废活性炭微波再生新工艺的研究

提出用微波加热一二氧化碳活化法再生乙酸乙烯合成用触媒载体废活性炭工艺。采用条件实验法研究了活化时间、二氧化碳流量和微波功率对活性炭碘吸附值，亚甲基蓝吸附值和再生得率的影响，得到微波辐射加热二氧化碳活化再生乙酸乙烯用触媒载体废活性炭的最佳工艺条件为活化时间25min，二氧化碳流量0．2L／min，微波功率700w。在此条件下制得的活性炭碘吸附值为1158．02mg／g、亚甲基蓝吸附值为240mv,／g、得率为74．19％。并对活性炭进行了比表面积的测定和孔结构的分析，活性炭的比表面积为1308．13m^2／g，总孔容为0．76mL／g。     

微波法对吸附扑热息痛废水活性炭的再生

通过微波加热的方式对用于扑热息痛废水的吸附的活性炭进行再生处理。考察了再生温度和再生时间两个因素对活性炭吸附性能和得率的影响。在最佳微波再生条件(温度为600℃,微波再生时间为15 min)下结果表明,活性炭在的亚甲基蓝吸附值和得率分别为187.5 mg/g和41.82%。对最佳条件下再生得到的活性炭进行孔结构表征,结果为,比表面积达947.9 m2/g,总孔体积为0.97 m L/g。中孔的比例占到71.18%说明活性炭主要以中孔为主。同时对废活性炭和再生活性炭进行了扫描电镜分析,结果表明,通过微波再生后的活性炭表面杂质明显减少。     

微波活化法制备加拿大一枝黄花活性炭及其性能表征

利用入侵植物加拿大一枝黄花为原料,采用在400℃氮气保护下,直接碳化90 min后,选择KOH为活化剂,微波活化的方法制备活性炭.研究了不同的KOH/C比值、微波功率及活化时间对活性炭吸附量及产率的影响.结果表明,最优活化条件为碱碳比2g/g、微波功率700w及微波辐射6 min,此时活性炭的亚甲基蓝吸附值、碘吸附值、...     

微波加热再生废弃的净化石油化工废水活性炭

为了对石油化工废水净化处理后的废弃活性炭实现循环利用,提出了在无保护气体和活化气体条件下进行微波加热的方法。主要评估了再生温度和再生时间对再生活性炭的吸附性能和得率的影响。结果表明,在再生温度为600℃,再生时间为15 min时,活性炭的碘吸附能力达到最大值971 mg/g,得率为82.36%。再生活性炭比表面积高达1 028m2/g,总孔体积为1.23 m L/g,平均孔径为4.89 nm。通过废弃活性炭和再生活性炭进行了SEM对比分析,再生活性炭表面杂质减少,孔隙数量明显增多。     

味精生产过程中产生的废弃活性炭的再生

为了实现味精生产过程中产生的废活性炭的循环利用,提出了在通保护气体(氮气)的情况下管式电阻炉加热的方法。本研究考察了物料的质量,再生温度和再生时间对再生活性炭的吸附性能和得率的影响。结果表明,在物料质量为10 g、再生温度为800℃、再生时间为15 min时,再生活性炭的亚甲基蓝的值为180 mg/g,得率为67.23%。再生活性炭的比表面积1 015 m2/g,总孔体积1.05 m L/g,平均孔径4.47 nm。考察了再生次数对活性炭吸附性能的影响。对废活性炭和再生活性炭进行扫描电镜分析,再生活性炭的表面杂质明显减少,孔隙数量明显增多。     

磷酸低温活化蔗渣基中孔生物炭及其影响因素

以甘蔗渣为原料,磷酸为活化剂,采用低温活化法制备蔗渣基中孔生物质炭.采用L9(34)4因素3水平正交实验,探讨制备蔗渣基中孔生物质炭的实验方案与工艺条件;分析了浸渍比、烘干时间、活化温度、活化时间在3个不同水平下,对蔗渣基生物质炭碘吸附值、亚甲基蓝吸附值的影响.结果表明,对蔗渣基生物质炭孔结构和得率影响最大的因素是活化温度,影响最小的因素是烘干时间;实验范围内,提高活化温度有利于材料中孔结构的形成;最佳条件下制备的蔗渣基生物质炭其低温氮气等温吸附线有明显的回滞环,BET比表面积和总孔容分别为939 m2/g和1.35 mL/g,中孔占总孔容比例为89％,亚甲基蓝吸附值高达240 mg/g,远高于木质净水用活性炭国家一级标准(135 mg/g),属于典型的中孔炭.     

