附性能和光催化性能最佳,NO_x最大转化率为30%.不同的气体组成会显著影响光催化剂对NO_x的吸附和光催化性能,其中对于NO竞争性吸附抑制效应的影响为CH₄≈CO₂>CO,而对于光催化性能的促进效应影响为CO > CH₄ > CO₂.增大紫外光辐照度可提高光催化活性,但降低了催化剂的稳定性.紫外光辐照度为6.4μW/cm²为合适的光照强度.增加催化剂的用量可显著增强NO的吸附性能和光降解NO_x的稳定性.当催化剂用量为15mg/cm²时,NO吸附容量为0.88mg/g,催化剂的稳定时间可达110min.通过简要分析该技术的经济性,表明光催化降解城市隧道NO_x的成本较低,具有良好的经济性.     

TiO2光催化膜反应器的实验研究

采用溶胶-凝胶法,分别在炻器管、不锈钢管和玻璃管内壁负载TiO₂催化剂膜,在连续式光催化膜反应器中研究TiO₂膜光催化降解水中有机物的实际应用性能.结果表明:负载于玻璃表面的TiO₂膜上出现了Na元素的渗透,而在不锈钢表面所形成的TiO₂膜层均匀度较差;利用炻器管负载TiO₂催化降解亚甲基蓝(MB)的速率常数是不锈钢管和玻璃管的2倍;反应过程中鼓气与否所得到的苯酚光催化速率常数分别为0.143和0.103min-1;溶液在管内的流速为1和9 L/min时流体的Re分别为4 000和10 000.      

O3/TiO2催化氧化工艺对饮用水中AOC的影响

以陶粒、硅胶和沸石为载体,分别负载二氧化钛（TiO₂）进行臭氧催化氧化去除硝基苯的实验,并对饮用水中生物可同化有机碳（AOC）所代表的小分子有机物(酮、醛、醇和羧酸类物质)的生成情况进行了研究.发现臭氧催化氧化比单纯的臭氧氧化能更彻底地将部分大分子有机物氧化成小分子中间产物,陶粒、硅胶和沸石负载TiO₂ 3种催化剂分别将AOC从大约300　μg·L^-1增加到 674.1　μg·L^-1、847.2　μg·L^-1和882.1　μg·L^-1,并且分别使AOC/TOC从原水的4.68%升高到30.5%、33.21%和46.04%,大大地提高了水中有机物的可生物降解性.如果增加臭氧投量,催化氧化可使小分子有机物部分被氧化,致使水样AOC又略有回降.在这一过程中,AOC-NOX所代表的羧酸类物质急剧增加,达到总AOC的90％以上,取代AOC-P17成为了AOC的主体组成部分.     

Photo-degradation of Acid-red 3B dye catalyzed by TiO2 nanotubes

Introduction A s one kind of novel functional m aterial, TiO 2 nanotube has been found potential applications in solar cell (B arbe et al., 1997), sem iconductor device (V inodgopal et al., 1993) and catalyst supports (Idakiev et al., 2005) etc. Since K a…     

染料废水在旋转式光催化反应器中的降解研究

采用旋转式光催化反应器处理染料废水,探讨染料ｐＨ值,液层厚度,反应器转速,光照时间对脱色效率的影响．结果表明,对所试染料品种,ｐＨ６为最佳值,２０ｍｉｎ为最佳反应时间．液层厚度和反应器旋转速度对半导体光催化氧化反应有一定影响．在优化条件下采用悬浮态ＴｉＯ２时,偶氮染料的脱色率为９８％,采用ＴｉＯ２器壁固定时为７８．５％～９１．５％     

Preparation of TiO2-MoO3 nano-composite photo-catalyst by supercritical fluid dry method

IntroductionTiO2 iswidelyusedinmultiphasephoto catalyticreactions ,andisalsooneofthemosteffectivecatalystsinthedegradationofenvironmentalcontaminants (Hoffmann ,1995 ;Fujishima ,2 0 0 0 ) .However,asasemiconductorofwidebandgap ,itcouldonlybeactivatedbyult…