草酸钾活化法制备榴莲壳活性炭及其表征

以榴莲壳为原料,选择K2C2O4为活化剂,在自制氛围气中进行化学活化制备活性炭。考察了活化剂/原料浸渍比、活化温度与活化时间对活性炭的碘和亚甲基蓝吸附值及得率的影响。结果表明,制备榴莲壳活性炭的理想条件为:活化剂/原料浸渍比1.5∶1、活化温度800℃和活化时间120 min;此时活性炭的SBET(BET比表面积)、总孔容和微孔孔容分别为1 195 m2/g、0.60 cm3/g和0.41 cm3/g。利用比表面和孔隙度分析仪、场发射扫描电镜(FE-SEM)和傅立叶红外光谱法(FT-IR)对活性炭的孔结构特征、微观形貌和表面官能团进行了表征。FE-SEM观测结果显示榴莲壳活性炭孔隙结构发达,且含有丰富的中孔。     

微波辐射回用活性炭对水中亚甲基蓝和Cd2＋去除效果的研究

考察了微波-活性炭联合处理技术对模拟染料废水中亚甲基蓝和Cd2＋的去除效果。对于100 mL浓度为1 000 mg/L的亚甲基蓝溶液、活性炭用量为10 g时,新活性炭对亚甲基蓝的去除率为99.99%;采用700 W微波对吸附亚甲基蓝的活性炭辐射10 min进行再生并回用,经微波辐射再生10次后活性炭对亚甲基蓝的去除率为99.68%,未经微波作用反复使用10次的活性炭对亚甲基蓝的去除率为85.41%。结果表明：微波处理有效地减缓了活性炭吸附能力的下降速率,实现了活性炭再生和反复使用。在吸附过程中,Cd2＋使活性炭对亚甲基蓝的吸附能力略有下降,而共存的亚甲基蓝则促进了活性炭对Cd2＋的吸附,对新炭和再生后活性炭物理化学特性的表征证明了活性炭对亚甲基蓝的吸附为物理吸附,对Cd2＋的吸附为化学吸附。     

微波辐射回用活性炭对水中亚甲基蓝和Cd~(2+)去除效果的研究

考察了微波-活性炭联合处理技术对模拟染料废水中亚甲基蓝和Cd2+的去除效果。对于100 mL浓度为1 000 mg/L的亚甲基蓝溶液、活性炭用量为10 g时,新活性炭对亚甲基蓝的去除率为99.99%;采用700 W微波对吸附亚甲基蓝的活性炭辐射10 min进行再生并回用,经微波辐射再生10次后活性炭对亚甲基蓝的去除率为99.68%,未经微波作用反复使用10次的活性炭对亚甲基蓝的去除率为85.41%。结果表明:微波处理有效地减缓了活性炭吸附能力的下降速率,实现了活性炭再生和反复使用。在吸附过程中,Cd2+使活性炭对亚甲基蓝的吸附能力略有下降,而共存的亚甲基蓝则促进了活性炭对Cd2+的吸附,对新炭和再生后活性炭物理化学特性的表征证明了活性炭对亚甲基蓝的吸附为物理吸附,对Cd2+的吸附为化学吸附。     

长柄扁桃核壳活性炭的制备及表征

以长柄扁桃核壳为原料采用磷酸活化法制备活性炭,分别研究了温度、时间、浸渍比和磷酸浓度对活性炭吸附性能的影响;进而采用氮气吸附曲线和SEM对最佳工艺条件下的活性炭进行了表征。结果表明,长柄扁桃核壳是一种优质的活性炭原料;当温度为400℃,活化时间2 h,浸渍比2：1,磷酸浓度60%时,得到产率为46.46%,碘吸附值和亚甲基蓝吸附值分别为1 073 mg/g、255 mg/g,比表面积高达1 740 m²/g,中孔率为73.12%的孔隙发达的高中孔率活性炭。     

微波法污水厂污泥制备活性炭的研究

研究了以污水厂污泥为原料、微波辐照下磷酸活化法制备污泥活性炭的工艺条件,探讨了微波功率、辐照时间以及磷酸浓度对活性炭碘值的影响.结果表明,微波功率480 W、辐照时间315 s、磷酸浓度40%～45%的条件下,制备的污泥活性炭碘值为301 mg/g,总孔孔容是0.37 mL/g,平均孔径8.8 nm,比表面积168 m2/g.将该污泥活性炭用于处理TNT红水,吸附效果良好.     

微波法污水厂污泥制备活性炭的研究

研究了以污水厂污泥为原料、微波辐照下磷酸活化法制备污泥活性炭的工艺条件,探讨了微波功率、辐照时间以及磷酸浓度对活性炭碘值的影响.结果表明,微波功率480 W、辐照时间315 s、磷酸浓度40%～45%的条件下,制备的污泥活性炭碘值为301 mg/g,总孔孔容是0.37 mL/g,平均孔径8.8 nm,比表面积168 m2/g.将该污泥活性炭用于处理TNT红水,吸附效果良好.     

磷酸微波活化多孔生物质炭对亚甲基蓝的吸附特性

以甘蔗渣为原料,采用微波辅助H3PO4活化法制备富含含氧酸官能团的中孔生物质炭。通过扫描电子显微镜SEM、傅立叶变换红外光谱FT-IR等技术对生物质炭物理化学性质进行表征,并通过静态实验法,探讨炭样对亚甲基蓝的吸附行为及热力学性质。结果表明,H3PO4活化制备蔗渣生物质炭的适宜条件为浸渍比1：1,烘干时间10h,活化功率900W,活化时间22min,在此条件下制得的生物质炭得率为39．2％,碘值为817mg／g,亚甲基蓝值为229mg／g,为国家一级品标准的1．7倍。红外光谱分析表明,炭样表面以羟基、羰基、羧基等酸性官能团为主。静态吸附实验表明,Freundlich方程与Redlich—Peterson方程能较好地描述等温吸附行为,表现为优惠吸附。热力学研究表明,吸附吉布斯自由能（△G0）〈0,说明吸附反应是自发过程,而吸附标准焓变（△H0）〉70KJ／mol,表明亚甲基蓝在制备炭样上的吸附是吸热反应,升温有利于吸附,且化学反应在吸附过程中发挥了重要作用。     

化学活化法制备羊骨基活性炭工艺的优化及其孔结构的表征

以氯化锌为活化剂,用羊骨为原料,利用化学活化法制备羊骨基活性炭。通过正交实验和单因素实验相结合得出最优工艺条件为:氯化锌溶液浓度0.05 g/100 mL、活化温度350℃、活化时间10 min、浸渍时间为36 h。在此最佳工艺条件下羊骨基活性炭的碘吸附量为407.35 mg/g,得率为62%;用此工艺制备的羊骨基活性炭等温曲线类型属于多层吸附;BET比表面积为59 m2/g,总孔容为0.1945 cm3/g,孔径分布落在1.31～20 nm之间,为中孔结构;羊骨基活性炭SEM图可看出,颗粒呈不规则状,结构疏松。     

Optimization of preparation process of activated carbon from chestnut burs assisted by microwave and pore structural characterization analysis

In this study, activated carbon was prepared from Chinese chestnut burs assisted by microwave irradiation with potassium hydroxide (KOH) as activator, and the process conditions were optimized employing Box-Behnken design (BBD) and response surface methodology (RSM). The optimized variables were irradiation time, impregnation time, and mass ratio of alkali-to-carbon, and the iodine adsorption value was used to evaluate the adsorption property of activated carbon. The optimal preparation conditions were determined as follows: irradiation time 17 min, impregnation time 240 min, and mass ratio of alkali-to-char 1.5:1. Meanwhile, the relatively high iodine adsorption value (1141.4 mg/g) was also obtained. Furthermore, the pore structural characterization of activated carbon was analyzed. The analyzed results showed a larger Brunauer-Emmett-Teller (BET) specific surface area (1254.5 m²/g) and a higher microporosity ratio (87.2%), a bigger total pore volume (0.6565 m³/g), but a smaller average pore size (2.093 nm), which demonstrated the obtained activated carbon possessed strong adsorption capacity and well-developed microporous structure. This research could not only establish the foundation of utilizing chestnut burs to prepare activated carbon, but also provide the basis for exploitation of Chinese chestnut by-products.

Implications: Because Chinese chestnut burs are the by-products and usually discarded upon harvesting subsequently, the utilization of chestnut burs as a potential source of activated carbon is of great profit to the chestnut processing industries.     

微波法制备污泥活性炭研究

采用微波加热法,以污水厂剩余污泥为原料,磷酸为污泥活化剂制备污泥活性炭.微波功率、辐照时间和磷酸浓度对污泥活性炭吸附性能具有显著影响,在最佳工艺条件微波功率480 W、辐照时间315 s和磷酸浓度40%条件下制得的活性炭碘值301 mg/g,比表面积168 m2/g,污泥中重金属绝大部分被固化.与传统商品炭相比,污泥炭孔隙结构以中孔为主.利用该活性炭处理城市生活污水处理厂出水,COD去除率可达87%以上,污泥炭的吸附等温线用Langmuir等温吸附模型进行描述.     

污泥活性炭对次甲基蓝废水的吸附

立足于污泥的资源化,利用化学活化法制得的污泥基活性炭,处理次甲基蓝染料废水.考察了污泥活性炭的粒径以及染料废水的pH值对染料脱色效果以及活性炭的吸附量的影响,并对吸附过程进行等温吸附线和吸附动力学分析.结果表明,在本研究的范围内,污泥活性炭的粒径越小、染料废水的pH值越高,则污泥活性炭对染料废水的吸附效果越好.当粒径在200目以上时,去除率及吸附量分别为88.2％和136.7 mg/g;当pH值为11时,去除率和吸附量分别为90.4％和91.9 mg/g.污泥活性炭对次甲基蓝染料的吸附脱除符合Langmuir吸附等温线和Lagergren准二级动力学方程.     

高比表面积活性炭的制备及对Cr(Ⅵ)吸附的研究

以椰树壳为原料,运用水蒸汽和二氧化碳复合物理活化法在4 h内制备了2 162.84 m2/g的高比表面积活性炭,其孔径分布范围为1.1~2.5 nm。应用此吸附剂考察了溶液pH、吸附剂用量、接触时间和初始浓度对Cr(VI)离子吸附效果的影响,并讨论了固定吸附床中不同溶液流量对Cr(VI)去除效果的影响。结果表明:在温度为298 K、溶液pH为1.96、吸附剂用量为0.10 g、铬离子初始浓度为100 mg/L与接触时间为70 min的条件下,活性炭对铬离子具有较高的吸附容量,去除率高达99.32%;铬离子在吸附床中的穿透曲线具有陡峭的传质锋面,但随着铬离子溶液流量的增大脱除果率降低。     

Preparation of activated carbon using low temperature carbonisation and physical activation of high ash raw bagasse for acid dye adsorption

Activated carbons were prepared from bagasse through a low temperature (160 degrees C) chemical carbonisation treatment and gasification with carbon dioxide at 900 degrees C. The merit of low temperature chemical carbonisation in preparing chars for activation was assessed by comparing the physical and chemical properties of activated carbons developed by this technique to conventional methods involving the use of thermal and vacuum pyrolysis of bagasse. In addition, the adsorption properties (acid blue dye) of these bagasse activated carbons were also compared with a commercial activated carbon. The results suggest that despite the high ash content of the precursor, high surface areas (614-1433 m2 g(-1)) and microporous (median pore size from 0.45 to 1.2 nm) activated carbons can be generated through chemical carbonisation and gasification. The micropore area of the activated carbon developed from chars prepared by the low temperature chemical carbonisation provides favourable adsorption sites to acid blue dye (391 mg g(-1) of carbon). The alkalinity of the carbon surface and total surface area were shown to have complementary effects in promoting the adsorption of acid blue dye. Adsorption of the anionic coloured component of the acid dye was shown to be promoted in carbon exhibiting alkaline or positively charged surfaces. This study demonstrates that activated carbons with high acid dye adsorption capacities can be prepared from high ash bagasse based on low temperature chemical carbonisation and gasification.     

稻壳基活性炭的制备及其对亚甲基蓝吸附的研究

以稻壳为原料,采用K2CO3活化法和H3P04活化法制备了比表面积为1312m^2／g和682m^2／g的活性炭,通过扫描电子显微镜（SEM）、X-射线衍射仪（XRD）对样品进行了表征,并将孔隙发达的活性炭样品用于对亚甲基蓝的吸附,结果表明,K2CO3活化法制备的活性炭样品具有更多的微孔结构;随着亚甲基蓝溶液初始浓度的增加、活性炭吸附时间的延长,亚甲基蓝的去除率呈现逐渐降低和逐渐增大的变化规律,当pH值为6时,活性炭对亚甲基蓝的吸附效果最佳;稻壳基活性炭对亚甲基蓝的吸附等温线符合Langmuir模型,Qm最高可达476．2mg／g;热力学参数△G^0△H^0和△S^0均为负值,表明稻壳基活性炭对亚甲基蓝的吸附是一个自发的放热反应。